• The Korean Journal of Ceramics
• /
• v.6 no.3
• /
• pp.219-223
• /
• 2000

The ferroelectric SBT films were deposited on Pt/Ti/SiO$_2$/Si substrates by liquid injection metalorganic chemical vapor deposition (MOCVD) with single-mixture solution of Sr[Ta(OEt)$_5$(dmae)]$_2$and Bi(C$_6$ 6/H$_5$)$_3$. The Sr/Ta and Bi/Ta ratio in SBT films depended on deposition temperature and mol ratio of precursor in the single-mixture solution. At the substrate temperature of 40$0^{\circ}C$, Sr/Ta and Bi/Ta ratio were close to 0.4 and 1 at precursor mol ratio of 0.5~1.0, respectively. As-deposited film was amorphous. However, after annealing at 75$0^{\circ}C$ for 30 min in oxygen atmosphere, the diffraction patterns indicated polycrystalline SBT phase. The remanent polarization (Pr) and coercive field (Ec) of SBT film annealed at 75$0^{\circ}C$ were 4.7$\mu$C/$\textrm{cm}^2$ and 115.7kV/cm at an applied voltage of 5V, respectively. The SBT films annealed at 75$0^{\circ}C$ showed practically no polarization fatigue up to 10$^10$ switching cycles.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.94-98
• /
• 2000

Polycrystalline SBTN ferroelectric thin films were prepared by sol-gel method with various Nb mole ratios on Pt/ $SiO_2$/Si (100) substrates. The films were annealed at different temperatures and characterized in terms of phase and microstructure. Relatively a well saturated hysteresis pattern was obtained at x =0.2 in S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$)$_2$ $O_{9+}$$\alpha$/ thin films. At an applied voltage of 5V, the dielectric constant ($\varepsilon$$_{r}$) and dissipation factor (tan $\delta$) of typical S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$)$_2$ $O_{9+}$$\alpha$/ thin film (x=0.2) were about 236.2 and 0.034. Measured remanent polarization (2Pr) and coercive field (Ec) were 4.28C/c $m_2$, and 38.88kv/cm respectively. No fatigue was observed up to 6$\times$10$_{10}$ switching cycles at 5V and the normalized polarization reduced by a factor of only 4%.%. 4%.%. 4%.%.%.%.%.

• Journal of the Korean Ceramic Society
• /
• v.41 no.1
• /
• pp.13-18
• /
• 2004

$La_{0.5}Sr_{0.5}CoO_3$ (LSCO) electrodes were prepared on ferroelectric $Sr_{0.9}Bi_{2.1}Ta_2O_9$(SBT) thin films by spin coating method using photosensitive sol-gel solution. Self-patterning technique of photosensitive sol-gel solution has advantages such as simple manufacturing process compared to photoresist/dry etching process. Lanthanum(III) 2-methoxyethoxide, Stronitium diethoxide. Cobalu(II)2-methoxyethoxide were used as starting materials for LSCO electrode. UV irradiation on LSCO thin films lead to decrease solubility by M-O-M bond formation and the solubility difference allows us to obtain self-patternine. There was little composition change of the LSCO thin films between before leaching and after leaching in 2-methoxyethanol. The lowest resistivity of LSCO thin films deposited on $SiO_2$/Si substrate was $1.1{\times}10^{-2}{\Omega}cm$ when the thin film was ennealed at $740^{\circ}C$. The values of Pr/Ps and 2Pr of LSCO/SBT/Pt capacitor on the applied voltage of 5V were 0.51, 8.89 ${\mu}C/cm^2$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.128-129
• /
• 2007

We fabricated seeded $SrBi_2Ta_2O_9$(SBT) thin films using seeding technique on the $LaZrO_x$ (LZO)/Si structure. To evaluate the ferroelectric properties of seeded SBT thin films, we investigated the crystalline phase, the surface morphology, the capacitance-voltage (C-V) curve and the current density-voltage (J-V) curve of seeded films and then compared with the physical and electrical properties of unseeded films. As the result of that, the characteristics of seeded and unseeded films have a slight difference. Therefore, the ferroelectric properties of seeded SBT thin films are not necessarily superior than unseeded films.

