• Journal of the Korean Ceramic Society
• /
• v.34 no.8
• /
• pp.803-810
• /
• 1997

Ba0.5Sr0.5TiO3 thin films were deposited by RF magnetron sputliring method in order to clarify the anneal condition and doping effect on loakage current Nb and Al were selected as electron donor and acceptor dopants respectively, in the BST films because they have been known to have nearly same ionic radii as Ti and thought to substitute Ti sites to influence the charge carrier and the acceptor state adjacent to the gram boundary. BST thin films prepared in-situ at elevated temperature showed selatively high leakage current density and low breakdown voltage. In order to achieve smooth surface and to improve electrical properties, BST thin films were deposited at room temperature and annealed at elevated temperature. Post-annealed BST thin films showed smoother surface morphology and lower leakage current density than in-situ prepared thin films. The leakage current density of Al doped thin films was measured to be around 10-8A/cm2, which is much lower than those of undoped and Nb doped BST films. The result clearly demonstrates that higher Schottky barrier and lower mobile charge carrier concentration achieved by annealing in the oxygen atmosphere and by Al doping are desirable for reducing leakage current density in BST thin films.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.3
• /
• pp.90-94
• /
• 2004

The variation of electrical properties of (Ba,Sr)$TiO_3$ [BST] thin films for Metal-Insulator-Semiconductor (MIS) capacitors was investigated. BST thin films were deposited on p-Si(100) substrates by the RF magnetron sputtering with temperature range of 500~$600^{\circ}C$. The dielectric properties of MIS capacitors consisting of AUBST/$SiO_2$/Si sandwich structure were measured for various conditions. We examined the characteristics of MIS capacitor with various oxygen pressure, substrate temperature and (Ba+Sr)/Ti ratio. It was found that the leakage current was reduced in MIS capacitor with high quality $SiO_2$ layer was grown on bare p-Si substrate by thermal oxidation. The BST MIS structure showed relatively high capacitance even though it is the combination of high-dielectric BST thin films and $SiO_2$ layer. The charge state densities of the MIS capacitors and Current-voltage characteristics of the MIS capacitor were investigated. By applying $SiO_2$ layer between BST thin films and Si substrate, low leakage current of $10^{-10}$ order was observed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.196-196
• /
• 2008

We have investigated that the effect of post annealing on the structural and electrical properties of $Ba_{0.5}Sr_{0.5}TiO_3$ thin films. The BST thin films were deposited on n-type 4H-silicon carbide(SiC) using pulsed laser deposition (PLD). The deposition was carried out in oxygen ambient 100mTorr for 5 minutes, which results in about 300nm-thick BST films. For the BST/4H-SiC, 200nm thick silver was deposited on the BST films bye-beam evaporation. The X-ray diffraction patterns of the BST films revealed that the crystalline structure of BST thin films has been improved after post-annealing at $850^{\circ}C$ for 1 hour. The root mean square (RMS) surface roughness of the BST film measured by using a AFM was increased after post-annealing from 5.69nm to 11.49nm. The electrical properties of BST thin film were investigated by measuring the capacitance-voltage characteristics of a silver/BST/4H-SiC structure. After the post-annealing, dielectric constant of the film was increased from 159.67 to 355.33, which can be ascribed to the enhancement of the crystallinity of BST thin films.

• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1429-1436
• /
• 1994

We have prepared Ba0.5Sr0.5TiO3 thin films on Si substrate without buffer layer. Deposition was carried out by off-axis rf magnetron sputtering method using Ba0.5Sr0.5TiO3 stoichiometric target. The substrate temperature was changed from 40$0^{\circ}C$ to $700^{\circ}C$ during deposition. As the substrate temperature increased, relative intensity of (110) peak increased up to $600^{\circ}C$, however preferred orientation changed from (110) to (h00) beyond $650^{\circ}C$ of substrate temperature. Deposited films showed microstructures with fine grains whose diameters are less than 100 nm, and columnar structure was observed in the cross-sectional SEM micrograph. AES depth profile showed no significant diffusion at the interfacial reaction area. The effective dielectric constant of films showed maximum value at $600^{\circ}C$, and the leakage current increased with increasing substrate temperature, which may be ascribed to the crystallization of amorphous phases at grain boundary.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.05a
• /
• pp.31-34
• /
• 2006

In this study, $(Ba_{0.7}\;Sr_{0.3})TiO_3$ was coated on Pt/Ti/$SiO_2$/Si wafer by using Sol-Gel method. Coating process was repeated 3~5 times and then sintered at 750[$^{\circ}C$] for 1 hour. Each specimen was analyzed structure and electrical characteristics. In structure characteristics, EDX analyzed the samples ratio of the formation on the structural property. Thermal behavior was observed with TG-DTA and concluded that the heat-treatment of the samples was degreed 750[$^{\circ}C$]. Surface and section of thin films were observed with SEM.

