Fabrecation and Characterization of $SrBi_2TaNbO_9$ Ferroelectric Thin Film Prepared by Sol-Gel Method

SOL-GEL법을 이용한 $SrBi_2TaNbO_9$ 강유전성 박막 제조 및 특성 평가

Polycrystalline SBTN ferroelectric thin films were prepared by sol-gel method with various Nb mole ratios on Pt/ $SiO_2$/Si (100) substrates. The films were annealed at different temperatures and characterized in terms of phase and microstructure. Relatively a well saturated hysteresis pattern was obtained at x =0.2 in S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$)$_2$ $O_{9+}$$\alpha$/ thin films. At an applied voltage of 5V, the dielectric constant ($\varepsilon$$_{r}$) and dissipation factor (tan $\delta$) of typical S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$)$_2$ $O_{9+}$$\alpha$/ thin film (x=0.2) were about 236.2 and 0.034. Measured remanent polarization (2Pr) and coercive field (Ec) were 4.28C/c $m_2$, and 38.88kv/cm respectively. No fatigue was observed up to 6$\times$10$_{10}$ switching cycles at 5V and the normalized polarization reduced by a factor of only 4%.%. 4%.%. 4%.%.%.%.%.