• Journal of the Korean Vacuum Society
• /
• v.9 no.2
• /
• pp.136-143
• /
• 2000

$SrBi_2Ta_2O_9;(SBT)$ films were deposited on p-type Si(100) at room temperature by rf magnetron sputtering method to confirm the possibility of application of $Pt/SBT/Pt/Ti/SiO_2/Si$ structure (MFM) for destructive read out ferroelectric RAM (random access memory). Their structural characteristics with the various annealing times and Ar/$O_2$ gas flow ratios in sputtering were observed by XRD (X-ray diffractometer) and the surface morphologies were observed by FE-SEM (field emission scanning electron microscopy), and their electrical properties were observed by P-V (polarization-voltage measurement) and I-V (current-voltage measurement). The Ar/$O_2$ gas flow ratios of sputtering gas were changed from 1 : 4 to 4 : 1 and SBT thin films were deposited at room temperature. The films show (105), (110) peaks of SBT by XRD measurement. SBT thin films deposited at room temperature were crystallized by furnace annealing at 80$0^{\circ}C$ in oxygen atmosphere during either one hour or two hours. Among their electrical properties, P-V curves showed shaped hysteresis curves, but the SBT thin films showed the asymmetric ferroelectric properties in P-V curves. When Ar/$O_2$ gas flow ratios are 1 : 1, 2: 1, the leakage current density values of SBT thin films are good, those values of 3 V, 5 V, and 7 V are respectively $3.11\times10^{-8} \textrm{A/cm}^2$, $5\times10^{-8}\textrm{A/cm}^2$, $7\times10^{-8}\textrm{A/cm}^2$.After two hours of annealing time, their electrical properties and crystallization are improved.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.35D no.3
• /
• pp.39-45
• /
• 1998

SrBi$_{2}$Ta$_{2}$O$_{9}$ (SBT) ferroelectric thin films for nonvolatile memory were prepared on Pt/Ti/SiO$_{2}$/Si and RuO$_{2}$/SiO$_{2}$/Si substrates by RF magnetron sputtering. The dependences of crystalline and electrical properties on the lower electrode type(Pt and RuO$_{2}$) and the annealing temperatures were investigated. SBT films regardless of their electrode types showed typeical Bi layered peroviskite crystal structures. The crystalline quality of as-deposited SBT films was improved by the rapid thermal annealing at 650.deg. C for 30 sec. The remanetn polarization of 2Pr (Pr+-Pr-) of the annealed SBT films deposited on Pt/Ti/SiO$_{2}$/Si substrates were about 11 .mu.C/cm$^{2}$ and 3 .mu.C/cm$^{2}$, respectively. The leakage currents at 3 V bias voltage were about 0.8 .mu.A/cm$^{2}$ for SBT/ Pt/Ti/SiO$_{2}$/Si and about 1 .mu.A/cm$^{2}$ for SBT/RuO$_{2}$/SiO$_{2}$/Si sample. SBT films annealed at 650 .deg. C showed no degradation in Pr values after 10$^{11}$ polarization switching cycles, indicating good fatigue properties. In addition, for SBT samples deposited on Pt/Ti/SiO$_{2}$/Si, Pr values increased to more than that of initial state, suggesting the increament of leakage current caused by repeated polarization.

• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.46-51
• /
• 2003

Ferroelectric $Sr_{0.7}Bi_{2.1}Ta_{2.0}O_9$ thin films with 200 nm thicknesses were deposited on $Pt/Ti/SiO_2/Si$ substrate by liquid delivery MOCVD process. In these experiments, $Sr(TMHD)_2{\cdot}pmdeta,\; Bi(ph)_3$ and $Ta(O^i/Pr)_4(TMHD)$ were used as precursors, which were dissolved in n-butyl acetate and pentamethyldiethylenetriamine. Substrate temperature and reactor pressure of this experiment was $570^{\circ}C$and 5 Torr, respectively. The remanent polarization value (2Pr) of SBT thin film with annealed at $780^{\circ}C$was$7.247{\mu}C/cm^2$and$8.485 {\mu}C/cm^2$by applying 3 V and 5 V, respectively.

