• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.11
• /
• pp.923-932
• /
• 2002

A stoichiometric mixture of evaporating materials for CdIn$\_$2/S$\_$4/ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, CdIn$\_$2/S$\_$4/ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by hot wall epitaxy(HWE) system. The source and substrate temperatures were 630 $\^{C}$ and 420 $\^{C}$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of CdIn$\_$2/S$\_$4/ single crystal thin films measured from Hall effect by van der Pauw method are 9.01$\times$10$\^$16/ cm$\^$-3/ and 219 ㎠/V$.$s at 293 K, respectively. From the optical absorption measurement, the temperature dependence of energy band gap on CdIn$\_$2/S$\_$4/ single crystal thin films was found to be Eg(T) ＝ 2.7116 eV - (7.74 $\times$ 10$\^$-4/ eV) T$\^$2//(T＋434). After the as-grown CdIn$\_$2/S$\_$4/ single crystal thin films was annealed in Cd-, S-, and In-atmospheres, the origin of point defects of CdIn$\_$2/S$\_$4/ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K. The native defects of V$\_$cd/, V$\_$s/, Cd$\_$int/ and S$\_$int/ obtained by PL measurements were classified as donors or accepters type. And we concluded that the heat-treatment in the S-atmosphere converted CdIn$\_$2/S$\_$4/ single crystal thin films to an optical p-type. Also, we confirmed that In in CdIn$\_$2/S$\_$4/GaAs did not from the native defects because In in CdIn$\_$2/S$\_$4/ single crystal thin films existed in the form of stable bonds.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.10
• /
• pp.829-838
• /
• 2007

The stochiometric mix of evaporating materials for the $CdGa_2Se_4$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, $CdGa_2Se_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $630^{\circ}C$ and $420^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD).The carrier density and mobility of $CdGa_2Se_4$ single crystal thin films measured from Hall effect by van der Pauw method are $8.27{\times}10^{17}\;cm^{-3},\;345\;cm^2/V{\cdot}s$ at 293 K. respectively. The temperature dependence of the energy band gap of the $CdGa_2Se_4$ obtained from the absorption spectra was well described by the Varshni's relation, $Eg(T)\;=\;2.6400\;eV\;-\;(7.721{\times}10^{-4}\;eV/K)T^2/(T+399\;K)$. After the as-grown single crystal $CdGa_2Se_4$ thin films were annealed in Cd-, Se-, and Ga -atmospheres, the origin of point defects of single crystal $CdGa_2Se_4$ thin films has been investigated by PL at 10 K. The native defects of $V_{Cd}$, $V_{Se}$, $Cd_{int}$, and $Se_{int}$ obtained by PL measurements were classified as donors or accepters. We concluded that the heat-treatment in the Cd-atmosphere converted single crystal $CdGa_2Se_4$ thin films to an optical p-type. Also, we confirmed that Ga in $CdGa_2Se_4/GaAs$ did not form the native defects because Ga in single crystal $CdGa_2Se_4$ thin films existed in the form of stable bonds.

• Journal of Radiation Protection and Research
• /
• v.21 no.1
• /
• pp.1-7
• /
• 1996

In this paper, we discussed the fabrication and characterization of bulk type CdZnTe detector for pocket surveymeter. The resistivity of CdZnTe single crystal grown by the High Pressure Bridgman method is in the mid of $10^9$ ohm-cm. The detector structure is Au/CdZnTe/Au and gold electrode is formed by electroless deposition method. Resolutions of 4.8keV and 2.2keV were observed at 22.2keV line of $^{109}Cd$ and 59.6keV line of $^{241}Am$ at room temperature, respectively. We also constructed the small size pocket surveymeter using home made CdZnTe detector. It shows the good linearity over a range from 1mR/hr to 10R/hr with deviation less than 5%. The sensitivity of the surveymeter developed is $2.2{\times}10^3 cps/Rad\;hr^{-1}$ for the 662keV of $^{l37}Cs\;{\gamma}-ray$.

