• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.4
• /
• pp.443-449
• /
• 2022

When fiber reinforced concrete is manufactured, it is useful to utilize lathe scrap as an aiternative material of steel fiber, because it is not only economical as an by-product of steel manufactures, but also has a very similar composition to that of steel fiber. The purpose of this experimental research is to evaluate the compressive strength and tensile behavior and then propose a material model of lathe scrap reinforced mortar. For this purpose, the lathe scrap reinforced mortars were ma de a ccording to their tota l volume fra ction of 1.5 % for wa ter-binder ra tio of 30 % a nd 40 %, respectively, a nd then the mechanical properties such as compressive strength, direct tensile strength, and stress-strain curve of those were evaluated. Also, based on the experimental results of lathe scrap reinforced mortar the material model for tensile behavior was suggested. It was revealed that the experimental results and the proposed material model corresponded relatively well.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.6
• /
• pp.40-45
• /
• 2016

It should be noted that the use of the lathe scrap for making fiber reinforced cementitious composites raised friendly environmental effect as well as economy because the lathe scrap is a by-product of steel manefactures and is occurred when lathe and milling works of them are conducted to process steel manufactures. Thus, the purpose of this experimental research is to investigate workability and strength characteristics of lathe scrap reinforced cementitious composites(LSRCCs). For this purpose, three types of lathe scraps were collected from processing plants of metal, and then LSRCCs containing these were made for 2mm width and 40mm length. As a result, it was observed from the test results that the workability of LSRCCs was slightly decreased than plain mortar and the flexural strength of LSRCCs were much larger than these of plain mortar and effect of types of lathe scrap on the characteristics of LSRCCs were somewhat large.

• Journal of the Society of Disaster Information
• /
• v.10 no.3
• /
• pp.432-441
• /
• 2014

The purpose of this research is to investigate characteristics of lathe scrap for manufacturing fiber reinforced cementitious composites(FRCCs) to use lathe scrap as a alternative materials of steel fiber. It should be noted that the use of the lathe scrap for making FRCCs raised friendly environmental effect as well as economy because the lathe scrap was a by-product of steel manufactures. For this purpose, various steel scraps were collected from processing plants of metal and then their physical properties were evaluated. Also, steel scraps were classified and analyzed according to the KS D 2101 and then of these scraps, lathe scrap as a alternative materials of steel fiber was suggested. In addition, FRCCs containing lathe scraps were made according to their total volume fractions of 0.0, 0.5, 1.0, 1.5, and 2.0% for water-binder ratios of 30%, 40%, respectively, and then characteristics, such as the workability, compressive strength, and flexural strength of those were evaluated. It was observed from the test result that the compressive strengths at 7 and 28 days of FRCCs containing lathe scrap were slightly small but the flexural strengths at 28 days of those increased by 10% compared with plain concrete.

• Magazine of RCR
• /
• v.13 no.1
• /
• pp.21-27
• /
• 2018

• Journal of the Korean Society for Advanced Composite Structures
• /
• v.6 no.2
• /
• pp.70-76
• /
• 2015

It should be noted that the use of the lathe scrap for making fiber reinforced cementitious composites(FRCCs) raised friendly environmental effect as well as economy because the lathe scrap is a by-product of steel manufactures and is occurred when lathe and milling works of them are conducted to process steel manufactures. Thus, the purpose of this research is to investigate the effect of measurements of lathe scrap on the characteristics of FRCCs. For this purpose, various lathe scraps were collected from processing plants of metal, and then these were processed 10mm, 20mm, and 40mm in lengths for 2mm and 4mm in widths, respectively. FRCCs containing lathe scraps were made according to their widths and lengths, and then characteristics such as the workability, compressive strength, and flexural strength of those were evaluated. As a result, it was observed from the test results that the optimum measurements of the lathe scrap for manufacturing FRCCs was 2mm in width and 40mm in length.