• Korean Journal of Materials Research
• /
• v.12 no.5
• /
• pp.382-386
• /
• 2002

We studied growth and characterization of $SrBi_2Ta_2O_9$ (SBT) thin films fabricated by low temperature process under vacuum and/or oxygen ambient. A metal organic decomposition (MOD) method based on a spin-on technique and annealing process using a rapid thermal annealing (RTA) method was used to prepare the SBT films. The crystallinity of a ferroelectric phase of SBT thin films is related to the oxygen partial pressure during RTA process. Under an oxygen partial pressure higher than 30 Torr, the crystallization temperature inducing the ferroelectric SBT phase can be lowered to $650^{\circ}C$. Those films annealed at $650^{\circ}C$ in vacuum and oxygen ambient showed good ferroelectric properties, that is, the memory window of 0.5~0.9 V at applied voltage of 3~7 V and the leakage current density of 1.80{\times}10^{-8}$ A/$\textrm{cm}^2$ at an applied voltage of 5V. In comparison with the SBT thin films prepared at 80$0^{\circ}C$ in $O_2$ ambient by furnace annealing process, the SBT thin films prepared at $650^{\circ}C$ in vacuum and oxygen ambient using the RTA process showed a good crystallization and electrical properties which would be able to apply to the virtul device fabrication precess.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.3
• /
• pp.183-187
• /
• 2000

In this study the SrBi$_2$Ta$_2$$O_{9}$ (SBT) thin films were etched by using magnetically enhanced inductively coupled Ar/CHF$_3$plasma as function of CHF$_3$/(Ar+CHF$_3$)gas mixing ratio. Maximum etch rate of SBT thin films was 1650 $\AA$/min and the selectivities of SBT to Pt and photoresist(PR) were 1.35 and 0.94 respectively under CHF$_3$/(Ar+CHF$_3$) of 0.1 For study on etching mechanism of SBT thin film X-ray photoelectron spectroscopy (XPS) surface analyses and secondary ion mass spectrometry (SIMS) mass analysis of etched SBT surfaces were performed. Among the elements of SBT thin film. M(Sr, Bi, Ta)-O bonds are broken by Ar ion bombardment and form SrF and TaF$_2$by chemical reaction with F. SrF and TaF$_2$are removed more easily by Ar ion bombardment. Scanning electron microscopy(SEM) was used for the profile examination of etched SBT film and the cross-sectional SEM profile of etched SBT film under CHF$_3$(Ar+CHF$_3$) of 0.1 was about 85$^{\circ}$X>.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.1
• /
• pp.7-15
• /
• 2004

The ferroelectric SBT thin films as a material of capacitors for non-volatile FRAMs have some problems that its remanent polarization value is relatively low and the crystallization temperature is quite high abovc 80$0^{\circ}C$. Therefore, in this paper, SBTN solution with S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$$O_{9}$ composition was synthesized by sol-gel method. Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. SBTN thin films with 200 nm thickness were deposited on Pt/Ti $O_2$/ $SiO_2$/Si substrates by spin-coating. UV-irradiation in a power of 200 W for 10 min and rapid thermal annealing in a 5-Torr-oxygen ambient at 76$0^{\circ}C$ for 60 sec were used to promote crystallization. The films were well crystallized and fine-grained after annealing at $650^{\circ}C$ in oxygen ambient. The electrical characteristics of 2Pr=11.94 $\mu$C/$\textrm{cm}^2$, Ps＋/Pr＋=0.54 at the applied voltage of 5 V were obtained for a 200-nm-thick SBTN films. This results show that 2Pr values of the UV irradiated and rapid thermal annealed SBTN thin films at the applied voltage of 5 V were about 57% higher than those of no additional processed SBTN thin films. thin films.lms.s.s.