• 한국전기전자재료학회논문지
• /
• 제21권8호
• /
• pp.699-705
• /
• 2008

Capacitance versus voltage (C-V) characteristics of Ge-nanocrystal (NC)-embedded metal-oxide-semiconductor (MOS) capacitors with $HfO_2$ gate material were investigated in this work. The current versus voltage (I-V) curves obtained from Ge-NC-embedded MOS capacitors fabricated with the $NH_3$ annealed $HfO_2$ gate material reveal the reduction of leakage current, compared with those of MOS capacitors fabricated with the $O_2$ annealed $HfO_2$ gate material. The C-V curves of the Ge-NC-embedded MOS capacitor with $HfO_2$ gate material annealed in $NH_3$ ambient exhibit counterclockwise hysteresis loop of about 3.45 V memory window when bias voltage was varied from -10 to + 10 V. The observed hysteresis loop indicates the presence of charge storages in the Ge NCs caused by the Fowler-Nordheim (F-N) tunneling. In addition, capacitance versus time characteristics of Ge-NC-embedded MOS capacitors with $HfO_2$ gate material were analyzed to investigate their retention property.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제49권1호
• /
• pp.1-7
• /
• 2000

The SNOSFET memory devices with ultrathin ONO(tunnel oxide-nitride-blocking oxide) gate dielectric were fabricated using n-well CMOS process and investigated its characteristics. The thicknesses of tunnel oxide, nitride and blocking oxide were $23{\AA},\; 53{\AA}\; and\; 33{\AA}$, respectively. Auger analysis shows that the ONO layer is made up of $SiO_2(upper layer of blocking oxide)/O-rich\; SiO_x\N\_y$. It clearly shows that the converting layer with $SiO_x\N\_y(lower layer of blocking oxide)/N-rich SiO_x\N\_y(nitride)/O-rich SiO_x\N\_y(tunnel oxide)$. It clearly shows that the converting layer with $SiO_x\N\_y$ phase exists near the interface between the blocking oxide and nitride. The programming condition of +8 V, 20 ms, -8 V, 50 ms is determined and data retention over 10 years is obtained. Under the condition of 8 V programming, it was confirmed that the modified Fowler-Nordheim tunneling id dominant charge transport mechanism. The programmed threshold voltage is distributed less than 0.1 V so that the reading error of memory stated can be minimized. An $8\times8$ NAND type flash EEPROM with SONOSFET memory cell was designed and simulated with the extracted SPICE parameters. The sufficient read cell current was obtained and the upper limit of $V_{TH}$ for write state was over 2V.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.358-361
• /
• 2002

Self-aligned MOSFETS using a polysilicon gate are widely fabricated in silicon technology. The polysilicon layer acts as a mask for the source and drain implants and does as gate electrode in the final product. However, the usage of polysilicon gate as a self-aligned mask is restricted in fabricating SiC MOSFETS since the following processes such as dopant activation, ohmic contacts are done at the very high temperature to attack the stability of the polysilicon layer. A metal instead of polysilicon can be used as a gate material and even can be used for ohmic contact to source region of SiC MOSFETS, which may reduce the number of the fabrication processes. Co-formation process of metal-source/drain ohmic contact and gate has been examined in the 4H-SiC based vertical power MOSFET At low bias region (<20V), increment of leakage current after RTA was detected. However, the amount of leakage current increment was less than a few tens of ph. The interface trap densities calculated from high-low frequency C-V curves do not show any difference between w/ RTA and w/o RTA. From the C-V characteristic curves, equivalent oxide thickness was calculated. The calculated thickness was 55 and 62nm for w/o RTA and w/ RTA, respectively. During the annealing, oxidation and silicidation of Ni can be occurred. Even though refractory nature of Ni, 950$^{\circ}C$ is high enough to oxidize it. Ni reacts with silicon and oxygen from SiO$_2$ 1ayer and form Ni-silicide and Ni-oxide, respectively. These extra layers result in the change of capacitance of whole oxide layer and the leakage current

• 전자공학회논문지D
• /
• 제35D권7호
• /
• pp.79-87
• /
• 1998

Nitrided oxides which have been investigated as alternative gate oxide for metal-oxide-semiconductor field effect devices were grown by two-step process using N$_{2}$O gas, and were chaacterized via a fowler-nordheim tunneling(FNT) electron injection technique. Electrical characteristics of nitrided gate oxides were superior to that of control oxides.Further, the FNT electron injection into the nitrided gate oxides reveals that gate oxides degrade more both if electrons were foreced to inject from the gate metal and if thicker nitrided gate oxides were used in the thickness range of 90~130.angs.. Models are suggested to explain these phenomena.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.354-357
• /
• 2002

Thermally grown gate oxide on 4H-SiC wafer was investigated. The oxide layers were grown at l150$^{\circ}C$ varying the carrier gas and post activation annealing conditions. Capacitance-Voltage(C-V) characteristic curves were obtained and compared using various gate electrode such as Al, Ni and poly-Si. The interface trap density can be reduced by using post oxidation annealing process in Ar atmosphere. All of the samples which were not performed a post oxidation annealing process show negative oxide effective charge. The negative oxide effective charges may come from oxygen radical. After the post oxidation annealing, the oxygen radicals fixed and the effective oxide charge become positive. The effective oxide charge is negative even in the annealed sample when we use poly silicon gate. Poly silicon layer was dope by POCl$_3$ process. The oxide layer may be affected by P ions in poly silicon layer due to the high temperature of the POCl$_3$ doping process.

