• Korean Chemical Engineering Research
• /
• v.55 no.2
• /
• pp.247-252
• /
• 2017

Hydrophilic coating solutions were prepared by reacting a silane coupling agent, aminosilane with colloidal silica (15~20 nm in diameter). Hydrophilic coating films were also obtained by depositing the hydrophilic coating solutions on polycarbonate substrates by dip-coating and subsequently by thermal curing at $120^{\circ}C$. During this process, the effect of types of aminosilane was studied on the properties of coating films. As a result, coating films, prepared with 3-aminopropyltriethoxysilane (APTES) as aminosilane, showed contact angles of $25{\sim}44^{\circ}$ and a poor pencil hardness of B. On the other hand, coating films, prepared with 3-aminopropyltrimethoxysilane (APTMS) as aminosilane, exhibited contact angles of $26{\sim}37^{\circ}$ and a good pencil hardness of 2H.

• Applied Chemistry for Engineering
• /
• v.27 no.1
• /
• pp.35-38
• /
• 2016

In this study, the mica used as a thermal-insulation material was modified with a silane coupling agent, octyltriethoxysilane (OTES), to improve its hydrophobicity. The modified mica was characterized using FT-IR spectrometer, water wettability test, and water contact angle measurement. The analysis exhibits that OTES for the modified mica sample was well bonded chemically and drastically enhanced the hydrophobicity. The reflectance observed as 73.9% (mica) and 86.4% (OTES/mica), respectively, for OTES/mica was improved about 12.5% before any modifications. Also the modified mica sample showed $7.2^{\circ}C$ decrease in the thermal-insulation performance of cool paints compared to that of using unmodified mica, indicating that the modification of mica with silane coupling agents could be effective in enhancing the thermal-insulation performance of the cool paint.

• Korean Chemical Engineering Research
• /
• v.50 no.2
• /
• pp.191-197
• /
• 2012

Acrylic terminated polyurethane prepolymers were synthesized by capping the NCO groups of polyurethane prepolymers, prepared from isophorone diisocyanate (IPDI), polycarbonate diol (PCD) and dimethylol propionic acid (DMPA), with pentaerythritol triacrylate (PETA). Subsequently, silylated acrylic terminated prepolymers were prepared by capping the NCO groups of acrylic terminated polyurethane prepolymers with different types of silane coupling agents, glycidoxypropyl trimethoxysilane (GPTMS) or aminopropyl triethoxysilane (APS). The average particle size of pure waterborne polyurethane solution, measured by the dynamic light scattering method, was increased from 14.3 nm to 208.6 nm by adding PETA and APS. Also, the coating film of silylated acrylic terminated waterborne polyurethane showed better abrasion resistance and pencil hardness than that of pure waterborne polyurethane.

• Applied Chemistry for Engineering
• /
• v.25 no.5
• /
• pp.520-525
• /
• 2014

In this paper, the effect of silane-treated silicas and epoxidized soybean oil (ESBO) addition on adhesion properties of silicas-filled epoxy adhesives was examined. The silicas were treated by ${\gamma}$-methacryloxy propyltrimethoxy silane (MPS), ${\gamma}$-glycidoxy propyl trimethoxy silane (GPS), and ${\gamma}$-mercapto propyl trimethoxy silane (MCPS). Surface and structural properties of the adhesives were determined by using scanning electron microscope (SEM) and Fourier transform infrared spectroscopy (FT-IR). The t-peel strength of the adhesives was estimated using the universal testing machine (UTM). And, the equilibrium spreading pressure, surface free energy, and specific surface area were investigated by BET methods with $N_2$/77 K adsorption. As a result, the peel strength of the adhesives was increased in the presence of silane-treated silicas in the adhesives compared to that of untreated silicas. This result indicated that the silane coupling agent played an important role in improving the dispersion of silicas in epoxy adhesives. And, the adhesives treated by MCPS were superior to the others in adhesion.

• Polymer(Korea)
• /
• v.37 no.3
• /
• pp.308-315
• /
• 2013

In this study, we performed surface modification of silica nanoparticles with bis[3-(triethoxysilylpropyl)]tetrasulfide (TESPT) silane coupling agent to study the effects of treatment temperature, treatment time, and amount of TESPT used on the silanization degree with Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), elemental analysis (EA) and solid state $^{13}C$ and $^{29}Si$ cross-polarization magic angle spinning (CP/MAS) nuclear magnetic resonance spectroscopy (NMR). We found peak area of isolated silanol groups at $3747cm^{-1}$ decreased, but peak area of $-CH_2$ asymmetric stretching of TESPT at $2938cm^{-1}$ increased with the amount of TESPT from FTIR measurements. We also used universal testing machine (UTM) to study mechanical properties of styrene butadiene rubber (SBR) nanocomposites with 20 phr (parts per hundred of rubber) of pristine and TESPT modified silicas, respectively. The tensile strength and 100% modulus of modified silica/SBR nanocomposite were enhanced from 5.65 to 9.38MPa, from 1.62 to 2.73 MPa, respectively, compared to those of pristine silica/SBR nanocomposite.

