• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.168-168
• /
• 2009

핸드폰, 노트북과 같이 최신경량 전자재료로 만들어지는 전자제품의 수요가 급증함에 따라 반도체 배선의 폭이 점점 작아지고, 이로 인해 프린팅공정을 이용한 미세 배선기술이 활발히 개발되고 있다. 이에 본 연구는 미세배선에 높은 전기전도도를 부여하기 위하여 전기도금을 실시하였으며, 균일한 도금층을 얻기 위하여 첨가제에 따른 분극거동을 분석하고 이를 바탕으로 양극 및 음극 형상에 따른 구리의 성장 거동을 시뮬레이션을 통하여 분석하였다. 균일한 증착을 위해서는 첨가제의 역할도 중요하지만 양극과 음극의 형상에 따라서도 구리성장 거동에 영향을 미치는 것을 알 수 있었다.

• Journal of the Korean Electrochemical Society
• /
• v.10 no.2
• /
• pp.94-103
• /
• 2007

The transition of interconnection metal from aluminum alloy to copper has been introduced to meet the requirements of high speed, ultra-large scale integration, and high reliability of the semiconductor device. Since copper, which has low electrical resistivity and high resistance to degradation, has different electrical and material characteristics compared to aluminum alloy, new related materials and processes are needed to successfully fabricate the copper interconnection. In this review, some important factors of multilevel copper damascene process have been surveyed such as diffusion barrier, seed layer, organic additives for bottom-up electro/electroless deposition, chemical mechanical polishing, and capping layer to introduce the related issues and recent research trends on them.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.23.2-23.2
• /
• 2009

기존에 사용되었던 알루미늄 배선 공정은 공정의 배선 크기가 줄어들면서 한계에 다다르고 있다. 따라서 이를 대체하기 위해 여러 가지 새로운 방법들이 고안되고 있으며, 그중 알루미늄을 비저항이 낮고 EM(electro-migration) 저항성이 뛰어난 구리로 대체하려는 연구가 진행되고 있다. 구리 배선은 이미 electroplating 공정을 이용해 산업에 적용되고 있으며, seed layer로는 sputtering 법을 이용하고 있다. 하지만 sputtering 을 포함한 PVD 법은 대부분 종횡비나 단차 피복도가 좋지 않기 때문에 이를 CVD로 교체한다면 많은 장점을 가질 수 있다. 하지만 CVD 공정을 진행하기 위해서는 많은 문제점들이 있는데, 이중 전구체에 대한 문제도 빼놓을 수 없는 이슈이다. Cu(dmamb)2 는 기존에 사용하던 $\beta$-diketonate 계열의 전구체보다 화학적으로 많은 장점을 가지고 있어, CVD 공정에 적합하다. 이에 따라 구리 박막 증착의 공정 조건을 설계하고, 고품질의 박막을 증착하기 위한 다양한 처리법을 고안하여 증착 실험을 진행하였다. 기본적으로 구리는 확산력이 좋아 실리콘계열의 기판에서 확산력이 매우 좋아 기판 내로 확산되기 때문에 이를 방지하기 위하여 Ta, Ti 계열의 박막을 사용하여 확산을 방지하고 있다. 따라서 전이 금속 박막의 표면과 증착 분위기 등을 고려하여 구리를 증착하였으며, 표면의 미세구조 및 성분을 FESEM 등을 통해 분석하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.300-300
• /
• 2011

