• 한국세라믹학회지
• /
• 제35권11호
• /
• pp.1130-1140
• /
• 1998

Thin films of $Bi_4Ti_3O_{12}\;nBaTiO_3(n=1&2)$ were prepared using sols erived Ba-Bi-Ti complex alkoxides. The sols were spin-cast onto $Pt/Ti/SiO_2/Si$ substrates and followed by pyrolysis for 1 hr at $620^{\circ}C,\;700^{\circ}C\;and\;750^{\circ}C$ In the thin films a pyrochlore phase seemed to be formed at a lower temperature and then tran-formed to the layered perovskite phase as the heating temperature increased. In the thin films pyrolyzed at formed to the layered perovskte phase as the heating temperature increased. In the films pyrolyzed at $750^{\circ}C$ the amount of $Bi_4Ti_3O_{12}{\cdot}BaTiO_3$ reached to 94% while $Bi_4Ti_3O_{12}{\cdot}BaTiO_3$ was 77% in composition. This result shows that the formation of the layered pervoskite phase becomes difficult as the amount of complexing $BaTiO_3$ increases. The microstructures and the electrical properties of the thin films were gen-erally improved with the incease of the heating temperature. However the presence of the pyrochlore phase could not be removed effectively. Our study showed that the electrical properties of $Bi_4Ti_3O_{12}{\cdot}BaTiO_3$ were pronouncedly improved with complexing with BaTiO3 when compared to those of $Bi_4Ti_3O_{12}$ while the presence of the pyrochlore phase was detrimental to the those of $Bi_4Ti_3O_{12}{\cdot}2BaTiO_3$.

• 한국전기전자재료학회논문지
• /
• 제23권9호
• /
• pp.681-684
• /
• 2010

The $TiO_2$/ZnS/Ag/ZnS/$TiO_2$ multilayered structure for the transparent electrodes in plasma display panel was designed by essential macleod program (EMP) and the multilayered film was deposited on a glass substrate by direct-current (DC)/radio-frequency (RF) magnetron sputtering system. During film deposition process, the Ag layer in $TiO_2$/Ag/$TiO_2$ structure became oxidized and the filter characteristic was degraded easily. In this study, ZnS layer was adopted as a diffusion blocking layer between $TiO_2$ and Ag to prevent the oxidation of Ag layer efficiently in $TiO_2$/ZnS/Ag/ZnS/$TiO_2$ structure. Based on the AES depth profiling analysis, the Ag layer was effectively protected by the ZnS layer as compared with the $TiO_2$/Ag/$TiO_2$ multilayered films without ZnS as an antioxidant layer. The 3 times stacked $TiO_2$/ZnS/Ag/ZnS/$TiO_2$ films have low sheet resistance of $1.22{\Omega}/{\square}$ and luminous transmittance was as high as 62% in the visible ranges.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.448-449
• /
• 2006

For the possible applicative pearl pigment, multi-layered $TiO_2/Al/TiO_2$, $TiO_2/Cr/TiO_2$ thin film was deposited on glass substrate by using sputtering method. $TiO_2$ and Al or Cr was selected as a possible high and low refraction materials at the film interface respectively. Optical properties including color effect were systematically studied in terms of different film thickness and film layers by using spectrometer. In order to expect the experimental results, the simulation program, the Essential Macleod Program(EMP) was adopted and compared with the experimental data. The film consisting of $TiO_2/Al/TiO_2$, $TiO_2/Cr/TiO_2$ layers show the wavelength range of 430 - 760nm, typically color ranges between bluish purple and red. It was confirmed that this experimental result was quite well matched with the experimental one.

• 대한전기학회논문지
• /
• 제45권2호
• /
• pp.242-248
• /
• 1996

The properties of TiN/TiSi$_{2}$ bilayer formed by a rapid thermal annealing is investigated when thin SiO$_{2}$ film exists at the Ti-Si interface. The competitive reaction for the TiN/TiSi_2 bilayer occurs above 600 .deg. C. The thickness of the TiSi$_{2}$ layer decreases with increasing SiO$_{2}$ film thickness and also decreases with increasing anneal temperture When the competitive reaction for the TiN/TiSi$_{2}$ bilayer is occured by rapid thermal annealing, the composition of TiN layer represents TiN$_{x}$O$_{y}$ due to the SiO$_{2}$ layer at the Ti-Si interface but the structures of the TiN and TiSi$_{2}$ layers were not changed.d.d.

