• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.73-76
• /
• 2001

We deposited epitaxial $Ba_{0.6}Sr_{0.4}TiO_{3}(BST)$ films having thickness of 400 nm on MgO(001) substrates, where a 10 nm thick $Ba_{1-x}Sr_{x}TiO_{3}$ (x = 0.1 - 0.7) interlayer was inserted between BST and MgO to manipulate the stress of the BST films. Since the main difference of those epitaxial BST films was the lattice constant of the interlayers, we were very successful in controlling the stress of the BST films. BST films under small tensile stress showed larger dielectric constant than that without stress as well as those under compressive stress. Stress relaxation was investigated using epitaxial BST films with various thicknesses grown on different interlayers. For BST films grown on $Ba_{0.7}Sr_{0.3}TiO_{3}$ interlayers, the critical thickness was about 600 nm. On the other hand, the critical thickness of single-layer BST film was less than 100 nm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.649-652
• /
• 1999

The (Ba, Sr)TiO$_3$(BST) thin films were fabricated on Pt/Ti/SiO$_2$/Si substrate by RF sputtering technique. The structural properties of the BST thin films were investigated with substrate temperature by XRD, SEM, EDS and AES depth profils. Increasing the substrate temperature, barium multi titanate phases were decreased. The BST thin film had a structure of perovskite type, and had peaks of (100), (200) at the substrate temperature of 50$0^{\circ}C$. When the BST thin films were deposited at the substrate temperature of 50$0^{\circ}C$, the composition ratio of Ba/sr was 52/48.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.11a
• /
• pp.37-40
• /
• 1998

(Ba.Sr)TiO$_3$(BST) ceramics were fabricated with different Ba/Sr ratios and the str dielectric properties of the BST bulk ceramics were investigated. As the Ba/sr ratios dielectric constant decreased. (Ba$_{0.7}$Sr$_{0.3}$)TiO$_3$ (BST(70/30)) showed a maximum dielec value of $\varepsilon$$_{r}$=8.856, this showed that the decrease of Ba/Sr ratios had made BST thin dielectrics. Targets were fabricated and made into film by PLD process and the thin film by PLD process have good stoichiometry with the targets.rgets.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.121-124
• /
• 1999

The (Ba,Sr)TiO$_3$[BST] thin film were fabricated on the Pt/Ti/SiO$_2$/Si substrate by RF sputtering technique. The structural properties of the BST thin films were investigated with deposition time and substrate temperature by XRD. In the case of the BST thin films which has the deposition thin of 20 min, second phases and BST (111) peaks were increased with increasing the temperature of substrate. The capacitance of the BST thin film (deposition time of 20 min.) was decreased with the substrate temperature and was 1500pF with applied voltage of 1V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.73-76
• /
• 2001

We deposited epitaxial $Ba_{0.6}$S $r_{0.4}$Ti $O_3$(BST) films having thickness of 400 nm on MgO(001) substrates, where a 10 nm thick $Ba_{1-x}$S $r_{x}$Ti $O_3$(x=0.1-0.7) interlayer was inserted between BST and MgO to manipulate the stress of the BST films. Since the main difference of those epitaxial BST films was the lattice constant of the interlayers, we were very successful in controlling the stress of the BST films. BST films under small tensile stress showed larger dielectric constant than that without stress as well as those under compressive stress. Stress relaxation was investigated using epitaxial BST films with various thicknesses grown on different interlayers. For BST films grown on $Ba_{0.7}$S $r_{0.3}$Ti $O_3$ interlayers, the critical thickness was about 600 nm. On the other hand, the critical thickness of single-layer BST film was less than 100 nm.00 nm.m.m.m.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.11
• /
• pp.933-938
• /
• 2002

(Ba,Sr)TiO$_{4}$ (BST) thin films on Pt/Ti/SiO$_{2}$/Si substrates were deposited by a sol-gel method and the etch characteristics of BST thin films have been investigated as a function of gas mixing ratio. The maximum etch rate of the BST films was 440 $AA$/min under such conditions as: CF$_{4}$(CF$_{4}$＋Ar) of 0.2, RF-power of 700 W, DC-bias voltage of -200 V, pressure of 15 mTorr and substrate temperature of 30 $^{circ}C$. The selectivities of BST to Pt, SiO$_{2}$ and PR were 0.38, 0.25 and 0.09, respectively. In the XPS (X-ray photoelectron spectroscopy) analysis, Barium (Ba) and Strontium (Sr) component in BST thin films formed low volatile compounds such as BaFx, SrFx, which are forms by the chemical reaction with F atoms and is removed by Ar ion bombardment. Titanium (Ti) is removed by chemical reaction such as TiF with ease. The result of secondary ion mass spectrometry (SIMS) analysis confirmed the existence of the BaFx, SrFK, TiFx.

