• Transactions on Electrical and Electronic Materials
• /
• v.6 no.1
• /
• pp.10-13
• /
• 2005

$Sr_{0.6}Ba_{0.4}Nb_{2}O_{6}$, hereafter SBN60, thin films of 300 nm thickness were deposited using ion beam sputtering technique, in which sintered ceramic target of the same composition was utilized and the $Ar:O_{2}$ gas ratio was controlled during deposition onto $Pt(100)/TiO_{2}/SiO_{2}/Si$ substrate. Crystallization and orientation behavior as well as electrical properties of the films were examined after annealing treatment at $650{\sim}800{\cric}C$. It was found that the film orientation was dependent upon $Ar:O_{2}$ratio, in which strong (00l) orientation was developed when the gas ratio was about 1:4 at $4.3{\times}10^{-4}$ torr. Typical remanent polarization (2Pr), the coercive field (Ec) and the dielectric constant of Pt/SBN60/Pt thin film capacitor were approximately $10{\mu}C/cm^{2}$, 60 kV/cm, and 615, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.111-115
• /
• 2003

200nm 정도의 두께를 가진 SBT 박막이 liquid delivery MOCVD 공정에 의해 (111) oriented Pt/Ti/$SiO_2$/Si 기판 위에 증착되었다 이 실험에서는 $Sr(TMHD)_2$tetraglyme, $Bi(ph)_3$ 그리고 $Ta(O^iPr)_4$(TMHD)를 출발 물질로 사용하였다. Sr 출발 물질의 열적 안정화를 위해서 adduct로 tetraglyme를 사용하여 실험하였고 유기 용매로는 n-butyl acetate를 사용하였다 Substrate temperature와 reactor pressure는 각각 $570^{\circ}C$와 5Torr로 유지시켰다. 또한 vaporizer의 용도는 $190-200^{\circ}C$, 그리고 delivery line 의 온도는 vaporizer 보다 높게 유지 $(220-230^{\circ}C)$하여 출발 용액을 분당 0.1ml로 50분간 주입하였다. 수송가스로 Ar, 산화제로 $O_2$ 가스를 사용하였다. 제조한 SBT 박막은 $750^{\circ}C$에서 열처리한 후 인가전압 3V와 5V에서 $2P_r$값이 각각 6.47, $8.98{\mu}C/cm^2$이었으며, $2E_c$값은 인가전압 3V와 5V에서 각각 2.05, 2.31V이었다 그리고 $800^{\circ}C$에서는$750^{\circ}C$에서 열처리한 SBT 박막보다 다소 우수한 이력특성을 나타내어 $2P_r$ 값은 인가전압 3V와 5V에서 각각 7.59, $10.18{\mu}C/cm^2$ 이었으며, $2E_c$값은 인가 전압 3V와 5V에서 각각 2.00, 2.21V 이었다.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.45-48
• /
• 2000

High dielectric (Ba,Sr)TiO$_3$thin films were etched in an inductively coupled plasma (ICP) as a function of C1$_2$/Ar gas mixing ratio. Under Cl$_2$(20)/Ar(80), the maximum etch rate of the BST films was 400$\AA$/min and selectivities of BST to Pt and PR were obtained 0.4 and 0.2, respectively. We investigated the etched surface of BST by x-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and x-ray diffraction (XRD). From the result of XPS analysis, we found that residues of Ba-Cl and Ti-Cl bonds remained on the surface of the etched BST for high boiling point. The surface roughness decreased as Cl$_2$increases in C1$_2$/Ar plasma because of non-volatile etching products. This changed the nature of the crystallinity of BST. From the result of XRD analysis, the crystallinity of etched BST film maintained as similar to as-deposited BST under Ar only and Cl$_2$(20)/Ar(80). However, (100) orientation intensity of etched BST film abruptly decreased at Cl$_2$only plasma. It was caused that Cl compounds were redeposited on the etched BST surface and damaged to crystallinity of BST film during the etch process.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.45-48
• /
• 2000

High dielectric (Ba,Sr)TiO$_3$ thin films were etched in an inductively coupled plasma (ICP) as a function of C1$_2$/Ar gas mixing ratio. Under Cl$_2$(20)/Ar(80), the maximum etch rate of the BST films was 400$\AA$/min and selectivities of BST to Pt and PR were obtained 0.4 and 0.2, respectively. We investigated the etched surface of BST by x-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and x-ray diffraction (XRD). From the result of XPS analysis, we found that residues of Ba-Cl and Ti-Cl bonds remained on the surface of the etched BST for high boiling point. The surface roughness decreased as Cl$_2$ increases in Cl$_2$/Ar plasma because of non-volatile etching products. This changed the nature of the crystallinity of BST. From the result of XRD analysis, the crystalliility of etched BST film maintained as similar to as-deposited BST under Ar only and Cl$_2$(20)/Ar(80). However, (100) orientation intensity of etched BST film abruptly decreased at Cl$_2$ only plasma. It was caused that Cl compounds were redeposited on the etched BST surface and damaged to crystallinity of BST film during the etch process.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.869-873
• /
• 2004

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient, piezoelectric, and a photo refractive properties. In this study, SBN60(x=0.6) thin film was manufactured by ion beam sputtering technique. Using the prepared SBN60 target in $Ar/O_2$ atmosphere as-deposited SBN60 thin film on Pt(100)/$TiO_2/SiO_2/Si$ substrate crystallization and orientation behavior as well as electric properties of SBN60 thin film were examined. SBN60 deposition up to $3000{\AA}$ in thickness, SBN60 thin film was heat-treated at $650^{\circ}C{\sim}800^{\circ}C$. The orientation was shown primarily along (001) plane from XRD pattern where working pressure was $4.3{\times}10^{-4}$ torr. The deposited layer was uniform, preferred orientatin and crystallization behavior resulted in the change of $O_2$ ratio was observed. In electric propertie of Pt/SBN60/Pt thin film capacitor remnant polarization (2Pr) value was $10{\mu}C/cm^2$, the coercive filed (Ec) 50 kV/cm, and the dielectric constant 615, respectively.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1553-1555
• /
• 1999

Recently, $SrBi_2Ta_2O_9$(SBT) and $Pb(ZrTi)O_3$(PZT) were much attracted as materials of capacitor for ferroelectric random access memory(FRAM) showing higher read/write speed, lower power consumption and nonvolartility. Bi-layered SBT thin film has appeared as the most prominent fatigue free and low operation voltage for use in nonvolatile memory. To highly integrate FRAM, SBT thin film should be etched. A lot of papers on SBT thin film and its characteristics have been studied. However, there are few reports about SBT thin film due to difficulty of etching. In order to investigate properties of etching of SBT thin film, SBT thin film was etched in $CF_4$/Ar gas plasma using magnetically enhanced inductively coupled plasma (MEICP) system. When $CF_4/(CF_4+Ar)$ is 0.1, etch rate of SBT thin film was $3300{\AA}/min$, and etch rate of Pt was $2495{\AA}/min$. Selectivities of SBT to Pt. $SiO_2$ and photoresist(PR) were 1.35, 0.6 and 0.89, respectively. With increasing $CF_4$ gas, etch rate of SBT thin film and $P_t$ decreased.