• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.6
• /
• pp.18-25
• /
• 2019

The cracks occurred during service life of concrete structure should be considered in durability design, because of the concrete's material property which is weak in tensile strength. In this study, the fly ash concrete mixtures considering 2 levels of strength is designed and outdoor exposure tests are conducted for those concrete specimens. The exposure environment is set to a splash zone, and in order to evaluate the effect of crack width on the behavior of chloride diffusion, the crack width of up to 1.0 mm is generated at intervals of 0.1 mm at each concrete mixture. After that, apparent chloride diffusion coefficient and surface chloride contents are deducted considering 3 levels of exposure periods(180 days, 365 days, 730 days). The diffusion coefficients of two types of mixture increase with the increase of crack width, and the diffusion coefficients decrease with the increase of exposure periods. In addition, the effect of the crack width on the diffusion coefficient is reduced as the exposure periods increase, which is attributed to the extra hydrate by chloride ion reducing the diffusivity of concrete. The behavior of the surface chloride contents does not significantly change by the increase in crack width, compared to the behavior of apparent chloride diffusion coefficient. Also, In the high strength FA concrete mixture, the surface chloride contents are 78.9 % ~ 90.7 % than the normal FA strength concrete mixture. Thus, Surface chloride contents have correlation with the strength of concrete.

• International Journal of Highway Engineering
• /
• v.9 no.4
• /
• pp.117-127
• /
• 2007

The exposed aggregate PCC(EAP) pavements have been successfully used in Europe and Japan as low-noise pavements. Coarse aggregate are exposed on the pavement surface texture of EAP by removing mortar of surface. The pavement surface texture should maintain not only low-noise characteristic but also adequate skid resistance level during the performance period. Skid resistance decreased with wearing and polishing of tire and pavement surface due to the repetition of tire-pavement contact. Since the tires mainly contact the exposed coarse aggregate, the shape and rock type of coarse aggregate significantly influence wearing and polishing of EAP pavements. The test for resistance to abrasion coarse aggregate by use of the Los Angeles machine(KS F 2508) and the method of test for resistance to abrasion coarse aggregate by use of the Accelerated Polishing Machine(ASTM D 3319-90) are generally used to evaluate polishing characteristics of aggregate. In this study, polishing of coarse aggregate of different five rock types were evaluated by KS F 2508(LA abrasion test) and ASTM D 3319-90(PSV method). The results of LA abrasion test and PSV method were contrary to each other. Since LA abrasion test is estimated the quantity of abrasion by the impact of aggregate, it may not be adequate to evaluate the polishing of aggregate by the repetition of tire. In the case of PSV method, the resistance of polishing is estimated the skid resistance variation of polished aggregate after repetition of tire. The PSV method is adequate for the evaluation on polishing of coarse aggregate. From the test results of PSV method, it was founded that rock type, specific gravity, coarse aggregate angularity, flat or elongated particles in coarse aggregate are significant to the resistance characteristic of coarse aggregate.

• 한국도로학회:학술대회논문집
• /
• 2008.03a
• /
• pp.15-29
• /
• 2008

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.105-106
• /
• 2016

The study of the sandwich wall with the increasing interest in building energy consumption have been actively conducted. This study designed exposed sandwich wall in the light of energy saving design standard and thermal bridge of share connection. The heat insulating performance was analyzed U-fator using calculation program provided in passive houses association and KS F 2277 (method of measuring thermal insulation of construction component materials).

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.164-165
• /
• 2016

To express the original texture of the concrete, exposed concrete finishing technique has been applied in many buildings. However, it is likely to cause quality problems after construction is completed. In addition, because of costs and time issues, reconstruction and maintenance works are difficult and ineffective. Therefore, step-by-step proactive quality management based on sufficient consensus among participants(client, designer, contractor) is very importatnt. This study analyzed factors causing low quality exposed concrete and quality contol points applied to 'A' headquarter construction project.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2012.04a
• /
• pp.290-293
• /
• 2012

화재는 콘크리트 구조물의 역학적 특성에 치명적 손상을 일으켜 건축물의 안전성을 급격하게 감소시킬 수 있다. 특히 고강도콘크리트는 폭렬이 발생하여 심각한 단면 손실과 노출된 철근으로 인하여 건축물의 안전성에 치명적인 영향을 미친다. 이러한 폭렬에 대하여 다양한 연구가 진행되고 있지만, 폭렬의 발생원인은 명백하게 밝혀지진 않았다. 이에 본 연구는 콘크리트의 함수율과 열응력이 폭렬에 미치는 영향을 분석하여 폭렬로부터 구조물의 안전성을 확보하기 위한 기초 자료를 제시하였다.

• Journal of the Korea Concrete Institute
• /
• v.24 no.5
• /
• pp.553-558
• /
• 2012

Airborne chlorides are transported to inland by sea wind to be attached to seashore concrete structure surface then penetrated into concrete structure members. Since the surface attached chloride amount are dependent on the amount of airborne chlorides, the prediction of distribution of airborne chlorides is important information in preventing chloride corrosion problems in seashore concrete structures. The prediction of surface chloride amount from airborne chlorides environment is extremely difficult than concrete directly in contact with seawater. In addition, their penetrating tendency is different from that of concrete immersed in seawater. In this study, properties of surface and penetrated chlorides under airborne chlorides environment are investigated. Concrete specimens were manufactured and exposed to marine environment for 3 years. The specimens were analyzed at the time durations of 1, 2, and 3 years to check surface chloride amount to penetrated chloride depth. The results revealed that there were certain differences according to surface roughness of concrete and with and without washing effect due to rainfalls. The evaluation results showed that penetrated chlorides depend on amount of airborne chlorides and duration of exposure. In addition, a notable tendency of having deeper chloride penetration and higher chloride content in concrete members under long-term exposure was observed.

• Magazine of the Korea Concrete Institute
• /
• v.18 no.6 s.95
• /
• pp.68-72
• /
• 2006

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.295-296
• /
• 2010

In this study, it was investigated basic properties of white concrete according to the binder composition for securing fundamental data for the construction site quality control.

• Magazine of the Korea Concrete Institute
• /
• v.14 no.3
• /
• pp.71-76
• /
• 2002

콘크리트는 거의 반영구적인 재료라고 인식되어져 왔으나, 최근들어 해양환경, 적설한랭지대, 도심과 같은 열악한 환경속에서 예상보다 빨리 조기열화 되는 현상이 널리 알려지면서 콘크리트 구조물의 구조적 성능뿐만 아니라, 장기적인 내구성에 대한 관심이 높아져 가고 있다. 실제로 여러 선진국에서 염해와 같은 열화환경의 피해를 받은 콘크리트 구조물이 예상공용년수 이전에 철거되거나. 개보수 비용이 초기 건설비용보다 더 많이 드는 예가 적지 않게 보고되면서, 적절한 내구성 유지대책 및 구조물의 장수명화를 위해 많은 연구와 노력이 진행되고 있다.(중략)