• Korean Journal of Materials Research
• /
• v.7 no.6
• /
• pp.510-516
• /
• 1997

반응성RF 마그네트론 스퍼터링 법으로 상온에서 c-축으로 우선 배향된 AIN 박막을 여러 기판 위에 증착하였다. SiO$_{2}$/Si, Si$_{3}$N $_{4}$Si, Si(100), Si(111)그리고 $\alpha$-AI$_{2}$O$_{3}$(0001) 기판에서 AIN(0002)로킹커브 피크의 표준편차는 각각 2.6˚, 3.1˚2.6˚, 2.5˚ 그리고 2.1˚ 의 값을 나타내었다. $\alpha$-AI$_{2}$O$_{3}$(0001) 기판에 증착된 AIN박막은 epitaxial 성장을 나타내었다. Si기판에 증착된 AIN박막에서 측정된 비저항과 1MHz 주파수에서 측정된 유전상수의 값은 각각 $10^{11}$Ωcm와 9.5였다. IDT/AIN/$\alpha$-AI$_{2}$O$_{3}$(0001)구저를 갖는 지연선 소자의 표면 탄성과 특성을 측정하였다. 상 속도, 전기기계 결합계수 그리고 전파손실은 H/λ가 0.17-0.5 범위에서 각각 5448-5640m/s, 0.13-0.17% 그리고 0.41-0.64dB/λ의 값을 나타내었다.다.

• Korean Journal of Materials Research
• /
• v.9 no.6
• /
• pp.583-588
• /
• 1999

The characteristics of copper thin films and pattern filling capability were investigated by ECD. Prior to deposition of copper film, seed-Cu/Ta(TaN)/$SIO_2$(BPSG)/Si structure was manufactured. Copper deposition was performed with various current waveforms(DC/PC, 1~10,000Hz) and current densities(10~60 mA/$\textrm{cm}^2$) after pretreatment (Oxident removal, wetting) of seed-layer. Conformal pattern filling was performed using PC method with fast deposition rate of 6,000~8,000$\AA$/min. Heat-treated($450^{\circ}C$, 30min) copper films showed good resistivities of 1.8~2.1$\mu$$\Omega$.cm. According to the XRD analysis, (111)-preferred orientation of copper film was found in ECD-Cu/seed-Cu/Ta/$Sio_2$/Si structure. Also, we have successfully achieved to fill via holes with 0.35$\mu\textrm{m}$ width and 4:1 aspect ratio.

• Korean Journal of Materials Research
• /
• v.18 no.2
• /
• pp.98-102
• /
• 2008

The ferroelectric properties of UV irradiated and non-irradiated PZT films prepared via photochemical metal-organic deposition using photosensitive precursors were characterized. Fourier transform infrared spectroscopy showed that complete removal of organic groups was possible through UV exposure of the spin-coated PZT precursor films at room temperature. The measured remnant polarization values of UV-irradiated and non-irradiated PZT films after annealing at $650^{\circ}C$ were 29 and $23\;{\mu}C/cm^2$, respectively. The UV irradiation was found to be effective for the enhancement of the <111> growth orientation and ferroelectric property of PZT film and in the direct patterning in the fabrication of micro-patterned systems without dry etching.

• Journal of the Architectural Institute of Korea Planning & Design
• /
• v.36 no.4
• /
• pp.103-111
• /
• 2020

Perforated metal sheets are used as panels of facades for controlling environmental factors while ensuring user's visibility. Despite their functional potentials, only a specific direction of facades or an orientation of a building was considered in the relevant studies. This study proposed a design methodology for the perforated panel facades that reflects the location on the facades and the user's requirements. The optimization of quantitative and qualitative performance is achieved through communication between designers and users in a VR system. In optimizing quantitative performances, designers use machine learning techniques such as clustering and genetic algorithm to allocate optimal panels on the facades. In optimizing qualitative performances, through the VR system, users intervene in evaluating performances whose preferences are depending on them. The experiment using the office project showed that designers were able to make decisions based on clustering using GMM to optimize multiple quantitative performances. The gap between the target and final performance could be narrowed by limiting the types of perforated panels considering mass customization. In assessing visibility as a qualitative performance, users were able to participate in the design process using the VR system.

• Korean Journal of Metals and Materials
• /
• v.49 no.9
• /
• pp.726-731
• /
• 2011

The present work shows how the flexural displacement-induced fracture strength of silicon devices, whose back surfaces have wafer grinding-induced scratch marks, depends on the crystallographic orientation. Experimental results indicate that silicon devices with scratch marks parallel to their lateral direction (i.e. reference axis in this work) are very susceptible to flexural fracture, as compared to devices with marks which deviated from the direction. The 3-point bending test shows that the fracture strength of silicon devices having marks which are oriented away from the reference axis is 2.6 times higher than that of devices with marks parallel to the axis. It was particularly interesting to see that silicon devices with identical preferred marks even reveal different fracture strengths, depending on whether the marks are involved in specific crystal planes such as {111} or {011}, called cleavage planes. This work demonstrates that silicon devices with the reference axis-aligned scratch marks not existing on such cleavage planes can have higher fracture strength approximately 20% higher than those existing on the planes.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.3
• /
• pp.37-40
• /
• 2006

