Poly(ethyleneglycol methacrylate-co-benzyl methacrylate) (P(PEGMA-co-BMA)) microgel was prepared by precipitation copolymerization of PEGMA and benzyl methacrylate in poly(acrylic acid)/ethanol solution. The microgels with various sizes were obtained by changing the concentration of poly(acrylic acid), monomer and nature of solvents. The particle size of P(PECMA-co-BMA) microgels was decreased with increasing the concentration of poly(acrylic acid) and increased with that of monomer. By increasing solubility parameter of solvents, the particle size was inecreased. The size of P(PEGMA-co-BMA) microgels was controlled by experimental conditions from $0.1{\mu}m$ to $0.35{\mu}m$.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.142-147
• /
• 2002

폴리머/세라믹 복합체는 내장형 캐패시터(embedded capacitor)의 유전 재료로 많은 관심을 불러 일으키고 있다. 본 연구는 BaTiO$_3$분말의 크기와 함량이 에폭시/BaTiO$_3$복합체 캐패시터의 유전 상수와 누설전류에 미치는 영향에 대해 살펴보고 이에 대해 고찰하고자 하였다. BaTiO$_3$분말이 67vo1% 함유된 Epoxy/BaTiO$_3$composite 필름의 유전상수는 전반적으로 사용한 BaTiO$_3$분말의 크기가 커짐에 따라 증가하였다. 이것은 입자의 크기가 증가함에 따른 입자의 유전상수의 증가 때문이며 XRD 분석을 통해 입자의 크기가 증가함에 따라 tetragonality가 증가함을 확인하였다. 복합체 필름의 누설전류도 또한 사용한 입자의 크기가 커짐에 따라 증가하였으며 이는 분말의 크기가 증가함에 따라 단위길이 당 입자의 수가 감소하는 것으로, 단위 길이 당 입자의 수가 감소하여 전류의 흐름을 방해하는 입자/폴리머/입자 계면의 수가 감소하기 때문이다. 분말의 함량에 따른 유전상수는 unimodal과 bimodal의 경우 각각 73vo1%와 80vo1%에서 최대 값을 나타냈으며 그 이상에서는 감소하는 것이 관찰되었는데 이는 과량의 분말이 조밀 충전을 깨고 필름의 밀도를 낮추기 때문이었다. 누설전류의 경우 unimodal과 bimodal 각각에 대해 73vo1%와 80vo1%에서 급격한 증가를 관찰 할 수 있었으며 이는 percolation 현상의 발생에 의해 입자와 입자간에 접촉이 이루어져 BaTiO$_3$분말을 따라 전류가 잘 흐를 수 있는 conduction path가 형성 되기 때문이다.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.30 no.3 s.47
• /
• pp.295-305
• /
• 2004

Colloid and surface chemistry have been focused on surface area and surface energy. Local surface properties such as surface density, interaction, molecular orientation and reactivity have been one of interesting subjects. Systems of such surface energy being important would be listed as association colloid, emulsion, particle dispersion, foam, and 2-D surface and film. Such nanoparticle systems would be applied to drug delivery systems and functional cosmetics with biocompatible and degradable materials, while nanoparticles having its size of several nm to micron, and wide surface area, have been accepted as a possible drug carrier because their preparation, characteristics and drug loading have been inves-tigated. The biocompatible carriers were also used for the solubilization of insoluble drugs, the enhancement of skin absorption, the block out of UV radiation, the chemical stabilization and controlled release. Nano/micro emulstion system is classified into nano/microsphere, nano/microcapsule, nano/microemulsion, polymeric micelle, liposome according to its prep-aration method and size. Specially, the preparation method and industrial applications have been introduced for polymeric micelles self-assembled in aqueous solution, nano/microapsules controlling the concentration and activity of high concen-tration and activity materials, and monolayer or multilayer liposomes carrying bioactive ingredients.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2011.04a
• /
• pp.116-118
• /
• 2011

일반적으로 나노입자의 크기는 나노복합체의 역학적 특성에 상당한 영향을 미친다. 이에 본 연구에서는 나노입자 크기를 고려한 나노복합체 재료 구성모델 (Kim et al., 2011)을 소개하고자 한다. Kim et al. (2011)에 의해서 나노입자 크기효과를 위한 Size-dependent Eshelby tensor가 미세역학 모델에 적용되었으며, 나노스케일 해석과 함께 다양한 수치해석을 수행하였다. 특히, 본 연구에서는 이를 활용하여 $SiO_2$/Epoxy 나노복합체의 역학적 특성을 예측해 보았다.

• Journal of the Korean Institute of Gas
• /
• v.18 no.5
• /
• pp.20-25
• /
• 2014

Explosion characteristics of micro-sized aluminum dusts had been studied by many researchers, but the research of nano-sized aluminum dusts were very insufficient. In this study, an experimental investigation was carried out on the influences of nano and micro-sized aluminum dusts (70 nm, 100 nm, $6{\mu}m$, $15{\mu}m$) on dust explosion properties of aluminum particles by using 20 L explosion apparatus. With decreasing of particle size in suspended aluminum dusts, the LEC (lower explosion concentration) of nano-sized aluminum is lower than that of micro-sized aluminum. The particle size change of nano-sized aluminum dusts seems no obvious explosion differences than that of micro-sized aluminum dusts. From the observation of nano-sized aluminum particles by TEM (Transmission Electron Microscopy), it is estimated that increase of particles aggregation may have effects on the explosion characteristics of aluminum nanopowders.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.3
• /
• pp.93-97
• /
• 2015

To synthesis of high purity micro silver particle, we extracted the silver from the waste by liquid-liquid extraction and used the rapid firing-liquid phase precursor (RF-LPP) method. The silver micro particle was synthesized at $500^{\circ}C$ for 3 hr in air atmosphere by RF-LPP method. As a result of the research, micro silver particle is measured X-ray diffraction (XRD), the main peak is nearly corresponded to the same as JCPDS card (No.87-0719). With using the RF-LPP method, the fine Ag micro particle indicated due to the control of nucleation site and the oxygen contents was decreased by reducing treatment. We expect this research contribute to advance in field of the recycling technology.

