• 한국초전도ㆍ저온공학회논문지
• /
• 제6권3호
• /
• pp.16-20
• /
• 2004

YB $a_2$C $u_3$$O_{7-x}$ (YBCO) films were deposited on (100) SrTi $O_3$ single crystal substrates by a metal organic chemical vapor deposition (MOCVD) system of hot-wall type using single liquid source. Under the condition of the mole ratio of Y(tmhd)$_3$:Ba(tmhd)$_2$:Cu(tmhd)$_2$= 1:2.1:2.9. the deposition pressure of 10 Torr. the MO source line speed of 15 cm/min. the Ar/ $O_2$ flow rate of 800/800 sccm. YBCO films were prepared at the deposition temperatures of 780∼89$0^{\circ}C$. In case of the YBCO films with 2.2 ${\mu}{\textrm}{m}$ thickness deposited for 6 minutes at 86$0^{\circ}C$. XRD pattern showed complete c-axis growth and SEM morphology showed dense and crack-free surface. The atomic ratios of Ba/Y and Cu/Ba in the film were 1.92 and 1.56. respectively. The deposition rate of the film was as high as 0.37 ${\mu}{\textrm}{m}$/min. The critical temperature ( $T_{c.zero}$) of the film was 87K. The critical current of the film was 104 A/cm-width. and the critical current density was 0.47 MA/$\textrm{cm}^2$. For the thinner film of 1.3 ${\mu}{\textrm}{m}$ thickness. the critical current density of 0.62 MA/$\textrm{cm}^2$ was obtained.d.

• The Korean Journal of Ceramics
• /
• 제6권3호
• /
• pp.258-261
• /
• 2000

Highly (h00)-oriented (Ba, Sr)TiO$_3$(BST) thin films were grown by pulsed laser deposition on the perovskite LaNiO$_3$(LNO) metallic oxide layer as a bottom electrode. The LNO films were deposited on SiO$_2$/Si substrates by rf-magnetron sputtering method. The crystalline phases of the BST film were characterized by x-ray $\theta$-2$\theta$, $\omega$-rocking curve and $\psi$-scan diffraction measurements. The surface microsturcture observed by scanning electron microscopy was very dense and smooth. The low-frequency dielectric responses of the BST films grown at various substrate temperatures were measured as a function of frequency in the frequency range from 0.1 Hz to 10 MHz. The BST films have the dielectric constant of 265 at 1 kHz and showed multiple dielectric relaxation at the low frequency region. The origin of these low-frequency dielectric relaxation are attributed to the ionized space charge carriers such as the oxygen vacancies and defects in BST film, the interfacial polarization in the grain boundary region and the electrode polarization. We studied also on the capacitance-voltage characteristics of BST films.

• Transactions on Electrical and Electronic Materials
• /
• 제7권2호
• /
• pp.67-71
• /
• 2006

In this paper, we have investigated the structure and dielectric properties of the $(Ba_{0.6}Sr_{0.4})TiO_3$ (BST) thin films fabricated on MgO(100)/Si substrate by an alkoxide-based sol-gel method. Both the structure and morphology of those films were analyzed by x-ray diffraction (XRD) and atomic force microscope (AFM). For the MgO(100)/Si substrate, the BST thin films exhibited highly (100) orientation. The highly (100)-oriented BST thin films showed high dielectric constant, tunability, and figure of merit (FOM). The dielectric constant, dielectric loss and tunability of the BST thin films annealed at $700^{\circ}C$ deposited on the MgO(100)/Si substrate measured at 10 kHz were 515.9, 0.0082, and 54.3%, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.266-267
• /
• 2007

$Ba_{0.5}Sr_{0.5}TiO_3$(BST) films with different deposition temperatures were deposited on $Al_2O_3$ substrate by Nd:YAG Pulsed Laser Deposition(PLD). The deposition conditions to achieve high crystal structures and dielectric properties were optimized for both techniques. The structural characterization on the BST thin films was performed by X-Ray Diffraction(XRD) and Atomic Force Microscopy (AFM). Effects of post-deposition annealing of BST films were investigated. The best dielectric properties were obtained on $800^{\circ}C$ deposited BST film with post-deposition annealing at $1100^{\circ}C$ in flowing $O_2$ atmosphere for 2hours.

• 한국재료학회지
• /
• 제9권1호
• /
• pp.25-29
• /
• 1999

We have developed a laser molecular beam epitaxy system for the layer-by-layer growth of oxide thin films. Using this system, we could grow and control oxide thin films of LaAlO$_3$in a molecular layer epitaxy mode on the atomically flat SrTiO$_3$ substrate with a LaAlO$_3$single crystal target. Very clear RHEED oscillations were observed during to growth of a LaAlO$_3$ film for a long period under the optimized conditions of substrate temperature at $650^{\circ}C$, oxygen pressure at 1$\times$10\ulcorner torr, and an incident laser fluence of 4.6J/$\textrm{cm}^2$. The height of mono-layer-LaAlO$_3$ film grown during one period of RHEED intensity oscillation was 3.8$\AA$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.22-25
• /
• 2002

