• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.3
• /
• pp.17-26
• /
• 2010

Pb-Sn solder is rapidly being replaced by lead-free solder for board-level interconnection in microelectronic package assemblies due to the environmental protection requirement. There is a general lack of mechanical reliability information available on the lead-free solder. In this study, thermo-mechanical behaviors of wire-bond plastic ball grid array (WB-PBGA) package assemblies are characterized by high-sensitivity moire interferometry. Experiments are conducted for two types of WB-PBGA packages that have Pb-Sn solder and lead-free solder as joint interconnections. Using real-time moire setup, fringe patterns are recorded and analyzed for several temperatures. Bending deformations of the assemblies and average strains of the solder balls are investigated and compared for the two type of WB-PBGA package assemblies. Results show that shear strain in #3 solder ball located near the chip shadow boundary is dominant for the failure of the package with Pb-Sn solder, while normal strain in #7 most outer solder ball is dominant for that with lead-free solder. It is also shown that the package with lead-free solder has much larger bending deformation and 10% larger maximum effective strain than the package with Pb-Sn solder at same temperature level.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.82-82
• /
• 2010

표면실장 공법을 통해 CSP 패키지를 보드에 실장 하는데 있어 무연솔더 접합부의 신뢰성에 영향을 미치는 인자 중 가장 중요한 것은 접합부에 형성되는 IMC (Intermetallic compound, 금속간화합물)인 것으로 알려져 있다. 접합부의 칩 부분에는 솔더와 칩의 UBM (Under bump metalization)이 접합하여 IMC가 형성되나, 보드 부분에는 솔더와 보드의 UBM 뿐만 아니라 그 사이에 솔더 페이스트가 함께 접합되어 IMC가 형성된다. 본 연구에서는 패키지의 신뢰성 연구를 위해 솔더 페이스트의 유무 및 두께에 따른 무연 솔더 접합부의 미세조직의 변화를 분석하였다. 본 실험에서는 Sn-3.0(Wt.%)Ag-0.5Cu 조성과 본 연구진에 의해 개발된 Sn-Ag-Cu-In 조성의 직경 $450{\mu}m$ 솔더 볼을 사용하였으며, 솔더 페이스트는 상용 Sn-3.0Ag-0.5Cu (ALPHA OM-325)를 사용하였다. 칩은 ENIG (Electroless nickel immersion gold) finish pad가 형성된 CSP (Chip scale package)를, 보드는 OSP (Organic solderability preservative)/Cu finish pad가 형성된 것을 사용하였다. 실험 방법은 보드를 솔더 페이스트 없이 플라즈마 처리 한 것, 솔더 페이스트를 $30{\mu}m$ 두께로 인쇄한 것, $120{\mu}m$의 두께로 인쇄한 것, 이렇게 3가지 조건으로 준비한 후, 솔더 볼이 bumping된 칩을 mounting하여, $242^{\circ}C$의 peak 온도 조건의 oven(1809UL, Heller)에서 reflow를 실시하여 패키지를 형성하였다. 이후 시편은 정밀 연마한 후, OM(Optical Microscopic)과 SEM(scanning electron microscope) 및 EDS(energy dispersive spectroscope)를 사용하여 솔더 접합부 IMC의 미세조직을 관찰, 분석하였다.

• Proceedings of the KSME Conference
• /
• 2005.11a
• /
• pp.221.2-221.2
• /
• 2005

• Proceedings of the KWS Conference
• /
• 2004.05a
• /
• pp.84-86
• /
• 2004

기존의 전자산업에서는 Sn-37Pb 공정솔더를 사용하였으나, 최근 납의 환경적인 문제로 인하여 무연 솔더에 관한 연구와 적용이 세계적으로 진행되고 있다. 무연 솔더의 실용화와 관련하여 Sn-37Pb 솔더와 같은 만능의 솔더는 없지만, 그 중 도입이 가장 유력시 되는 것으로 Sn-Ag-Cu계 솔더가 있다. (중략)

• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.3
• /
• pp.55-61
• /
• 2022

In this study, properties of Pb-free solder joints which were combined using Sn-3.0Ag-0.5Cu (SAC305) Pb-free solder with a mid-temperature type of melting temperature and Sn-57Bi-1Ag Pb-free solder with a low-temperature type of melting temperature were reported. Combined Pb-free solder joints were formed by reflow soldering processes with ball grid array (BGA) packages which have SAC305 solder balls and flame retardant-4 (FR-4) printed circuit boards (PCBs) which printed Sn-57Bi-1Ag solder paste. The reflow soldering processes were performed with two types of temperature profiles and interfacial properties of combined Pb-free solder joints such as interfacial reactions, formations of intermetallic compounds (IMCs), diffusion mechanisms of Bi, and so on were analyzed with the reflow process conditions. In order to compare reliability characteristics of combined Pb-free solder joints, we also conducted thermal shock test and analyzed changes of mechanical properties for joints from a shear test during the thermal shock test.

• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.4
• /
• pp.11-17
• /
• 2010

The electromigration phenomenon in lead-free flip-chip solder joint has been one of the serious problems. To understand the mechanism of this phenomenon, the crystallographic orientation of Sn grain in the Sn-Ag-Cu solder bump has been analyzed. Different time to failure and different microstructural changes were observed in the all test vehicle and bumps, respectively. Fast failure and serious dissolution of Cu electrode was observed when the c-axis of Sn grain parallel to electron flow. On the contrary of this, slight microstructural changes were observed when the c-axis of Sn perpendicular to electron flow. In addition, underfill could enhance the electromigration reliability to prevent the deformation of solder bump during EM test.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.2 s.43
• /
• pp.23-33
• /
• 2007

The growing environmental regulation governs the use of lead by RoHS, WEEE, and then. The electronic industry is moving to replace Pb-bearing solder with Pb-free solder. To use the Pb-free solder, microelectronic industry needs consequently the new reliability appraisal such as the packaging for high temperature process, various mechanical change caused by new solder, and the development of Pb-free sloder for long life of product. The evaluation of solder bar and mechanical properties of joint were performed compared with international standard, and new appraisal standard was established. The solderability and spread ability of Sn-0.7Cu solder material showed up to the standard. Shear test of solder joint using by the solder resulted that the shear strengths after thermal shock or after aging were not much lower than the shear strength of as-soldered and that they were also up to the standard.

• Proceedings of the Korean Reliability Society Conference
• /
• 2005.06a
• /
• pp.287-294
• /
• 2005

전자 패키지가 열을 받을 때 회로기판과 칩의 열팽창계수 차이에 의해 발생되는 응력은 솔더 조인트의 파손에 영향을 미친다. 본 연구에서는 이 영향을 정량적으로 규명하기 위하여 열충격시험기를 이용해 얻어진 솔더조인트의 전기저항 변화와 수명과의 상관관계를 규명하였고, BGA 솔더조인트의 수명을 정량적으로 도출하였다. 또한 Sn-3.5Ag-0.5Cu 무연솔더와 63Sn-37Pb 유연솔더를 위의 실험에 동시에 적용시켜 건전성을 FORM(first-order reliability method)과 Weibull Function Model을 이용해 비교하였다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.29.2-29.2
• /
• 2007

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.10a
• /
• pp.695-696
• /
• 2012