• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.130.1-130
• /
• 2003

• Korean Journal of Materials Research
• /
• v.5 no.1
• /
• pp.36-41
• /
• 1995

Dielectric properties were investigated at Mn doped $(Pb_{1-x}Ca_{x})ZrO_{3}$ with x=0.38 in microwavefrequencies. Both the density and Q values of sintered ceramics increased with increasing calciningtemperature. In the sample sintered at $1300^{\circ}C$ for 2 hrs, the deped Mn ions completely solubled in $(Pb,Ca)ZrO_{3}$ phase until 0.5wt% and the grain size was independent of doping amount. It was observed thathigh dielectric constant of 90 - 100 and high quality factor of 1300 at 4 GHz for O.l5wt% Mn doped$(Pb_{0.62}Ca_{0.38})ZrO_{3}$. The Mn" and Mn" worked as acceptors in $(Pb,Ca)ZrO_{3}$ which created the oxygen vacancies and affected the increment of the Q values. However, the excess Mn doping more than 0.5wt% resulted in decreasing Q values.decreasing Q values.

• Korean Journal of Materials Research
• /
• v.29 no.10
• /
• pp.586-591
• /
• 2019

This study describes the doping effect of $Yb_2O_3$ on microstructure, electrical and dielectric properties of $ZnO-V_2O_5-MnO_2-Nb_2O_5$ (ZVMN) ceramic semiconductors sintered at a temperature as low as $900^{\circ}C$. As the doping content of $Yb_2O_3$ increases, the ceramic density slightly increases from 5.50 to $5.54g/cm^3$; also, the average ZnO grain size is in the range of $5.3-5.6{\mu}m$. The switching voltage increases from 4,874 to 5,494 V/cm when the doping content of $Yb_2O_3$ is less than 0.1 mol%, whereas further doping decreases this value. The ZVMN ceramic semiconductors doped with 0.1 mol% $Yb_2O_3$ reveal an excellent nonohmic coefficient as high as 70. The donor density of ZnO gain increases in the range of $2.46-7.41{\times}10^{17}cm^{-3}$ with increasing doping content of $Yb_2O_3$ and the potential barrier height and surface state density at the grain boundaries exhibits a maximum value (1.25 eV) at 0.1 mol%. The dielectric constant (at 1 kHz) decreases from 592.7 to 501.4 until the doping content of $Yb_2O_3$ reaches 0.1 mol%, whereas further doping increases it. The value of $tan{\delta}$ increases from 0.209 to 0.268 with the doping content of $Yb_2O_3$.

• Journal of Powder Materials
• /
• v.17 no.5
• /
• pp.399-403
• /
• 2010

The effects of $MnO_2$ doping on the crystal structure, ferroelectric, and piezoelectric properties of (K,Na)$NbO_3$ (KNN) ceramics have been investigated. $MnO_2$ was found to be effective in enhancing the densification and grain growth during sintering. X-ray diffraction analysis indicated that Mn ions substituted B-site Nb ions up to 2 mol%, however, further doping induced unwanted secondary phases. In comparison with undoped KNN ceramics, the well developed microstructure and the substitution to B-sites in 2 mol% Mn-doped KNN ceramics resulted in significant improvements in both piezoelectric coupling coefficient and electromechanical quality factor.

• Journal of the Korean Ceramic Society
• /
• v.35 no.6
• /
• pp.619-625
• /
• 1998

Mn doped {{{{ {Zn {Ga }_{2 }O }_{4 } }} thin film phosphors were prepared on Si(100) wafers and ITO coated glass substrates by rf magnetron sputtering technique and the effects of the substrates dopant and the sputtering paramet-ers were analyzed, Changes of the oreintation were observed after annealine tratment. The grain size of {{{{ {Zn {Ga }_{2 }O }_{4 } }} : Mn thin film deposited on Si wafer was smaller than that on ITO/glass substrate which resulted in higher PL intensity. The PL spectra of Mn doped {{{{ {Zn {Ga }_{2 }O }_{4 } }} thin films showed sharp green luminescence spec-trum. According to CL spectrum it could be concluded that Mn ions acted as an actuator for green emission by substituting Zn atom sites.

• Korean Journal of Materials Research
• /
• v.29 no.3
• /
• pp.150-154
• /
• 2019

This study investigates the effect of MnO2 and CuO as acceptor additives on the microstructure and piezoelectric properties of $0.96(K_{0.5}Na_{0.5})_{0.95}Li_{0.05}Nb_{0.93}Sb_{0.07}O_3-0.04BaZrO_3$, which has a rhombohedral-tetragonal phase boundary composition. $MnO_2$ and CuO-added $0.96(K_{0.5}Na_{0.5})_{0.95}Li_{0.05}Nb_{0.93}Sb_{0.07}O_3-0.04BaZrO_3$ ceramics sintered at a relatively low temperature of $1020^{\circ}C$ show a pure perovskite phase with no secondary phase. As the addition of $MnO_2$ and CuO increases, the sintered density and grain size of the resulting ceramics increases. Due to the difference in the amount of oxygen vacancies produced by B-site substitution, Cu ion doping is more effective for uniform grain growth than Mn ion doping. The formation of oxygen vacancies due to B-site substitution of Cu or Mn ions results in a hardening effect via ferroelectric domain pinning, leading to a reduction in the piezoelectric charge coefficient and improvement of the mechanical quality factor. For the same amount of additive, the addition of CuO is more advantageous for obtaining a high mechanical quality factor than the addition of $MnO_2$.