• Journal of the Korean Applied Science and Technology
• /
• v.36 no.2
• /
• pp.531-540
• /
• 2019

Hydrophilic and hydrophobic nanosilica and tetraethyl orthosilicate (TEOS) as a coupling agent was used to form a coarse spike structure as well as an excellent reactive hydroxyl groups on the glass surface. Then, a second treatment was carried out using a trichloro-(1H,1H,2H,2H)perfluorooctylsilane(TPFOS) solution for ultimate water repellent glass surface formation. The formation of hydrophobic coating layer on glass surface using silica aerosol, which is hydrophobic nanosilica, was not able to form a durable hydrophobic coating layer due to the absence of reactive -OH groups on the surface of nanosilica. On the other hand, a glass surface was first coated with a coating liquid prepared with hydrophilic hydroxyl group-containing nanosilica and hydrolyzed TEOS, and then coated with a TPFOS solution to introduce a hydrophobic surface on glass having a water contact angle of $150^{\circ}$ or more. The sliding angle of the coated glass was less than $1^{\circ}$, which meant the surface had a super water-repellent property. In addition, as the content of hydrophilic nanosilica increased, the optical transmittance decreased and the optical transmittance also decreased after 2nd coating with the TPFOS solution. The super-hydrophobic property of the coated glass was remained up to 50 times of rubbing durability test, but only hydrophobic property was shown after 200 times of rubbing durability test. Conclusively, the optimal coating conditions was double 1st coatings with the HP3 coating solution having a hydrophilic nanosilica content of 0.3 g, and subsequent 2nd coating with the TPFOS solution. It is believed that the coating solution thus prepared can be used as a surface treatment agent for solar cells where light transmittance is also important.

• Korean Chemical Engineering Research
• /
• v.46 no.2
• /
• pp.310-315
• /
• 2008

Organic-inorganic hybrid solutions were made using glycidoxypropyl trimethoxysilane (GPTMS) and vinyltriethoxysilane (VTES) as starting materials by sol-gel method. Photochromic coating solutions were prepared by mixing the solution of photochromic dye (spiropyran) dissolved in ethylacetate with the organic-inorganic hybrid solutions. Photochromic films were prepared on polycarbonate sheets by spin coating and cured for 2 h at $100^{\circ}C$. The resulting films exhibited a reversible color change upon irradiation with UV light from transparent to blue. The color-fading speed and pencil hardness of the coating films increased with increasing the GPTMS content in the coating solutions.

• Polymer(Korea)
• /
• v.36 no.1
• /
• pp.16-21
• /
• 2012

Organic-inorganic hybrid coating film using 1,2-bis(2,4-dimethyl-5-phenyl-3-thienyl)-3,3,4,4,5,5-hexafluoro-1-cyclopentene (BTHFC) as a photochromic material was prepared under various reaction conditions such as the amounts of tetramethoxysilane (TMOS), various silane coupling agents, and solvent. It was found that color-fading speed and absorbance of the coating film was strongly dependent upon the polarity of silane coupling agent and solvent. In addition, the mole ratio of TMOS and methacryloyloxypropyltrimethoxysilane (MPTMS) was an important factor to determine color-fading speed and absorbance of the coating film. With increasing TMOS contents in coating film, the pencil hardness was increased. On the other hands, the transmittance of coating film was relatively decreased with the increase of TMOS.

• Applied Chemistry for Engineering
• /
• v.9 no.4
• /
• pp.608-613
• /
• 1998

The purpose of this experiment was the physical properties of rubber compounds with DPCB and pure carbon black. Si-O peak in the silcia surface was observed at the range of wavenumber from 1,100 to 1,200 in the DPCB by FT-IR analysis. Cure rate of rubber compounds containing DPCB and organic silane coupling agent were (Si69) delayed compared with those containing pure carbon black. 300% modulus and interaction coefficient of DPCB with silane coupling agent were higher than those of pure carbon black and PICO weight loss amount showed constant value. It was found that $0^{\circ}C$ tan$\delta$ of rubber compounds with DPCB was larger than those of pure carbon black at 2.0% silane coupling agent based on 50 phr DPCB and $60^{\circ}C$ tan$\delta$ of rubber compounds with DPCB decreased as increasing the usage coupling agent. Consequently, it is postulated that DPCB is strong candidate material for lowering rolling resistance under constant abrasion resistance.

• Composites Research
• /
• v.24 no.6
• /
• pp.18-24
• /
• 2011

The effect of surface treatments with the atmospheric pressure flame plasma (APFP) and epoxy silane (ES) is experimentally investigated to yield the best mechanical properties of silica ($V_f=40%$) reinforced elastomeric composites. The tensile strength of the composites is increased significantly with decrease the mean diameter. When the diameter is $2.2{\mu}m$, that of the composite is increased about 1.4 times compared to the matrix (2.52 MPa). Also, the tensile strength of silica reinforced composites with APFP and ES treated is increased 8.8~13.3%, 9.9~12.5%, respectively. When the diameter is $26.6{\mu}m$, the tensile modulus of the composite is increased about 2 times compared to the matrix (0.88MPa), and the tensile modulus of silica reinforced composites with APFP and ES treated is increased 15.6~22.8%, 21.1~5.8%, respectively. Conventional silane coupling agent treatment have a few disadvantages because of using organic solvents. However APFP treatment is a fast, economic and eco-friendly method to improve the mechanical properties.