• JSTS:Journal of Semiconductor Technology and Science
• /
• 제3권1호
• /
• pp.13-20
• /
• 2003

Both MgO and $Sc_2O_3$ are shown to provide low interface state densities (in the $10^{11}{\;}eV^{-1}{\;}cm{\;}^{-2}$ range)on n-and p-GaN, making them useful for gate dielectrics for metal-oxide semiconductor(MOS) devices and also as surface passivation layers to mitigate current collapse in GaN/AlGaN high electron mobility transistors(HEMTs).Clear evidence of inversion has been demonstrated in gate-controlled MOS p-GaN diodes using both types of oxide. Charge pumping measurements on diodes undergoing a high temperature implant activation anneal show a total surface state density of $~3{\;}{\times}{\;}10^{12}{\;}cm^{-2}$. On HEMT structures, both oxides provide effective passivation of surface states and these devices show improved output power. The MgO/GaN structures are also found to be quite radiation-resistant, making them attractive for satellite and terrestrial communication systems requiring a high tolerance to high energy(40MeV) protons.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.128-129
• /
• 2008

The annealing effects of $SiO_2/Si_3N_4$ stacked tunneling dielectrics were investigated. I-V characteristics of band gap engineered tunneling gate stacks consisted of $Si_3N_4/SiO_2/Si_3N_4$(NON), $SiO_2/Si_3N_4/SiO_2$(ONO) dielectrics were evaluated and compared with $SiO_2$ single layer using the MOS(Metal-Oxide-Semiconductor) capacitor structure. The leakage currents of engineered tunneling barriers (ONO, NON stacks) are lower than that of the conventional $SiO_2$ single layer at low electrical field. Meanwhile, the engineered tunneling barriers have larger tunneling current at high electrical field and improved electrical characteristics by annealing processes than $SiO_2$ layer.

• EDISON SW 활용 경진대회 논문집
• /
• 제5회(2016년)
• /
• pp.362-364
• /
• 2016

본 논문에서는 MOS(Metal Oxide Semiconductor) Capacitor의 산화막내에 다양한 원인에 의해 존재하는 비이상적인 전하들 중 Fixed Oxide Charge가 소자의 문턱전압에 어떤 영향을 주는지 분석했다. 분석한 결과 n+ polysilicon Gate를 가지고, 산화막인 $SiO_2$의 두께가 3nm이고, 도핑농도가 $10^{18}cm^{-2}$인 P형 실리콘 기판으로 이루어진 MOS Capacitor에서 Fixed Oxide Charge Density가 $C/cm^2$ 이상일 때 문턱전압을 0.01V 이상 감소시키고 $C/cm^2$ 이하일 때 문턱전압을 0.01V 이상 증가시켰다.

• 전기전자학회논문지
• /
• 제22권4호
• /
• pp.1230-1233
• /
• 2018

에어로졸 데포지션 (aerosol deposition)공정을 통해 $Al_2O_3$막을 4H-SiC 상에 50 nm 두께로 제조하였고, 후열처리 공정에 따른 전기적 특성을 분석하였다. 그 결과 $N_2$분위기 열처리 시 $Al_2O_3$와 SiC 계면의 고정전하량이 감소하였으나 산소공공 생성에 의한 누설전류의 증가를 확인하였다. 본 결과로부터 계면특성 향상과 누설전류의 감소를 위해서는 적절한 $N_2$와 $O_2$가스의 혼합이 중요함을 확인하였다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2008년도 International Meeting on Information Display
• /
• pp.620-621
• /
• 2008

Transparent electronics has been one of the key terminologies forecasting the ubiquitous technology era. Several researchers have thus extensively developed transparent oxide-based thin-film transistors (TFTs) on glass and plastic substrates although in general high voltage operating devices have been mainly studied considering transparent display drivers. However, low voltage operating oxide TFTs with transparent electrodes are very necessary if we are aiming at logic circuit applications, for which transparent complementary or one-type channel inverters are required. The most effective and low power consuming inverter should be a form of complementary p-channel and n-channel transistors but real application of those complementary TFT inverters also requires electrical- and even photo-stabilities. Since p-type oxide TFTs have not been developed yet, we previously adopted organic pentacene TFTs for the p-channel while ZnO TFTs were chosen for n-channel on sputter-deposited $AlO_x$ film. As a result, decent inverting behavior was achieved but some electrical gate instability was unavoidable at the ZnO/$AlO_x$ channel interface. Here, considering such gate instability issues we have designed a unique transparent complementary TFT (CTFTs) inverter structure with top n-ZnO channel and bottom p-pentacene channel based on 12 nm-thin nano-oxide/self assembled monolayer laminated dielectric, which has a large dielectric strength comparable to that of thin film amorphous $Al_2O_3$. Our transparent CTFT inverter well operate under 3 V, demonstrating a maximum voltage gain of ~20, good electrical and even photoelectric stabilities. The device transmittance was over 60 % and this type of transparent inverter has never been reported, to the best of our limited knowledge.