• Bulletin of the Korean Chemical Society
• /
• 제34권12호
• /
• pp.3609-3614
• /
• 2013

Orthorhombic and hexagonal lanthanum(III) hydroxycarbonate ($LaCO_3OH$) and $Ln^{3+}$-doped $LaCO_3OH$ ($LaCO_3OH:Ln^{3+}$, where Ln = Ce, Eu, Tb, and Ho) powders were prepared by a hydrothermal reaction under ambient pressure and characterized by thermogravimetry, powder X-ray diffraction, infrared and luminescence spectroscopy, and field-emission scanning electron microscopy. The polymorph of $LaCO_3OH$ depended on the reaction temperature, inorganic salt additive, species of $Ln^{3+}$ dopant, and solvent. The calcination of orthorhombic $LaCO_3OH:Ln^{3+}$ (2 mol %) powers at $600^{\circ}C$ yielded a mixture of hexagonal and monoclinic $La_2O_2CO_3:Ln^{3+}$ powders. The relative quantity of the latter increased with decreasing ionic radius of the $Ln^{3+}$ dopant ion and increasing doping concentrations. On the other hand, the calcination of hexagonal $LaCO_3OH:Ln^{3+}$ (2 mol %) powders at $600^{\circ}C$ resulted in a pure hexagonal $La_2O_2CO_3:Ln^{3+}$ powder, regardless of the species of $Ln^{3+}$ ions (Ln = Ce, Eu, and Tb). The luminescence spectra of $LaCO_3OH:Ln^{3+}$ and $La_2O_2CO_3:Ln^{3+}$ were measured to examine the effect of their polymorph on the spectra.

• 한국세라믹학회지
• /
• 제36권3호
• /
• pp.301-306
• /
• 1999

CO2 감지용 La2O3-SnO2 계 후막형 소자를 제조하여 CO2가스에 대한 기초 감지 특성을 조사하였고, 감지 분말의 입자크기와 제조방법에 따른 감도 변화를 고찰하였다. 후막 소자는 40$0^{\circ}C$의 작동온도와 4wt.%의 La2O3가 첨가되 srjt에서 가장 좋은 감도를 나타내었고, 낮은 습도영역에서 우수한 감지 특성을 보였다. 분말 혼합법에 의해 제조된 소자에 있어서 La2O3와SnO2 분말의 입자가 미세할수록 우수한 감도를 나타내었고, La2O3의 입도가 SnO2의 입도 보다 감도에 더 큰 영향을 주었다. SnO2 후막 표면에 La 용액을 코팅하여 제조된 센서는 가장 우수한 CO2 감도특성을 보였다.

• 한국표면공학회지
• /
• 제29권6호
• /
• pp.839-846
• /
• 1996

Epitaxial (La, Sr)$CoO_3/Pb(Zr,\;Ti)O_3/(La,\;Sr)CoO_3$by pulsed laser deposition for ferroelectric field effect transistor. Epitaxial $LaCoO_3/Pb(Zr,\;Ti)O_3/(La,\;Sr)CoO_3$ heterostructures exhibited 70$\mu C/cm^2$ and 17 $\mu C/cm^2$at a positively and negatively poled states, respectively. On the other hand, epitaxial (La, Sr)$CoO_3/Pb(Zr,\;Ti)O_3/LaCoO_3$heterostructures show the remnant polarization states opposite to the $LaCoO_3/Pb(Zr,\;Ti)O_3/(La,\;Sr)CoO_3$ heterostructures. This indicates that the interface between (La, Sr)$CoO_3$ (LSCO) and $Pb(Zr, Ti)O_3(PZT)$ layers affects the asymmetric polarization remanence through electrochemical nature. The resistivity of $LaCoO_3$ (LCO) layer was found to be dependent on an ambient oxygen, primarily the ambient oxygen pressure during deposition. The resistivity of the LCO layer varied in the range of 0.1-100 $\Omega$cm. It is suggested that, with an appropriate resistivity of the LCO layer, the LCO/PZT/LSCO heterostructure can be used as the ferroelectric field effect transistor.

