• International Journal of Highway Engineering
• /
• v.9 no.4
• /
• pp.93-104
• /
• 2007

This study evaluates the mechanical properties of steel fiber reinforced porous concrete for pavement according to content of slag aggregate and fly ash to elicit the presentation of data and the way to enhance its function for the practical field application of porous concrete as a material of pavement. As a result, void ratio and permeability coefficient of porous concrete for pavement increased a little as mixing rate of slag aggregates increased. Void ratio and permeability coefficient increased a lot as mixing rate of fly ash decreased. As fly ash was mixed, national regulation of permeable concrete for pavement(8% and 0.1 cm/sec) was met. Compressive strength and flexural strength decreased as mixing rate of slag aggregates increased, but they increased a lot as mixing rate of fly ash increased. Even when slag aggregates were mixed 50% with 5% fly ash mixed, national regulation of pavement concrete(18MPa and 4.5MPa) was met. In addition, compared to non-mixture, flexural strength increased about 22.8% when 0.75vol.% of steel fiber was added. Regarding sliding resistance, BPN increased as mixing rate of slag aggregates increased. But BPN decreased as fly ash was mixed. Compared to crushed stone aggregates, abrasion resistance and fleers-thaw resistance decreased as mixing rate of slag aggregates increased. When fly ash was mixed, abrasion resistance and freeze-thaw resistance improved remarkably. Compared to non-mixture, 10% mixture of fly ash improved abrasion resistance and freeze-thaw resistance about 5.6% and 14.3 respectively.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.41 no.4
• /
• pp.341-345
• /
• 2021

Known to improve resistance to chloride ingress, blast furnace slag is a widely used supplementary cementitious material. However, a detailed characterization of cements blended with slag exposed to seawater remains unavailable. This study employs thermodynamic modeling as a toolkit for assessing the long-term phase evolution of slag cement in seawater. The modeling result shows that slag incorporation leads to the formation of phases that are less prone to structural alteration in seawater. Formation of more ettringite is expected to induce expansion in both plain and blended cements, while brucite is unstable in the blended systems. Despite this, the porosity is expected to increase in the blended cements, and aluminate hydrates with a higher chloride binding capacity are more abundant in the blended cements. The results suggest that the use of slag in concrete improves the durability performance of concrete in marine environments.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.2
• /
• pp.152-160
• /
• 2021

Converter steel slag(BOF slag) is a vast amount of solid waste generated in the steelmaking process which has very low utilization rate in Korea. Due to the presence of free CaO which can derive bad volume stability in BOF slag, it usually land filled. For recycling BOF and identify its applicability as fine aggregate, this study investigates the fundamental characteristics of mortar with cement replaced ferronickel slag(FNS), which has the potential to be used as a binder. The results suggest that the mineral phases of BOF slag mainly include larnite(CaSiO₄), mayenite(Ca₁₂Al₁₄O₃₃) and wuestite(FeO) while olivine crystallines are shown in FNS. The results of flow and setting time reveals that the flowability and process of hardening increased when the amount of FNS and BOF slag incorporated was increased. The length change shows that the amount of change in the length of the mortar was almost constant regardless of mix proportion while compressive strength was reduced. Micro structure test results revealed that FNS or/and BOF slag mix took a long time to react in the cement matrix to form a complete hydration products. To achieve the efficient utilization of B OF slag as construction materials, proper replacement rate is necessary.

• Resources Recycling
• /
• v.18 no.4
• /
• pp.31-37
• /
• 2009

The purpose of this study was to evaluate the effects of fly-ash and blast-furnace slag on strength development and durability of ternary blended concrete (TBC) and ordinary portland cement concrete as fly ash and slag contents. Main experimental variables were performed fly ash contents (0%, 10%) and slag contents (0%, 10%, 20%, 30%). The compressive and flexural strengths, chloride-ion rapid permeability and chemical attacks resistance were measured to analyze the characteristic of the developed TBC on hardened concrete. The test results showed that compressive and flexural strength of TBC increased as the slag contents increased from 0% to 30% at the long term of curing. It considers blast furnace slag used when fly ash content was up to 10%. The permeability resistance of TBC(fly ash 10%, blast 30%) was extremely good at the curing time 90 days. Also, the effects of added blast furnace slag on OPC and TBC were increased on the permeability and chemical attacks resistance.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.3
• /
• pp.79-87
• /
• 2011

