• Restorative Dentistry and Endodontics
• /
• v.31 no.6
• /
• pp.452-459
• /
• 2006

Competition will usually develop between the opposing walls as the restorative resin shrinks during polymerization. Magnitude of this phenomenon may be depended upon cavity configuration and volume. The purpose of this sturdy was to evaluate the effect of cavity configuration and volume on microleakage of composite resin restoration that has margins on the enamel site only. The labial enamel of forty bovine teeth was ground using a model trimmer to expose a flat enamel surface. Four groups with cylindrical cavities were defined, according to volume and configuration factor(Depth x Diameter / C-factor) - Group I : 1.5 mm ${\times}$ 2.0 mm / 4.0, Group II : 1.5 mm ${\times}$ 6.0 mm / 2.0, Group III : 2.Omm ${\times}$ 1.72 mm / 5.62, Group IV : 2.0 mm ${\times}$ 5.23 mm / 2.54. After treating with fifth-generation one-bottle adhesive - BC Plus$^{TM}$ (Vericom, AnYang, Korea), cavities were bulk flted with microhybrid composite resin - Denfill$^{TM}$ (Vericom). Teeth were stored in distilled water for one day at room temperature and were finished and polished with Sof-Lex system. Specimens were thermocycled 500 times between 5$^{\circ}$C and 55$^{\circ}$C for 30 second at each temperature. Teeth were isolated with two layers of nail varnish except the restoration surface and 1 mm surrounding margins. Electrical conductivity (${\mu}$A) was recorded in distilled water by electrochemical method. Microleakage scores were compared and analyzed using two-way ANOVA at 95% level. The results were as follows: 1. Small cavity volume showed lower microleakage score than large one, however, there was no statistically significant difference. 2. There was no relationship between cavity configuration and microleakage. Factors of cavity configuration and volume did not affect on microleakage of resin restorations with enamel margins only.

• Restorative Dentistry and Endodontics
• /
• v.28 no.6
• /
• pp.457-466
• /
• 2003

The aim of study was to investigate the effect of flow, specimen geometry and adhesion on the measurement of linear polymerization shrinkage of light cured composite resins using linear shrinkage measuring device. Four commercially available composites - an anterior posterior hybrid composite Z100, a posterior packable composite P60 and two flowable composites, Filtek flow and Tetric flow-were studied. The linear polymerization shrinkage of composites was determined using 'bonded disc method' and 'non-bond-ed' free shrinkage method at varying C-factor in the range of 1∼8 by changing specimen geometry. These measured linear shrinkage values were compared with free volumetric shrinkage values. The viscosity and flow of composites were determined and compared by measuring the dropping speed of metal rod under constant load. In non-bonded method, the linear shrinkage approximated one third of true volumetric shrink-age by isotropic contraction. However, in bonded disc method, as the bonded surface increased the linear shrinkage increased up to volumetric shrinkage value by anisotropic contraction. The linear shrinkage value increased with increasing C-factor and approximated true volumetric shrinkage and reached plateau at about C-factor 5∼6. The more flow the composite was, reduced linear shrinkage was measured by compensation radial flow.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.34 no.1
• /
• pp.62-72
• /
• 2007

The purpose of present study was to determine whether different kinds of curing lights can alter microtensile bond strength(MTBS) of class I cavity pulpal and axial wall specimens in primary molar. Thirty clean mandibular 2nd primary molar's occlusal enamel were removed and class I cavity, size of $2{\times}4{\times}2mm$ was prepared. Dentin bonding agent was applied according to manufacturer's manual. Each group was cured with Halogen Curing Unit, Plasma Curing Unit and LED Curing Unit. Composite resin was bulk filled and photo cured with same curing unit. MTBS specimens which size is $0.7{\times}0.7{\times}4mm$ were prepared with low speed saw. Specimens were coded by their curing lights and wall positions (Halogen - Axial wall group, Halogen - Pulpal wall group, Plasma - Axial wall group, Plasma - Pulpal wall group, LED - Axial wall group, LED - Pulpal walt group). MTBS were tested at 1 mm/min cross Head speed by Universal Testing Machine. Fractured surface and bonding surface was observed with SEM. T-test between axial and pulpal specimens in each curing lights, one-way ANOVA among different curing light specimens in each wall positions were done. Weibull distribution analysis was done. The results were as follows : Mean MTBS of pulpal wall specimens were significantly greater than that of axial wall specimens at each curing units(p<.05). There was no significant difference in the MTBS among three curing units at axial wall and pulpal wall. In Weibull distribution, pulpal wall specimens were more homogeneous than axial wall specimens.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.43 no.4
• /
• pp.427-434
• /
• 2016

