• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.295-298
• /
• 2000

Vanadate glasses in the Li$_2$O-P$_2$O$_{5}$-V$_2$O$_{5}$ system containing 10~20mo1% glass former, P$_2$O$_{5}$ were prepared by melting the batch in pt. crucible followed by quenching on the copper plate. We found that Li$_2$O-P$_2$O$_{5}$-V$_2$O$_{5}$ g1ass-ceramics obtained from crystallization of glass showed significantly higher capacity and longer cycle life than Li$_2$O-P$_2$O$_{5}$-V$_2$O$_{5}$ g1ass. In the present paper, we describe electro-chemical properties during crystallization process and find the best crystallization condition of Li$_2$O-P$_2$O$_{5}$-V$_2$O$_{5}$ g1ass as cathod material. Li$_2$O-P$_2$O$_{5}$-V$_2$O$_{5}$ glass-ceramics shows superior rechargeable capacity of 220 mAh/g in the cycling between 2.0 and 3.9V. between 2.0 and 3.9V.

• Journal of the Korean Ceramic Society
• /
• v.38 no.5
• /
• pp.424-430
• /
• 2001

Cut-off 전압 변화에 따른 충방전 특성을 알아보기 위하여 Mn을 다른 전이 금속이 Co와 Ni로 소량 치환시킨 Li(M $n_{1-{\delta}}$ $n_{\delta}$)$_2$ $O_4$(M=Ni, Co, $\delta$=0, 0.05, 0.1, 0.2)를 고상 반응법으로 80$0^{\circ}C$에서 48시간 동안 유지하여 합성하였다. 충방전의 cut-off 전압은 2.5~4.4V, 3.0~4.5V, 3.5~4.5V, 3.5V~4.7V의 네 가지 전압범위고 하였다. 충방전 실험결과, Li(M $n_{1-{\delta}}$ $n_{\delta}$)$_2$ $O_4$의 용량은 각각 Co와 Ni의 $\delta$=0.1에서 최대를 보였다. Co 치환 조성 재료와 순물질 모두에서 최대의 용량을 보인 cut-off 전압대는 3.5~4.5V 이었는데 이때의 Li(M $n_{0.9}$ $Co_{0.1}$)$_2$ $O_4$와 LiM $n_2$ $O_4$의 초기 충전용량과 초기 방전용량은 각각 118, 119mAh/g과 114, 104mAh/g 이었다. 또한 모든 cut-off 전압대에서 Li(M $n_{0.9}$ $Co_{0.1}$)$_2$ $O_4$는 순수한 LiM $n_2$ $O_4$보다 더 높은 용량과 우수한 싸이클 성능을 보였으며 그 결과는 밀착형 전지구성에서도 일치하였다.하였다.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1261-1262
• /
• 2007

At first the $Ba_{0.5}Sr_{0.5}TiO_{3}$-MgO powder with $B_{2}O_{3}-Li_{2}CO_{3}$ were made by the Sol-Gel method. And then the thick films of BST-MgO with $B_{2}O_{3}-Li_{2}CO_{3}$ were fabricated on the $Al_{2}O_{3}$ substrates coated with Pt by the screen printing method. The structural and dielectric properties of the BST-MgO thick film with $B_{2}O_{3}-Li_{2}CO_{3}$ addition were investigated. The structure of the BST-MgO with $B_{2}O_{3}-Li_{2}CO_{3}$ thick films were dense and homogeneous with no pores. The dielectric constant and dielectric loss were increased with decreasing the $B_{2}O_{3}-Li_{2}CO_{3}$ addition ratio.

• Journal of Electrochemical Science and Technology
• /
• v.5 no.3
• /
• pp.87-93
• /
• 2014

The fluorine-substituted $0.3Li_2MnO_3{\cdot}0.7Li[Mn_{0.60}Ni_{0.25}Co_{0.15}]O_{2-x}F_x$ cathode materials were synthesized by using the transition metal precursor, $LiOH{\cdot}H_2O$ and LiF. This was to facilitate the movement of lithium ions by forming more compact SEI layer and to reduce the dissolution of transition metals. The $0.3Li_2MnO_3{\cdot}0.7Li[Mn_{0.60}Ni_{0.25}Co_{0.15}]O_{2-x}F_x$ cathode material was sphere-shaped and each secondary particle had $10{\sim}15{\mu}m$ in size. The fluorine-substituted cathodes initially delivered low discharge capacity, but it gradually increased until 50th charge-discharge cycles. These results indicated that fluorine substitution gave positive effects on the structural stabilization and resistance reduction in materials.

• Journal of the Korean Ceramic Society
• /
• v.13 no.1
• /
• pp.30-34
• /
• 1976

In general the chemical composition of glass ceramics in Li2O-Al2O3-SiO2 system is similar to the composition of $\beta$-spodumene (Li2O-Al2O3-4SiO2). With the object to manufacture the glass ceramics which can be produced in the domestic pot the composition of glass was so settled at 1.0 Li2O.0.9Al2O3.6.0SiO2 in order to reduce the contents of Li2O, to prevent the corrosion of the pot and to decrease the cost of raw materials. 0.2 mole and 0.1 mole of the mixture of TiO2 and ZrO2 as nucleants were added to the basic composition of 1.0 Li2O-0.9Al2O3-6.0SiO2. Each sample was divided into two kinds with a TiO2/ZrO2 ratio of 2 to 1 and the other with a TiO2/ZrO2 ratio fo 1 to 1. Thermal expansion coefficient, the most important property of glass ceramics, was tested. The softening point and the melting point of the samples were observed by the use of a heating microscope. The results obtained were as follows. The manufacturing of glass ceramics seems to be possible in the industrial plant using the domestic pot. 1) The composition of the glass which can be melted in the domestic pot process was near 1.0 Li2O.0.9Al2O3.6.0SiO2. 2) The temperature range of crystal creation and crystal growth was between 850-94$0^{\circ}C$, and 5 hours holding the samples at the temperature range was enough to crystallize them. The major crystal was $\beta$-spdumene and there existed petalite partialy. 3) The thermal expansion coefficient fo the crystallized glass was negative. 4) The deforming point of the crystallized glass was 1435$^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.5
• /
• pp.298-302
• /
• 2016

