• E2M - 전기 전자와 첨단 소재
• /
• 제10권7호
• /
• pp.674-681
• /
• 1997

Ternary compound ceramics, (1-y-x) BaTiO$_3$-y SrTiO$_3$-x MgTiO$_3$(0.00 x 0.20), were fabricated by the conventional ceramic process. The structural and dielectric properties of specimens were investigated while varying the composition and sintering temperature(1,200~1,45$0^{\circ}C$) in order to obtain the optimum condition of capacitor. As is well known, Curie temperature(T$_{c}$) of high dielectric-based ceramic(BaTiO$_3$) was shifted and temperature of capacitance was decreased in according to increase of solid solution with (Sr, Mg)TiO$_3$. As a result, a suitable condition of compound rate for capacitor was obtained such as the BSM-11(0.8BaTiO$_3$-0.1SrTiO$_3$-0.1MgTiO$_3$), and sintering temperature was sintered at 1,25$0^{\circ}C$ for two hours. In this case, dielectric constant<1,300, dielectric loss(tan$\delta$)<0.03, and the variation rate of capacitance had less than 3% in the range -10~7$0^{\circ}C$.>.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.289-290
• /
• 2006

[ $SrTiO_3$ ] is usually added as shifters in order to move the $T_C$ of $BaTiO_3$ to lower temperatures because it is well established that the $T_C$ of $BaTiO_3$ decreases linearly with a solid solution of $Sr^{+2}$ in place of $Ba^{+2}$. It is not fully understood yet, however, how $SrTiO_3$ influences on the peak value of the dielectric constant $(\varepsilon_{max})$ at the $T_C$ of $BaTiO_3$. This research reports the effect of $SrTiO_3$ addition on εmax at the $T_C$ of $BaTiO_3$ ceramics. Based on the chemical composition and the grain size dependence of the dielectric property of $BaTiO_3$ ceramics, functionally graded $(Ba,Sr)TiO_3$ composites were designed and fabricated. Multi-layered $(Ba,Sr)TiO_3$ composites with a compositional gradient of $SrTiO_3$ exhibited a low temperature coefficient and high dielectric constant in a wide temperature range.

• 한국분말재료학회지
• /
• 제15권2호
• /
• pp.107-113
• /
• 2008

Ultrafine TiC-5%Co powders were synthesized by spray drying of aqueous solution of TiO$(OH)_2$ slurry and cobalt nitrate, followed by calcination and carbothermal reaction. The oxide powders with carbon powder was reduced and carburized at $900^{\circ}C{\sim}1250^{\circ}C$ under hydrogen atmosphere. During reduction, CO gas was mainly evolved by reducing reaction of oxides. Ultrafine TiC-5%Co powders were easily formed by carbothermal reaction at $1250^{\circ}C$ due to using ultrafine powders as raw materials. The ultrafine WC-TiC-Co alloy prepared by sintering of mixed powder of ultrafine WC-13%Co powder and ultrafine TiC-5%Co powder has higher sintered density and mechanical properties than WC-TiC-Co alloy prepared by commercial WC, TiC and Co powders.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2002년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.94-96
• /
• 2002

The $0.97MgTiO_3-0.03SrTiO_3$ ceramics with $B_2O_3$(10wt%) were prepared by the conventional mixed oxide method. The structural properties were investigated with sintering temperature by XRD and SEM. According to the X-ray diffraction patterns of the $0.97MgTiO_3-0.03SrTiO_3$ ceramics with $B_2O_3$(10wt%), the ilmenite $MgTiO_3$ and perovskite $SrTiO_3$ structures were coexisted and secondary phase $MgTi_2O_5$ were appeared. Increasing the sintering temperature. the grain size was increased. In the case of $0.97MgTiO_3-0.03SrTiO_3$ ceramics with $B_2O_3$(10wt%), dielectric constant, quality factor and temperature coefficient of resonant frequency were $13.52{\sim}18.13,\;32750{\sim}51736GHz$, $-15.78{\sim}25.64ppm/^{\circ}C$, respectively.