• Journal of the Korean Chemical Society
• /
• v.35 no.6
• /
• pp.630-635
• /
• 1991

The crystal structure of a bromine sorption complex of dehydrated fully $Ca^{2+}$-exchanged zeolite A (a = 12.211(2) ${\AA}$) has been determined by single-crystal X-ray diffraction techniques in the cubic space group, Pm3m at $21(1)^{\circ}C$. The crystal was prepared by dehydration at $360^{\circ}C$ and 2 ${\times}$ $10^{-6}$ Torr for 2 days, followed by exposure to about 180 Torr of bromine vapor at $24^{\circ}C$ for 30 min. In the resulting structure, six $Ca^{2+}$ ions are located on two different threefold axes associated with 6-ring oxygens. A total of six dibromine molecules are sorbed per unit cell. Each $Br_2$ molecule approaches a framework oxide ion axially, with O-Br = 3.12(7) ${\AA}$, Br-Br = 2.64(9) ${\AA}$ and O-Br-Br = $178(2)^{\circ}$, indicating a charge-transfer interaction. Full-matrix least-squares refinement converged to a conventional R index of 0.104 using the 103 independent reflections for which I > 3${\sigma}$ (I).

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.18 no.3
• /
• pp.42-51
• /
• 1981

Boron was predeposited into p (100) Si wafer at 94$0^{\circ}C$ for 60minutes to make the back surface field. High tempreature diffusion process at 1145$^{\circ}C$ for 3 hours was immediately followed without removing boron glass to obtain high surface concentration Back boron was annealed at 110$0^{\circ}C$ for 40minutes after boron glass was removed. N+ layer was formed by predepositing with POCI3 source at 90$0^{\circ}C$ for 7~15 minutes and annealed at 80$0^{\circ}C$ for 60min1es under dry Of ambient. The triple metal layers were made by evaporating Ti, Pd, Ag in that order onto front and back of diffused wafer to form the front grid and back electrode respectively. Silver was electroplated on front and back to increase the metal thickness form 1~2$\mu$m to 3~4$\mu$m and the metal electrodes are alloyed in N2 /H2 ambient at 55$0^{\circ}C$ and followed by silicon nitride antireflection film deposition process. Under artificial illumination of 100mW/$\textrm{cm}^2$ fabricated N+PP+ cells showed typically the open circuit voltage of 0.59V and short circuit current of 103 mA with fill factor of 0.80 from the whole cell area of 3.36$\textrm{cm}^2$. These numbers can be used to get the actual total area(active area) conversion efficiency of 14.4%(16.2%) which has been improved from the provious N+P cell with 11% total area efficiency by adding P+ back.

• Journal of the Korean Chemical Society
• /
• v.38 no.5
• /
• pp.339-344
• /
• 1994

The crystal structure of a methanol sorption complex of dehydrated partially Co(II)-exchanged zeolite A, $Co_4Na_4-A{\cdot}6.5CH_3OH$ (a = 12.169(1) $\AA)$, has been determined by single-crystal X-ray diffraction techniques in the cubic space group Pm$\bar3$m at $21(1)^{\circ}C. $Co_4Na_4$-A was dehydrated at $360^{\circ}C\;and\;2{\times}10^{-6}$ torr for 2 days, followed by exposure to about 104 torr of methanol vapor at $22(1)^{\circ}C$ for 1 hr. The structure was refined to final error indices, $R_1$ = 0.061 and $R_2$ = 0.060 with 147 reflections, for which I > $3\sigma(I).$ In this structure, four $Co^{2+}$ ions and 1.5 $Na^+$ ions per unit cell lie at 6-ring positions: the $Na^+$ ions are recessed 0.44 $\AA$ into the sodalite unit and the Co(II) ions extend ca. 0.55 $\AA$ into the large cavity. 2.5 $Na^+$ ions lie in an 8-oxygen ring plane. The 6.5 methanol molecules are sorbed per unit cell. The 6.5 methanol oxygens, all in the large cavity, associate with the 4 $Co^{2+}$ ions and 2.5 $Na^+$ ions.

• Journal of the Korean Magnetics Society
• /
• v.12 no.2
• /
• pp.41-45
• /
• 2002

The low-field tunnel-type magnetoresistance (MR) properties of sol-gel derived $La_{0.7}Pb_{0.3}MnO_3(LPMO)$ thin film deposited on different substrate have been investigated. Polycrystalline thin films were fabricated by spin-coating on $SiO_2/Si(100)$ substrate and that with yttria-stabilized zirconia (YSZ) buffer layer, while c-axis-oriented thim film was grown on $LaAlO_3(001)$ (LAO) single crystal substrate. The full width half maximum (FWHM) of the rocking curve scan of LPMO/LAO film is $0.32^{\circ}$. Tunnel-type MR ratio is 0.52 % in $LPMO/SiO_2/Si$(100) film and that of $LPMO/YSZ/SiO_2/Si$(100) film is as high as 0.68 %, whereas that of LPMO/LAO(001) film is less than 0.4 % under the applied field of 500 Oe at 300 K. Well-pronounced MR hysteresis was registered with an MR peak in the vicinity of the coercive field. The low-field tunnel-type MR characteristics of thin films deposited on different substrates originates from the behavior of grain boundary properties.