Concrete incorporating high volume blast-furnace slag placed in cold weather regions might be in danger of initial frost damage because dependently on the mix proportions, the setting and the hardening would be remarkably delayed. Therefore, this study investigated to effect of the degree of frost on the strength development and the resistance to freezing and thawing of the concrete incorporating blast-furnace slag when being subjected to freeze at early age. As the experimental results, the concrete incorporating blast-furnace slag attacked by initial frost damage showed the remarkable reduction of both the compressive strength development and the resistance to freezing and thawing. Especially, the resistance to freezing-thawing of the concrete incorporating high volume blast-furnace slag became much lower than that of the normal concrete.

• Journal of the Society of Disaster Information
• /
• v.9 no.4
• /
• pp.469-475
• /
• 2013

The purpose of this experimental research is to estimate compressive strength and resistance to freezing and thawing of recycled aggregate concrete containing ground granulated blast furnace slag. For this purpose, concrete specimens according to substitution ratio of recycled aggregate were made for different replacement ratio of ground granulated blast furnace slag(GGBFS), and then compressive strength and resistance to freezing and thawing were evaluated for those. It was observed from the test results that compressive strength at 28 days of recycled aggregate concrete containing GGBFS of 20% was much more excellent than plain concrete and when air content of concrete was maintained 4 to 6%, influence of substitution ratio of recycled aggregate and replacement ratio of GGBFS on resistance to freezing and thawing was little up to 300 cycles of freezing and thawing.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.1
• /
• pp.1-7
• /
• 2020

GGBFS(Ground Granulated Blast Furnace Slag) is one of the most actively used mineral admixtures with excellent long-aged strength and chloride diffusion resistance. Unlike Standard covering GGBFS in Japan and the U.K., the domestic standard for GGBFS does not contain low fineness of GGBFS under 4000 grade. In this paper, several basic tests are carried out for the concrete with 3,000 grade GGBFS concrete and ternary blended concrete for reducing hydration heat by mixing 4,000 grade GGBFS and fly ash, such as fresh concrete properties, compressive strength, and shrinkage properties. The air content and slump between the ternary blended concrete and the concrete with low-fineness GGBFS showed the similar level, and the results of difference in setting time from them were less than 20 minutes, showing no significant difference. In the evaluation of compressive strength and shrinkage characteristics, the ternary blended concrete showed lower long-aged strength and higher shrinkage than the low-fineness GGBFS concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.5
• /
• pp.189-196
• /
• 2007

The purpose of this study was to analyze steel corrosion resistance of concrete containing copper slag. The specimens were made with normal portland cement and pozzolan materials with various replacement ratio and with W/B ratio ranging from 35% to 55%. Compressive strength, coefficient of chloride diffusion, corrosion area ratio and weight reduction ratio were determinated for the test. The results show that the concrete with pozzolan materials is superior resistant to chloride ions compared to the concrete without pozzolan materials. It was observed that blast furnace slag replacement ratio of 20% gives the best results with respect to chloride ion penetration and corrosion tests and observed that copper slag replacement ratio of 10% gives the seperior resistance compared to normal concrete.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.267-275
• /
• 2018

This study is to investigate the effect of various temperature and humidity conditions on the strength and efflorescence of alkali activated slag cement(AAS) using the red mud. As a result of examining the strength and efflorescence characteristics of AAS mixed with red mud according to the curing conditions, The compressive strength and flexural strength were the highest at 28 days, but the absorption rate, efflorescence area and soluble $Na^+$ elution were lowest in standard wet curing compared to the air curing, high temperature curing and low temperature curing.

• Journal of the Korea Concrete Institute
• /
• v.14 no.2
• /
• pp.164-170
• /
• 2002

Effect of the polymer-binder ratio and slag content on the properties of combined wet/dry-cured polymer-modified mortars using granulated blast-furnace slag are examined. Results shows that the flexural and compressive strengths of polymer-modified mortar using the slag tend to increase with increasing slag content, and reaches a maximum at a slag content of 40 ％, and is inclined to increase with increasing polymer-binder ratio. Water absorption, carbonation depth and chloride ion penetration depth tend to decrease with increasing polymer-binder ratio and slag content. Accordingly, the incorporation of slag into polymer-modified mortars at a slag content of 40％ is recommended for a combined wet/dry curing regardless of the types of polymer.