The aim of this study was to compare the mechanical properties of high viscosity bulk-fill resin composites, $Filtek^{TM}$ Bulk Fill Posterior Restorative (FBF) and $Tetric^{(R)}$ N-Ceram Bulk Fill (TBF), with conventional composite ($Filtek^{TM}$ Z-350 XT, Z-350). The Vickers hardness test which indicates the degree of conversion was performed and the dye penetration test was performed to measure the microleakage which indicates polymerization shrinkage amount. To minimize experimental error, the standardized 3D-printed molds and the bovine teeth were used. Obtained data were analyzed by the Kruskal-Wallis test and Mann-Whitney test with the confidence interval of 95%. In the microhardness test within 1 hour of polymerization, lower surface of FBF and TBF showed significantly lower value than that of Z-350 (p < 0.05). But after 24 hours, the microhardness of FBF had increased and showed no significant difference with Z-350 (p > 0.05). In top and 2 mm depth surface, mean microhardness values were in the following order: Z-350 > FBF > TBF (p < 0.05). The mean microleakage value of TBF was significantly lower than others (p < 0.05). For clinical application of bulk-fill resin composites, caution for applying masticatory forces during 24 hours after polymerization is advised and further studies to decrease microleakage should be conducted.

• Polymer(Korea)
• /
• v.35 no.1
• /
• pp.94-98
• /
• 2011

Poly(2-hydroxyethyl methacrylate), PHEMA, hybrid gels containing Pluronic and acrylic acid (AAc) were prepared as new biocompatible and stimuli-responsive hydrogels by photo-polymerization technique. The prepared hybrid gel showed reversible, temperature-responsive swelling behavior due to the presence of Pluronic component, which underwent sol-gel transition at an elevated temperature to cause gel shrinkage. The hydrogel also exhibited increased swelling degrees and pH-sensitivity due to the AAc component with ionizable carboxylic acid groups. The microporous gel morphology and its changes upon stimuli was observed by scanning electron microscopy.

• Journal of Technologic Dentistry
• /
• v.43 no.1
• /
• pp.1-5
• /
• 2021

Purpose: To perform a comparative study on curing shrinkage according to the thickness of photopolymerization resin. Methods: Stainless steel molds of 2, 4, and 6 mm heights were prepared. The 2, 4, and 6 mm-height molds were classified as the 2H, 4H, and 6H groups, respectively. A photopolymerization resin was injected into the stainless steel mold. Photopolymerization was carried out using a photopolymer machine. During photopolymerization, the wavelength and intensity of 400~405 nm were set to 10, the highest intensity among 1~10. Photopolymerization was performed for 30 min per specimen (each group=10). The inner and outer areas of the specimen were measured. The data were analyzed using one-way ANOVA and Kruskal-Wallis H test (α=0.05). Results: In terms of the inner and outer diameters of the photopolymerization resin specimen, the 2H group contracted the most, whereas the 6H group contracted the least. A statistically significant difference was found between the groups (p<0.05). Conclusion: The amount of light irradiation of the photopolymerization resin must be adjusted according to the thickness.

• Restorative Dentistry and Endodontics
• /
• v.19 no.1
• /
• pp.135-147
• /
• 1994

This study was conducted to evaluate whether the fatigue toughness of visible light cured composite resins could be improved and how much percentage of polymerzation shrinkage could be affected by additional heat treatment. 7 materials were investigated for this study: P-50, Lite-fil CR inlay, Pekafil, Clearfil CR inlay, Clearfil photo posterior, Z -100 and Progress. Diametral tensile strengths and linear shrinkages of composite resins were taken under visible light cured and additional post-cure heated condition and compared each other. A fatigue toughness of above materials was evaluated by measuring diametral tensile strength after they were repeatedly loaded with 120kgf/$cm^2$ up to 3000 cycles. The results obtained were as follows : 1. When composite resins were cured just by visible light, Lite fil CR inlay, Z -100 and Progress showed respectively higher diametral tensile strength than the other materials. Clearfil CR inlay, Clearfil photo posterior and Progress exhibited strong fatigue toughness compared to P-50 and Pekafil. 2. Post-cure heat treated composite resins had higher diametral tensile strengths than visible light cured composite resins at fatigue toughness test as well as no fatigue toughness test. 3. When Composite resins were additionally polymerized by post-cure heat treatment, P-50 showed weak fatigue toughness, on the contrary, Clearfil CR inlay, Z-100, Progress showed strong one. 4. When composite resins were cured just by visible light, percentage of polymerization linear shrinkage was the lowerest in Clearfil CR inlay, followed by, in ascending order, Clearfil photo posterior, Lite-fil CR inlay, Progress, Pekafil, P-50, and Z-100. In the case of post- cure heat treated composite resins, percentage of linear shrinkage was the lowest in Clearfil photo posterior, followed by, in ascending order, Lite-til CR inlay, Clearfil CR inlay, Progress, P-50, Pekafil and Z-100. 5. Percentage of polymerization linear shrinkage was greater in the post-cure heat treated composite resins than in the visible light cured composite resins and linear shrinkage increased significantly in Pekafil, Clearfil CR inlay, and Clearfil photo posterior between at the visible light cured and at the post-cure heat treated condition. The above results is saying that additional post-cure heat treatment on the composite resins for posterior restoration is able to affect on improvement of strength and fatigue toughness and lead to increase polymerization of composite resins.

