Reactivity and Preparation of Perovskite-Type Mixed Oxides LaBO3(B = Mn, Fe, Co) by Citrate Sol-Gel Method

Citrate Sol-Gel법에 의한 Perovskite형 복합 산화물 LaBO3(B = Mn, Fe, Co)의 생성 및 환원 반응성

  • 황호순 (성균관대학교 이과대학 화학과) ;
  • 박일현 (성균관대학교 이과대학 화학과)
  • Published : 19940400
Download PDF
⟨ Previous Next ⟩

Abstract

Perovskite-type mixed oxides LaBO$_3$(B = Mn, Fe, Co) were prepared by citrate sol-gel method in $air(850^{\circ}C$, 24h). The oxygen stoichiometries and structures of these oxides were determined by XRD and TPR results as followings; LaMnO$_{3.16}$(a = 5.507, c = 13.329 $\AA$, hexagonal), LaFeO$_{3.17}$(a = 5.554, b = 5.555, c = 7.863 $\AA$, orthorhomibic), LaCoO$_{3.0}$(a = 5.436, c = 13.095 $\AA$, hexagonal). The temperature programmed reduction(TPR) experiments in static 300 torr H$_2$ atmosphere shows that the reduction reaction of LaBO$_3$(B = Mn, Fe, Co) proceeds into two stages, and thermal stabilities of these oxides decreased in the order of LaMnO$_3$ > LaFeO$_3$ > LaCoO$_3$. According to the kinetic analysis the lowest activation energy was obtained for LaCoO$_3$.

Citrate sol-gel법을 이용하여 perovskite형 복합산화물 LaBO$_3$(B = Mn, Fe, Co)을 공기 중 $850^{\circ}C$에서 24시간 동안 소성하여 제조하였다. X-선 회절분석(XRD)과 TPR결과에 의하면 이들 산화물의 결정구조와 산소화학양론은 LaMnO$_{3.16}$(a = 5.507, c = 13.329 $\AA$, hexagonal), LaFeO$_{3.17}$(a = 5.554, b = 5.555, c = 7.863 $\AA$, orthorhomibic), LaCoO$_{3.0}$(a = 5.436, c = 13.095 $\AA$, hexagonal)으로 수소 분위기(300torr)에서의 TPR결과에 의하면 이들 산화물은 2단계 환원반응으로 반응이 진행되며, 열적안정성은 LaMnO$_3$ > LaFeO$_3$ > LaCoO$_3$순으로 나타났고, 반응속도론적 결과 역시 LaCoO$_3$의 활성화에너지 값이 가장 낮음을 보였다.

Keywords

References

  1. Science v.195 Voorhoeve, R. J. H.;Johnson, D. W.
  2. J. Chem. Soc., Faraday Trans. I v.81 Tascon, J. M. D.;Pierro, J. L. G.;Tejuca, L. G.
  3. J. Catal. v.89 Pirro, J. L. G.;Tason, J. M. D.;Tejuca, L. G.
  4. J. Am. Chem. Soc. v.113 Klabunde, B. J.;Scherwood, K. J.
  5. J. Appl. Surf. Sci. v.31 Tejuca, L. G.;Fierro, J. L. G.
  6. J. Appl. Phys. v.44 no.12 Sis, L. B.;Wirtz, G. P.
  7. Phys. Rev. B. v.22 no.12 Lan, D. I.;Veal, B. W.
  8. Surf. Sci. v.130 Kojima, I.;Adachi, H.;Yasumori, I.
  9. Catal. Rev. Sci. Eng. v.24 no.2 Hurst, N. W.;Gentry, S. J.;Jones, A.;Mcnicol, B. D.
  10. Chme. Lett. Shimizu, T.
  11. Ann, N. Y. Acad. Sci. v.3 Voorhoeve, R. J. H.;Remeica, J. P.;Trimble, L. E.
  12. J. Catal v.36 Yao, Y. F. Y.
  13. Mat. Res. Bull. v.1 Gallagher, P. K.;Jonson, D. W.;Schrey, F.
  14. Power Technol. v.7 Courty, Ph.;Ajot, H.;Marcilli, Ch.;Delmon, B.
  15. J. Solid State Chme. v.10 Tofield, B. C.;Scott, E. R.
  16. J. Am. Ceram. Soc. v.60 Voge, E. M.;Jonson, D. W.;Gallagher, P. K.
  17. Acta. Chim. Acad. Sci. Hung. v.104 Wachowski, L.;Zielinski, S.;Burewicz, A.
  18. Acta. Chim. Acad. Sci. Hung. v.106 Wachowski, L.;Zielinski, S.;Burewicz, A.