In this paper, we deposited MgO buffer layer on p-type (100)Si substrate in the condition of substrate temperature 400$^{\circ}C$, working gas ratio Ar:O$_2$=80:20, RF Power 50W, working pressure 10mtorr, and the thickness of the film was about 300${\AA}$. Then we deposited Ba$\sub$0.5/Sr$\sub$0.5/TiO$_3$ thin film using RF Magnetron sputtering method on the MgO/Si substrate in various RF power of 25W, 50W, 75W. The film deposited in 50W showed the best crystalline from the XRD measurement. To know the electrical properties of the film, we manufactured Al/BSTMgO(300${\AA}$)/Si/Al structure capacitor. In the result of I-V measurement, The leakage current density of the capacitor was lower than 10$\^$-7/A/$\textrm{cm}^2$ at the range of ${\pm}$150kV/cm. From C-V characteristics of the capacitor, can calculate the dielectric constant and it was 305. Finally we deposited BST thin film on bare Si substrate and (100)MgO substrate in the same deposition condition. From the comparate of the properties of these samples, we found the properties of BST thin film which deposited on MgO/Si substrate were better than on bare Si substrate and similar to on MgO substrate.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.213-214
• /
• 2008

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/SiO2/Si) using RF sputtering method at various substrate temperature. The optimum conditions of RF power and Ar/O2 ratio were 60[W] and 70/30, respectively. The crystallinity of SBN thin films were increased with increase of substrate temperature in the temperature range of 100~400[$^{\circ}C$]. The capacitance of SBN thin films were increased with the increase of substrate temperature.

• 한국재료학회지
• /
• 제30권7호
• /
• pp.333-337
• /
• 2020

Orthorhombic DyMnO₃ films are fabricated epitaxially on Nb-1.0 wt%-doped SrTiO₃ single crystal substrates using pulsed laser deposition technique. The structure of the deposited DyMnO₃ films is studied by X-ray diffraction, and the epitaxial relationship between the film and the substrate is determined. The electrical transport properties reveal the diodelike rectifying behaviors in the all-perovskite oxide junctions over a wide temperature range (100 ~ 340 K). The forward current is exponentially related to the forward bias voltage, and the extracted ideality factors show distinct transport mechanisms in high and low positive regions. The leakage current increases with increasing reverse bias voltage, and the breakdown voltage decreases with decrease temperature, a consequence of tunneling effects because the leakage current at low temperature is larger than that at high temperature. The determined built-in potentials are 0.37 V in the low bias region, and 0.11 V in the high bias region, respectively. The results show the importance of temperature and applied bias in determining the electrical transport characteristics of all-perovskite oxide heterostructures.

• 마이크로전자및패키징학회지
• /
• 제11권3호
• /
• pp.63-70
• /
• 2004

The structural, electrical properties of $(Ba, Sr)TiO_3[BSTO]/RuO_2$ thin films were examined by the addition of amorphous BSTO layer between crystlline BSTO film and $RuO_2$ substrate. We prepared BSTO films with double-layered structure, that is, amorphous layers deposited at $60^{\circ}C$ and crystalline films. Crystalline films were prepared at 550 on amorphous BSTO layer. The thickness of the amorphous layers was varied from 0 to 170 nm. During the deposition of crystalline films, the crystallization of the amorphous layers occurred and the structure was changed to circular while crystalline BSTO films showed columnar structure. Due to insufficient annealing effect, amorphous BSTO phase was observed when the thickness of the amorphous layers exceeded 30 nm. Amorphous BSTO layer could also prevent the formation of oxygen deficient region in $RuO_2$ surface. Leakage current of total BSTO films decreased with increasing amorphous layer thickness due to structural modifications. Dielectric constant showed maxi-mum value of 343 when amorphous layer thickness was 30 nm at which the improvement by grain growth and the degradation by amorphous phase were balanced.

• Transactions on Electrical and Electronic Materials
• /
• 제8권6호
• /
• pp.241-245
• /
• 2007

[ $(Ba_{0.9-x}Sr_xCa_{0.10})TiO_3$ ] (x=0.33, 0.36) powders were prepared by sol-gel method. $(Ba,Sr,Ca)TiO_3$(BSCT) thick films, undoped and doped with $MnCO_3$ and $Yb_2O_3(0.1{\sim}0.7mol%)$, were fabricated by the screen printing method on the alumina substrate. The coating and drying procedure was repeated 6-times. The Pt bottom electrode was screen printing method on the alumina substrate. These BSCT thick films were annealed at $1420^{\circ}C$ for 2 hr in atmosphere. The upper electrodes were fabricated by screen printing the Ag paste and then firing at $590^{\circ}C$ for 10 min. And then the structured and dielectric properties as a function of the doping amount of $Yb_2O_3$ were studied. As a result of the TG-DTA, exothermic peak was observed at around $670^{\circ}C$ due to the formation of the polycrystalline perovskite phase. All BSCT thick films showed XRD patterns of typical cubic peroveskite structure. The average thickness of BSCT thick films was about $70^{\mu}m$. The curie temperature and the dielectric constant decreased with increasing $Yb_2O_3$ doped content and the relative dielectric constant of the specimen, doped with 0.5 mol% $Yb_2O_3$ at BSCT(54/36/10), showed a best value of 5018 at curie temperature.