• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.3
• /
• pp.514-526
• /
• 1992

본 연구에서는 Taguchi 방법에 사용된 직교배열 이용 실험 계획법에 의한 최 적화 방법으로 보강된 복합재 쉘 구조의 좌굴강도 최적화를 수행하고 타당성을 고찰하 였다.한 방향의 압축하중을 받는 단순 지지된 복합재 평판과 Cut-out을 가진 원통 형 판넬의 보강재 및 섬유방향 최적 설계에 본 방법을 적용시켜 본 결과, 현저한 설계 개선과 아울러 각 설계 변수가 좌굴강도에 미치는 영향을 파악할 수 있었다. 특히 이 방법은 함수의 미분값을 이용한 민감도 해석대신에 함수값의 평균치 분석(ANOM)및 분산 분석(ANOVA)을 사용하기 때문에 설계변수의 변화에 덜 민감한 설계를 얻을 수 있 다.

• Composites Research
• /
• v.23 no.6
• /
• pp.7-13
• /
• 2010

Type3 cylinder is a composite pressure vessel fully over-wrapped with carbon/epoxy composite layers over an aluminum liner, which is the most ideal and safe high pressure gas container for CNG vehicles due to the lightweight and the leakage-before-burst characteristics. During service in CNG vehicle, if a fiber cut damage occurs in outer composite layers, it can degrade structural performance, reducing cycling life from the original design life. In this study, finite element modeling and analysis technique for the composite cylinder with fiber-cut crack damage is presented. Because FE analysis of type3 cylinder is path dependant due to plastic deformation of aluminum liner in autofrettage process, method to introduce a crack into FE model affect analysis result. A crack should be introduced after autofrettage in analysis step considering real circumstances where crack occurs during usage in service. For realistic simulation of this situation, FE modeling and analysis technique introducing a crack in the middle of analysis step is presented and the results are compared with usual FE analysis which has initial crack in the model from the beginning of analysis. Proposed analysis technique can be used effectively in the evaluation of influence of damage on composite layers of type3 cylinder and establish inspection criteria of composite cylinder in service.

• Composites Research
• /
• v.17 no.6
• /
• pp.52-57
• /
• 2004

In this study, mechanical tensile properties of carbon fiber reinforced polymeric (CFRP) composite cycled with thermo-mechanical loading under cryogenic temperature (CT) were measured using cryogenic environmental chamber. Thermo-mechanical tensile cyclic loading (up to 10 times) was applied to graphite/epoxy unidirectional laminate composites far room temperature (RT) to $-50^{\circ}C$, RT to $-100^{\circ}C$ and RT to $-150^{\circ}C$. Results showed that tensile stiffness obviously increased as temperature decreased while the thermo-mechanical cycling has little influence on it. Tensile strength, however, decreased as temperature down to CT while the reduction of strength showed little after CT-cycling. For the analysis of the test results, coefficient of thermal expansion (CTE) of laminate composite specimen at both RT and CT were measured and the interface between fiber and matrix was observed using SEM images.

• Composites Research
• /
• v.30 no.6
• /
• pp.331-337
• /
• 2017

The composite lattice structures have advantages of high specific stiffness and strength and are mainly applied to the structures of launch vehicles that carry the compressive load. However, since these structures are manufactured by filament winding technology, there are some defects and voids found in the knots. For these reasons, the stiffness and strength of the lattice structures have to be compared with finite element model for predicting design load. But, the full scale test is difficult because time and space are limited and the shape of structure is complex, and hence the simple and reliable test methods for examination of stiffness are needed. In this paper, subelements of composite lattice structures were prepared and compressive and bending test were conducted for examination of stiffness of helical and hoop rib. Test methods for subelements of composite lattice structures that has curved and twisted shape were supposed and compared with finite element analysis results.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.46 no.6
• /
• pp.471-478
• /
• 2018

Static tests of the composite wing structure were performed to verify damage tolerance design. Both 5 cases of DLLT and 3 cases of DULT were completed to meet requirements for static strength. After inducing BVID and open hole damages on the critical areas of the composite wing based on associated regulations, the DULT and fracture test were performed. In major wing parts, the measured strains and displacements agreed well with those of structural analysis. The initial structural fracture occurred at the area having minimum margin of safety as expected by analysis. As a result, it was confirmed that results from analytic model and strength evaluation were similar to behaviors of the composite wing structure.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.1 no.2
• /
• pp.1-11
• /
• 1997

During hydroproof test of composite pressure vessel, acoustic emission signal was measured and analyzed to evaluate structural integrity of composite motor case. When pressure was held for 1 min. at constant pressure from low pressure level to high pressure level, the pattern of hit rate of good composite pressure vessel is increased with higher value than that of bad composite pressure vessel. This report also presents detection possibility of burst location approximately in the range of 25∼36％ of burst pressure using energy rate. In case that it is difficult to detect burst location of composite motor case, it is possible to detect burst location, i.e. structurally weak location of composite pressure vessel with applying same pressure lower than maximum expected operating pressure(MEOP) repeatedly.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.3
• /
• pp.313-318
• /
• 2001

To establish nondestructive test method for aerospace composite materials, various composite specimens were tested and analyzed using acoutic emission. The hit rate of acoustic emission closely was rotated with crack initiation and propagation. This report also presents defection capability of crack initiation pressure, initial crack active location, and crack propagation using acoustic emission.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2012.05a
• /
• pp.403-407
• /
• 2012

The purpose of this study is to find the optimum skirt size for a composite pressure vessel using optimum analysis technique. The size optimization for skirt shape of a composite pressure vessel was conducted using sub-problem approximation method and batch processing codes programmed by APDL(ANSYS Parametric Design Language). The thickness and length of skirt part were selected as design variables for the optimum analysis. The objective function and constraints were chosen as weight and displacement of skirt part, respectively. The numerical results showed that the weight of skirt of a composite pressure vessel would be saved by maximum 4.38% through the size optimization analysis for the skirt shape.

• Composites Research
• /
• v.36 no.3
• /
• pp.154-161
• /
• 2023

This study explored the feasibility of replacing a metal link with a carbon fiber/epoxy composite link and assessed its capacity to withstand a given load condition using failure criteria. The micromechanics of failure (MMF) criterion was employed to predict the failure mode of the composite material, and mechanical tests were conducted to obtain reference strength parameters for MMF. The findings revealed that the stress distribution was concentrated near the hole, and weaknesses were found around the hole and at the end of the link under bending conditions. Based on the failure index, matrix tensile failure was predicted at the end of the link, and fiber compression failure occurred near the hole. The methods and results obtained from this study can provide valuable guidelines for assessing the safety of composite materials under specific load conditions when replacing metal parts with carbon fiber/epoxy composites to achieve weight reduction.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.1
• /
• pp.55-60
• /
• 2010

The honeycomb composite joint structure designed for application to a tilting KTX railroad car body is subjected to bending loads of a cantilever type. Honeycomb sandwich composite panel-joint attached in the real tilting car body was fabricated and sectioned as several beam-joint specimens for the bending test. The fracture behaviors of these specimens under static loads were different from those under cyclic loads. Static bending loads caused shear deformation and fracture in the honeycomb core region, while fatigue cyclic bend loading caused delamination along the interface between the composite skin and the honeycomb core, and/or caused a fracture in the welded part jointed with the steel under-frame. These fracture behaviors could occur in other industrial honeycomb composite joints with similar sub-structures, and be used for improving design parameters of a honeycomb composite joint structure.