• Journal of Magnetics
• /
• v.18 no.1
• /
• pp.26-29
• /
• 2013

$Mn_xFe_{3-x}O_4$ powders have been fabricated by using sol-gel methods; their crystallographic and magnetic properties were investigated by using X-ray diffraction, scanning electron microscopy, M$\ddot{o}$ssbauer spectroscopy, and vibrating sample magnetometer. The $Mn_xFe_{3-x}O_4$ ferrite powders annealed at $500^{\circ}C$ had a single spinel structure regardless of the $Mn^{2+}$-doping amount and their lattice constants became larger as the $Mn^{2+}$ concentration was increased. Their Mossbauer spectra measured at room temperature were fitted with 2 Zeeman sextets due to the tetrahedral and octahedral sites of Fe ions, which made them ferrimagnetic. The magnetic behavior of $Mn_xFe_{3-x}O_4$ powders showed that the $Mn^{2+}$-doping amount made their saturation magnetization increase, but there were no severe effects on their coercivities. The saturation magnetization of the $Mn_xFe_{3-x}O_4$ powder varied from 38 emu/g to 70.0 emu/g and their minimum coercivity was 111.1 Oe.

• Journal of Powder Materials
• /
• v.26 no.1
• /
• pp.49-57
• /
• 2019

Layered $LiNi_{0.83}Co_{0.11}Mn_{0.06}O_2$ cathode materials single- and dual-doped by the rare-earth elements Ce and Nd are successfully fabricated by using a coprecipitation-assisted solid-phase method. For comparison purposes, non-doping pristine $LiNi_{0.83}Co_{0.11}Mn_{0.06}O_2$ cathode material is also prepared using the same method. The crystal structure, morphology, and electrochemical performances are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) mapping, and electrochemical techniques. The XRD data demonstrates that all prepared samples maintain a typical ${\alpha}-NaFeO_2$-layered structure with the R-3m space group, and that the doped samples with Ce and/or Nd have lower cation mixing than that of pristine samples without doping. The results of SEM and EDS show that doped elements are uniformly distributed in all samples. The electrochemical performances of all doped samples are better than those of pristine samples without doping. In addition, the Ce/Nd dual-doped cathode material shows the best cycling performance and the least capacity loss. At a 10 C-rate, the electrodes of Ce/Nd dual-doped cathode material exhibit good capacity retention of 72.7, 58.5, and 45.2% after 100, 200, and 300 cycles, respectively, compared to those of pristine samples without doping (24.4, 11.1, and 8.0%).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.134-137
• /
• 2004

새로운 리튬 2차전지용 양극활물질인 Li[NiMnCo]O2를 간단히 합성할 수 있는 방법과 Si의 doping에 의해 그 특성을 향상하였다. 원하는 당량비의 Li, Ni, Co, Mn의 nitrate를 고순도의 에탄올에 용해하고 여기에 Si의 원료물질로서 poly(methyl phenyl siloxane)을 원하는 양(전체 전이금속 이온의 $2{\sim}10\;mol%$)만큼 첨가한 후 약 30분 정도 교반하였다. 이 용액을 약 $70{\sim}80^{\circ}C$ 정도의 온도에서 고점도의 진흙 상태가 될 정도로 가열하고 $450{\sim}500^{\circ}C$의 온도에서 약 5시간 정도 열처리 하여 유기물이 없는 상태의 전구체를 제조하였다. 이 전구체를 분말형태로 분쇄하고 $600{\sim}650^{\circ}C$ 정도의 온도에서 3시간, $900{\sim}950^{\circ}C$ 정도의 온도에서 5시간 연속적으로 열처리 하여 최종 활물질을 제조하였다. 이렇게 제조된 활물질은 175mAh/g 정도의 높은 비용량을 나타내었으며 4.5V 충전 조건에도 우수한 수명특성을 나타내었다. Si이 doping되지 않은 활물질에 비해 Si이 doping된 물질은 율특성, 수명특성에서 보다 우수한 특성을 나타내었는데 이것은 층상구조 활물질의 격자상수 증가와 impedance 증가 억제에 기인한 것으로 분석되었다.

• Journal of the Korean Ceramic Society
• /
• v.27 no.1
• /
• pp.7-12
• /
• 1990

The influence of MnO2 on the sintering property and PTCR behavior of(Ba0.8Sr0.2)TiO2 has been investigated. And the densities, grain sizes and electrical resitivities of specimens were measured as a function of doping with Mn ion of varying concentration. The density and grain size of the sintered specimens were almost the same regardless of MnO2 addition up to 0.2mol% MnO2. But in the case of 0.25mol% MnO2 addition, abnormal grain growth was appeared. So the grain size distribution was wide and density decreased greatly. The room-temperature resistivity increased as Mn content increased and the temperature coefficient of resistivity was highest in the case of 0.15mol% MnO2 addition.