• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.73-76
• /
• 2001

We deposited epitaxial $Ba_{0.6}$S $r_{0.4}$Ti $O_3$(BST) films having thickness of 400 nm on MgO(001) substrates, where a 10 nm thick $Ba_{1-x}$S $r_{x}$Ti $O_3$(x=0.1-0.7) interlayer was inserted between BST and MgO to manipulate the stress of the BST films. Since the main difference of those epitaxial BST films was the lattice constant of the interlayers, we were very successful in controlling the stress of the BST films. BST films under small tensile stress showed larger dielectric constant than that without stress as well as those under compressive stress. Stress relaxation was investigated using epitaxial BST films with various thicknesses grown on different interlayers. For BST films grown on $Ba_{0.7}$S $r_{0.3}$Ti $O_3$ interlayers, the critical thickness was about 600 nm. On the other hand, the critical thickness of single-layer BST film was less than 100 nm.00 nm.m.m.m.

• Journal of the Korean Ceramic Society
• /
• v.43 no.6 s.289
• /
• pp.362-368
• /
• 2006

Epitaxial $Ba_{0.5}Sr_{0.5}TiO_3$ (BSTO) thin films have been grown on TiN buffered Si (001) substrates by Pulsed Laser Deposition (PLD) method and the effects of substrate temperature and oxygen partial pressure during the deposition on their dielectric properties and crystallinity were investigated. The crystal orientation, epitaxy nature, and microstructure of oxide thin films were investigated using X-Ray Diffraction (XRD) and Transmission Electron Microscopy (TEM). Thin films were prepared with laser fluence of $4.2\;J/cm^2\;and\;3\;J/cm^2$, repetition rate of 8 Hz and 10 Hz, substrate temperatures of $700^{\circ}C$ and ranging from $350^{\circ}C\;to\;700^{\circ}C$ for TiN and oxide respectively. BSTO thin-films were grown on TiN-buffered Si substrates at various oxygen partial pressure ranging from $1{\times}10^{-4}$ torr to $1{\times}10^{-5}$ torr. The TiN buffer layer and BSTO thin films were grown with cube-on-cube epitaxial orientation relationship of $[110](001)_{BSTO}{\parallel}[110](001)_{TiN}{\parallel}[110](001)_{Si}$. The crystallinity of BSTO thin films was improved with increasing substrate temperature. C-axis lattice parameters of BSTO thin films, calculated from XRD ${\theta}-2{\theta}$ scans, decreased from 0.408 m to 0.404 nm and the dielectric constants of BSTO epitaxial thin films increased from 440 to 938 with increasing processing oxygen partial pressure.

• Bulletin of the Korean Chemical Society
• /
• v.29 no.2
• /
• pp.427-430
• /
• 2008

BaTiO3 and SrTiO3 thin films were fabricated on Pt/Ti/SiO2/Si substrate by the pulsed laser deposition process. The dependence of the deposited film quality upon the partial oxygen pressure during the deposition process was importantly examined. Regardless of the oxygen pressure, the as-deposited films were not fully crystallized. However, the film deposited at low oxygen pressure became well crystallized after the annealing process. It was concluded, therefore, that the partial oxygen pressure is reduced as low as possible during the deposition process and then anneal the as-deposited samples at ambient pressure to fabricate the well crystallized SrTiO3 and BaTiO3 films by laser ablation.

• Proceedings of the KIEE Conference
• /
• 1999.11d
• /
• pp.845-847
• /
• 1999

(Ba, Sr)$TiO_3$[BST] thin films were fabricated on Pt/$TiO_2/SiO_2$/Si substrate by RF sputtering. The structural and dielectric properties of the BST thin films were investigated with the deposition time. Increasing the deposition time from 20 min. to 60 min., second phases were decreased, and EST (111), (100), (200) peaks were increased. The relative dielectric constant and dielectric loss of the EST thin films with the thickness of 3000$\AA$ were 300 and 0.018, respectively at 1[kHz]. The relative dielectric constants was decreased and dielectric losses was increased as increasing the frequency.

• Proceedings of the KIEE Conference
• /
• 1998.11c
• /
• pp.740-742
• /
• 1998

In this paper, we described the effect of rapid thermal annealing on the electrical properties of interfacial layer between various top electrodes and $(Ba_{0.5}Sr_{0.5})TiO_3$ thin films. BST thin films were fabricated on Pt/TiN/$SiO_2$/Si substrate by RF magnetron sputtering technique. AI, Ag, and Cu films for the formation of top electrode were deposited on BST thin films by thermal evaporator. Top electrodes/BST/Pt capacitor annealed with rapid thermal annealing at various temperature. In $(Ba_{0.5}Sr_{0.5})TiO_3$ thin films with Cu top electrode annealed at $500^{\circ}C$, the dielectric constant was measured to the value of 366 at 1.2 [kHz] and the leakage current was obtained to the value of $5.85{\times}10^{-7}\;[A/cm^2}$ at the forward bias of 2 [V].

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.05a
• /
• pp.57-57
• /
• 2002

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.05a
• /
• pp.22-22
• /
• 1999

• Korean Journal of Materials Research
• /
• v.4 no.4
• /
• pp.453-458
• /
• 1994

$(Ba_{0.5}Sr_{0.5)/TiO_3$(BST) thin films were prepared for the application of 256 Mb DRAM by RF magnetron sputtering. The crystallinity of BST thin films increased with increasing deposition tempera lure. The composition of thin films was $(Ba_{0.48}Sr_{0.48)/TiO_{2.93}$ Pt/Ti barrier layer suppressed the diffusion of Si into BST layer. The films showed a dielectric constant of 320 and a dissipation factor of 0.022 at 100 kHz. the change of capacitance of the films with applied voltage was small, showing paraelectric property. The charge storage density and leakage current density were 40fC/$\mu \textrm{m}^{2}$ and 0.8$\mu A/\textrm{cm}^2$, respectively at a field of 0.15 MV/cm. The BST films obtained by RF magnetron sputtering appeared to be potential thin film capacitors for 256 Mb DRAM application.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.11a
• /
• pp.243-246
• /
• 1998

(Ba, Sr)TiO$_3$[BST] thin films were fabricated on Pt/SiO$_2$/Si substrate by RF sputtering technique. The structural, dielectric and electrical properties of BST thin films were investigated with Ar/O$_2$ ratio. Dielectric constant and dielectric loss of the BST thin film were about 1020 and 2.0[%], respectively. (at RF power 80W, post annealing temperature $650^{\circ}C$, deposition pressure of 5mTorr and Ar/O$_2$=80/20). For the BST(Ar/O$_2$=80/20) thin film with Polarization switching cycles of 10$^{10}$ , remanent polarization and coercive field were 0.084[$\mu$C/cm$^2$], 1.954[kV/cm], respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.217-220
• /
• 1997

(Ba,Sr)TiO$_3$ thin film capacitors were prepared on SiO$_3$/Si(100)wafer by RF sputtering technique. The structural and crystallographic properties were studied with deposition conditions and annealing temperatures. Microstructural properties of (Ba,Sr)TiO$_3$ thin films were investigated by the SEM, XRD. The thickness and grain size were studied for the varying of RF power and temperature.