알루미늄을 이용한 배선은 반도체 소자가 초집적화와 초소고속화 됨에 따라, 피로현상과 지연시간 등 배선으로서의 많은 문제점을 가지고 있어, 차세대 배선 재료로서 전기적인 특성 등이 우수한 구리에 대한 연구가 많이 진행되고 있다. 하지만, 구리는 낮은 온도에서 확산이 잘되어 배선 층간의 절연에 문제점을 야기 시킨다. 따라서, 구리를 배선에 적용하여 신뢰성 있는 제품을 만들기 위해서는 확산방지막이 필요하다. 확산방지막은 집적화와 더불어 배선의 두께가 줄어 듦에 따라 소자의 특성에 영향을 미치지 않는 범위 내에서 저항은 낮고, 두께는 얇아야 하며, 높은 종횡비를 갖는 구조에서도 균일한 박막을 형성하여야 하므로, 원자층 증착공정을 이용한 연구가 주를 이루고 있다. 텅스텐 질화막을 이용한 확산방지막은 WF6 전구체를 이용한 보고가 많지만, 높은 증착 온도와 부산물로 인한 부식가능성 이라는 문제점을 안고 있다. 따라서 본 연구에서는, 기존의 할라이드 계열을 이용한 원자층 증착공정의 단점을 보완하기 위하여, 아마이드 계열의 전구체를 사용하여 텅스텐 질화막을 형성하였으며, 이를 통해 공정온도를 낮출 수 있었다.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.11a
• /
• pp.7-12
• /
• 2002

반도체 공정에서 구리(Cu) 배선의 미세구조와 신뢰성에 대해 연구하였는데, 특히 CVD Cu와 전기도금 Cu를 사용하여 신뢰성에 대한 texture와 결정 구조의 영향을 연구하였다 CVD Cu의 경우 여러 가지 시드층(seed layer)을 사용함으로서, 결정입자의 크기는 비슷하지만 texture가 전혀 다른 Cu 박막을 얻을 수 있었는데, 신뢰성 검사결과 (111) texture를 가진 Cu 배선의 수명이 (200) texture를 가진 Cu 배선의 수명보다 약 4배 가량 길게 나왔다. 전기도금 Cu 박막의 경우 항상 (111) texture를 갖고 있었으며 결정립의 크기도 CVD Cu의 것보다 더 컸다. Damascene 공법으로 회로 형성한 Cu 배선의 경우에도 전기도금 Cu의 결정립 크기가 CVD Cu의 것보다 더 크게 나타났으며, 신뢰성 검사결과 배선의 수명도 더 길게 나타났는데 그 차이는 0.4 $\mu\textrm{m}$ 이하의 미세선폭 영역에서 더욱 현저했다. 따라서 전기도금 Cu가 CVD Cu보다 신뢰성 측면에서 더 우수한 것으로 판명되었다.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.1
• /
• pp.21-25
• /
• 2015

Bending fatigue characteristics of Cu films and $8{\mu}m$ width Cu interconnects on flexible substrates were investigated, and fatigue reliability improvement was achieved through Mo-Ti alloy adhesion layer. Tensile bending fatigue reliability of Cu interconnects is 3 times lower than that of Cu films, and even compressive bending fatigue reliability of Cu interconnects is 6 times lower than that of Cu films. From these results, mechanical crack formation could be fatal in Cu interconnects. With Mo-Ti adhesion layer, fatigue reliability of Cu films and interconnects were enhanced due to the increase of adhesion strength and the suppression of slip induced crack initiation.

• Korean Chemical Engineering Research
• /
• v.59 no.4
• /
• pp.632-638
• /
• 2021

With the copper interconnection in the semiconductor process, complex residues including copper oxide, fluoride, and polymeric fluorocarbon are formed by plasma etching. In this study, a cleaning solution was prepared with a component having an amine group (-NH₂) and a carboxyl group (-COOH), and the characteristics of removing post-etch residues in the copper wiring process were analyzed. In the cleaning solution containing an amine group, the length of the component substituted with nitrogen and the length of the carbon chain influenced the cleaning effect, and the etching rate of copper oxide increased as the pH of the cleaning solution increased. The activity of the amine group is in the basic region, and the activity of the carboxyl group is in the acidic region, and the cleaning process proceeds through complex formation with copper or copper oxide in each region.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.3-4
• /
• 2008

