• Journal of Conservation Science
• /
• 제26권3호
• /
• pp.269-276
• /
• 2010

This study aims to extract manufacturing techniques by analysing metallurgical characteristics of the cast-iron pot from Bubjusa, examining corrosion status and microstructure with a optical microscope, SEM-EDS, micro vickers hardness tester and XRD. The microstructure analysis has presented that ferrite and partial portion of pearlite exist within the corroded outer layer. The analysis of the inner layer revealed that there is pearlite and graphite of feather shape. The one of the middle layer, which is placed between outer and inner layer, showed that corrosion has been heavily developed. Micro vickers hardness values range from 217Hv to 698Hv in constituent layers and such values lie within the ranges of the ancient iron relics. The result of EDS analysis for each microstructure presented that the outer layer has been more decarbonized than the inner layer. XRD analysis of iron corrosion compound revealed that Goethite and Hematite had been produced from the corrosive process of iron. The study concludes that the large iron pot was made by casting technique, and microstructure of inner layer had a gray cast iron. Outer layer has been decarbonized through repetitive process of heating and cooling. This results can be used as fundamental data for comparative study to reveal manufacturing techniques of large cast-iron pot.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 한국재료학회 2003년도 춘계학술발표강연 및 논문개요집
• /
• pp.244-244
• /
• 2003

나노인덴테이션은 시편에 압자를 침투시켜 재료의 기계적 특성을 파악할 수 있는 경도시험법이다. 압입범위를 나노미터범위로 조절할 수 있어 기존에 접근할 수 없었던 극 미소부분에로 응용이 넓어지고 있다. 경도시험시 재료의 탄성 및 소성 작용에 의해 재료는 변형되고, 표면변화 관찰을 통해 표면아래 부분에서 이루어지고 있는 거동을 예측할 수 있다. 이러한 관점에서 나노인덴테이션 시험시에도 발생하는 파일업과 싱크인 현상에서 재료가 나노미터 범위에서 어떠한 양상으로 변형을 하는지를 고찰하는 것은 의미가 있을 것이다. 본 연구에서 파일업과 싱크인의 양상을 파악하고 그 양을 정량화하기 위하여 가공경화양에 따른 표면변화와 압입하중 변화에 따른 표면변화를 관찰하였다. 어닐링한 봉상 알루미늄을 압축변형을 0%, 5%, 20%, 40%, 50% 로 변형시켜 가공경화를 일으켰고, 표면은 전해연마하여 나노압입시험이 가능하도록 하였다. 각각의 시편을 나노인덴테이션 압입하중을 변화시켜 재료에서 하중 변화에 따라 나타나는 표면변화를 관찰하였고, 위의 각 조건에서 파일업양을 정량화 하였다. 연구결과에 대해 ANSYS 유한요소분석 프로그램을 사용하여 재료의 변형양상을 시뮬레이션 하였고, 실제 실험데이터와 비교 분석하였다.

• Korean Journal of Materials Research
• /
• 제6권11호
• /
• pp.1090-1098
• /
• 1996

개조한 가스 금속 아아크 용접공정을 이용하여 SiC/AI 금속기 복합재료를 제조하고 그 특성을 조사하였다. AI 모재위에 강화입자의 크기와 부피분율을 변화하여 다양한 SiC/AI 복합재료층을 제조하였고, 만들어진 복합재료층의 특성은 미세조직관찰과 미소경도시험을 통하여 이루어졌다. 복합재료층의 두께는 약 7-8mm로 측정되었고 균일한 강화입자의 분포도를 얻을 수 있었다. 분산입자의 부피분률은 Ar가스의 유량에 의하여 조절하였고 분산입자의 부피분률이 증가하고 크기가 작아짐에 따라 기지의 수지상 응고조직은 더욱 미세화되었다. 복합재료의 부피경도는 분산입자의 부피분률이 감소함에 따라 낮아졌으나 입자 크기에는 크게 변화가 없는 것으로 나타났다.

• Transactions of the Korean Society of Mechanical Engineers
• /
• 제9권3호
• /
• pp.301-308
• /
• 1985

본 논문에서는 불규칙 하중을 받는 부재에 대한 연구의 고초로서 간단한 응력 모델을 설정하고 이들 변동응력이 가해지는 시기를 명확히 구분하여 크랙전파곡선의 거동을 고찰하였다. 특히 부하되는 응력 진폭의 크기에 따라서 크랙선단부의 미시적 인 변화의 크기가 다르고 이로인하여 크랙전파에 대한 피해의 정도가 달라진다고 하면 크랙전파의 지연 및 가속현상이 나타날 것이 예측이 되고 따라서 이때 나타나는 피해 정도의 크기를 미소 경도치로 환산하여 그것과 피로크랙 전파 특성과를 비교 검토 하 였다.

• Korean Journal of Materials Research
• /
• 제11권2호
• /
• pp.104-114
• /
• 2001

To investigate the effects of the addition of Nb and Sn on the recrystallization of Zr- Sn-Nb alloys, both Vickers micro-hardness test and TEP measurement were carried out on cold-worked specimens annealed at various temperatures from $300^{\circ}C$ to 75$0^{\circ}C$. The microstructures of heat treated specimens were analyzed by optical microscope, SEM, and TEM. The study of microhardness and microstructures showed that both recrystallization process and grain growth were retarded as the activation energy was increased by the addition of Nb and Sn. Especially, the addition of Sn was more effective on retarding recrystallization. Precipitates were formed more easily when Nb was added because the solubility of Nb into Zr is lower than that of Sn. However, the recrystallization process was affected more by Sn than Nb because the strain field formed by substitutional Sn repressed the dislocation movement. TEP was increased due to the decrease of electron scattering as recovery and recrystallization were proceeded and saturated when the recrystallization completed. However, when precipitates formed, TEP was increased because the decrease of solute concentration near the precipitates caused the decrease of electron scattering.