• 한국전기전자재료학회논문지
• /
• 제17권11호
• /
• pp.1149-1155
• /
• 2004

In this paper, novel methods for improvement of thermal stability of Ni-germano Silicide were proposed for nano CMOS applications. It was shown that there happened agglomeration and abnormal oxidation in case of Ni-germano Silicide using Ni only structure. Therefore, 4 kinds of tri-layer structure, such as, Ti/Ni/TiN, Ni/Ti/TiN, Co/Ni/TiN and Ni/Co/TiN were proposed utilizing Co and Ti interlayer to improve thermal stability of Ni-germano Silicide. Ti/Ni/TiN structure showed the best improvement of thermal stability and suppression of abnormal oxidation although all kinds of structures showed improvement of sheet resistance. That is, Ti/Ni/TiN structure showed only 11 ohm/sq. in spite of 600 $^{\circ}C$, 30 min post silicidation annealing while Ni-only structure show 42 ohm/sq. Therefore, Ti/Ni/TiN structure is highly promising for nano-scale CMOS technology.

• 한국재료학회지
• /
• 제31권2호
• /
• pp.92-96
• /
• 2021

We report the growth and enhanced photoelectrochemcial (PEC) water-splitting reactivity of few-layer MoS2 nanosheets on TiO2 nanowires. TiO2 nanowires with lengths of ~1.5 ~ 2.0 ㎛ and widths of ~50~300 nm are synthesized on fluorine-doped tin oxide substrates at 180 ℃ using hydrothermal methods with Ti(C4H9O)4. Few-layer MoS2 nanosheets with heights of ~250 ~ 300 nm are vertically grown on TiO2 nanowires at a moderate growth temperature of 300 ℃ using metalorganic chemical vapor deposition. The MoS2 nanosheets on TiO2 nanowires exhibit typical Raman and ultraviolet-visible light absorption spectra corresponding to few-layer thick MoS2. The PEC performance of the MoS2 nanosheet/TiO2 nanowire heterostructure is superior to that of bare TiO2 nanowires. MoS2/TiO2 heterostructure shows three times higher photocurrent than that of bare TiO2 nanowires at 0.6 V. The enhanced PEC photocurrent is attributed to improved light absorption of MoS2 nanosheets and efficient charge separation through the heterojunction. The photoelectrode of the MoS2/TiO2 heterostructure is stably sustained during on-off switching PEC cycle.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 가을 학술논문 발표대회
• /
• pp.85-86
• /
• 2020

With the increasing importance of environmental issues, the cementitious materials with self-cleaning or photocatalytic properties by introducing TiO₂ materials have been gaining a lot of attention. In this work, the influence of TiO₂ particle size and structure on its photocatalytic effect in cement paste was investigated. The degradation of methylene blue solution was used as the parameter for evaluating the photocatalytic effect of micro-TiO2 (m-TiO₂), nano-TiO2 (n-TiO₂), and TiO₂ nanotube (TNT). Moreover, the effect of these three TiO₂ materials on the cement hydration products was characterized by X-ray diffraction (XRD) and thermgravimetric analysis (TG). According to the results, it can be found that all of the TiO₂ materials promoted the formation of hydration products, especially TNT. On the other hand, the m-TiO₂ exhibited a better photocatalytic effect compared to other materials.