• Applied Chemistry for Engineering
• /
• v.7 no.4
• /
• pp.777-786
• /
• 1996

Uniform sized-porous poly(acrylonitrile-ethylene glycol dimethacrylate) (PAN) microgels were synthesized by seed polymerization using monodisperse polystyrene seed particles. The effect of weight ratios of monomer/seed (M/S) and diluent/monomer (DIM), concentration of crosslinking agent and the type of diluent was investigated on the formation of PAN microgels. The particle size distribution of PAN microgels was found to be monodisperse in that the weight ratio of M/S is less than 50. More porous microgels were formed and the interstices between small sized interior microspheres present inside of PAN microgels were also smaller with increasing crosslinking agent concentration. Well-developed pore structure was found to be in that weight ratio of D/M is 1 and toluene is used as a diluent.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.89.2-89.2
• /
• 2012

$150^{\circ}$ 이상의 접촉각을 가지는 초소수성 표면은 self-cleaning, anti-fingerprint, anti-contamination 등의 특성을 가지므로 전자, 도료, 자동차 등 다양한 산업에서 활용될 수 있다. 재료 표면의 친/소수성은 물리적 요인과 화학적 요인 두 가지 요인을 조절함으로써 제어할 수 있다. 즉, 표면의 거칠기를 크게 하거나 표면에너지를 낮춰줌으로써 초소수성 표면을 구현할 수 있다. 실리카는 자연계에 매우 풍부하게 존재하고 있으며, 생체무해하며 내구성과 내마모성, 화학적 안정성, 고온 안정성 등을 지니고 있어 박막소재로 이용하기에 우수한 특징을 지니고 있다. 이러한 실리카 초소수성 코팅층을 형성하는 방법으로 본 연구에서는 전기분무법으로 마이크로 크기의 실리카 입자로 형성된 코팅층을 형성하였다. 이러한 마이크로 구조의 표면거칠기를 더욱 높이기 위하여 금 나노입자를 부가적으로 형성시켜 마이크로-나노구조 혼성의 계층구조를 만들고자 하였다. 금 나노입자는 자외선 조사 광환원법을 사용하였고, 이러한 계층구조에 플루오린 처리를 하여 계층구조 초소수성 코팅층을 형성하였다. 계층구조를 가지는 실리카 코팅층은 물 이외에 표면장력이 낮은 용액에서도 높은 접촉각을 보였고, 이러한 코팅층의 고온 안정성과 내구성, UV 저항성 등을 조사하여 실제 응용 가능성을 검토하였다.

• Proceedings of the KAIS Fall Conference
• /
• 2008.05a
• /
• pp.46-48
• /
• 2008

나노복합 블레이드가 반도체 웨이퍼 가공을 위한 마이크로급 나노장치나 그 이상의 나노급 구조체를 위해 사용되었다. 금속 블레이드는 실리콘 웨이퍼 가공을 위해 사용되어 왔다. 그러나, 최근 레진 복합 블레이드는 반도체나 핸드폰의 쿼츠 웨이퍼 가공에 사용된다. 유기 또는 비유기 재료 선정은 기계가공성, 전기 전도성, 강도, 연성 및 웨이퍼 저항을 가진 블레이드를 만드는데 중요하다. 고성능 응용의 증대 요구에 따라 개발된 고기술 비유기성 재료의 혼합은 낮은 가격에 고기능의 신뢰도를 필요로 한다. 나노 입자의 크기를 가진 레진 복합물의 마이크로 설계는 입자간 상호작용의 제어가 필요하다. 형상 제작 동안 마이크로 차원에 두께를 유지하기 위해서는 마이크로/나노급 제작을 위한 가공기술이 중요한 것 중의 하나이다. 본 연구에서는 핫 프레스 구조물이 원래 설계 기준과 두께 차이의 실험 접근법을 사용해 만들어졌다. 다른 습식 공정 기술은 차원의 허용치를 개선하기 위해 만들었다. 실험들과 해석들은 신뢰성 결과가 사용가능함을 보여주었다. 반도체 시장에 사용될 레진 복합 블레이드의 개선 효과가 논의되었다.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2017.05a
• /
• pp.791-796
• /
• 2017

In this study, the combustion characteristics of paraffin blended fuel on aluminum particle size were investigated. The combustion experiments were carried out using aluminum particles with an average particle size of 100 nm and $8{\mu}m$ and microcrystalline paraffin wax (Sasol 0907). A series of comparison was conducted on the regression rate, the pressure curve and the characteristic velocity of pure paraffin and paraffin blended fuels with aluminum particles. It was found that the micro-sized particles enhance the regression rate as the oxidizer mass flux increased. However, the nano-sized particles decrease the regression rate as the oxidizer mass flux is increased.