• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.859-860
• /
• 2006

TiC-$TiB_2$-SiC system was a ternary eutectic, whose eutectic composition was 34TiC-$22TiB_2$-44SiC (mol%). TiC-$TiB_2$-SiC ternary eutectic composite were synthesized by a floating zone method using TiC, $TiB_2$ and SiC powders as starting materials. The TiC-$TiB_2$-SiC eutectic composite showed a lamellar texture. TiC(022), $TiB_2(010)$ and SiC(111) of the eutectic composite were perpendicular to the growth direction. TiC-$TiB_2$-SiC ternary eutectic composite had specific relationship among the crystal planes: TiC[011]//$TiB_2[010]$//SiC[112], TiC(200)//$TiB_2$(001)//SiC(402) and $TiC(1\bar{1}1)$//$TiB_2(101)$//SiC(220).

• Journal of the Korean Ceramic Society
• /
• v.36 no.1
• /
• pp.7-14
• /
• 1999

TiZrB2 solid solution was synthesized using fine powders of Ti, Zr and B by SHS microwave process. The characterization of the synthesized powder and sintered bodies ws investigated. The combustion temperature and rate were increased with increasing the mole ratio of Zr in temperature profile, and showed the maximum combustion temperature and velocity values of 285$0^{\circ}C$ and 14.6mm/sec in Ti0.2Zr0.8B2 composition. Phase separation has been occured into a composite with TiB2 and ZrB2 phases from TiZrB2 solid solution, which was hot pressed sintering at 30 MPa for an hour at 190$0^{\circ}C$. At the composition of Ti0.8Zr0.2B2 the best properties has been obtained in relative density, bending strength, fracture toughness and hardness, with 99%, 680 MPa, 7.3MPa.m1/2 and 2750 Kg/$\textrm{mm}^2$ respectively.

• Korean Journal of Materials Research
• /
• v.14 no.1
• /
• pp.73-77
• /
• 2004

The mechanical and electrical properties of $Cu-TiB_2$ composites prepared by hot extrusion and cold drawing according to the variation of $TiB_2$ contents and the size of $TiB_2$ particle have been studied. The experimental results showed that the electrical conductivity was decreased with increasing the $TiB_2$ content, and their tensile strength and hardness increased inversely. In the case of the same content of $TiB_2$ particle, the smaller $TiB_2$ particle, the higher their mechanical properties. The electrical conductivity of $Cu-TiB_2$ composites showed more than 70%IACS. Their yield strength and hardness were more than 120 MPa and HRB 60～70, respectively.

• Korean Journal of Materials Research
• /
• v.14 no.4
• /
• pp.246-250
• /
• 2004

We have investigated the effects of boron added to Cu film on the Cu-Ti reaction and microstructural evolution of Cu(B) alloy film during annealing of Cu(B)/Ti/$SiO_2$/Si structure. The result were compared with those of Cu(B)/$SiO_2$ structure to identify the effects of Ti glue layers on the Boron behavior and the result grain growth of Cu(B) alloy. The vacuum annealing of Cu(B)/Ti/$SiO_2$ multilayer structure allowed the diffusion of B to the Ti surface and forming $TiB_2$ compounds at the interface. The formed $TiB_2$ can act as a excellent diffusion barrier against Cu-Ti interdiffusion up to $800^{\circ}C$. Also, the resistivity was decreased to $2.3\mu$$\Omega$-cm after annealing at $800^{\circ}C$. In addition, the presence of Ti underlayer promoted the growth Cu(l11)-oriented grains and allowed for normal growth of Cu(B) film. This is in contrast with abnormal growth of randomly oriented Cu grains occurring in Cu(B)/$SiO_2$ upon annealing. The Cu(B)/Ti/$SiO_2$ structure can be implemented as an advanced metallization because it exhibits the low resistivity, high thermal stability and excellent diffusion barrier property.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.1
• /
• pp.20-26
• /
• 2001

Titanium boride ($\textrn{TiB}_{x}$) films were deposited on (100) silicon substrates at the substrate temperature of $500^{\circ}C$ by means of the co-evaporation of titanium and boron evaporants during deposition. The co-evaporation method makes it possible to deposit the non-stoichiometric films with different boron-to-titanium ratio($0{\le}B/Ti \le 2.5$). The resistivity increases linearly as the boron-to-titanium ratio in the as-deposited films is increased. The surface roughness of $\textrn{TiB}_{x}$ films is changed as a function of the boron-to-titanium ratio. The XRD spectrum for pure titanium film shows a highly (002) preferred orientation. For B/Ti=0.59 ratio only a single TiB phase that shows a (111) preferred orientation is observed. However, the $\textrn{TiB}_{x}$ phase with the hexagonal structure of the $AlB_2$(C32) type appears as the boron concentration increase, and only a single $\textrn{TiB}_{x}$ phase is observed for $B/Ti \ge 2.0$ ratio. The $\textrn{TiB}_{x}$/Si samples reveal a tensile stress (3~$20{\times}^9$dyn/$\textrm{cm}^2$) in the overall composition of the films, although the magnitude of the residual stresses is depended on the nominal B/Ti ratio.