• Proceedings of the Optical Society of Korea Conference
• /
• 2001.02a
• /
• pp.6-11
• /
• 2001

More than ten kinds of oxide thin films and their heterostructure have been successfully fabricated on SrTiO$_3$(001) substrates by laser molecular beam epitaxy (laser MBE). Measurements of atomic force microscopy (AFM), high-resolution transmission electron microscopy (HRTEM) and X-ray small-angle reflectivity reveal that the surfaces and interfaces are atom-level-smooth. The unit cell layers and the lattice structure are perfect. The electrical and optical properties of BaTiO$_3$-x thin films and BaTiO$_3$/SrTiO$_3$ (BTO/STO) superlattices were examined. The all-perovskite oxide P-N junctions have been successfully fabricated and the better I-V curves were observed.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.6
• /
• pp.504-510
• /
• 2002

Recently, thin film capacitors of high dielectric constant and low leakage current are applied to integrated devices. In this study, (Ba, Sr)$TiO_3$ (BST) thin films for low cost were prepared by Sol-Gel method. BST solution was spin-coated on Pt/$SiO_2$/Si substrate at 4,000 rpm for 10 seconds. Coating process was repeated 3 times and then sintered at $700^{\circ}C$ for 30 minutes. Structural and electrical characteristics of each specimen were analyzed by TG-DTA, SEM, fractal phenomenon, voltage-current and dielectric factor. Thickness of BST ceramics thin films are about 2,600~2,800 ${\AA}$ at depositing 3 times. Dielectric constant of thin films was decreased in 1 kHz~1 MHz. Dielectric constant and loss to frequency were 250 and 0.02 in $(Ba_{0.7}Sr_{0.3})TiO_3$ (BST3). Leakage current of BST3 was $10^{-9}\sim10^{-11}$/ A under 3 V.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.3 s.32
• /
• pp.63-70
• /
• 2004

The structural, electrical properties of $(Ba, Sr)TiO_3[BSTO]/RuO_2$ thin films were examined by the addition of amorphous BSTO layer between crystlline BSTO film and $RuO_2$ substrate. We prepared BSTO films with double-layered structure, that is, amorphous layers deposited at $60^{\circ}C$ and crystalline films. Crystalline films were prepared at 550 on amorphous BSTO layer. The thickness of the amorphous layers was varied from 0 to 170 nm. During the deposition of crystalline films, the crystallization of the amorphous layers occurred and the structure was changed to circular while crystalline BSTO films showed columnar structure. Due to insufficient annealing effect, amorphous BSTO phase was observed when the thickness of the amorphous layers exceeded 30 nm. Amorphous BSTO layer could also prevent the formation of oxygen deficient region in $RuO_2$ surface. Leakage current of total BSTO films decreased with increasing amorphous layer thickness due to structural modifications. Dielectric constant showed maxi-mum value of 343 when amorphous layer thickness was 30 nm at which the improvement by grain growth and the degradation by amorphous phase were balanced.

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1491-1493
• /
• 1997

In this study, Sol-Gel derived $Ba_{0.7}Sr_{0.3}TiO_3$ (BST(70/30)) thin films were investigated. The stock solution of BST were fabricated and spin-coated on the Pt/Ti/$SiO_2$/Si and ITO/glass substrates. The coated specimen were dried at $300^{\circ}C$ and finally annealed at $650{\sim}750^{\circ}C$. To analyse crystallization condition and microstructural morphology for different substrates, XRD, and SEM analysis were processed. In the BST(70/30) composition. dielectric constant and loss characteristics measured at 1kHz were 173, 0.01% for Pt/Ti/$SiO_2$/Si substrates and 181, 0.019% for ITO/glass substrates, respectively.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.160-160
• /
• 1999