• Journal of the Korea Concrete Institute
• /
• v.14 no.6
• /
• pp.851-863
• /
• 2002

Corrosion products of reinforcement in concrete induce pressure to the adjacent concrete due to the expansion of steel. This expansion causes tensile stresses around the reinforcing bar and eventually induces cracking through the concrete cover The cracking of concrete cover will adversely affect the safety as well as the service life of concrete structures. The purpose of the this study is to examine the critical corrosion amount which causes the cracking of concrete cover. To this end, a comprehensive experimental and theoretical study has been conducted. Major test variables include concrete strength and cover thickness. The strains at the surface of concrete cover have been measured according to the amount of steel corrosion. The corrosion products which penetrate into the pores and cracks around the steel bar have been considered in the calculation of expansive pressure due to steel corrosion. The present study indicates that the critical amount of corrosion, which causes the initiation of cracking, increases with an increase of compressive strength. A realistic relation between the expansive pressure and average strain of corrosion product layer in the corrosion region has been derived and the representative stiffness of corrosion layer was determined. A concept of pressure-free strain of corrosion product layer was introduced to explain the relation between the expansive pressure and corrosion strain. The proposed theory agrees well with experimental data and may be a good base for the realistic durability design of concrete structures.

• Journal of the Korea Concrete Institute
• /
• v.22 no.6
• /
• pp.867-873
• /
• 2010

This study investigated the corrosion properties of reinforced concrete with the addition of steel fibers. The transport properties of steel fiber-reinforced concrete such as permeable void, absorption by capillary action, water permeability and chloride diffusion were first measured to evaluate the relationship with the corrosion of steel rebar. Test results showed a slight increase on the compressive strength with the addition of steel fibers as well as considerable improvement of penetration resistance to mass transport of harmful materials into concrete. The addition of steel fibers in reinforced concrete accelerated the initiation of steel corrosion contrary to the expected results based on the measured transport properties. The NaCl ponding surface showed the spalling failure due to the corrosion expansion of steel fibers and the cut-surface around the steel rebar showed the localized steel fiber's corrosion. The wet-dry cycling with high chloride ions as well as high temperature seems to induce the increase of salt crystallization on the pores continually and the increased pressure with the steel fiber's corrosion on the pores caused the spalling failure on the exposed surface. The microcracking on the surface therefore accelerated the movement of water, chloride ions and oxygen into the embedded steel rebar. The mechanism affecting corrosion of embedded steel reinforcement with steel fibers in this study are not yet fully understood and require further study comprising of accurate experimental design to isolate the effect of steel fiber's potential mechanism on the corrosion process.

• Composites Research
• /
• v.33 no.5
• /
• pp.251-255
• /
• 2020

In this study, TiC ceramic particulate reinforced steel composites was fabricated using a liquid pressing infiltration process. Studies were conducted on microstructure analysis and basic physical properties such as hardness and corrosion characteristics in salt water environment for comparison with commercial nodular cast iron. As a result of comparison of corrosion characteristics in a salt water environment, both corrosion potential and corrosion current density were lower than that of ductile graphite cast iron. The lower calculated corrosion rate confirms that the TiC-Fe metal composite has superior corrosion resistance than the cast iron.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.3
• /
• pp.681-686
• /
• 2017

Degradation is commonly observed in field-aged PV modules due to corrosion of the photovoltaic ribbon. The reduced performance is caused by a loss of fill factor due to the high series resistance in the PV ribbon. This study aimed to mitigate the degradation by corrosion using five sacrificial anodes - Al, Zn and their alloys - to identify the most effective material to mitigate the corrosion of the PV ribbon. The corrosion behavior of the five sacrificial anode materials were examined by open circuit potential measurements, potentiodynamic polarization tests, and galvanic current density and potential measurements using a zero resistance ammeter. Immersion tests for 120 hours were also conducted using materials and damp heat test tests were performed for 1500 hours using 4 cell mini modules. The Al-3Mg and Al-3Zn-1Mg sacrificial anodes had a low corrosion rate and reduced drop in power, making then suitable for long-term use.

• International Journal of Highway Engineering
• /
• v.10 no.3
• /
• pp.149-158
• /
• 2008

This study was estimated on performance of deicers, corrosion inhibitors and low corrodible deicer used for removal of snow or ice on the road and on influence on structure. The weight loss rate after freezing and thawing of low corrodible deicer is lower than one of deicer, corrosion inhibitors and these combination. Relative dynamic elastic modulus of all except water, low corrodible deicer and NaCl+JF-1004 was radically reduced after freezing and thawing 150 cycles. And concretes after freezing and thawing were showed severe surface damage. It was found that individual use of low corrodible deicer and corrosion inhibitors had a problem of field application because of lack of early ice melting effect and considerably low durability. Products combined with NaCl was showed rapid weight loss by metal corrosion. Therefore, It will need to circumspectly select combination of deicers having low effect on concrete pavement and bridge if possible.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.309-312
• /
• 2008