• 한국재료학회지
• /
• 제1권3호
• /
• pp.168-174
• /
• 1991

Ti-Silicides를 single-Si wafer와 그 위에 oxide를 성장시킨 기판위에 composite target($TiSi_{2.6}$)을 sputtering함으로써 증착시켰다. 증착된 비정질 상태의 Ti-silicide는 급속 열처리(RTA)방법으로 $600^{\circ}C$에서 $850^{\circ}C$가지 20초간 처리하였다. RTA온도가 $800^{\circ}C$가 되어서야 비로소 안정한 $TiSi_2$가 형성되었으며, 그 때의 비저항 값은 $27~29{\mu}\Omega-cm$로 Ti-metal reactive방법에 의한 $TiSi_2$보다 약간 높은 값으로 드러났다. X-ray로 상천이를 조사한 결과 역시 $750^{\circ}C$가지 C49 $TiSi_2$가 형성되고, $800^{\circ}C$가 되어서야 안정한 C54 $TiSi_2$로의 상천이가 일어남을 나타내고 있다. 또한 완전히 형성된 Ti-silicide의 조성비는 x-ray photoelectron spectroscopy(XPS)결과에서 Ti : Si이 1 : 2로 드러났으며, 그 동안 reactive 시켰을 때 $TiSi_2$의 단점으로 지적되어 왔던 형성 완료된 $TiSi_2$의 surface roughness는 $17{\pm}1mm$이내로 매우 우수한 값으로 판명되어, device에 대한 응용 가능성을 높이고 있다.

• 한국세라믹학회지
• /
• 제41권12호
• /
• pp.915-920
• /
• 2004

[ $BaTi_{4}O_9$ ]계 세라믹스에 borosilicate계 유리 프리트를 첨가할 때 주결정상이 $BaTi_{5}O_{11}$로 변화되는 현상을 XRD와 TEM으로 분석하였다. Borosilicate계 유리 프리트가 $BaTi_{4}O_9$상으로부터 Ba 이온을 선택적으로 흡수함으로써 주상인 $BaTi_{4}O_9$ 상보다 Ti-rich인 $BaTi_{5}O_{11}$상으로 변화하는 것으로 추측하였다. 이와 같은 결과는 유리의 첨가량과 열처리 온도에 따라 영향을 받는데 $BaO-TiO_2$계의 Ti-rich 영역에 속하는 $Ba_{4}Ti_{13}O_{30},\;Ba_{2}Ti_{9}O_{20}$ 등의 결정상도 상변화 과정에 참여하고 있음을 관찰하였다. 중-고유전율 LTCC 조성개발을 위하여 유리 첨가에 의한 중-고유전율 모재료의 저온소결을 시도할 때 적정한 저온소결특성을 확보하면서도 상변화를 고려한 유리 프리트 첨가량 제어가 필요함을 알 수 있었다.

• 멤브레인
• /
• 제20권2호
• /
• pp.120-126
• /
• 2010

본 연구에서는 $TiO_2$ 나노입자로 표면침적된 polyethersulfone (PES) 정밀여과 분리막이 자연유기물로 인한 분리막 막힘현상(파울링)에 미치는 영향을 관찰하였다. $TiO_2$ 나노입자로 표면침적된 PES 정밀여과 분리막의 자연유기물 파울링 거동에 $TiO_2$ 나노입자의 결정구조와 용액의 pH 그리고 $Ca^{+2}$이 미치는 영향을 관찰하였다. 연구결과, $TiO_2$ 나노입자로 표면 개질된 정밀여과 분리막은 자연유기물에 의한 파울링 현상을 현저하게 감소시킬 수 있음을 확인 할 수 있었다. 그러나 이와같은 현상은 $TiO_2$ 나노입자의 결정구조와 용액의 성상에 매우 의존하는 것으로 나타났다. 자연유기물 파울링의 감소는 결정구조가 상대적으로 불안정한 anatase $TiO_2$ 나노입자를 분리막에 표면침적 시, 용액 중 $Ca^{+2}$이 존재하지 않을 때 상대적으로 높은 pH에서 효과적인 것으로 관찰되었다. 그러나 $Ca^{+2}$의 첨가 시 이와 같은 효과는 높은 pH에서 더욱 증가할 수 있음을 확인할 수 있었다. 반면, 결정구조가 상대적으로 안정한 rutile $TiO_2$ 나노입자의 경우 자연유기물의 파울링 감소는 용액의 조성에 큰 영향을 받지 않는 것으로 나타났다.