• Bulletin of the Korean Chemical Society
• /
• 제31권2호
• /
• pp.344-350
• /
• 2010

The improved photocatalytic performance of a carbon/$TiO_2$ composite was studied for the Bisphenol A (BPA) decomposition. Titanium tetraisopropoxide (TTIP) and a rice husk from Korea were heterogeneously mixed as the titanium and carbon sources, respectively, for 3 h at room temperature, and then thermally treated at $600^{\circ}C$ for 1 h in $H_2$ gas. The transmission electron microscopy (TEM) images revealed that the bulk carbon partially covered the $TiO_2$ particles, and the amount that was covered increased with the addition of the rice husk. The acquired carbon/$TiO_2$ composite exhibited an anatase structure and a novel peak at $2{\theta}=32^{\circ}$, which was assigned to bulk carbon. The specific surface area was significantly enhanced to 123~164 $m^2/g$ in the carbon/$TiO_2$ composite, compared to $32.43m^2/g$ for the pure $TiO_2$. The X-ray photoelectron spectroscopy (XPS) results showed that the Ti-O bond was weaker in the carbon/$TiO_2$ composite than in the pure $TiO_2$, resulting in an easier electron transition from the Ti valence band to the conduction band. The carbon/$TiO_2$ composite absorbed over the whole UV-visible range, whereas the absorption band in the pure$TiO_2$ was only observed in the UV range. These results agreed well with an electrostatic force microscopy (EFM) study that showed that the electrons were rapidly transferred to the surface of the carbon/$TiO_2$ composite compared to the pure $TiO_2$. The photocatalytic performance of the BPA removal was optimized at a Ti:C ratio of 9.5:0.5, and this photocatalytic composite completely decomposed 10.0 ppm BPA after 210 min, whereas the pure $TiO_2$ achieved no more than 50% decomposition under any conditions.

• 공업화학
• /
• 제19권5호
• /
• pp.554-558
• /
• 2008

전구체로서 알콕사이드[Tetraethyl orthosilicate (TEOS), Titanium (IV) isopropoxide (TiP)]를 사용하여 졸-겔 방법으로 전기방사에 적합한 졸을 제조한 후, $(1-x)SiO_2-(x)TiO_2$계 복합 나노섬유를 제조하였다. 제조된 광활성 무기나노섬유의 표면 및 구조적 특성은 X-선회절분석(XRD), 주사전자현미경(SEM), 투과전자현미경(TEM), 열중량분석 및 미분주사칼로리미터분석 (TGA-DSC), 적외선분광분석((FT-IR)을 통하여 확인하였다. $(1-x)SiO_2-(x)TiO_2$계에서 $TiO_2$ 양이 증가하면 전기방사된 복합섬유직경은 증가하였으며, 저온에서 안정한 아나타제 $TiO_2$ 결정에서 루타일로의 상전이는 $1000^{\circ}C$에서의 열처리 후에도 고루 분산되어 있는 $SiO_2$로 인해 $0.6SiO_2-0.4TiO_2$계까지는 아나타제상으로 존재하였다. $SiO_2-TiO_2$계 복합체 나노섬유의 광활성은 메틸렌블루 광분해 실험 및 UV-vis/DRS 분석을 통해 자외선 영역에서 나타남을 확인하였다.

• 대한화학회지
• /
• 제9권2호
• /
• pp.71-74
• /
• 1965

Reduction of Ti(Ⅳ)-oxalate complex on dropping mercury electrode has been studied as a function of oxalate concentration and of pH varied with HCl. Assuming there are equilibrium $TiO(C_2O_4)_2= \;+\;2H^+\;=\;Ti^{+4}\;+\;2C_2O_4\;=\;+\;H_2O,\;K_4$ in addition to $TiO(C_2O_4)_2\;^=\;=\;TiO^{++}\;+\;2C_2O_4=\;K_2\;Ti(C_2O_4)_2\;^-\;=\;Ti^{+3}\;+\;2C_2O_4=\;K_3$ in the system cathodic wave has been well explained for that pH is higher than 0.5. The equilibrium constants $K_2,\;K_3$ and $K_4$ have been to be $2{\times}10^{-12},\;5{\times}10^{-13}$ and $10^{-11}$, respectively. The reduction of Ti(Ⅳ)-oxalate system is $Ti^{+4}\;+\;e\;{\to}\;Ti^{+3}$ in the concentration of hydrochloric acid, higher than 3M.

