• Journal of the Korea Institute of Building Construction
• /
• v.17 no.2
• /
• pp.127-134
• /
• 2017

In this study, moist curing equipment was used in the exist gang-form system. By achieving sufficient spray curing, the quality of the concrete was improved and the cracking occurred in building's side wall was decreased. The following results could be made as the conclusion. For the compressive strength, all zones showed the similar results. Comparing with the zone without using moist curing equipment, the zone used moist curing equipment showed higher rebound hardness results. For the cracking, the zone utilized moist curing equipment showed the cracking averaged as 6.6 m and the zone without using moist curing equipment showed the cracking averaged as 10.3m. The effectof reducing cracking by utilizing moist curing equipment is about 36 %. Using moist curing equipment is considered as a good solution to reduce the cracking in the structure. Considering all the factors analysed, using moist curing equipment improved the quality of the concrete and decreased the cracking. When this equipment was used in the construction site, it is expected that the construction periodcan be shrunk and the ratio of defect caused by drying shrinkage can be decreased. In this research conditions, The 0.3mm sized moist curing equipment provided the most desirable results on concrete quality and preventing cracking.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.7 no.3
• /
• pp.203-212
• /
• 1987

The hydration and strength of concrete are affected by curing conditions, especially curing temperature. In this paper, the hydration temperature of heated curing concrete specimen are measured by thermo-couples instead of conduction calorimeter, and strengths of concrete are tested. The results of this study show that the compressive strengths of concrete are especially dependent on the curing temperature. And the strength results of concrete agree approximately with the results of approach to the hydration process of cement concrete.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.05b
• /
• pp.31-34
• /
• 2011

In this study, for the evaluation of field application of low heat concrete using high volume mineral admixture, the characteristics of hydration heat generation and engineering properties of low heat concrete was investigated by mock-up test according to the replacement ratio of mineral admixture. Also, it was evaluated the compressive strength of low heat concrete with curing temperatures and ages for effective concrete mix design considering seasonal change.

• Cement
• /
• s.189
• /
• pp.41-48
• /
• 2011

고로시멘트는 포틀랜드시멘트와 고로슬래그의 혼합시멘트로, 최근에는 특히 저탄소 녹색성장 환경에 우수한 시멘트로서 관심이 모아지고 있다. 1824년 영국의 연와공 조셉 아스프딘(Joseph Aspdin)에 의해 발명된 포틀랜드시멘트는 약 184년의 역사를 가지고 있는 반면에, 일본의 슬래그시멘트 역사는 작년이 탄생부터 정확히 100년이 되기 때문에, 잠시 그 역사의 일부를 돌이켜 생각해 보고자 한다. 최근 슬래그시멘트는 건설시장에서 보통포틀랜드시멘트와 경쟁하기 위하여 발열억제를 위한 저발열고로시멘트를 개발하고, 강도경쟁에 의한 품질안정을 위하여 분리분쇄 추진, 고로슬래그에 적합한 클링커를 개발하고, 자기 수축 저감 등을 위한 연구도 병행하고 있다. 날로 심화되는 건설환경에서 살아 남기 위한 여러 방법들이 강구되고 있는 것이다. 고로시멘트는 보통포틀랜드시멘트와 비교해서 중성화, 강도발현을 위한 충분한 습윤양생 등 몇 가지 약점도 있지만, 슬래그시멘트 본연의 고유의 특성을 잘 나타내는 내해수성, 내염성, ASR 등의 장점들도 않고 "환경에 뛰어난" 시멘트로 각인된 만큼, 갖고 있는 특징들을 충분히 잘 활용하고, 개선 보완 시켜나가면 21세기의 최상의 재료로 평가 받을 수 있다고 기대해 본다. 끝으로, 본 자료는 신일철고로시멘트(주)단(檀)이 기고한 (콘크리트공학 2010년 10월호) 논문을 요약 발췌한 것이다.

• 전기의세계
• /
• v.22 no.2
• /
• pp.75-86
• /
• 1973

본 연구에서는 전기온돌의 안방열손실을 감소시키고 축열효과를 향상시키기 위한 방법을 검토하였으며 전기온돌에서 발생하는 진동소음을 감살시킬 수 있는 대책을 제시하였다. 저육들은 6.6[m$^{2}$] 크기의 전기온돌 model을 이용하여 건물의 구조차이와 하향열단열층의 설치유무에 따른 보온특성의 차이를 기록분석하였으며 그 결과 열전도계수가 0.03[kcal/m.hr.deg. C]정도인 내열성 Styropol과 지석 Mortar로 구성된 하향열단열층을 전기온돌의 마닥에 설치할 경우 난방부하의 감소로 인하여 축열효율이 약 2배나 향상된다는 결론을 얻었다. 또한 전기온돌공사시에 발열선을 지지할 수 있는 대각선형 Spacer를 설치하고 발열선이 매설콘크리트가 완전히 양생된 이후에 전력을 인가하면 흔히 전기온돌에서 발생하는 120-960[Hz]의 가청진동소음을 방지할 수 있다는 사실을 실험적으로 확인하였다.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2009.04a
• /
• pp.315-318
• /
• 2009