• Journal of Sensor Science and Technology
• /
• v.13 no.2
• /
• pp.157-167
• /
• 2004

A stoichiometric mixture of evaporating materials for $CuAlSe_{2}$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $CuAlSe_{2}$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $680^{\circ}C$ and $410^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CuAlSe_{2}$ single crystal thin films measured with Hall effect by van der Pauw method are $9.24{\times}10^{16}cm^{-3}$ and $295cm^{2}/V{\codt}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CuAlSe_{2}$ obtained from the absorption spectra was well described by the Varshni's relation, $E_{g}(T)$ = 2.8382 eV - ($8.68{\circ}10^{-4}$ eV/K)$T^{2}$/(T + 155 K). The crystal field and the spin-orbit splitting energies for the valence band of the $CuAlSe_{2}$ have been estimated to be 0.2026 eV and 0.2165 eV at 10 K, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_{5}$ states of the valence band of the $CuAlSe_{2}$. The three photocurrent peaks observed at 10 K are ascribed to the $A_{1-}$, $B_{1-}$, and $C_{1-}$ exciton peaks for n = 1.

• Journal of Sensor Science and Technology
• /
• v.23 no.1
• /
• pp.51-57
• /
• 2014

The evaporating materials for $MgGa_2Se_4$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $MgGa_2Se_4$ compounded polycrystal powder was deposited on thoroughly etched semi-insulated GaAs(100) substrate by the hot wall epitaxy (HWE) method system. The source and substrate temperatures of optimized growth conditions, were $610^{\circ}C$ and $400^{\circ}C$, respectively.The source and substrate temperatures were $610^{\circ}C$ and $400^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by double crystal X-ray diffraction (DCXD). The temperature dependence of the energy band gap of the $MgGa_2Se_4$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=2.34\;eV-(8.81{\times}10^{-4}\;eV/K)T^2/(T+251\;K)$. After the as-grown $MgGa_2Se_4$ single crystal thin films was annealed in Mg-, Se-, and Ga-atmospheres, the origin of point defects of $MgGa_2Se_4$ single crystal thin films has been investigated by the photoluminescence (PL) at 10 K. The native defects of $V_{Mg}$, $V_{Se}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the Se-atmosphere converted $MgGa_2Se_4$ single crystal thin films to an optical n-type. Also, we confirmed that Ga in $MgGa_2Se_4$/GaAs did not form the native defects because Ga in $MgGa_2Se_4$ single crystal thin films existed in the form of stable bonds.

• Journal of the Korean Vacuum Society
• /
• v.17 no.1
• /
• pp.51-57
• /
• 2008

we have demonstrated structural evolution and optical properties of Si-nanowires (NWs) synthesized on Si (111) substrates with nanoscale Au-Si islands by rapid thermal chemical vapor deposition (RTCVD). The Au-Si nano-islands (10-50nm in diameter) were employed as a liquid-droplet catalysis to grow Si-NWs via vapor-liquid-solid mechanism. The Si-NWs were grown by a mixture gas of SiH4 and H2 at a pressure of 1.0 Torr and temperatures of $500{\sim}600^{\circ}C$. Scanning electron microscopy measurements showed that the Si-NWs are uniformly sized and vertically well-aligned along <111> direction on Si (111) surfaces. The resulting NWs are ${\sim}60nm$ in average diameter and ${\sim}5um$ in average length. High resolution transmission microscopy measurements indicated that the NWs are single crystals covered with amorphous SiOx layers of ${\sim}3nm$ thickness. In addition, the optical properties of the NWs were investigated by micro-Raman spectroscopy. The downshift and asymmetric broadening of the Si main optical phonon peak were observed in Raman spectra of Si-NWs, which indicates a minute stress effects on Raman spectra due to a slight lattice distortion led by lattice expansion of Si-NW structures.