Characterisitics of the Copper Converter Slag -Recovery of Copper from the Copper Converter Slag(I)-

동제연소 전노슬래그의 생성에 관하여 -동제연소 전노슬래그로 부터 동의 회수(I)-

As a basic study to recover the copper from the copper converter slag, the characterisitcs of converter slag was studied. The results obtained in this work are as follows. 1. The copper converter slag is composed of Cu, $Cu_2$S, $Fe_3$$O_4$, Fayalite and silicate. 2. It is supposed that magnetite in converter slag is oxidized to hematite at $720^{\circ}C$ and this phase is soluted to fayalite. 3. As the converter slag is added in the water solution, pH increased and the heavy metal ions in the water are adsorbed on the slag. 4. Work index of the converter slag cooled for the 10 hour and the 2 hour are 25~27 kWh/ton and 35 kWh/ton, respectively. 5. In the case of grinding test of converter slag, fayalite in converter slag is easily grinded than magnetite in converter slag.

본 연구에서는 전로슬래그를 부선공정하기 앞서 전로슬래그의 물성을 파악하고, 이를 통하여 회소코자 하는 Ca 성분의 분포특성을 조사하였다. 그리고 슬래그의 재용융시 반응특성과 수용액중에서의 특성 및 마광시 필요한 Work Index값을 구하였으며 이를 통하여 다음과 같은 결론을 얻었다. 1. 전로슬래그의 조직은 금속동(Cu), 황동광(Cu$_{2}$S), 자철광(Fe$_{3}O_{4}$), Fayalite(2FeO${\cdot}$S$_{1}O_{2}$) 및 편석부의(silicate 와 철산화물0로 되어 있으며, 이중 슬래그 내부로 혼입된 매트상들은 Cu 단상, Cu$_{2}$S 단상, Cu-Cu$_{2}$S 이혼공창화직으로 되어있다. 2. 전로슬래그는 재용융시 720$^{\circ}C$ 부근에서 Magnetite가 Hematite로 산화되어 Fayalite와 고락체를 형성하는 것으로 사료된다. 3. 전로슬래그는 수용액 중에서 용액의 pH를 상승시키며, 용액중의 중금속이온을 흡착하였다. 4. 본 연구는 사용한 전로슬래그의 work index는 10시간 영각 고화 슬래그의 경우 25~27 kWh/ton이고, 2시간 영각 고화 슬래그의 경우는 35kWh/ton이다. 5. 전로슬래그의 성분별 마광특서을 조사한 결과, Faylite(2FeO${\cdot}SiO_{2}$에 비해 Magnetite(Fe$_{3}O_{4}$가 마광도가 낮았다.