• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.186.1-189
• /
• 2001

Ferroelectric $Bi_{4-x}$La$_{x}$Ti$_3$O$_{12}$ (BLT)thin films with various compositions(x=0.65, 0.70, 0.75) were prepared on Pt//Ti/SiO$_2$/Si(100) substrate by metal-organic deposition. The electrical and structural characteristics of BLT thin films were investigated to develop ferroelectric thin films for capacitor layers of FRAM. After spin coating, thin films were annealed at $650^{\circ}C$ for 1hour in oxygen atomosphere. Scanning electron micrographs showed uniform surfaces composed of rod-like grains. The $Bi_{4-x}$La$_{x}$Ti$_3$O$_{12}$ (x=0.70) thin film capacitors with a Pt top electrode showed better ferroelectric properties than other films. At the applied voltage of 5V, the dielectric constant($\varepsilon$$_{r}$), dissipation factor(tan$\delta$),remanent polarization(2Pr), and coercive field(2Ec) of the $Bi_{4-x}$La$_{x}$Ti$_3$O$_{12}$ (x=0.70)thin films were about 272.54, 0.059, 32.4 $\mu$C/cm$^2$, 2Ec=119.9kV/cm. Also the capacitor did not show any significant fatigue up to 4.8$\times$10$^{10}$ read/write switching cycles.hing cycles.s.

• 한국표면공학회지
• /
• 제25권5호
• /
• pp.215-221
• /
• 1992

This research is aimed at developing(110) preferred TiS2 cathode films and glass typed solid electro-lytes which have high ionic migrations and low electron conductivities for thin secondary solid batteries. To obtain preferred oriented TiS2 thin films on a substrate by CVD method using TiCl4 and H2S gases three factors of heating temperature, inner pressure of furnace and TiCl4/H2S gas mole fraction were ex-amined systematically. To obtain solid films of Li2O-B2O3-SiO2 electrolytes by r.f. sputtering for thin proto-type batteries of Li/Li2O-B2O3-SiO2TiS2, sputtering conditions were examined. TiS2 cathode films showed columnar structure, namely c axis oriented parallely. At low pressure of reaction chamber and low heating temperature, surface of smooth TiS2 films couldd be obtained. Ionic conductivity of Li2O-B2O3-SiO2 films manufactured by r.f. magnetron sputtering were 3$\times$10-7$\Omega$-1cm-1 and electron conductivities were 10-11$\Omega$-1cm-1. Open cell voltage of thin lithium batteries were 2.32V with a designed prototype cell.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.315-318
• /
• 2001

The optical and dielectric properties of TiO$_2$ thin films prepared with mixtures of Epoxy, bits-(4, 4'-p-toluenesulfonylacidic isoproplylidene)-cyclohexadiol and UVI 6990 in dry sol-gel process were investigated. The absorption peak of the films was showed at 360nm. Photocurrent of the thin films doped with 50 wt% of TiO$_2$was higher than that of nondoped thin films. Energy gap was lowered from 3.6 to 3.3 eV with increasing amount of TiO$_2$. Relative dielectric constants of samples were 1.5 to 3 and showed a characteristics of lower dielectric materials.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2007년도 Techno-Fair 및 추계학술대회 논문집 전기물성,응용부문
• /
• pp.116-117
• /
• 2007

The $V_2O_5$ thin films deposited on Pt/Ti/$SiO_2$/Si substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_2O_5$ thin films annealed at $300^{\circ}C$ were 37.7, with a dielectric loss of 2.535, respectively. Also, the TCR values of the $V_2O_5$ thin films annealed at $300^{\circ}C$ were about -2.65%/K.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.1
• /
• pp.420-423
• /
• 2003

[ $TiO_2$ ] thin films were fabricated by DC magnetron sputtering system at by controlling deposition times, ratios of $Ar:O_2$ partial presser ratio and substrate conditions. And the surface, cross-section morphology, microstructure, and composition ratio of the films were analyzed by FE-SEM, TEM and XPS. Besides, the optical absorption and transmittance of the $TiO_2$ films were measured by a UV-VIS-NIR Spectrophotometer, and photocatalytic properties were studied by G C Analyzer & Data Analysis system. As the result, when $TiO_2$ thin film was made at deposition time of 120[min] and $Ar:O_2$ ratio of 60:40, the best structural and optical properties among many thin films could be accepted. The best results of properties were as follows: thickness; $360{\sim}370[nm]$, grain size; 40[m], gap between two peak binding energy, $5.8{\pm}0.05[eV]$ ($2p_{3/2}$ peak and $2p_{1/2}$ peak of Ti was show at $458.3{\pm}0.05[eV]$ and $464.1{\pm}0.05[eV]$ respectively), binding energy; $530{\pm}0.05\;[eV]$, opticalenergy band gap; 3.4[eV].

