• 한국세라믹학회지
• /
• 제32권12호
• /
• pp.1383-1391
• /
• 1995

Hexagonal $\delta$-FeOOH was coated with Ba-Sol, which was produced by hydrolizing Ba(OC2H5)2, Ba-Sol coated $\delta$-FeOOH spread on a stainless plate, dried at 8$0^{\circ}C$ and then heat-treated. In this way, Ba-ferrite fine particles were produced. although there was a difference in a degree of hydrolysis of Ba(OC2H5)2, crystalline phase of Ba-ferrite appeared around 617$^{\circ}C$, and Ba-ferrite single phase was obtained after heat treatment at 80$0^{\circ}C$ for 2 hr. When Ba-ferrite was made from Ba-Sol coated $\delta$-FeOOH, $\delta$-FeOOH was thermally decomposed to $\alpha$-Fe2O3 at $700^{\circ}C$, producing a porous structure which was observed by TEM photographs. But the porous structure was not observed at 80$0^{\circ}C$. Ba-ferrite, heat-treated at 80$0^{\circ}C$ for 2 hr, had mean particle size of 1000$\AA$, lattice parameter of a0=5.889243 $\AA$ and c0=23.214502 $\AA$, a saturation magnetization ($\sigma$8) of 45.3 emu/g and a coercive force (Hc) of 5200Oe.

• E2M - 전기 전자와 첨단 소재
• /
• 제10권8호
• /
• pp.819-829
• /
• 1997

The microwave dielectric materials of the BaO-Nd$_2$O$_3$-TiO$_2$and BaO-(Sm, Nd)$_2$O$_3$-TiO$_2$system were synthesized by conventional ceramic processing and sintered 1220 to 140$0^{\circ}C$ for 2 hours respectively. Their crystallization and dielectric properties were examined. In the BaO-Nd$_2$O$_3$-TiO$_2$ and BaO-(Sm, Nd)$_2$O$_3$-TiO$_2$system. Nd$_2$Ti$_2$O$_{7}$ and (Sm, Nd)$_2$Ti$_2$O$_{7}$ were observed as a second phase respectively. The maximum relative dielectric constant were 79,99 for the BaO-Nd$_2$O$_3$-TiO$_2$system and 105.07 for the BaO-(Sm,Nd)$_2$O$_3$-TiO$_2$system and their Q-value were over 2000 at 3GHz.GHz.

• Journal of the Optical Society of Korea
• /
• 제18권1호
• /
• pp.45-49
• /
• 2014

Well-crystallized $BaSi_2O_5:Eu^{2+}$ phosphor films were synthesized by heat treatment of spin-coated BaO:Eu on $SiO_2$ glass. We investigated luminescence-structure properties of these phosphor films as a function of heat-treatment temperature. From x-ray diffraction patterns, our $BaSi_2O_5:Eu^{2+}$ phosphor films revealed that (111)- and (204)-crystal planes of $BaSi_2O_5$ crystal were dominantly increased with an increase of heat-treatment temperature. Photoluminescence intensities of $BaSi_2O_5:Eu^{2+}$ phosphor films were increased with amount of these crystal planes. It can be explained that $Eu^{2+}$ ions were stably occupied at specific crystal orientation of $BaSi_2O_5$ crystal, enhancing the luminescent intensities of $BaSi_2O_5:Eu^{2+}$ phosphor films. In addition, our $BaSi_2O_5:Eu^{2+}$ phosphor films had transmittance of 70% at 510 nm,.due to the dense morphology and specific crystallinity of $BaSi_2O_5:Eu^{2+}$ phosphor films.

• Korean Chemical Engineering Research
• /
• 제45권5호
• /
• pp.448-454
• /
• 2007

미세 $BaTiO_3$ 분말의 합성을 위해 함수 티타니아와 수산화바륨을 원료로 수열합성 실험을 수행하여, 반응시간, 온도, 농도 변화에 따른 전화율, 결정구조 및 생성 분말의 물성을 조사하였다. 전화율에 미치는 영향은 시간 < 온도 < 농도 순이었으며, 2.0 M의 원료를 $180^{\circ}C$에서 2 h 수열합성 시킬 때 최대 전화율을 99.5%를 얻을 수 있었다. 낮은 농도(0.25 M)에서는 고온에서도 미반응 $BaCO_3$와 미반응 $TiO_2$ 생성을 피할 수 없었으며, 이 미반응 물질들은 고온에서 $BaTi_2O_5$를 생성시켜 불순물로 존재하였다. 농도를 높일수록 합성 $BaTiO_3$ 분말의 크기는 작아졌으며, 분말의 Ba/Ti 비도 1에 접근하였다. 2.0M 이상의 농도에서는 $180^{\circ}C$, 2 h 반응에서 Ba/Ti 비는 $1{\pm}0.005$ 이였다.

• 공학논문집
• /
• 제2권1호
• /
• pp.139-145
• /
• 1997

촉매연소용 촉매담체인 $\gamma$-$Al_2O_3$의 열안정화에 미치는 Ba의 첨가 효과에 대하여 연구하였다. Ba의 첨가는 $Ba(No_3)_3$.$6H_2O$를 $\gamma$-$Al_2O_3$ 분말에 wet impergnation시키는 방법으로 행하였다. Ba는 $\gamma$-$Al_2O_3$의 소결을 억제함으로써 $\gamma$-$Al_2O_3$의 열안정화에 효과적인 첨가제임을 확인하였으며 최적의 첨가량은 전체 열처리 조건에서 5 mol%임을 알 수 있었다. 이러한 Ba첨가에 의한 열안정화 효과는 이온반경이 큰 $Ba^{2+}$이온이 $\Al^{3+}$이온의 자리에 치환하여 $\Al^{3+}$이온의 표면 확산을 억제하는 효과에서 기인하는 것으로 사료된다.