This paper describes ultimate load tests which were performed to show the effects of prestress loss and tendon corrosion on the flexural strength of post-tensioned concrete beams and the occurrence of wire fracture. Five test specimens were fabricated in laboratory with the variations of the prestress of tendons and the loss of tendon area. For two specimens, small area of tendon at the center of the beam was exposed by using diameter 25mm drill and the exposed tendon was corroded using accelerated corrosion equipment. During the tests, deflections, crack width, and strain changes were measured and acoustic events were monitored with two acoustic sensors. Tests results show that the ultimate flexural strength of test specimens with corroded tendons is smaller than the predicted flexural strength which is calculated considering the loss of tendon area. It is considered that estimation of flexural strength of PSC beams with corroded tendons is very complicated just based on the loss of tendon area obtained by one-side visual inspection.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.28 no.5
• /
• pp.563-570
• /
• 2015

The existing research on the damage detection method for building structures has considered the damages from the excessive loadings such as the earthquake. However, the structural performance of building structures could be reduced due to the deterioration based on the chloride, carbonation during the long-term time. Thus, to effectively manage the healthiness of structures, the deterioration influences on the structures should be checked. In this study, the corrosion of rebars by the chloride is considered as the deterioration factor. To consider the structural performance reduction of the corroded rebars, the yield strength, cross-sectional area, rupture strain of rebars and the compressive strength of cover concrete based on the corrosion level are estimated. These properties of rebars and cover concrete are used for the procedure to evaluate the structural performance reduction of structural member level and the building level. The moment-curvature analysis is performed to evaluate the structural performance reduction of structural member level. Also, the eigenvalue analysis and the pushover analysis are performed to investigate the natural period and mode shape and the strength and deformation performance of buildings, respectively.

• Journal of the Korea Concrete Institute
• /
• v.16 no.4 s.82
• /
• pp.451-458
• /
• 2004

This study describes the basic concept and the applicability of Hybrid Reinforcement System using conventional steel reinforcing bars and Fiber Reinforced Polymer bars. The concrete bridge decks are assumed to be supported by beams and reinforced with two layers of reinforcing bars. In concrete bridge deck using HRS, the top tensile force for negative moment zone on beam supports is assumed to be resisted by FRP reinforcing bars, and the bottom tensile force for positive moment zone in the middle of hem supports is assumed to be resisted by conventional steel reinforcing bars, respectively. The FRP reinforcing bars are non-corrosive. Thus, the steel reinforcement is as far away as possible from the top surface of the deck and protected from intrusion of corrosive agent. HRS concrete bridge deck has sufficient ductility at ultimate state as the following reasons; 1) FRP bars have lower elastic modulus and higher ultimate strain than steel re-bars have, 2) FRP bars have lower ultimate strain if provided higher reinforcement ratio, 3) ultimate strain of FRP bars can be reduced if FRP bars are unbonded. Test results showed that FRP and HRS concrete slabs are not failed by FRP bar rupture, but failed by concrete compression in the range of ordinary reinforcement ratio. Therefore, in continuous concrete bridge deck using HRS, steel reinforcing bars for positive moment yield and form plastic hinge first and compressive concrete fail in the bottom of supports or in the top of the middle of supports last. Thus, bridge deck consumes significant inelastic strain energy before its failure.

• Journal of the Korea Concrete Institute
• /
• v.20 no.6
• /
• pp.681-687
• /
• 2008

This study presents a technique to quantitatively measure the corrosion level of a reinforcing bar using infrared thermography system. We found out electric heating method having an important effect on thermal data in previous study. This study purposed an efficient way for grip standardization to reduce constriction resistance problem, and providing reliable thermal data using infrared thermographic method. Using vise type earth clamp, the surface resistance of rebar was smaller than that of traditional plier type earth clamp through temperature-distribution relationship. Also this study contains experiments with toque wrench to improve heating contact problem.

• Clean Technology
• /
• v.24 no.4
• /
• pp.339-347
• /
• 2018

In order to cope with environmental problems and climate change caused by fossil fuels, renewable energy supply is increasing year by year. Currently, waste energy accounts for 60% of renewable energy production. However, waste has a lower calorific value than fossil fuels and contains various harmful substances, which causes serious problems when applied to power generation boilers. In particular, the chlorine in the waste fuel increases slagging and fouling of boiler heat exchangers, leading to a reduction in thermal efficiency and the main cause of high temperature corrosion, lowering facility operation rate and increasing operating cost. In this study, the high temperature corrosion experiments of superheater materials (ASME SA213/ASTM A213 T2, T12 and T22 alloy steel) by alkali chlorides were conducted, and their corrosion characteristics were analyzed by the weight loss method and SEM-EDS. Experiments show that the higher the temperature and chloride content, the more corrosion occurs, and KCl further corrodes the materials compared to NaCl under the same condition. In addition, the higher the chromium content of the material, the better the corrosion resistance to the alkali chlorides.