로직 디바이스에서는 알루미늄을 대신하여 구리로 backend-of-line(BEOL) 금속화공정이 대체되고 있다. 그러나 메모리 디바이스에서 구리 배선으로의 전환이 쉽지 않다. Cu-seed layer는 구리 배선을 메모리 디바이스에 적용하기 위해서 필요한 gap-fill 확장성을 개선하기 위한 중요한 부분을 차지한다. Cu-seed layer 증착을 위한 향상된 PVD 장비인 Eni 스퍼터를 소개한다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.260-260
• /
• 2012

최근 IT산업의 급속한 발달로 모바일 제품과 반도체 및 IC 패키지 등의 전자제품의 소형화, 경량화 및 고성능화되어 가고 있다. 따라서 반도체 공정에서 단위소자의 고속화를 구현하기 위한 금속배선공정에 사용되는 금속재료가 최근에 최소 선폭을 갖는 디바이스에서는 구리를 배선 재료로 전환하고, 향후에는 모든 디바이스가 구리를 주요 배선재료로 사용할 것으로 예측되고 있다. 반도체 소자 공정 중 시료 표면 위에 형성되는 오염물은 파티클, 유기오염물, 금속 불순물 그리고 자연 산화막으로 나눌 수 있다. 구리 표면에 생성되는 부식생성물의 종류에는 CuO, $Cu_2O$, $Cu(OH)_2$, $CuCO_3{\cdot}Cu(OH)_2$와 같은 생성물들이 있다. 이러한 부식생성물이 구리박막 표면에 형성이 되면 성장된 구리박막의 특성을 저하시키게 된다. 이러한 다양한 오염물들을 제거하기 위해서 여러 가지 전처리 공정에 대한 연구가 보고되고 있다. 본 연구에서, 스퍼터 방식으로 구리를 증착한 웨이퍼 (Cu/Ti/Si) 를 대기 중에 노출시켜 자연 산화막을 성장시키고, 이 산화막과 대기로부터 흡착된 불순물을 제거하기 위해 계면 활성제인 TS-40A와 $NH_4OH$ 수용액을 사용하여 이들 수용액이 구리 표면층에 미치는 영향에 대해 조사 분석하였다. 사용된 TS-40A는 알칼리 탈지제로서 웨이퍼 표면의 유기물을 제거하는 역할을 하며, $NH_4OH$는 구리를 제거하는 부식액으로 산업현장에서 널리 사용되고 있다. 다양한 표면 전처리 조건에 따른 구리박막 표면의 형상 및 미시적 특성변화를 SEM과 AFM을 이용하여 관찰하였고, 표면의 화학구조 및 성분 변화를 관찰하기 위해 XPS를 측정하였으며, 전기적 특성변화를 관찰하기 위해 4-point prove를 사용하여 박막의 면저항을 측정하였다.

• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.1
• /
• pp.45-50
• /
• 2014

Effects of wet chemical treatment and thermal cycle conditions on the quantitative interfacial adhesion energy of $Cu/SiN_x$ thin film interfaces were evaluated by 4-point bending test method. The test samples were cleaned by chemical treatment after Cu chemical-mechanical polishing (CMP). The thermal cycle test between Cu and $SiN_x$ capping layer was experimented at the temperature, -45 to $175^{\circ}C$ for 250 cycles. The measured interfacial adhesion energy increased from 10.57 to $14.87J/m^2$ after surface chemical treatment. After 250 thermal cycles, the interfacial adhesion energy decreased to $5.64J/m^2$ and $7.34J/m^2$ for without chemical treatment and with chemical treatment, respectively. The delaminated interfaces were confirmed as $Cu/SiN_x$ interface by using the scanning electron microscope and energy dispersive spectroscopy. From X-ray photoelectron spectroscopy analysis results, the relative Cu oxide amounts between $SiN_x$ and Cu decreased by chemical treatment and increased after thermal cycle. The thermal stress due to the mismatch of thermal expansion coefficient during thermal cycle seemed to weaken the $Cu/SiN_x$ interface adhesion, which led to increased CuO amounts at Cu film surface.