• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.05a
• /
• pp.108-109
• /
• 2014

The purpose of this study is to enhance durability of solidifying mat. solidifying mat excellent mechanical properties of geotextile. multi-layer coating system is applied to the mat and the chloride ions penetration resistance, chemical resistance, accelerated carbonation test were evaluated by testing the durability. Durability test results are as follows. chloride ions penetration resistance results are coated mat is approximately 70 % lower than plain. chemical resistance test results are coated mat no discoloration. accelerated carbonation test results are coated mat is approximately 90 % lower than the plain.

• Journal of the Korean GEO-environmental Society
• /
• v.12 no.1
• /
• pp.71-80
• /
• 2011

In period of rapid economic development, as doing river conservation work by using harmful materials environmental pollution has adversely effected humans, animals and plants frequently. For recovery of environmental pollution it needs a lot of time and cost. Therefore, in this study, in order to take an environment-friendly method which is also economical and durable both results of the laboratory model test and field test were compared and analyzed. According to the results of the laboratory model test, those methods such as concrete paving, asphalt paving, bentonite mat, stabilized soil method and mixed soil method have small amount of seepage, but on the other hand compaction soil, grassland and permeable materials have considerable amount of seepage. The results of field test show a similar tendency with laboratory test and have been satisfied to assess standard of domestic water permeability below $1.0{\times}10^{-7}cm/sec$ and unconfined compressive strength is also than 1.0MPa so it has been satisfied about standard. In conclusion, as compaction rate increased, as unconfined compression strength increased and coefficient of permeability decreased.

• Resources Recycling
• /
• v.1 no.1
• /
• pp.14-22
• /
• 1992

As a basic study to recover the copper from the copper converter slag, the characterisitcs of converter slag was studied. The results obtained in this work are as follows. 1. The copper converter slag is composed of Cu, $Cu_2$S, $Fe_3$$O_4$, Fayalite and silicate. 2. It is supposed that magnetite in converter slag is oxidized to hematite at $720^{\circ}C$ and this phase is soluted to fayalite. 3. As the converter slag is added in the water solution, pH increased and the heavy metal ions in the water are adsorbed on the slag. 4. Work index of the converter slag cooled for the 10 hour and the 2 hour are 25~27 kWh/ton and 35 kWh/ton, respectively. 5. In the case of grinding test of converter slag, fayalite in converter slag is easily grinded than magnetite in converter slag.