Abstract
A surface of polytetrafluoroethylene(PTFE) was modified with changing ion doses by 1 keV $Ar^+$ ion irradiation and Cu films having thickness $5000\;{\AA}$ were deposited on the modified PTFE. The SEM study showed that the surface texture of modified PTFE was in the form of cones whose height increased depending on ion doses. Through XPS spectra, it was found that the intensity of F ls peaks decreased with ion doses by preferential sputtering of F atoms and the C-C and / or C-F chains were formed by the crosslinking in the newly unstable chains. Cu films were deposited uniformly along the filaments formed on the modified PTFE. In x-ray diffraction (XRD) spectra of deposited Cu films on modified PTFE, a preferred orientation along (111) and (200) planes was found and the peak intensity of (111) plane increased as surface roughness of modified PTFE increased. The resistivity of Cu films was changed from $2.7{\mu}{\Omega}cm$ of unmodified PTFE to $4.3{\mu}{\Omega}cm$ of modified PTFE at ion dose of $1{\times}10^{16}/\textrm{cm}^2$ and the abrupt increase of resistivity in the modified PTFE at ion dose of $1{\times}10^{17}/\textrm{cm}^2$ was due to being cut off the film which resulted from the increased surface roughness.
1 keV $Ar^+$ 이온빔을 이용하여 polytetrafluoroethylene (PTFE)의 표면을 개질하고 그 위에 $5000\;{\AA}$의 구리 박막을 이온빔 스퍼터링법을 이용하여 증착하였다. 이온빔 조사에 의하여 PTFE의 표면에는 cone이 형성되며 cone의 높이는 이온 조사량이 증가함에 따라 점차로 증가함을 알 수 있었다. x-ray photoelectron spectroscopy (XPS) 분석을 통하여 조사된 PTFE의 표면에서는 이온 조사량이 증가함에 따라 Fls peak의 강도가 감소하며 이는 F 원자의 선택적인 스퍼터링에 기인한 것으로 생각된다. 또한 이온 조사에 의해 생성된 불안정한 사슬들은 crosslinking에 의하여 새로운 C-F 계열의 결합들을 생성하였다. 이온빔 스퍼터링법에 의하여 증착된 구리 박막은 PTFE 표면의 cone을 따라 균일하게 증착되며 PTFE의 표면 거칠기가 증가함에 따라 (111) 방향으로 우선 성장함을 알 수 있었다. 증착된 구리 박막의 비저항은 개질전 PTFE의 $2.7{\mu}{\Omega}cm$에서 $1{\tiems}10^{16}/\textrm{cm}^2$의 이온 조사량으로 개질된 PTFE의 $4.3{\mu}{\Omega}cm$까지 이온 조사량에 따라 점차로 증가하였다. $1{\tiems}10^{17}/\textrm{cm}^2$의 이온 조사량으로 개질된 PTFE 위에 증착된 구리 박막의 갑작스런 비저항 증가는 구리 박막의 단락에 의한 것으로 보인다.