• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.7
• /
• pp.652-657
• /
• 2009

Strength characteristics of $Si_3N_4$ composite ceramics has been studied as functions of heat-treatment temperature and additive $SiO_2$. $SiO_2$ colloidal could significantly increase the bending strength. Crack healing temperature decreased 300 K by additive $TiO_2$. Bending strength of specimen added $SiO_2$ is higher than that of non-added $SiO_2$. Moreover, bending strength of specimen with $SiO_2$ colloidal coating is much higher that of non-coated specimen. In in-situ observation, crack-healed specimen at 1,573 K shows phenomenon like a fog on the surface. By SPM, both crack-healed specimen, non-coating and coating of $SiO_2$ colloidal, at 1,273 K were healed completely but both of 1,573 K exist crack. This was made by evaporation of $SiO_2$ at high temperature. Crack-healing materials of $Si_3N_4$ composite ceramics is crystallized $Y_2Si_2O_7$, $Y_2Ti_2O_7$ and $SiO_2$. A large amount of Si and O, and little C were detected by EPMA. Si and O increase but C decreases according to heat treatment temperature. Specimens with additive $SiO_2$ were more detected Si and O than that of non-additive $SiO_2$. Specimen with $SiO_2$ colloidal coatings were much more detected O.

• 연구논문집
• /
• s.26
• /
• pp.103-112
• /
• 1996

$Al_2O_3/SiC$ Hybrid-Composite has been fabricated by conventional powder process. The addition of $\alpha-Al_2O_3$ as seed particles in the transformation of $\gamma-Al_2O_3 to $\alpha-Al_2O_3$ provided a homogeneity of the microstructure, resulting in increase of mechanical properties. The grain growth of $Al_2O_3$ are significantly surpressed by the addition of nano-sized. SiC particles, increasing in fracture strength. The addition of SiC plates to $Al_2O_3$ nano-composite decreased the fracture strength, but increased the fracture toughness. Coated SiC plates with nitrides such as BN and /SiC$Si_3N_4$ enhanced fracture toughness much more than uncoated SiC plates by inducing crack deflection.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.11
• /
• pp.1233-1238
• /
• 2009

This study analyzed the characterization of high temperature strength of $Si_3N_4$ composite ceramics additive based on variations in the amount of nano colloidal $SiO_2$ added. Semi-elliptical cracks about 100 ${\mu}m$ length were obtained from a Vickers indenter using a load of 24.5 N. The results showed that the heat-treated smooth specimens with $SiO_2$ nano colloidal coating exhibited the highest bending strength at 0.0 wt% $SiO_2$ nano colloidal added, which is amounted to a 187 % increase over that of smooth specimen. Limiting temperature for bending strength of crack-healed zone for bending strength was about 1273 K. However, the bending strength of SSTS-3 and SSTS-4 was considerably increased while that of SSTS-1 and SSTS-2 was decreased at a temperature of 1,573K.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2006.11a
• /
• pp.166-168
• /
• 2006

$Si_3N_4/SiC$ composite ceramics was sintered in order to investigate their bending strength behavior after crack healing. $Y_2O_$ and $TiO_2$ power was added as sintering additives to enhance it's sintering property. A three-point bending specimen was cut out from sintered plates. About $100\;{\mu}m$ semi-circular surface cracks were made on the center of the tension surface of the three-point bending specimen using Vickers indenter. After the crack-healing processing from $500^{\circ}C$ to $1300^{\circ}C$, for 1 h, in air, the bending strength behavior of these crack-healed specimen coated with $SiO_2$ colloidal were determined systematically at room temperature. $Si_3N_4/SiC$ ceramics using additive powder ($Y_2O_3+TiO_2$) was superior to that of additive powder $Y_2O_3$. The additive powder $TiO_2$ exerted influence at growth of $Si_3N_4$. The optimum crack healing conditions coated $SiO_2$ colloidal were $1000^{\circ}C$ at $Si_3N_4/SiC$ using additive powder ($Y_2O_3+TiO_2$), and $1300^{\circ}C$ at $Si_3N_4/SiC$ using additive powder $Y_2O_3$.

• Korean Journal of Materials Research
• /
• v.6 no.4
• /
• pp.428-435
• /
• 1996

초미립 SiC분말과 SiC platelet을 2차성으로 Si3N4에 첨가하여 SiC/Si3N4 하이브리드 복합체를 가압소결로 제조한 후 2차상의 영향을 조사한 결과핫프레스법을 이용한 경우 SiC platelet은 Si3N4 기지 복합채의 치밀화를 저해하지 않고 초미립의 SiC 첨가는 Si3N4의 입성장을 효과적으로 억제하여 미세한 $\beta$-Si3N4의 grain을 형성함을 관찰하였다. 초미립 SiC첨가를 통한 복합체의 강도 증진은 상대적으로 $\beta$-Si3N4입자의 미세화에 의한 인성의 저하를 유도하나 SiC platelet을 첨가하여 급격한 강도 저하 없이 높은 인성을 갖는 하이브리드 복합체를 제조할 수 있었으며 SiC/Si3N4 하이브리드 복합체의 인성증진은 elongated $\beta$-Si3N4와 platelet SiC의 debonding에 의한 grain pull-out 영향임을 알 수 있었다.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.3
• /
• pp.89-94
• /
• 2005