In this work, $LiMn_2O_4$ and $LiNi_{1/3}Mn_{1/3}Co_{1/3}O_2$ cathode materials are mixed by some specific ratios to enhance the practical capacity, energy density and cycle performance of battery. At present, the most used cathode material in lithium ion batteries for EVs is spinel structure-type $LiMn_2O_4$. $LiMn_2O_4$ has advantages of high average voltage, excellent safety, environmental friendliness, and low cost. However, due to the low rechargeable capacity (120 mAh/g), it can not meet the requirement of high energy density for the EVs, resulting in limiting its development. The battery of $LiMn_2O_4-LiNi_{1/3}Mn_{1/3}Co_{1/3}O_2$ (50:50 wt%) mixed cathode delivers a energy density of 483.5 mWh/g at a current rate of 1.0 C. The accumulated capacity from $1^{st}$ to 150th cycles was 18.1 Ah/g when the battery is cycled at a current rate of 1.0 C in voltage range of 3.2~4.3 V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.474-477
• /
• 2001

The properties of LiMnO$_2$ was studied as a cathode active material for lithium polymer batteries. LiMnO$_2$ cathode active materials were synthesized by the reaction of LiOH . $H_2O$ and Mn$_2$O$_3$at various temperature under argon atmosphere. For lithium polymer battery applications, the LiMnO$_2$cell was characterized electrochemically by charge-discharge experiments and a.c. impedance spectroscopy. And the relationship between the characteristics of powders and electrochemical properties was studied in this research. A maximum discharge capacity of 160-170 mAh/g for ο-LiMnO$_2$ cell was achieved. Used that SP270 as electric active material in LiMnO$_2$, it is excellent than property of electric active material used Acetylene black or KS6 at charge/discharge capacity.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.4
• /
• pp.297-303
• /
• 2008

$LiNiO_2$ cathode powders with fine size have been synthesized by spray pyrolysis from the spray solution with citric acid and ethylene glycol. The as-prepared powders with spherical shape, porous structure and micron size turned into $LiNiO_2$ powders with micron size and regular morphology after post-treatment at $800^{\circ}C$. The initial discharge capacities of the $LiNiO_2$ powders changed from 199 to 171mAh/g when the concentrations of the citric acid and ethylene glycol added to the spray solutions were changed from 0 to 1 M. The maximum initial discharge capacity of the $LiNiO_2$ powders obtained from the spray solution with citric acid and ethylene glycol was 198 mAh/g when the lithium component added to the spray solution was 6 mol% excess of the stoichiometric amount. The discharge capacities of the fine-sized $LiNiO_2$ powders dropped from 198 to 163 mAh/g by the 30 th cycle at a current density of 0.1 C.

• Journal of the Korean Ceramic Society
• /
• v.41 no.8
• /
• pp.567-572
• /
• 2004

The variation of the sintered density and grain size of UO$_2$ as a function of the Li$_2$O amount and sintering atmosphere was observed. Li$_2$O enhanced the grain growth of the UO$_2$ pellet in H$_2$, but rather hindered it in $CO_2$ atmosphere. Grain size of the UO$_2$ and UO$_2$-0.1 wt%Li$_2$O pellets was, respectively, 8 $\mu$m and 100 $\mu$m at 168$0^{\circ}C$ in the H$_2$ atmosphere, and that of each pellet was, respectively, 24 $\mu$m and 17 $\mu$m at the same temperature in the $CO_2$ atmosphere. As-received Li$_2$O powder, which had been composed of Li$_2$O and LiOH, was converted to the Li$_2$CO$_3$ phase after heating to 80$0^{\circ}C$ in $CO_2$. On the other hand, the Li$_2$O and LiOH phases remained unchanged in H$_2$ atmosphere. In the H$_2$, the as-received Li$_2$O powder began to evaporate at about 105$0^{\circ}C$ and then about 20 wt% residue was left at 150$0^{\circ}C$. But, most of the Li elements evaporated at 150$0^{\circ}C$ in the $CO_2$ atmosphere.

• Korean Chemical Engineering Research
• /
• v.52 no.1
• /
• pp.52-57
• /
• 2014

The MCMB-$Li_4Ti_5O_{12}$ with core-shell structure was prepared by sol-gel process to improve low cycle capability of MCMB in this study. The electrochemical characteristics were investigated for hybrid capacitor using MCMB-$Li_4Ti_5O_{12}$ as the negative electrode and $LiMn_2O_4$, Active carbon fiber as the positive electrode. The electrochemical behaviors of hybrid capacitor using organic electrolytes ($LiPF_6$, EC/DMC/EMC) were characterized by charge/discharge, cyclic voltammetry, cycle and impedance tests. The hybrid capacitor using MCMB-$Li_4Ti_5O_{12}/LiMn_2O_4$ electrodes had better capacitance than MCMB hybrid systems and was able to deliver a specific energy with 67 Wh/kg at a specific power of 781 W/kg.