• Journal of dental hygiene science
• /
• v.14 no.2
• /
• pp.94-100
• /
• 2014

The purpose of this study was to evaluate the accuracy of digitized elastomeric impression materials of crown abutment, using non-contact white light scanner and virtual three-dimensional superimpositional analysis. The stone models and impressions were digitized white light scanner to create three-dimensional surface models. Stone models were used as CAD reference model (CRM). The resulting point clouds (ASC file) from digitization of impressions using converting software. Discrepancies between the points in the point clouds and CRM were measured by superimpositional software. Mean and standard deviation of values of discrepancies were analyzed by one-way ANOVA and multiple comparison (${\alpha}=0.05$). The mean discrepancy between the impressions for the extra-light body (XLB), light body (LB), and heavy body (HB) group were $5.10{\pm}1.45{\mu}m$, $6.30{\pm}1.87{\mu}m$, $9.80{\pm}1.52{\mu}m$, respectively. The different impression materials affected the digitization of impressions significantly (p<0.05). As a result, digitization of elastomeric impression materials on dental scanner was influenced by material sort.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.30 no.2
• /
• pp.196-203
• /
• 2003

The application of sealants is a highly technique-sensitive procedure, requiring an extremely dry field prior to placement. Moisture contamination of the etched enamel surface before sealant placement is cited as the main reason for sealant failure. The purpose of this study was to evaluate the effects of different methods of sealant application on the shear bond strength of sealants to enamel. In groups 1, 2, 3, 4 Teethmate(unfilled sealant) was used, while Ultraseal XTplus(filled sealant) was used in groups 5, 6, 7, 8. Groups 1 and 5(control) were acid etched for 15 seconds using 35% phosphoric acid, washed and then dried. In groups 2, 6 drying agents were applied, and in groups 3, 7 bonding agents were applied and light cured. In groups 4 and 8 both drying agent and bonding agent were applied. Then sealant was cured to the specimen using molds 3mm in diameter and 2mm in height. Thermocycling was performed and shear bond strength was finally measured. The following results were obtained : 1. Groups using filled sealant(groups 5, 6, 7, 8) showed higher shear bond strengths compared to groups using unfilled sealant(groups 1, 2, 3, 4). 2. Among groups using unfilled sealant(groups 1, 2, 3, 4), groups 2, 3, 4 showed significantly higher shear bond strength compared to group 1(p<0.05). There were no significant differences among groups 2, 3 and 4. 3. There were no significant differences(p>0.05) among groups using filled sealant(groups 5, 6, 7, 8). 4. When modes of fracture were examined, cohesive failure was observed in groups 2, 3 and 4.

• Restorative Dentistry and Endodontics
• /
• v.33 no.5
• /
• pp.472-480
• /
• 2008

This study was conducted to evaluate the influence of the C-factor on the bond strength of a 6th generation self-etching system by measuring the microtensile bond strength of four types of restorations classified by different C-factors with an identical depth of dentin. Eighty human molars were divided into four experimental groups, each of which had a C-factor of 0.25, 2, 3 or 4. Each group was then further divided into four subgroups based on the adhesive and composite resin used. The adhesives used for this study were AQ Bond Plus (Sun Medical, Japan) and XenoIII (DENTSPLY, Germany). And composite resins used were fantasists (Sun Medical, Japan) and Ceram-X mono (DENTSPLY, Germany). The results were then analyzed using one-way ANOVA, a Tukey's test, and a Pearson's correlation test and were as follows. 1. There was no significant difference among C-factor groups with the exception of groups of Xeno III and Ceram-X mono (p<0.05). 2. There was no significant difference between any of the adhesives and composite resins in groups with C-factor 0.25, 2 and 4. 3. There was no correlation between the change in C-factor and microtensile bond strength in the Fantasista groups. It was concluded that the C-factor of cavities does not have a significant effect on the microtensile bond strength of the restorations when cavities of the same depth of dentin are restored using composite resin in conjunction with the 6th generation self-etching system.