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 센서 박막재료 반도체 세라믹
• /
• pp.154-157
• /
• 2003

$TiO_2$ thin films were fabricated by RF magnetron sputtering system at by controlling deposition times, ratios of $Ar:O_2$ partial presser ratio and substrate conditions. And the surface, cross-section morphology, microstructure, and composition ratio of the films were analyzed by FE-SEM, TEM and XPS. Besides, the optical absorption and transmittance of the $TiO_2$ films were measured by a UV-VIS-NIR Spectrophotometer, and photocatalytic properties were studied by G${\cdot}$C Analyzer & Data Analysis system. As the result, when $TiO_2$ thin film was made at deposition time of 120[min] and $Ar:O_2$ ratio of 60:40, the best structural and optical properties among many thin films could be accepted. The best results of properties were as follows: thickness; 360~370[nm), grain size; 40[nm], gap between two peak binding energy; $5.8{\pm}0.05[eV]$ ($2_{p3/2}$ peak and $2_{p1/2}$ peak of Ti was show at $458.3{\pm}0.05[eV]$ and $464.1{\pm}0.05[eV]$ respectively), binding energy; $530{\pm}0.05[eV]$, optical energy band gap; 3.4[eV].

• Transactions on Electrical and Electronic Materials
• /
• 제14권5호
• /
• pp.242-245
• /
• 2013

Sn-doped $In_2O_3$ (ITO) thin films were prepared by radio frequency magnetron sputtering without intentional substrate heating on bare glass and $TiO_2$-deposited glass substrates to investigate the effect of a $TiO_2$ buffer layer on the electrical and optical properties of ITO films. The thicknesses of $TiO_2$ and ITO films were kept constant at 5 and 100 nm, respectively. As-deposited ITO single layer films show an optical transmittance of 75.9%, while $ITO/TiO_2$ bi-layered films show a lower transmittance of 76.1%. However, as-deposited $ITO/TiO_2$ films show a lower resistivity ($9.87{\times}10^{-4}{\Omega}cm$) than that of ITO single layer films. In addition, the work function of the ITO film is affected by the $TiO_2$ buffer layer, with the $ITO/TiO_2$ films having a higher work-function (5.0 eV) than that of the ITO single layer films. The experimental results indicate that a 5-nm-thick $TiO_2$ buffer layer on the $ITO/TiO_2$ films results in better performance than conventional ITO single layer films.

• 한국세라믹학회지
• /
• 제40권12호
• /
• pp.1189-1196
• /
• 2003

Sol-gel법으로 강유전성 B $i_{3.25}$L $a_{0.75}$ $Ti_3$ $O_{12}$ (BLT) stock solution을 합성하고 Pt/Ti $O_2$/ $SiO_2$/Si 기판위에 스핀코팅법으로 BLT 박막을 증착하였다. 본 실험에서는 Bi(TMHD)$_3$, La(III)2-Methoxyethoxide, Ti(IV)i-propoxide를 출발물질로 사용하였으며 2-Methoxyethanol을 용매로 사용하였다. 급속열처리(RTA)가 BLT 박막의 결정성장을 촉진시키기 위해 사용되었고, RTA를 실시한 시편과 RTA를 실시하지 않은 시편의 전기적 특성을 비교하였다. RTA를 실시한 후 72$0^{\circ}C$에서 로 열처리 한 BLT 박막의 경우 5V 인가 전압 하에서 2Pr 값은 RTA를 실시하지 않은 경우보다 27% 증가한 20.46$\mu$C/$ extrm{cm}^2$이었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1993년도 춘계학술대회 논문집
• /
• pp.142-145
• /
• 1993

$TiO_2-V_2O_5$ thin films are fabricated by Sol-Gel method and humidity sensing properties have been investigated. As the results of humidity sensing properties of thin films fabricated as humidity sensor, it is confirmed to have good humidity sensing properties in high humidity and low frequency regions.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2008년도 제39회 하계학술대회
• /
• pp.1248-1249
• /
• 2008

The $V_{1.8}W_{0.2}O_5$ thin films deposited on $Pt/Ti/SiO_2/Si$ substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_{1.8}W_{0.2}O_5$ thin films annealed at 400$^{\circ}C$ were 38.11, with a dielectric loss of 0.134, respectively. Also, the TCR values of the $V_{1.8}W_{0.2}O_5$ thin films annealed at 400$^{\circ}C$ were about -3.15%/K.