• Korean Journal of Materials Research
• /
• 제7권6호
• /
• pp.453-459
• /
• 1997

용탕단조법에 의해 제조된 Mg-9AI-2Zn 합금을 미세조직관찰, 미소경도측정, 인장시험 등을 행하여 시효거동과 기계적 성질을 조사하였다. 용탕에 가압을 한 결과 주조결함이 제거된 미세한 주조조직을 얻었으며 미세조직은 초정 $\alpha$(Mg 고용체), 과포화고용체 $\alpha$상 및 $\beta$(Mg$_{17}$AI$_{12}$)화합물의 3가지 상으로 구성되어 있었다. 16$0^{\circ}C$및 20$0^{\circ}C$에서 시효열처리한 결과 $\beta$석출물에 의한 피크 경도값이 나타났으며 피크경도에서의 석출물의 형태는 lamella 형태의 불연속 석출물이 대부분이었고 과시효에 따라 불연속석출물의 조대화와 함께 연속석출물의 분율이 증가하였다. 용탕단조방법에 의해 제조된 Mg-9AI-2Zn 합금의 인장특성은 인장강도 261.4MPa, 연산율 7.6%로서 상용 AZ 92 합금보다 인장강도 및 연신율에서 우수한 기계적 성질을 가졌는데 이는 Zn의 고용강화 및 용탕의 가압에 의한 효과였다.다.

• Korean Journal of Materials Research
• /
• 제10권6호
• /
• pp.422-429
• /
• 2000

To investigate the effect of annealing temperature and time on the recrystallization behavior and microstructure of Zr-based alloys, the specimens of Zr-0.8Sn-0.4Nb-0.4Fe-0.2Cu, Zr-1Nb, Zircaloy-4, and unalloyed Zr were cold-worked and annealed at 400, 500, 600, 700, 800, $900^{\circ}C$ for 30 to 5000 minutes. The hardness, microstructure and precipitate of the specimens were investigated by using micro-hardness tester, optical microscope and transmission electron microscope, respectively. The recrystallization of Zr-based alloys occurred between $400^{\circ}C$ and $600^{\circ}C$. As the content of alloying elements increased, the hardness and recrystallization temperature of the alloys increased though the grain sizes after recrystallization decreased. It was supposed that the hardness of Zr-based alloy with Fe or Cu increased during recovery by the formation of Fe or Cu precipitates.

• Journal of the Korean Institute of Gas
• /
• 제19권1호
• /
• pp.57-63
• /
• 2015

The hydrogen was charged TRIP steel by electrochemical method under 0.5M $H_2SO_4$ electrolyte and 0.5M NaOH electrolyte with hydrogen charging conditions respectively. The degree of hydrogen embrittlement of TRIP steel was evaluated by using micro Vickers hardness tests. These results showed that the degree of hydrogen embrittlement in acidic electrolyte with hydrogen penetration and hydrogen diffusion through the depth of specimen was more sensitive than its alkaine electrolyte between two type electrolytes. However, it was investigated that micro Vickers hardnesses of surface in acidic electrolyte under two electrolyte were higher than those of alkaine electrolyte. It was thought that in case of hydrogen embrittlement in acid-ice electrolyte, hydrogen charging time was more effective than current density, in case of alkaine electrolyte, hydrogen current density was more effective than charaging time.

• Journal of the Korean Vacuum Society
• /
• 제9권4호
• /
• pp.328-334
• /
• 2000

DLC (Diamond-Like Carbon) films were deposited by ECR-PECVD (electron cyclotron resonance plasma-enhanced chemical vapor deposition) method with the variation of substrate bias voltage under the others are constant except it. We have investigated the ion bombardment effect induced by the substrate bias voltage on films during the deposition of film. The characteristics of the film were analyzed using the Dektak surface profiler, SEM, FTIR spectroscopy, Raman spectroscopy and Nano Indentation tester. FTIR spectroscopy analysis shows that the amount of dehydrogenation in films was increased with the increase of substrate bias voltage and films thickness was decreased. Raman scattering analysis shows that integrated intensity ratio $(I_D /I_G)$ of the D and G peak was increased as the substrate bias voltage increased, and films hardness was increased. From these results, it can be concluded that films deposited at this experimental have the enhanced characteristics of DLC because of the ion bombardment effect on films during the deposition of film.

• Korean Journal of Materials Research
• /
• 제8권12호
• /
• pp.1176-1181
• /
• 1998

Characteristics of high frequency induction- hardened bearing steel have been investigated using 0.55wt.% C-1.68wt.% Mn specimens produced by vacuum induction melting (VIM). The K4 value in DIN 57602 of the specimens was assessed to be 6.41, high level of cleanliness. The specimens were high frequency induction-hardened to form heterogeneous submicron- lath martensite in the surface hardened layer with about 2.5mm in effective depth. Rolling contact fatigue tests were conducted in elasto-hydrodynamic lubricating conditions under a maximum Hertzian contact stress of$ 492kgmm^{-2}$ . It was found that microhardness in the subsurface, up to about $500\mu\textrm{m}$ in depth, below the raceway of rolling contact fatigued specimens was increased in comparison with that of induction-hardened layers. The depth of maximum microhardness- increased region was about $100\mu\textrm{m}$ from surface, showing white etching area. Crack initiation and propagation in the white etching area below the raceway of rolling contact fatigued specimens were observed.