We investigate the reaction stability of cobalt and nickel with side-wall materials of $SiO_2\;and\;Si_3N_4$. We deposited 15nm-Co and 15nm-Ni on $SiO_2(200nm)/p-type$ Si(100) and $Si_3N_4(70 nm)/p-type$ Si(100). The samples were annealed at the temperatures of $700\~1100^{\circ}C$ for 40 seconds with a rapid thermal annealer. The sheet resistance, shape, and composition of the residual materials were investigated with a 4-points probe, a field emission scanning electron microscopy, and an AES depth profiling, respectively. Samples of annealed above $1000^{\circ}C$ showed the agglomeration of residual metals with maze shape and revealed extremely high sheet resistance. The Auger depth profiling showed that the $SiO_2$ substrates had no residual metallic scums after $H_2SO_4$ cleaning while $Si_3N_4$ substrates showed some metallic residuals. Therefore, the $SiO_2$ spacer may be appropriate than $Si_3N_4$ for newly proposed Co/Ni composite salicide process.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.11
• /
• pp.957-962
• /
• 2008

Crack-healing behavior of $Si_3N_4$ composite ceramics has been studied as functions of heat-treatment temperature and amount of additive $SiO_2$ colloidal. Results showed that optimum amount of additive $SiO_2$ colloidal and coating of $SiO_2$ colloidal on crack could significantly increase the bending strength. The heat-treatment temperature has a profound influence on the extent of crack healing and the degree of strength recovery. The optimum heat-treatment temperature depends on the amount of additive $SiO_2$ colloidal. Crack healing strength was far the better cracked specimen with $SiO_2$ colloidal coating on crack surface. After heat treatment at the temperature 1,273 K in air, the crack morphology almost entirely disappeared by scanning prob microscope. At optimum healing temperature 1,273 K, the bending strength with additive $SiO_2$ colloidal 0.0 wt.% without $SiO_2$ colloidal coating recovered to the value of the smooth specimens at room temperature for the investigated crack sizes $100\;{\mu}m$. But that with $SiO_2$ colloidal coating increase up to 140 %. The amount of optimum additive $SiO_2$ colloidal was 1.3 wt.% and crack healed bending strength with $SiO_2$ colloidal coating increase up to 160 % to smooth specimen of additive $SiO_2$ colloidal 0.0 wt.%. Crack closure and rebonding of the crack due to oxidation of cracked surfaces were suggested as a dominant healing mechanism operating in $Si_3N_4$ composite ceramics.

• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1102-1107
• /
• 1999

SiC-Si3N4 composites were prepared by mixing $\alpha$-Si3N4 powder to $\alpha$-SiC powder in the range of 10 to 30 vol% with 10vol% interval. 6wg% Al2O3 and 6wt% Y2O3 were respectively added as sintering aids. Hot pressing was performed at 1,80$0^{\circ}C$ for 1 hour with 25 MPa pressure. In the case of adding 20vol% of $\alpha$-Si3N4 powder the relative density to theoretical value and the flexural strength were 99.1% and 34,420 MPa respectively and the worn amount was 2.09$\times$10-3 mm2 which were the highest values in the all range of he composition. Although the composite containig 10 vol% of $\alpha$-Si3N4 powder showed the highest fracture toughness(KIC) of 4.65MN/m3/2 the reduction of the wear resistance in this composite is likely to be affected by the homogeneity and the uniformity of the grain coalescence and growth during the sintering process.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.9
• /
• pp.82-88
• /
• 2001

In order to fulfil the requirements of the various performance profiles of ceramic cutting tools, six different SiC-based ceramics have been fabricated by hot-pressing (SiC--${Si}_3 {N}_4$composites) or by hot-pressing and subsequent annealing (monolithic SiC and SiC-TiC composites). Correlation between the annealing time and the corresponding microstructure and the mechanical properties of resulting ceramics have been investigated. The grain size of both ${Si}_3 {N}_4$and SiC in SiC-${Si}_3 {N}_4$composites increased with the annealing time. Monolithic SiC has the highest hardness, SiC-TiC composite the highest toughness, and the SiC-${Si}_3 {N}_4$composite the highest strength among the ceramics investigated. The hardness of SiC-${Si}_3 {N}_4$composites was relatively independent of the grain size, but dependent on the sintered density. The cutting performance of the newly developed SiC-based ceramic cutting tools will be described in Part 2 of this paper.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.153.1-153.1
• /
• 2007