• Korean Journal of Crystallography
• /
• v.14 no.2
• /
• pp.73-78
• /
• 2003

(Ba/sub 1-x/Sr/sub x/)TiO₃ (BST, 0.4< x <0.65) single crystals were successfully grown by the TSSG (Top-Seeded Solution Growth) method, using a commercial [100] SrTiO₃ or as-grown [100] BST single crystals as seed crystals. To obtain the BST single crystals with various compositions x, the Ba/sr molar ratios in the solutions were systematically controlled while the Ti ion content among all cations was fixed at 67 mol%. A linear regression curve between their x values and the molar ratios of Sr/(Ba + Sr) in the solutions could be obtained, which in turn could used to select the initial composition to produce BST crystal with an aimed x value. In addition, the isothermal growth was found more effective for obtaining a compositional uniformity than a slow cooling process.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.2
• /
• pp.221-226
• /
• 1998

Amorphous (Ba, Sr)$TiO_3$[BST] layer(30, 70 nm) was introduced between crystalline BST and $RuO_2$electrode to realize double-layered BST structure in order to improve the properties of BST film. The structure and surface morphology of double-layered BST film were modified by the application of amorphous BST layer; that is, surface became smoother and grain size increased abruptly. Amorphous layer thicker than 30 nm was effective to hinder the influence of $RuO_2$surface on the structure of as-grown BST films by in-situ process. Dielectric constant of double-layered BST film was improved dramatically from 152 to 340 and leakage current was lowered from $1.25{\times}10^{-5}A/{\textrm}{cm}^2);to;6.85{\times}10^{-7}A/{\textrm}{cm}^2$, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.9
• /
• pp.711-717
• /
• 1998

BST(70/30) and BST(50/50) thin films were prepared by Sol-Gel method and studied about the microstructural and dielectric properties with Pt and ITO bottom electrodes. The stock solution was synthesized and spin coated on the Pt/Ti$SiO_2$/Si and Indium Tin Oxide(ITO)/ glass substrate. the coated films were dries at 350$^{\circ}C$ for 10 minutes and annealed at $750^{\circ}C$ for 1 hour for the crystallization. The thin films coated on ITO substrate were crystallized easily and the packing density and roughness of surface were better that those of films coated on Pt substrates. In the BST(50/50) composition the structural properties were similar to the BST(70/30) composition and grain size were decreased with increasing the contents of Sr. The dielectric constant was higher in the BST(50/50) composition compared with the BST(70/30) composition. Using the ITO substrate, the dielectric constant was higher than the Pt substrate while the dielectric loss was showed a reverse trend. The dielectric constant with and increase of temperature was decreased slowly.

• Transactions on Electrical and Electronic Materials
• /
• v.1 no.4
• /
• pp.30-39
• /
• 2000

The variation of electrical properties of (Ba, Sr)TiO$_3$[BST] thin films deposited of RuO$_2$electrode with (Ba+Sr)/Tr ration was investigated. BST thin films with various (Ba+Sr)/Tr ration were deposited on RuO$_2$/Si substrates using in-situ RF magnetron sputtering. It was found that the electrical properties of BST films depends on the composition in the film. The dielectric constant of the BST films is about 190 at the (Ba+Sr)/Tr ration of 1.0, 1,025 and does not change markedly. But , the dielectric constant degraded to 145 as the (Ba+Sr)/Tr ratio increase to 1.0. In particular, the leakage current mechanism of the films shows the strong dependence on the (Ba+Sr)/Tr ration in the films. At the ration (Ba+Sr)/Tr=1,025, the Al/BST/RuO$_2$ capacitor show the most asymmetric behavior in the leakage current density, vs, electric field plot. It is considered that the leakage current of the (Ba+Sr)/Tr=1,025 thin films is controlled by the battier-Iimited process, i,e, Schottky emission.