• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.73-76
• /
• 2001

We deposited epitaxial $Ba_{0.6}$S $r_{0.4}$Ti $O_3$(BST) films having thickness of 400 nm on MgO(001) substrates, where a 10 nm thick $Ba_{1-x}$S $r_{x}$Ti $O_3$(x=0.1-0.7) interlayer was inserted between BST and MgO to manipulate the stress of the BST films. Since the main difference of those epitaxial BST films was the lattice constant of the interlayers, we were very successful in controlling the stress of the BST films. BST films under small tensile stress showed larger dielectric constant than that without stress as well as those under compressive stress. Stress relaxation was investigated using epitaxial BST films with various thicknesses grown on different interlayers. For BST films grown on $Ba_{0.7}$S $r_{0.3}$Ti $O_3$ interlayers, the critical thickness was about 600 nm. On the other hand, the critical thickness of single-layer BST film was less than 100 nm.00 nm.m.m.m.

• 한국세라믹학회지
• /
• 제43권6호
• /
• pp.362-368
• /
• 2006

Epitaxial $Ba_{0.5}Sr_{0.5}TiO_3$ (BSTO) thin films have been grown on TiN buffered Si (001) substrates by Pulsed Laser Deposition (PLD) method and the effects of substrate temperature and oxygen partial pressure during the deposition on their dielectric properties and crystallinity were investigated. The crystal orientation, epitaxy nature, and microstructure of oxide thin films were investigated using X-Ray Diffraction (XRD) and Transmission Electron Microscopy (TEM). Thin films were prepared with laser fluence of $4.2\;J/cm^2\;and\;3\;J/cm^2$, repetition rate of 8 Hz and 10 Hz, substrate temperatures of $700^{\circ}C$ and ranging from $350^{\circ}C\;to\;700^{\circ}C$ for TiN and oxide respectively. BSTO thin-films were grown on TiN-buffered Si substrates at various oxygen partial pressure ranging from $1{\times}10^{-4}$ torr to $1{\times}10^{-5}$ torr. The TiN buffer layer and BSTO thin films were grown with cube-on-cube epitaxial orientation relationship of $[110](001)_{BSTO}{\parallel}[110](001)_{TiN}{\parallel}[110](001)_{Si}$. The crystallinity of BSTO thin films was improved with increasing substrate temperature. C-axis lattice parameters of BSTO thin films, calculated from XRD ${\theta}-2{\theta}$ scans, decreased from 0.408 m to 0.404 nm and the dielectric constants of BSTO epitaxial thin films increased from 440 to 938 with increasing processing oxygen partial pressure.

• Bulletin of the Korean Chemical Society
• /
• 제29권2호
• /
• pp.427-430
• /
• 2008

BaTiO3 and SrTiO3 thin films were fabricated on Pt/Ti/SiO2/Si substrate by the pulsed laser deposition process. The dependence of the deposited film quality upon the partial oxygen pressure during the deposition process was importantly examined. Regardless of the oxygen pressure, the as-deposited films were not fully crystallized. However, the film deposited at low oxygen pressure became well crystallized after the annealing process. It was concluded, therefore, that the partial oxygen pressure is reduced as low as possible during the deposition process and then anneal the as-deposited samples at ambient pressure to fabricate the well crystallized SrTiO3 and BaTiO3 films by laser ablation.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1999년도 추계학술대회 논문집 학회본부 C
• /
• pp.845-847
• /
• 1999

(Ba, Sr)$TiO_3$[BST] thin films were fabricated on Pt/$TiO_2/SiO_2$/Si substrate by RF sputtering. The structural and dielectric properties of the BST thin films were investigated with the deposition time. Increasing the deposition time from 20 min. to 60 min., second phases were decreased, and EST (111), (100), (200) peaks were increased. The relative dielectric constant and dielectric loss of the EST thin films with the thickness of 3000$\AA$ were 300 and 0.018, respectively at 1[kHz]. The relative dielectric constants was decreased and dielectric losses was increased as increasing the frequency.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1998년도 추계학술대회 논문집 학회본부 C
• /
• pp.740-742
• /
• 1998

In this paper, we described the effect of rapid thermal annealing on the electrical properties of interfacial layer between various top electrodes and $(Ba_{0.5}Sr_{0.5})TiO_3$ thin films. BST thin films were fabricated on Pt/TiN/$SiO_2$/Si substrate by RF magnetron sputtering technique. AI, Ag, and Cu films for the formation of top electrode were deposited on BST thin films by thermal evaporator. Top electrodes/BST/Pt capacitor annealed with rapid thermal annealing at various temperature. In $(Ba_{0.5}Sr_{0.5})TiO_3$ thin films with Cu top electrode annealed at $500^{\circ}C$, the dielectric constant was measured to the value of 366 at 1.2 [kHz] and the leakage current was obtained to the value of $5.85{\times}10^{-7}\;[A/cm^2}$ at the forward bias of 2 [V].

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 춘계 학술발표강연 및 논문개요집
• /
• pp.57-57
• /
• 2002

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1999년도 춘계학술발표강연 및 눈문개요집
• /
• pp.22-22
• /
• 1999

• 한국재료학회지
• /
• 제4권4호
• /
• pp.453-458
• /
• 1994

256Mb DRAM에서 박막 커패시터로의 적용을 위해서$(Ba_{0.5}Sr_{0.5)/TiO_3$(BST)박막이 RF Magnetron Sprttering방법에 의해 제조되었다. BST박막의 결정화도는 기판온도가 높아짐에 따라 증가하였고 증착된 박막의 조성은 $(Ba_{0.48}Sr_{0.48)/TiO_{2.93}$이었다. 이때 Pt/Ti장벽층은 Si의 BST계면으로의 확산을 억제하였다. 100kHz에서의 유전상수 및 유전손실은 각각 320 및 0.022이었다. 인가전계도 (Charge Storage Density)는 40fC/$\mu \textrm{m}^{2}$, 누설전류밀도(Leakage Current Density)는 0.8$\mu A/\textrm{cm}^2$ 로서 RF Matnetron sputtering방법에 의해 제조된 BST 박막이 256Mb DRAM 적용 가능함을 보였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 추계학술대회 논문집
• /
• pp.243-246
• /
• 1998

(Ba, Sr)TiO$_3$[BST] thin films were fabricated on Pt/SiO$_2$/Si substrate by RF sputtering technique. The structural, dielectric and electrical properties of BST thin films were investigated with Ar/O$_2$ ratio. Dielectric constant and dielectric loss of the BST thin film were about 1020 and 2.0[%], respectively. (at RF power 80W, post annealing temperature $650^{\circ}C$, deposition pressure of 5mTorr and Ar/O$_2$=80/20). For the BST(Ar/O$_2$=80/20) thin film with Polarization switching cycles of 10$^{10}$ , remanent polarization and coercive field were 0.084[$\mu$C/cm$^2$], 1.954[kV/cm], respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1997년도 추계학술대회 논문집
• /
• pp.217-220
• /
• 1997

(Ba,Sr)TiO$_3$ thin film capacitors were prepared on SiO$_3$/Si(100)wafer by RF sputtering technique. The structural and crystallographic properties were studied with deposition conditions and annealing temperatures. Microstructural properties of (Ba,Sr)TiO$_3$ thin films were investigated by the SEM, XRD. The thickness and grain size were studied for the varying of RF power and temperature.