• Transactions on Electrical and Electronic Materials
• /
• v.1 no.1
• /
• pp.22-25
• /
• 2000

Polycrystalline SBTN layered ferroelectric thin film with various Nb mole ratios were prepared by sol-gel method Pt/ $SiO_2$/Si (100) substrates. The films were annealed at different temperature and characterized in terms of phase and microstructure. The films were crystallized with a high (105) diffraction intensity and had rodike structure, SBTN films fired at 800$^{circ}C$ revealed standard hysteresis loops with no fatigue for up to 10$^{10}$ cycles. At an applied voltage of 5V the dielectric constant($varepsilon$) , dissipation factor (tan $delta$), remanent polarization(ZPr) and coercive field(Ec) of typical S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$) $O_{9+}$$alpha$/ thin film(x=0.1) prepared on Pt/ $SiO_2$/Si (100) were about 277.7, 0.042, 3.74$mu$C/$textrm{cm}^2$, and 24.8kv/cm respectively.ly.y. respectively.ly.y.y..

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.112-112
• /
• 2009

In this study, the effect of a long post-deposition thermal annealing(600 and 1000 $^{\circ}C$) on the surface acoustic wave (SAW) properties of polycrystalline (poly) aluminum-nitride (AlN) thin films grown on a 3C-SiC buffer layer was investigates. The poly-AlN thin films with a (0002) preferred orientation were deposited on the substrates by using a pulsed reactive magnetron sputtering system. Experimental results show that the texture degree of AlN thin film was reduced along the increase in annealing temperature, which caused the decrease in the electromechanical coupling coefficient ($k^2$). The SAW velocity also was decreased slightly by the increase in root mean square (RMS) roughness over annealing temperature. However, the residual stress in films almost was not affect by thermal annealing process due to small lattice mismatch different and similar coefficient temperature expansion (CTE) between AlN and 3C-SiC. After the AlN film annealed at 1000 $^{\circ}C$, the insertion loss of an $IDT/AlN/3C-SiC/SiO_2/Si$ structure (-16.44 dB) was reduced by 8.79 dB in comparison with that of the as-deposited film (-25.23 dB). The improvement in the insertion loss of the film was fined according to the decrease in the grain size. The characteristics of AlN thin films were also evaluated using Fourier transform-infrared spectroscopy (FT-IR) spectra and X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM) images.

• Korean Journal of Materials Research
• /
• v.12 no.5
• /
• pp.387-390
• /
• 2002

A new approach of using double buffer layers of AlN and GaN for growth of GaN films on Si has been undertaken via molecular beam epitaxy using ammonia. The first buffers layer of AlN was grown using $N_2$plasma and the second of GaN was grown using ammonia. The surface roughness of the grown films was investigated by atomic force microscope and was compared with the normally grown films on sapphire. Double crystal x-ray rocking curve and low temperature photoluminescence techniques were employed for structural and optical properties examination. Donor bound exciton peak at 3.481 eV with full width half maximum of 41 meV was observed at 13K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.94-98
• /
• 2000

Polycrystalline SBTN ferroelectric thin films were prepared by sol-gel method with various Nb mole ratios on Pt/ $SiO_2$/Si (100) substrates. The films were annealed at different temperatures and characterized in terms of phase and microstructure. Relatively a well saturated hysteresis pattern was obtained at x =0.2 in S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$)$_2$ $O_{9+}$$\alpha$/ thin films. At an applied voltage of 5V, the dielectric constant ($\varepsilon$$_{r}$) and dissipation factor (tan $\delta$) of typical S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$)$_2$ $O_{9+}$$\alpha$/ thin film (x=0.2) were about 236.2 and 0.034. Measured remanent polarization (2Pr) and coercive field (Ec) were 4.28C/c $m_2$, and 38.88kv/cm respectively. No fatigue was observed up to 6$\times$10$_{10}$ switching cycles at 5V and the normalized polarization reduced by a factor of only 4%.%. 4%.%. 4%.%.%.%.%.

