• Applied Chemistry for Engineering
• /
• v.31 no.2
• /
• pp.215-219
• /
• 2020

In this study, nanoporous iron oxide layers were fabricated by the anodization of 304 series stainless steel. K₂HPO₄/glycerol solution was used as an electrolyte for anodization. We investigated the anodization behavior according to various parameters such as electrolyte concentration, reaction temperature, applied voltage, and reaction time. As a result of anodization, we confirmed that the anodic growth rate of oxide layer on 304 series stainless steel increased with increasing the electrolyte temperature and applied potential. In order to form well-ordered porous nanostructures, the electrolyte temperature was at 160 ℃, and the applied potential was at 30 V in 10 wt% K₂HPO₄/glycerol electrolyte.

• Journal of the Korean Electrochemical Society
• /
• v.14 no.4
• /
• pp.196-200
• /
• 2011

The formation of niobium oxide microcones on niobium substrates was investigated in NaF to the HF electrolytes. This condition builds on the uniqueness of the microstructures niobium oxide. The dimensions and integrity of the bulk microstructures were found to be strongly dependent on potential, temperature, electrolyte composition, and anodization time. The anodic oxide was initially amorphous at all temperatures, but crystalline oxide nucleated during anodization. From XRD patterns of the anodized specimens, the microcones consisted of crystalline $Nb_2O_5$. We demonstrated niobium oxide microcone structures with nanorods. The anodized niobium oxide microcone texture revealed nanorod bundles. The surface of $Nb_2O_5$ microcones is very regular and has a nano-scale. The surface morphologies of the nanorods were examined using FE-SEM. EDS analyses show that the anodically prepared niobium oxide consists of $Nb_2O_5$. The aim of this study is to find the condition of forming the favorable nanorods by anodization method.

• Journal of the Korean Ceramic Society
• /
• v.41 no.12 s.271
• /
• pp.900-906
• /
• 2004

Solid oxide fuel cells have a limitation in their low-temperature application due to the low ionic conductivity of electrolyte materials and difficulties in thin film formation on porous gas diffusion layer. These problems can be solved by improvement of ionic conductivity through controlled nanostructure of electrolyte and adopting nanoporous electrodes as substrates which have homogeneous submicron pore size and highly flattened surface. In this study, ultra-thin oxide films having submicron thickness without gas leakage are deposited on nanoporous substrates. By oxidation of metal thin films deposited onto nanoporous anodic alumina substrates with pore size of $20nm{\sim}200nm$ using dc-magnetron sputtering at room temperature, ultra-thin and dense ionic conducting oxide films with submicron thickness are realized. The specific material properties of the thin films including gas permeation, grain/gran boundaries formation, change of crystalline structure/microstructure by phase transition are investigated for optimization of ultra thin film deposition process.

• Clean Technology
• /
• v.20 no.1
• /
• pp.7-12
• /
• 2014

Hydrogenolysis of glycerol to propylene glycol was performed over binary and ternary metal oxide catalysts. The conversion of glycerol and selectivity to propylene glycol were increased on Cu/Zn and Cu/Cr mixed oxides compared to pure CuO and ZnO oxides. The addition of alumina into Cu/Zn mixed oxide very highly increased the conversion of glycerol and selectivity to propylene glycol. The conversion of glycerol was increased with increasing the reaction temperature but the selectivity to propylene glycol was shown to have maximum value at $200^{\circ}C$ and then decreased at $250^{\circ}C$. The conversion of glycerol and selectivity to propylene glycol were decreased with increasing the glycerol concentration.

• Journal of the Korean Applied Science and Technology
• /
• v.33 no.2
• /
• pp.401-410
• /
• 2016

The $Pt-Sn/Al_2O_3$ catalysts mixed with metal oxides for propane dehydrogenation were studied. $Cu-Mn/{\gamma}-Al_2O_3$, $Ni-Mn/{\gamma}-Al_2O_3$, $Cu/{\alpha}-Al_2O_3$ was prepared and mixed with $Pt-Sn/Al_2O_3$ to measure the activity for propane dehydrogenation. As standard sample, $Pt-Sn/Al_2O_3$ catalyst mixed with glassbead was adopted. In the case of catalytic activity test after non-reductive pretreatment of catalyst and metal oxide, $Pt-Sn/Al_2O_3$ mixed with $Cu-Mn/{\gamma}-Al_2O_3$ showed higher conversion of 15% and similar selectivity at $576.5^{\circ}C$, compared to conversion of 8% in standard sample. In the case of catalytic activity test after reductive pretreatment of catalyst and metal oxde, $Cu/{\alpha}-Al_2O_3$ showed higer yield than standard sample. But, increase of yield of most of samples after reductive pretreatment was not significant, so it was found that lattice oxygen of $Cu-Mn/{\gamma}-Al_2O_3$ is effective to propane dehydrogenation.