• 한국세라믹학회지
• /
• 제37권6호
• /
• pp.612-616
• /
• 2000

The effect of Co dopant on the (La, Sr)MnO3 cathode was investigated. La2Zr2O7 and SrZrO3 were formed as the reaction products between YSZ and LSMC. The reactivity of LSMC with YSZ increased with increasing Co content. However, the cathodic polarization resistance decreased with increasing Co doping. Therefore, doping Co at Mn site in the (La, Sr)MnO3 cathode was effective on controlling the polarization resistance of the cathode. The polarization property of LSMC-YSZ composite(60 wt%: 40 wt%) cathode was better than that of LSMC single cathode.

• 한국수소및신에너지학회논문집
• /
• 제18권1호
• /
• pp.32-39
• /
• 2007

CO oxidation and selective CO oxidation of $La_xCe_{1-x}Co_yCu_{1-y}O_{3-{\alpha}}$ perovskite(x=1, 0.9, 0.7. 0.5; y=1, 0.9, 0.7, 0.5) were investigated. For CO oxidation, catalytic activities were studied according to different preparation conditions such as pH and calcination temperature. The influence of the change of the $O_2$ concentration for selective CO oxidation was studied, too. The substitution of Ce for La improved the catalytic activity for CO oxidation and selective CO oxidation and best activity was observed for $La_{0.7}Ce_{0.3}CoO_3$ prepared at pH 11 and calcined at $600^{\circ}C$. The temperature of 90% CO conversion for CO oxidation using $La_{0.7}Ce_{0.3}CoO_3$ was $230^{\circ}C$. In contrast to the enhancement effect by Ce substitution, the partial substitution of Cu for Co in $LaCo_yCu_{1-y}O_{3-{\alpha}}$ decreased catalytic activities for CO oxidation reaction compared to that using $LaCoO_3$. For selective CO oxidation, the best CO conversion was 66% at $230^{\circ}C$ for $La_{0.7}Ce_{0.3}CoO_3$. The CO conversion of $La_{0.7}Ce_{0.3}CoO_3$ was greatly increased from 66% to 91% as increasing $O_2$ concentration from 1% to 2%.

• 한국세라믹학회지
• /
• 제36권5호
• /
• pp.564-569
• /
• 1999

• 한국결정성장학회지
• /
• 제28권5호
• /
• pp.211-216
• /
• 2018

폐니켈수소전지에 함유된 희토류들의 회수는 자원 재활용을 위한 중요한 이슈 중의 하나이다. 본 논문에서는 폐니켈수소전지에 함유된 주요 희토류 성분 중의 하나인 란탄의 회수와 산화물로 전환되는 메커니즘 연구를 위하여, 재활용 공정에서 확보되는 희토류 침전물($NaRE(SO_4)_2{\cdot}H_2O$, RE = La, Nd, Ce)과 같은 단일 조성의 $NaLa(SO_4)_2{\cdot}H_2O$ 분말을 합성하였다. 합성된 분말은 $70^{\circ}C$에서 진행된 탄산나트륨과의 이온치환반응을 통해 판상형의 $La_2(CO_3)_3{\cdot}xH_2O$ 결정상을 나타냈으며, 비교를 위해 상온에서 진행된 치환 반응을 진행하였다. 이후 산화란탄 합성을 위해 TG 분석 결과를 바탕으로, $La_2(CO_3)_3{\cdot}xH_2O$ 분말을 $300^{\circ}C$, $500^{\circ}C$ 및 $1000^{\circ}C$에서 후열처리를 진행하였으며, 이에 따른 결정구조의 변화를 분석하였다. FESEM 결과 본 연구에서 합성된 각각의 분말들은 각기둥($NaLa(SO_4)_2{\cdot}H_2O$), 판상($La_2(CO_3)_3{\cdot}xH_2O$) 및 특정 형상 없이 불규칙적으로 응집된 형태($La_2O_3$)를 나타내었다.

