• Journal of the Korean Wood Science and Technology
• /
• v.35 no.1
• /
• pp.44-50
• /
• 2007

The objective of this study was to investigate the influence of the vehicle resin on the coating performance of Dan-Chung. The starch glue (F), fish glue (G), and aqueous acrylic resin emulsion (E) were used as vehicle resins. Panels coated with Dan-Chung were tested at accelerated weathering and outdoor conditions. Aqueous acrylic resin was proved as an excellent vehicle resin for Dan-Chung, because there was no flaking in Dan-Chung film after accelerated weathering and outdoor exposure. Discoloration of Dan-Chung using E was the smallest among the acceleratedly weathered panels. Adhesive property of Dan-Chung film using G was. remarkably improved by G-undercoating. On the contrary, G-undercoating lowered adhesive property of Dan-Chung film using E.

• Proceedings of the KAIS Fall Conference
• /
• 2009.12a
• /
• pp.659-662
• /
• 2009

본 연구는 건축자재로 널리 사용되는 PVC 바닥상재 표면의 오염성 및 정전기로부터 보호하기 위하여 기존에 사용하는 광경화형 우레탄-아크릴 수지에 내오염/대전성을 향상시킨 광경화형 내오염 코팅액 개발에 관한 것이다. PVC 바닥상재용으로 사용되는 내오염성이 없는 우레탄-아크릴 수지에 4가 암모늄을 사용한 수용성 대전방지제와 아크릴용 대전방지제, 폴리우리탄용 대전방지제를 수지의 양 대비 함량(wt%) 5~20%로 변화하여 첨가한 후 1000rpm에서 30분간 고속 배합하여 수지의 내오염/대전성을 향상시킨 내오염 코팅액을 제조하였다. 제조한 내오염 코팅액은 코팅 층의 두께조절이 가능한 코팅(Bar-coating)을 사용하여 PVC 바닥상재에 코팅 한 후 내오염성, 대전성, 부착력, 코팅두께 등의 코팅 층 표면물성을 평가하였다. 연구결과, 수지에 수용성대전방지제 15%를 혼합하여 제조한 코팅액을 Bar-coater No.12로 코팅한 코팅표면이 전기저항($3.24{\times}10^9{\Omega}/cm^2$), 내오염도(매직 Test, 먼지부착 Test) 및 부착력(100%) 모두 가장 좋은 물성을 보였으며, 전반적으로 함량이 많을수록 전기저항과 오염도에서 우수한 것으로 나타났다. 그러나 대전방지제가 과량으로 들어간 경우 migration 현상이 보이는 것을 알 수 있었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.214-215
• /
• 2006

Colloidal Silica(CS)와 유기수지를 혼합하여 서로의 단점을 보완하는 나노복합재료를 합성하기 위해 친수성인 CS를 유기실란으로 표면처리하여 소수성화하고 유기수지와 복합체를 제조하였다. CS표면의 -OH기와 실란의 -OH기가 축합반응하여 화학결합을 형성함으로서 CS의 표면은 실란의 $CH_3$에 의해 소수성화되어 CS sol이 제조된다. CS sol과 유기수지는 공동용매에 의해 균일한 분산이 가능하고 필름 및 코팅제로의 제조가 가능하다. 사용된 무기물은 40nm 의 크기를 가지므로 가시광선영역의 빛을 산란하지 않아 투명하고 사용된 수지 또한 투명하여 우수한 광학적 특성을 나타낸다. 만들어진 필름은 CS의 영향으로 유기수지의 내열성보다 향상된 열분해온도와 높은 접촉각, 높은 절연율을 보였다.

• Korean Chemical Engineering Research
• /
• v.54 no.1
• /
• pp.120-126
• /
• 2016

Eco-friendly acrylic resin/clay nanocomposites containing pristine montmorillonite (PM) or modified clays (30B and 25A) were prepared from acrylic and styrenic monomers using non-aqueous dispersion (NAD) polymerization. Effect of nanoclays on physical properties of polymerization product and resulting nanocomposites was investigated. In view of NAD particle stability, addition of nanoclay at the beginning of polymerization is proved to be good. Results of gel fraction, acid value and viscosity of the NAD product showed that nanocomposites containing clay 25A showed better physical properties than the ones with other clays. GPC results exhibit the increase in molecular weight and decrease in polydispersity index for the 25A nanocomposite. Increase in layer distance confirmed from XRD analysis showed good dispersion of 25A in the nanocomposite. Thermal and dynamic mechanical analysis showed that highest glass transition temperature and storage modulus for 25A nanocomposites. These results indicate that 25A nanoclay gives the best properties in the process of non-aqueous dispersion polymerization of acrylic resin/nanoclay nanocomposites.