• Information Display
• /
• v.13 no.3
• /
• pp.11-18
• /
• 2012

보호막으로서 우수한 성능을 발휘하여 왔던 MgO 박막을 대체하여, 고 Xe 방전 개스에서 방전 전압이 낮고, 높은 방전 효율을 나타낼 수 있는 차세대 보호막의 개발 현황에 대하여 간략하게 살펴보았다. 차세대 보호막은 1) FCC와 같은 등방성 결정 구조를 가져야 하고, 2) band gap 에너지가 작아야 하며, 3) 수화물 및 탄산염이 쉽게 분해되는 산화물이어야 하고, 4) 재료내에 비 화학 당량 결함이 많은 천이 금속 산화물과 같이 결함이 많아서는 되지 않아야 하고, 5) 이온간의 결합력이 커서 내 스퍼터링 특성이 우수하여야 하는 조건을 만족하여야 한다. 이러한 특성을 만족시킬 수 있는 것으로 다양한 재료가 개발되어 왔으나, 실용적으로 적용 가능성이 있는 것으로(Mg,Ca)O 합금 보호막이 가능한 것으로 판단된다.

• Proceedings of the KAIS Fall Conference
• /
• 2011.12a
• /
• pp.367-369
• /
• 2011

본 연구에서는 글리세롤과 우레아를 이용하여 글리세롤카보네이트를 합성하는 반응을 진행하였다. ZnO와 Zn-Al 이원계 금속 산화물 촉매를 제조하고, 제조되어진 촉매를 사용하여 글리세롤의 전환율과 글리세롤카보네이트의 수율을 확인하였고, Al의 첨가에 따른 촉매 특성의 분석과 글리세롤카보네이트 합성반응에서의 역할에 대해 확인하였다. 글리세롤카보네이트 합성 반응에서 ZnO를 단독으로 촉매를 사용한 경우보다 Zn-Al 혼합 산화물을 촉매로 사용하여 반응하였을 때, 부반응이 억제되어 전환율 및 수율이 증가함을 확인하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.310-310
• /
• 2013

본 연구에서는 Titanium (Ti) source/drain 전극 접합이 차세대 비정질 InGaZnO (IGZO) 기반 박막형 트랜지스터에 미치는 영향을 화학적, 구조적, 전기적 특성 분석을 통하여 관찰하고 Ti/IGZO 접합 특성을 설명할 수 있는 메커니즘을 제시하였다. IGZO 기반 박막형 트랜지스터 소자의 구동 특성은 transmission line method (TLM) 패턴 공정을 이용하여 정량적으로 분석되었다. 비정질 IGZO 기반의 박막형 트랜지스터에서 Ti source/drain 전극 접합에 의한 구동 특성 변화 및 영향을 확인하기 위하여 금속/산화물 계면 반응성이 낮은 silver (Ag) source/drain 전극이 reference로 비교되었으며, 그 결과 Ti source/drain 전극 접합이 적용된 비정질 IGZO 트랜지스터의 경우 Ti 금속과 IGZO 산화물 계면에 형성되는 열역학적으로 안정한 $TiO_x$ 층의 형성에 의해 VT ($-{\Delta}0.52V$) shift 및 saturation mobility ($8.48cm^2$/Vs) 상승됨을 확인하였다. 뿐만 아니라 TLM 패턴을 이용한 IGZO 트랜지스터의 전기적 변수 도출 및 수치적 해석으로부터 $TiO_x$ 계면층 형성이 Ti 금속과 비정질 InGaZnO 계면에서의 effective contact resistivity를 효과적으로 낮출 수 있음을 확인하였다. Ti source/drain 전극 접합에 의해 발생되는 $TiO_x$ 계면층의 화학적, 구조적 특성과 $TiO_x$ 계면층 생성에 의한 소자 특성 변화를 연관시켜 해석함으로써, IGZO 기반 박막형 트랜지스터에서의 Ti source/drain 전극 접합이 비정질 IGZO 기반 박막형 트랜지스터에 미치는 영향을 설명하였다.

• Applied Chemistry for Engineering
• /
• v.26 no.5
• /
• pp.521-525
• /
• 2015

Graphene-based electrode materials have been widely explored for supercapacitor applications due to their unique two-dimensional structure and properties. In particular, Three-dimensional (3D) graphene materials are of great importance for preparing electrode materials because they can provide large surface area, efficient and rapid electron and ion transfer, and mechanical stability. Recently, a number of 3D hybrid architecture of graphene/metal oxides have been developed to increase simultaneously energy and power densities of supercapacitors. This review presents the recent progress of 3D nanocomposites based on graphene and metal oxides. Preparation methods and structures of these 3D nanocomposites and their great potential in supercapacitor applications have been summarized.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.114.1-114.1
• /
• 2017

불용성 전극이 고속 전기도금 공정에 사용되기 위해서는 전기화학 반응이 우수하고, 높은 내구성을 가져야 한다. 불용성 전극의 내구성은 기지층 표면전처리, 금속산화물 조성, 코팅층 두께, 소결 온도 등 다양한 전극제조 공정인자들에 의해 영향을 받는다. 본 연구에서는 불용성 전극의 내구성을 향상시키기 위해 전극 전처리 및 백금족 산화물 조성비의 공정변수로 전극을 제조하였고, 가속수명평가법을 사용하여 전극의 내구성을 평가하였다. 고속 전기도금 공정환경에서는 이리듐(Ir)계 및 탄탈륨(Ta)계 산화물 조성을 가지는 불용성전극의 내구수명이 우수한 경향을 나타내었으며, 귀금속 산화물 코팅층 두께가 얇을수록 불용성전극의 내구수명은 크게 저하되었다. 또한, Ir-Ta 조성 불용성전극의 경우 내구성 향상 기지체 표면전처리를 통해 전극의 내구수명이 10배 이상 향상되었음을 확인하였다.