In this study, (Ba,Sr)TiO$_3$(BST) thin films were etched with a magnetically enhanced inductively coupled plasma(MEICP). Etching characteristics of BST thin films including etch rate and selectivity were evaluated as a function of the etching parameters such as gas mixing ratio, rf power, dc bias voltage and chamber pressure. The maximum etch rate of the BST films was 1700 $\AA$/min at Ar(90)/CF$_4$(10), 600 W/350 V and 5 mTorr. The selectivity of BST to PR was 0.6, 0.7, respectively. To analyze the composition of surface residue remaining after the etching, samples etched with different CF$_4$/Ar gas mixing ratio were investigated with X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectrometry (SIMS). From the results of XPS and SIMS, there are chemical reaction between Ba, Sr, Ti and C, F radicals during the etching and remained on the surface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.377-380
• /
• 2001

The BST thin films to composite (Ba$\sub$x/Sr$\sub$l-x/)TiO$_3$ using sol-gel method were fabricated on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric materials was investigated by structural and electrical properties. BST solution was composited by moi ratio, and then spin-coated (from 3 times to 5 times coating on Pt/SiO$_2$/Si substrate. Thickness of BST ceramics thin films are about 2600∼2800[${\AA}$] in 3 times deposition. The property of leakage current was stable when the applied voltage was 3[V]. Leakage current of 3 times coated BST thin film was 10$\^$-9/∼10$\^$-11/[A] at 0∼3[V].

• Journal of the Korean Vacuum Society
• /
• v.9 no.3
• /
• pp.242-248
• /
• 2000

BST thin films were prepared with various deposition conditions by rf-magnetron sputtering. As substrate temperature increases and Ar/$O_2$ratio decreases, the electrical properties of the BST films improve. The conventional Schottky model and modified-Schottky model were introduced in order to investigate the leakage-current-conduction mechanisms of the deposited films. It was found that the modified-Schottky model better describes the current-conduction mechanism in the BST films than the conventional Schottky model. From the modified-Schottky model, optical dielectric constant ($\varepsilon$), electronic drift mobility ($\mu$), and barrier height $({\phi}_b)are calculated as $\varepsilon$=4.9, $\mu$=0.019 $\textrm{cm}^2$/V-s, and ${\phi}_b=0.79 eV.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.55-56
• /
• 2006

In this paper, we first applied the chemical mechanical polishing (CMP) process to the planarization of ferroelectric film in order to obtain a good planarity of electrode/ferroelectric film interface. BST ($Ba_{0.6}Sr_{0.4}TiO_3$), PZT ($Pb_{1.1}(Zr_{0.52}TiO_{0.48})O_3$) and BTO ($BaTiO_3$) ferroelectric film are fabricated by the sol-gel method. And then, we compared the structural characteristics before and after CMP process of BST, PZT, BTO films. Their dependence on slurry composition was also investigated. We expect that our results will be useful promise of global planarization for ferroelectric random access memories (FRAM) application in the near future.

• The Korean Journal of Ceramics
• /
• v.3 no.4
• /
• pp.274-278
• /
• 1997

(Ba, Sr) TiO$_3$(BST) thin films were prepared on RuO$_2$/Si substrates by rf magnetron sputtering and annealing was followed at temperatures ranging from 550 to 80$0^{\circ}C$ in $N_2$or $O_2$atmosphere. The effects of annealing conditions on the properties of BST film deposited on RuO$_2$bottom electrodes were investigated. It was found that the crystallinity. surface roughness, and grain size of BST films vary with the annealing temperature but they are not dependent upon the annealing atmosphere. The flat region in the current-voltage (I-V) curves of BST capacitors shortened with increasing annealing temperature under both atmospheres. This is believed to be due to the lowering of potential barrier caused by unstable interface and the increase of charge The shortening of the flat region by $O_2$annealing was more severe than that by $N_2$-annealing. As a result, there was no flat region when the films were annealed at 700 and 80$0^{\circ}C$ in $O_2$atmosphere. The dielectric properties of BST films were improved by annealing in either atmosphere. however, a degradation with frequency was observed when the films were annealed at relatively high temperature under $O_2$atmosphere.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.183.2-183
• /
• 2000

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.05a
• /
• pp.37-37
• /
• 1996

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.263-266
• /
• 2001

In this paper, we investigated dielectric properies for BST thin films that was deposited on MgO/Si substrates using RF magnetron sputtering. In here, MgO film was used to perform that a diffusion b arrier between the BST film and Si substrate and a buffer layer to assist the BST film growth. A d eposition condition for MgO films was RF Power of 50W, substrate temperature of room temperature and the working gas ratio of Ar:O$_2$ were varied from 90:10 to 60:47. Finally we manufactured the cap acitor of Al/BST/MgO/Si/Al structure to know electrical properties of this capacitor through I-V, C-V measurement. In the results, C-V aha racteristic curves was shown a ferroelectric property so we measured P-E. A remanent poliazation and coerceive electric field was present 2$\mu$C/cm$^2$ and -27kV/cm respectively at Ar:O$_2$=90:10. And a va clue of dielectric constant was 86 at Ar:02=90:10.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05b
• /
• pp.107-110
• /
• 2002

The optical memory devices of BST thin films to composite $(Ba_{0.7}\;Sr_{0.3})TiO_{3}$ using sol-gel method were fabricated by changing of the depositing layer number on $Pt/Ti/SiO_{2}/Si$ substrate. The structural properties of optical memory devices to be ferroelectric was investigated by fractal analysis and 3-dimension image processing. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was $2500[\AA]$, $3500[\AA]$ and $3800[\AA]$. BST thin films exhibited the most pronounced grain growth. The surface morphology image was roughness with coating numbers. The thin films increasing with coating numbers shows a more textured and complex configuration.