• 한국염색가공학회지
• /
• 제25권2호
• /
• pp.94-101
• /
• 2013

Poly(acrylonitrile) (PAN) nanofibers containing different amounts of titanium dioxide ($TiO_2$) have been prepared by electrospinning technique. Photocatalytic activity of these electrospun PAN/$TiO_2$ nanofibers and the effect of $TiO_2$ content on the photocatalytic efficiency of PAN/$TiO_2$ nanofibers have been evaluated by monitoring the photodecomposition of fluorescein dye, rhodamine B and methylene blue under UV irradiation with respect to irradiation time. Moreover, the effect of hydrogen peroxide ($H_2O_2$) on the photocatalytic behavior of PAN/$TiO_2$ nanofibers has also been investigated. The results showed that PAN/$TiO_2$ nanofibers are effective photocatalyst and their photocatalytic efficiency increases with the increase of $TiO_2$ content in the PAN/$TiO_2$ nanofibers. It is also observed that the presence of $H_2O_2$ significantly enhances the photocatalytic ability of PAN/$TiO_2$ nanofibers. The morphology and the photocatalytic behavior of the PAN/$TiO_2$ nanofibers containing different amounts of $TiO_2$ nanoparticles have been investigated by field-emission scanning electron microscopy (FE-SEM) and UV/Visible spectroscopy, respectively.

• 전기화학회지
• /
• 제18권4호
• /
• pp.156-160
• /
• 2015

파이로프로세싱 전해환원은 사용후핵연료의 재활용을 위해 우라늄산화물을 금속으로 전환하는 공정으로 핵물질을 사용하기 이전에 대체 금속산화물을 이용한 실험을 통해 환원 장치의 성능을 평가하고 개선한다. 본 연구에서는 전해환원 장치 개발을 위한 대체 금속산화물로 타이타늄 산화물(TiO와 $TiO_2$)을 선정하고 $650^{\circ}C$의 $Li_2O$-LiCl 용융염에서의 용해도 및 전해환원 특성을 평가하였다. 1.0 wt.% $Li_2O$-LiCl 용융염에서 TiO와 $TiO_2$의 침지 실험을 통해 두 산화물 모두 염에 일부 용해됨을 확인하였는데, $TiO_2$(2100 ppm)가 TiO(156 ppm)에 비해 더 높은 용해도를 보였다. 1.0 wt.% $Li_2O$-LiCl 용융염에서 TiO와 $TiO_2$의 전해환원을 각각 수행하여 Ti 금속을 성공적으로 제조하였다. 그러나 염 내 용해도가 낮은 TiO는 환원에 사용된 백금 양극 표면에서 Ti이 검출되지 않은 반면 $TiO_2$의 백금 표면에서는 Ti이 검출되었다.

• 한국세라믹학회지
• /
• 제30권6호
• /
• pp.510-516
• /
• 1993

$PbTiO_3$ thin films have been formed by rapid thermal annealing(RTA) of $TiO_2$/Pb/$TiO_2$ multilayer films deposited on Si wafers by RF sputtering. Based on the optimal depositon conditions of TiO2 and Pb, $TiO_2$/Pb/$TiO_2$ three layers were deposited for 900$\AA$ each. These films were subjected to RTA process at the temperatures ranging from $400^{\circ}C$ to $900^{\circ}C$ for 30 seconds in air, and were analyzed by X-ray diffraction and transmission electron microscopy to investigate the phases and the microstructures. As a result, perovskite $PbTiO_3$ phases was obtained above $500^{\circ}C$ with the trace of unreacted $TiO_2$. RBS analysis revealed the anisotropic behavior of diffusion that the diffusivity of Pb to the bottom $TiO_2$ layer was faster than that of Pb to the top $TiO_2$ layer. The amorphous Pb-silicate was formed between film and Si substrate due to the diffusion of Pb, but Pb-silicate existed locally at the interface and the amount of that phase was very small. Therefore the effect of bottom $TiO_2$ layer as a diffusion barrier was confirmed. $PbTiO_3$ films formed by current technique showed a relative dielectric constant of 60, and the maximum breakdown field reached 170kV/cm.