• Journal of the Korean Vacuum Society
• /
• v.12 no.S1
• /
• pp.7-9
• /
• 2003

Solid-state reactions in Ni/Si multilayered films (MLF) with an overall stoichiometry of $Ni_2Si$, NiSi and $NiSi_2$, induced by ion-beam mixing (IBM) and thermal annealing, were studied by using spectroscopic ellipsometry and magneto-optical spectroscopy as well as x-ray diffraction (XRD). The mixing was performed with Ar+ ions of an energy of 80 keV and a dose of $1.5 x\times10^{16}$ $Ar^+$/$\textrm{cm}^2$. It was shown that the IBM induces structural changes in the Ni/Si MLF, which cannot be detected by XRD but are confidently recognized by the optical method. A thermal annealing at 673 K of the Ni/Si MLF with an overall stoichiometry of NiSi and $NiSi_2$ causes formation of the first η -NiSi phase. The first trace for $NiSi_2$ phase on the background of NiSi one was detected by XRD after an annealing at 1073 K while, according to the optical results, $NiSi_2$ turns out be the dominant phase for the annealed Ni/Si MLF with an overall stoichiometry of $NiSi_2$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.11a
• /
• pp.1-1
• /
• 1994

;The electronic state calculations for various types of ceramic materials have beell performed by the use of $DV-X\;{\alpha}$ cluster method. The molecular orbital levels and wave functions for model clusters have been computed to study the electronic properties ami chemical bonding of the ceramics. For ${\beta}-sialon(Si_{6-z}Al_zO_zN_{8-z})$ which is a high temperature structural material based on ${\beta}-Si_3N_4$, we have made model cluster calculations to estimate the strength of chemical bonding between atoms by the Mulliken population analysis. It is found that the covalent bonding between Si and N atoms is very strong in pure ${\beta}-Si_3N_4$, but the covalency around solute atom is considerably weakened when Si atom is substituted by AI. This tendency is enhanced by an additional substitution of oxygen atom for N. The result calculated can well explain the experimental data of changes in mechanical properties such as the reductions of Young's modulus and Vickers hardness with increment of z-value in ${\beta}-sialon$. Various model clusters for transition metal oxides which show many interesting physical and chemical properties have also been calculated. High-valent perovskite-type iron oxides EMFe0_3E(M=Ca and Sr) possess very interesting magnetic and chemical properties. In these oxides, iron exists as $Fe^{4+}$ state, but the experimental measurement of Mossba~er effect suggests that disproportionation $2Fe^{4+}=Fe^{3+}+Fe^{5+}$ takes place for $CaFe0_3$ at low temperatures. The model cluster calculations for these compounds indicated the existence of considerably strong covalent bonding of Fe-O. The calculations of hyperfine interaction at iron neucleus show very good agreement with the experimental Mossbauer measurements. The result calculated also implies that the disproportionation reaction is strongly possible by assuming the quenching of breathing phonon mode at low temperatures.tures.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.6
• /
• pp.580-586
• /
• 2016

Cr-Si-Al-N coating with different Si content were deposited by hybrid physical vapor deposition (PVD) method consisting of unbalanced magnetron (UBM) sputtering and arc ion plating (AIP). The deposition temperature was $300^{\circ}C$, and the gas ratio of $Ar/N_2$ were 9:1. The CrSi alloy and aluminum targets used for arc ion plating and sputtering process, respectively. Si content of the CrSi alloy targets were varied with 1 at%, 5 at%, and 10 at%. The phase analysis, composition and microstructural analysis performed using x-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM) including energy dispersive spectroscopy (EDS), respectively. All of the coatings grown with textured CrN phase (200) plane. The thickness of the Cr-Si-Al-N films were measured about $2{\mu}m$. The friction coefficient and removal rate of films were measured by a ball-on-disk test under 20N load. The friction coefficient of all samples were 0.6 ~ 0.8. Among all of the samples, the removal rate of CrSiAlN (10 at% Si) film shows the lowest values, $4.827{\times}10^{-12}mm^3/Nm$. As increasing of Si contents of the CrSiAlN coatings, the hardness and elastic modulus of CrSiAlN coatings were increased. The morphology and composition of wear track of the films was examined by scanning electron microscopy (SEM) and energy dispersive spectroscopy, respectively. The surface energy of the films were obtained by measuring of contact angle of water drop. Among all of the samples, the CrSiAlN (10 at% Si) films shows the highest value of the surface energy, 41 N/m.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.29A no.2
• /
• pp.68-76
• /
• 1992