Oxide buffer layers for YBCO coated conductors were fabricated using MOD processing and development of microstructure and texture were investigated. A $CeO_2$ buffer layers were formed on RABiTS tape. Acetate-based precursor solution was employed to synthesize the precursor solution. Subsequently, the precursor solution was stabilized and modified with triethanolamine. $CeO_2$ precursor gel film was coated and annealed in $Ar/H_2$ atmosphere at high temperature. An annealed $CeO_2$ film shows mixed orientation with high (001) texturing. It was shown that (111) texture of $CeO_2$ layers were enhanced by multiple coating. This degradation was attributed to development of microcracks in the multiply coated $CeO_2$ films. Also discussed are the synthesis and the characterization of $La_2Zr_2O_7$ (LZO) buffer layers on RABiTS tape. A biaxially textured LZO buffer layer was fabricated with MOD processing method using metal alkoxide based precursor solution. It was shown that the LZO film were epitaxially grown on RABiTS tape and crack-free & uniform surface was obtained after annealing in $Ar/H_2$ atmosphere.

• Journal of the Korean Vacuum Society
• /
• v.6 no.S1
• /
• pp.75-79
• /
• 1997

Optical and mechanical characteristics of $TiO-2, ZrO_2 \;and\; SiO_xN_y$ thin films prepared by ion assisted deposition (IAD) were investigated. IAD films were bombarded by Ar or nitrogen ion beam from a Kaufman ion source while they were grown in as e-beam evaporator. The result shows that the Ae IAD increases the refractive index and packing density of $TiO_2 films close to those of the bulk. For $ZrO_2$ films the Ar IAD increases the average refractive index decreases the negative inhomogeneity of refractive index and reverses to the positive inhomogeneity. The optical properties result from improved packing density and denser outer layer next to air The Ar-ion bombardment also induces the changes in microstructure of $ZrO_2$ films such as the preferred (111) orientation of cubic phase increase in compressive stress and reduction of surface roughness. Inhomogeneous refractive index SiOxNy films were also prepared by nitrogen IAD and variable refractive index of $SiO_xN_y$ film was applied to fabricate a rugate filter.

• Journal of the Korean Vacuum Society
• /
• v.9 no.2
• /
• pp.99-101
• /
• 2000

The fabrication of the submicron size hole has been interesting due to the potential application of the near field optical sensor or liquid metal ion source. The 2 micron size dot array was photolithographically patterned. After formation of the V-groove shape by anisotropic KOH etching, dry oxidation at $1000^{\circ}C$ for 600 minutes was followed. In this procedure, the orientation dependent oxide growth was performed to have an etch-mask for dry etching. The reactive ion etching by the inductively coupled plasma (ICP) system was performed in order to etch ~90 nm $SiO_2$ layer at the bottom of the V-groove and to etch the Si at the bottom. The negative ion energy would enhance the anisotropic etching by the $Cl_2$ gas. After etching, the remaining thickness of the oxide on the Si(111) surface was measured to be ~130 nm by scanning electron microscopy. The etched Si aperture can be used for NSOM sensor.

• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.77-82
• /
• 2000

A surface of polytetrafluoroethylene(PTFE) was modified with changing ion doses by 1 keV $Ar^+$ ion irradiation and Cu films having thickness $5000\;{\AA}$ were deposited on the modified PTFE. The SEM study showed that the surface texture of modified PTFE was in the form of cones whose height increased depending on ion doses. Through XPS spectra, it was found that the intensity of F ls peaks decreased with ion doses by preferential sputtering of F atoms and the C-C and / or C-F chains were formed by the crosslinking in the newly unstable chains. Cu films were deposited uniformly along the filaments formed on the modified PTFE. In x-ray diffraction (XRD) spectra of deposited Cu films on modified PTFE, a preferred orientation along (111) and (200) planes was found and the peak intensity of (111) plane increased as surface roughness of modified PTFE increased. The resistivity of Cu films was changed from $2.7{\mu}{\Omega}cm$ of unmodified PTFE to $4.3{\mu}{\Omega}cm$ of modified PTFE at ion dose of $1{\times}10^{16}/\textrm{cm}^2$ and the abrupt increase of resistivity in the modified PTFE at ion dose of $1{\times}10^{17}/\textrm{cm}^2$ was due to being cut off the film which resulted from the increased surface roughness.

• Journal of Cadastre & Land InformatiX
• /
• v.48 no.1
• /
• pp.111-121
• /
• 2018

RIn this research, digital elevation models, true-ortho image and 3-dimensional digital complied data was generated and evaluated using unmanned aircraft vehicle stereoscopic images by applying photogrammetric principles. In order to implement stereoscopic vision, digital Photogrammetric Workstation should be used necessarily. For conducting this, in this study GEOMAPPER 1.0 is used. That was developed by the Ministry of Trade, Industry and Energy. To realize stereoscopic vision using two overlapping images of the unmanned aerial vehicle, the interior and exterior orientation parameters should be calculated. Especially lens distortion of non-metric camera must be accurately compensated for stereoscope. In this work. photogrammetric orientation process was conducted using commercial Software, PhotoScan 1.4. Fixed wing KRobotics KD-2 was used for the acquisition of UAV images. True-ortho photo was generated and digital topographic map was partially produced. Finally, we presented error analysis on the generated digital complied map. As the results, it is confirmed that the production of digital terrain map with a scale 1:2,500~1:3,000 is available using stereoscope method.