• Journal of the Korean Ceramic Society
• /
• v.29 no.7
• /
• pp.577-585
• /
• 1992

TiB2 and TiC were prepared from the mixture of metal titanium, boron and graphite powders in Argon atmosphere by Self-propagating High-temperature Synthesis method. The sintered properties of TiB2-TiC composite as a function of TiC content and sintering temperature were investigated in TiB2 matrix. The sintered properties were the most excellent at 10 wt% TiC content in TiB2-TiC composite. The relative density, M.O.R strength, hardness and fracture toughness of TiB2-10 wt% TiC composite sintered at 190$0^{\circ}C$ for 90 min by hot-pressing under the pressure of 30 MPa were 98.6%, 634 MPa, 2128.1 kg/$\textrm{mm}^2$ and 4.09 MN/m3/2, respectively.

• Korean Journal of Materials Research
• /
• v.14 no.12
• /
• pp.829-834
• /
• 2004

Annealing of $Cu(B)/Ti/SiO_2$ in vacuum has been carried out to investigate the effects of Ti underlayer on microstructure in $Cu(B)/Ti/SiO_2$ structures. For comparison, $Cu(B)/Ti/SiO_2$ structures was also annealed in vacuum. Three different temperature dependence of Cu growth can be seen in $Cu(B)/Ti/SiO_2$; B precipitates- pinned grain growth, abnormal grain growth, normal grain growth. The Ti underlayer having a strong affinity for B atoms reacts with the out-diffused B to the Ti surface and forms titanium boride at the Cu-Ti interface. The formation of titanium boride acts as a sink for the out-diffusion of B atoms. The depletion of boron in grain boundaries of Cu films, as results of the rapid diffusion of B along the grain boundaries and the insufficient segregation of B to the grain boundaries, induces grain boundaries to migrate and causes the abnormal grain growth. The increased bulk diffusion coefficient of B within Cu grains can be responsible for the normal grain growth occurring in the annealed $Cu(B)/Ti/SiO_2\;at\;600^{\circ}C$. In contrast, the $Cu/SiO_2$ structures show only the abnormal growth of grains and their sizes increasing as the temperature increases above $400^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.552-560
• /
• 1994

A composite of TiB2-Al2O3 system was successfully prepared from a mixture of TiO2, B2O3, and Al by self-propagating high temperature synthesis (SHS) with a novel characteristic, utilizing the internal oxidation heat of aluminium metal of the mixture, instead of by a conventional technique, externally heating a mixture of Ti, B and Al2O3. From a mixture with B/Ti molar ratio of =2.0, pure two phases of TiB2 and $\alpha$-Al2O3 with good crystallinity and small, uniform sizes were formed. However, when the B/Ti molar ratio of the mixture goes to a value less than 2.0, in addition to the above main minerals, a small smounts of metastable phases such as TiB and Ti3B4 were formed. It was found that about 60%, the optimum green density of compacts gave their highest reaction rate and temperature during SHS process. TiB2-Al2O3 system composite with B/Ti molar ratio of =2.0 could be pressurelessly sintered even at 190$0^{\circ}C$ under Ar gas flows without any addition of sintering aids, showing their good properties such as 91.2% in relative density, 2750 kgf/$\textrm{mm}^2$ in Vickers hardness and 2620 kgf/$\textrm{cm}^2$ in flexural strength.

• Journal of the Korean Ceramic Society
• /
• v.40 no.8
• /
• pp.777-783
• /
• 2003

The mechanical properties of B$_4$C/Al composites normally depend on the species and quantity of reaction products between B$_4$C and Al and then the control of reaction products is necessary to make desirable composites for lightweight advanced or armor materials. TiB$_2$ is chemically inert with aluminum and has a lower contact angle (85$^{\circ}$ at 100$0^{\circ}C$) to liquid aluminum than B$_4$C. Thus, TiB$_2$ coating on B$_4$C may lower infiltration temperature of aluminum when the B$_4$C/Al composites is fabricated by infiltration process. In this study, the effects of TiB$_2$ on the microstructure and mechanical properties of the B$_4$C/Al composites have been investigated. TiB$_2$ coated B$_4$C powder was prepared using the sol-gel technique. It was found that the B$_4$C surface is homogeneously covered with TiB$_2$ having a particles size of 20-50 nm. While the B$_4$C/Al composites prepared by infiltration after TiB$_2$ coating had 17 wt% of unreacted Al, on the other hand, the B$_4$C/Al composites without coating included 14 wt% of Al. As a result, the composites infiltrated after the coating showed higher fracture toughness and lower hardness. This strongly suggests that TiB$_2$ not only lowers the infiltration temperature, but also inhibits the reaction between B$_4$C and Al.

• Proceedings of the KSR Conference
• /
• 2004.10a
• /
• pp.704-709
• /
• 2004

The wear behavior and the mechanical property of Cu-$TiB_2$ composites were examined. Cu-$TiB_2$ composites were fabricated by hot extrusion and cold drawing with $TiB_2$ contents(1$\∼$5vol.$\%$) and the size of $TiB_2$ particles(10$\mu$m and 20$\mu$m). The pin-an-disk wear test was carried out under dry sliding wear conditions which loads varied with from 20N to 100N. At the time, counterpart wear material used SM45C. The experimental results showed that the friction coefficient and wear rate decreased with increasing the $TiB_2$ contents and decreasing the size of $TiB_2$ particle. Also, the depth of plastically deformed zone decreased with increasing the $TiB_2$ contents and decreasing the size of $TiB_2$ particle.