• 대한화학회지
• /
• 제38권4호
• /
• pp.276-282
• /
• 1994

Citrate sol-gel법을 이용하여 perovskite형 복합산화물 LaBO$_3$(B = Mn, Fe, Co)을 공기 중 $850^{\circ}C$에서 24시간 동안 소성하여 제조하였다. X-선 회절분석(XRD)과 TPR결과에 의하면 이들 산화물의 결정구조와 산소화학양론은 LaMnO$_{3.16}$(a = 5.507, c = 13.329 $\AA$, hexagonal), LaFeO$_{3.17}$(a = 5.554, b = 5.555, c = 7.863 $\AA$, orthorhomibic), LaCoO$_{3.0}$(a = 5.436, c = 13.095 $\AA$, hexagonal)으로 수소 분위기(300torr)에서의 TPR결과에 의하면 이들 산화물은 2단계 환원반응으로 반응이 진행되며, 열적안정성은 LaMnO$_3$ > LaFeO$_3$ > LaCoO$_3$순으로 나타났고, 반응속도론적 결과 역시 LaCoO$_3$의 활성화에너지 값이 가장 낮음을 보였다.

• 분석과학
• /
• 제15권3호
• /
• pp.256-262
• /
• 2002

평균입자크기가 200 ${\mu}m$인 코디어라이트 분말을 사용하여 다공성 필터를 제조한 후, 진공함침법으로 $V_2O_5$, CuO, $LaCoO_3$ 촉매를 담지시킨 후 NO와 $SO_2$ 기체를 촉매 담지 세라믹필터에 동시 통과시키면서 NOx/SOx의 동시제거효율을 측정하였다. 제조된 다공성 필터의 기공률은 61.6%였고, 압축강도는 12.3 MPa이었으며, 면속도 5 cm/sec에서의 차압은 147 Pa이었다. NO와 $SO_2$의 동시제거효율을 분석해 본 결과, 페로브스카이트계 $LaCoO_3$ 촉매의 동시제거효율이 가장 우수함을 확인하였으며, $LaCoO_3$ 촉매의 NO에 대한 제거효율은 90% 이상, $SO_2$에 대해서는 80% 이상이었다.

• 한국세라믹학회지
• /
• 제41권8호
• /
• pp.593-598
• /
• 2004

1 $\mu$m이하의 전고상 리튬 박막전지의 구현을 위해 펄스 레이저 증착법을 이용하여 Pt/TiO$_2$/SiO$_2$/Si 기판위에 LiCoO$_2$정극을 증착온도와 Li/Co 간의 몰 비율을 변화시켜가며 성장시켰다. 특히, Li/Co=1.2의 조성을 갖는 LiCoO$_2$를 50$0^{\circ}C$의 증착온도에서 성장시킬 경우 53 $\mu$Ah/$cm^2$-$\mu$m의 높은 초기 용량값을 가지며 100 싸이클 후에도 67.6%의 용량값을 유지하였다. LiCoO$_2$/Pt/TiO$_2$/SiO$_2$/Si위에 고체 전해질인 (Li, La)TiO$_3$를 비정질상으로 하여 PLD방법으로 낮은 온도대역에서 증착온도를 다양하게 하여 증착하였다. 10$0^{\circ}C$의 증착온도에서 LiCoO$_2$Pt/TiO$_2$/SiO$_2$/Si위에 성장시킨 (Li, La)TiO를 가지고 LiClO$_4$ in PC 안에서 Li anode와 충$.$방전 측정 결과 약 51$\mu$Ah/$cm^2$-$\mu$m의 초기 용량값을 나타내었으며 100싸이클 후에도 90%의 훌륭한 방전용량의 보존력을 나타내었다. 비정질상의 (Li, La)TiO$_3$ 고체 전해질은 전고상 박막전지로의 구현이 가능하다.