본 논문에서는 해상 기초 교각 매스 콘크리트의 수화열 저감 방안을 다루었다. 저발열 콘크리트, Mesh형 거푸집 공법 등에 대한 실험을 수행하여 각각의 수화열 저감효과를 평가하였다. 현장 실험은 사용 시멘트와 거푸집의 종류, 거푸집의 사용 면수에 따라 총 4 type으로 구성하였으며, 이에 대한 실험 결과와 유한 요소 해석 결과를 비교, 검증하여 최종적인 수화열 저감 성능을 도출하고자 하였다. 실험을 통해, 저발열 시멘트와 유로폼을 사용하는 것이 수화열 저감을 위해 효과적인 방법으로 판명되었으나 추가 공사비의 발생으로 효율성이 떨어질 것으로 판단된다. 또한 Mesh형 거푸집 적용 면 수와 온도 상승 저감 효과는 비례하는 것을 알 수 있었지만 내 외부 온도차가 다소 크게 나타나 수화열에 의한 균열 발생 확률면에서는 다소 불리하게 나타났다. 그러나 실험 단계에서 생략된 양생과 관리를 통하여 균열의 저감효과를 거둘 수 있을 것으로 판단되며, 추가적으로 거푸집 해체 단계를 생략함으로 공기단축 측면에서 유리할 것으로 판단된다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.359-360
• /
• 2009

This Study is performed Mock-up test accounting for height of placement to review behavior of mass concrete according to kinds of cement & form. First, we measured hydration heat and show a different hydration heat generation characteristics as compared with each other. And we measured mortar outflow, the strength of concrete core and standard specimens, concrete's ability to resist chloride ion penetration in order to durability estimation of concrete. This study was aims to improve quality of mass concrete under marine environment.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.1
• /
• pp.67-76
• /
• 2016

Concrete exposed to severely low temperature below $-20^{\circ}C$ should be provided with proper heat supplying curing to protect the concrete from early frost damage at the time of pouring.meanwhile, so far, effective heat curingmethods of the concrete under severely low temperature are not well established in Korea. For this reason, the objective of this paper is to provide effective heat curingmethod of concrete exposed to severely low temperature to protect early frost damage by varying the combination of heat curingmaterial combinations. Temperature history,maturity development and core strength results are investigated. Fourmock-up specimens simulating slab, wall and column were prepared and heat insulation, heat supplying and both were applied. Test results indicate that the combination of quadruple layer bubble sheet(4BS) and embedding of heating cable has desirable performance for a slab, and heat supplying curing inside heat enclosure and heat generationmat also shows desirable performance for a wall, and for a column, use of EPS heat insulation has proper performance against early frost damage, which reaches $45^{\circ}D{\cdot}D$ and helps the concretemaintain above $0^{\circ}C$ within 3 days. Themethodsmentioned above are believed to be optimum protection from early frost damage of the concrete under $-20^{\circ}C$.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.249-252
• /
• 2008

In recent large-scale structures, as mass concrete type structure is frequently applied to the building, temperature crack due to hydration heat needs to be considered. Since a volume change is internally or externally restricted in a mold after placing concrete, temperature crack of mass concrete takes place. By this reason, the reduction method to control this crack is required. In this study, low heat mixture and hydration heat difference is used to execute the analysis of hydration heat, considering the changes of heat transfer coefficient according to curing conditions and block placement of mass concrete. For the analytical modelling, original portland cement and concrete of low heat mixture are placed in the upper and lower payer, respectively. A convection boundary condition is fixed because mass concrete of block placement is characterized by the difference of mold form and curing condition. Through the analysis results considering the changes of low heat mixture, block placement, and heat transfer coefficient, we check out the temperature and stress distribution and analyze the temperature crack reduction effect.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.28 no.3
• /
• pp.47-58
• /
• 2024

This study were conduced experimentally to analyze the heat-generating performance, flexural strength, and microstructure of conductive mortar mixed with micro steel fiber and multi-wall carbon nanotube (MWCNT). In the conductive mortar heat-generating performance and flexural strength tests, the mixing concentration of MWCNT was selected as 0.0wt%, 0.5wt%, and 1.0wt% relative to the weight of cement, and micro steel fibers were mixed at 2.0vol% relative to the volume. The performance experiments were conducted with various applied voltages (DC 10V, 30V, 60V) and different electrode spacings (40 mm, 120 mm) as parameters, and the flexural strength was measured at the curing age of 28 days and compared and analyzed with the normal mortar. Furthermore, the surface shape and microstructure of conductive mortar were analyzed using a field emission scanning electron microscope (FE-SEM). The results showed that the heat-generating performance improved as the mixing concentration of MWCNT and the applied voltage increased, and it further improved as the electrode spacing became narrower. However, even if the mixing concentration of MWCNT was added up to 1.0 wt%, the heat-generating performance was not significantly improved. As a result of the flexural strength test, the average flexural strength of all specimens except the PM specimen and the MWCNT mixed specimens was 4.5 MPa or more, showing high flexural strength due to the incorporation of micro steel fibers. Through FE-SEM image analysis, Through FE-SEM image analysis, it was confirmed that a conductive network was formed between micro steel fibers and MWCNT particles in the cement matrix.