Concurrent Junction process (simultaneous formation of a silicide and a junction on the implanted substrate) by Rapid Thermal Annealig has been investigated. Electrical and material properties of CoSi$_2$ films were analyzed with Alpha Step, 4-point probe, X-ray diffraction(XRD) and Scanning Electron Microscope(SEM). And CoSi$_2$ junctions were examined with Spreading Resistance probe in order to see the redistribution of electrically activated dopants and determined the junction depth. Two step annealing process, which was 80$0^{\circ}C$ for 30sec and 100$0^{\circ}C$ for 30sec in NS12T ambient was employed to form CoSi$_2$ and shallow junctions. Resistivity of CoSi$_2$ was turned out to be 11-15${\mu}$cm and shallow junctions less than 0.1$\mu$m were successfully formed by the process. It was found that the dopant concentration at CoSi$_2$/Si interface increased as decreasing the thickness of Co films in case of $p^{+}/n$ and $n^{+}/p$ junctions while the junction depth decreased as increasing CoSiS12T thickness in case of $p^{+}/n$ junction.

• Journal of the Korean Vacuum Society
• /
• v.5 no.4
• /
• pp.333-340
• /
• 1996

The properties of TiN as a barrier against Cu diffusion ere studied by sheet resistance measurement, X-ray diffraction, scanning electron microscopy, Auger electron spectroscopy, and capacitance-voltage(C-V) measurement. The sensitivities of the various methods were compared. Specimens with Cu/TiN/Ti/SiO2/Si structure were prepared by various deposition techniques and annealed at various temperatures ranging from $500^{\circ}C$ to $800^{\circ}C$ in 10%H2/90%Ar ambient for hours. As the effectiveness of the barrier property of TiN against Cu diffusion was vanished, the irregular-shaped sports were observed and outdiffused Si were detected on the surface of the Cu thin film. The C-V characteristics of the MOS capacitors varied drastically with annealing temperatures. In C-V measurement, the inversion capacitance decreased at annealing temperature range from $500^{\circ}C$ to $700^{\circ}C$ and increased remarkably at $800^{\circ}C$. These variations may be due to the Cu diffusion through TiN into $SiO_2$ and Si.

• Korean Journal of Materials Research
• /
• v.9 no.11
• /
• pp.1129-1136
• /
• 1999

TIN films were prepared on Si(100) substrate by ICP-CVD(inductive1y coupled plasma enhanced chemical vapor deposition) using TEMAT(tetrakis ethylmethamido titanium : Ti$[\textrm{N}\textrm{(CH)}_{3}\textrm{C}_{2}\textrm{H}_{5}]_{4}$) precursor at various deposition conditions. Phase, microstructure, and the electrical properties of TIN films were characterized by x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS), high resolution transmission electron microscopy (HRTEM) and electrical measurements. Polycrystalline TiN films with B1 structure were grown at temperatures over $200^{\circ}C$. Preferentially oriented along TiN(111) films were obtained at temperatures over $300^{\circ}C$ with the flow rates of 10, 5, and 5 sccm for TEMAT, $\textrm{N}_{2}$ and Ar gas. The TiN/Si(100) interface was flat and no chemical reaction between TIN and $\textrm{SiO}_2$ was found. The resistivity, carrier concentration and the carrier mobility for the TiN sample prepared at $500^{\circ}C$ are 21 $\mu\Omega$cm, 9.5$\times\textrm{10}^{18}\textrm{cm}^{-3}$ and $462.6\textrm{cm}^{2}$/Vs, respectively.