• Elastomers and Composites
• /
• v.33 no.5
• /
• pp.324-334
• /
• 1998

SBR, polyurethane, acryl and epoxy latex were seperately mixed with ethylene-vinylacetate emulsion(EVA) in the range of $0{\sim}50%$ (wt.% ). For the mixtures, the various physical properties were examined. The viscosity of mixtures was mainly influenced by compatability with EVA emulsion, was decreased within 20% (wt.% ) of latex content, and showed the similar values over 20% (wt.% ) of latex content. The workable time of cement mixtures was mainly depended on the reactivity with cement. The formation of film could be only within $30{\sim}40$ minutes from mixing cement. The tack-free time of mixtures was influenced by the sorts of resin and the quantity of cement. The slow order of tack-free time was epoxy mixtures>SBR mixtures>urethane mixtures>acryl mixtures. The pencil hardness of mixtures was $4B{\sim}2H$, represented higher value in cement mixtures than in emulsion state.

• Polymer(Korea)
• /
• v.30 no.4
• /
• pp.350-356
• /
• 2006

In order to investigate the effect of the composition of weather-resistant coatings on physical properties, three different weather-resistant coatings were prepared by varying the ratio of a mill-base silicone/acrylic resin and let-down silicone/acrylic resin in weight ratios of 2 : 8, 3 : 7, and 4 : 6. The physical properties and weather-resistance of the prepared coatings were tested. It was found that the thermal stability, salt spray exposure, and weather-resistance were improved with increasing the amount of silicone. The optimum mixing ratio of mill-base silicone/acrylic resin to the let-down silicone/acrylic resin was 2 : 8. The coating containing silicone component of 30 wt% was found to be suitable as high weather-resistant coatings.

• Elastomers and Composites
• /
• v.35 no.3
• /
• pp.196-204
• /
• 2000

SBR, polyurethane, acryl and epoxy latex were separately mixed with ethylene -vinylacetate emulsion(EVA) in the range of $0{\sim}50wt%$. For the mixtures, the various physical properties such as defoamerability, mechanical property, and water resistance were experimentally examined. The excellent defoamer was BYK-021 and the appropriate use of it was 0.3 phr for the total components. The shrinkage of compounds was influenced by the compatability of resins and the formation of voids. The mechanical properties was related to the cohesive force of resin particles, the coagulation of cement particles and the co-bonding of resin particles with cement particles. Mixing latex separately showed better properties then non-mixing in the shrinkage ratio, flexural strength, adhesive strength, and impact strength. The water resistance of composites mixed with cement was worse than that of EVA resin.

• Polymer(Korea)
• /
• v.30 no.3
• /
• pp.230-237
• /
• 2006

Copolymers(HSA-98-20, HSA-98-0, HSA-98+20) which we acrylic resin containing 80% solid content were synthesized by the reaction of monomers, including methyl methacrylate, n-butyl acrylate, and 2-hydroxyethyl acrylate with a functional monomer, acetoacetoxyethyl methacrylate (AAEM), which nay give improvements in cross-linking density and physical properties of films. The physical properties of prepared acrylic resins, containing AAEM, are as follows viscosities, $1420\sim5760cps$ ; number average molecular weight, $2080\sim2300g/mol$; polydispersity index, $2.07\sim2.19$ ; and conversions, $88\sim93%$. In the next step, high-solid coatings (HSA-98-20C, HSA-98-0C, HSA-98+20C) were prepared by the curing reaction between acrylic resins containing 80% solid content and isocyanate at room temperature. Various properties were examined on the film coated with the prepared high-solid coatings. The introduction of AAEM to the coatings enhanced the abrasion resistance and solvent resistance, which indicated the possible use of high- solid coatings for top-coating materials of automobile. Since the curing by viscoelastic measurement occurred in sequence of HSA-98+20C > HSA-98-0C > HSA-98-20C, it was concluded that the curing rates became faster with incresing $T_g$ values.

• International Journal of Highway Engineering
• /
• v.11 no.3
• /
• pp.1-11
• /
• 2009

This study focuses on evaluating the applicability of an acryl based polymer concrete to the thin bridge deck pavements. The acryl concrete developed in this study is composed of Methyl Methacrylate(MMA) resin, benzol peroxide and fillers. To study the effects of the types and amounts of the components on the physical characteristics of the acryl concrete, viscosity, compressive strength and bending tests were conducted. The optimum mixture design was then determined based on the testing results. Several different types of laboratory tests, such as water and chlorine ion penetration tests, shrinkage and thermal coefficients tests, and tensile bonding strength tests were performed for the optimum acryl concrete and conventional cement concrete. The testing results show that water and chroline ion resistance, bonding strength between acryl and cement concrete and crack resistance of the acryl concrete is better than those of the conventional cement concrete. There are shortcomings that the conventional acryl concrete has a higher shrinkage and thermal coefficients. However, it was confirmed that to use newly developed rubberized MMA resin in this study reduces the crack resistance with substantially increased ductility.

• Journal of Adhesion and Interface
• /
• v.18 no.4
• /
• pp.159-165
• /
• 2017

In this study, we synthesized UV-curable urethane acrylates with different contents of BA, reactive diluent and characterized their physical properties such as thermal, mechanical properties, adhesive strength and flexibility resistance. From a result of DSC, Tg of polyol and acrylate resin were separated as the BA content increased more than 40%. Also, tensile strength, elongation and adhesive strength decreased with increasing the BA content. The UV-curable urethane acrylate with 40% BA has shown good flexibility resistance compared to other resin due to poor hardness and Tm of acrylate resin.