• 한국세라믹학회지
• /
• 제20권4호
• /
• pp.340-346
• /
• 1983

The effect of aging coprecipitate obtained by the reaction of mixed solution 1.1 mol FeCl-0.1 mol $BaCl_2$ and 4.0 mol. NaOH-1.0 mol $K _2 CO_3$ on the synthesis process of Baferrite $(BaFe_{12}O_{19})$ was investigated by means of DTA, TGA, XRD and electron microscope. The no-aged coprecipitate seems to be the aggregate of amorphosus $Fe_3$ .$nH_2O$ and (1-X) $BaCO_3$.$xBa(OH)_2$, but the 30 days-aged to be composed of crystalline $Fe_2O_3H_2O$ and $BaCO_3$. The decomposition temperature of $BaCO_3$ in the coprecipitate increases from 400-$700^{\circ}C$ to 700-90$0^{\circ}C$ with increment of aging-time. In the no-aged coprecipitate Ba-ferrite is synthesized through the surface reaction of amorphous Fe_2O_3$ and skeleton crystal BaO at 800-90$0^{\circ}C$ with more compact crystalization. During calcination of the 30 days-aged coprecibitate the intermediate phase BaFe_2O_4$ is formed at 600-$700^{\circ}C$ and completely transformed to Ba-ferrite at 800-90$0^{\circ}C$.

• 한국재료학회지
• /
• 제5권4호
• /
• pp.433-444
• /
• 1995

BaCe$O_{3}$를 첨가하여 용융공정으로 제조한 단결정형 Y$Ba_{2}$$Cu_{3}$$O_{x}$(1-2-3) 초전도체의 온도에 대한 자화특성을 연구하였다. 고상반응법과 용융공정으로 0에서 30wt% BaCe$O_{3}$를 1-2-3 결정내에 미세 분산시켰다. 초전도체의 자화특성은 VSM(vibrating sample magnetometer)을 사용하여 77K, 60K, 40K와 20K, 2 Tesla 자장범위에서 측정하였다. BaCe$O_{3}$를 첨가하지 않은 겨우나 5wt% BaCe$O_{3}$를 첨가한 1-2-3 결정의 경우, 77K, 외부자장이 증가시 자화율 차이가 증가하는 비정상 자화특성이 관찰된다. 측정온도가 60K에서는 제2차 최대점이 나타나는 자장값이 고자장쪽으로 이동한다. 20K와 40K의 저온에서는 비정상자화특성이 2 T의 자장범위까지 관찰되지 않았다. 15wt%와 20wt% BaCe$O_{3}$첨가한 시편에서는 자장이 증가하면 자화율차이가 단순히 감소한다. Y-Ba-Cu-O의 flux pinning 기구를 BaCe$O_{3}$첨가에 의한 미세조직변화로 설명하였다.

• 농업과학연구
• /
• 제5권1호
• /
• pp.1-5
• /
• 1978

딸기의 meristem culture에 있어서의 기관의 분화(分化)는 배지 조성상의 생장조절물질의 종류와 농도에 따라 각 기관의 형성을 달리하였다. Cytokinin인 BA를 첨가하였을 경우 농도가 높아감에 따라 분화된 shoot의 신장(伸長)보다 새로운 plantlet의 연속적인 분화(分化)가 나타났으며, IAA 1.0ppm은 root의 분화(分化)를 촉진하였으나, BA 1.0ppm과 혼합 첨가 할 경우 rooting이 저조하였다. 2.4-D의 첨가는 기관의 callus화(化)를 유도하였고 특히 BA와의 농도 비율에 따라 각기 다른 양상을 나타내어 BA/2.4-D의 비율이 높을 경우 shoot의 분화(分化)가 나타났고, 이 비율이 낮아질 경우 callus의 분화(分化)가 나타났다. 결국 BA, IAA, 2.4-D의 세가지 물질은 기관분화에 대하여 특색을 갖고 있어 BA는 shoot의 분화(分化), IAA는 root의 분화(分化), 그리고 2.4-D는 callus의 분화(分化)를 유도하고 있음을 알 수 있다.

• 한국재료학회지
• /
• 제31권2호
• /
• pp.61-67
• /
• 2021

Fabrication of a ferromagnetic composite powder for the magnesium and BaFe12O19 system by mechanical alloying (MA) is investigated at room temperature. Mixtures of Mg and BaFe12O19 powders with a weight ratio of Mg:BaFe12O19 = 4:1, 3:2, 2:3 and 1:4 are used. Optimal MA conditions to obtain a ferromagnetic composite with fine microstructure are investigated by X-ray diffraction, differential scanning calorimetry (DSC) and vibrating sample magnetometer (VSM) measurement. It is found that Mg-BaFe12O19 composite powders in which BaFe12O19 is dispersed in Mg matrix are successfully produced by MA of BaFe12O19 with Mg for 80 min. for all compositions. Magnetization of Mg-BaFe12O19 composite powders gradually increases with increasing the amounts of BaFe12O19, whereas coercive force of MA powders gradually decreases due to the refinement of BaFe12O19 powders with MA time for all compositions. However, it can be seen that the coercivity of Mg-BaFe12O19 MA composite powders with a weight ratio of Mg:BaFe12O19=4:1 and 3:2 for MA 80 min. are still high, with values of 1260 Oe and 1320 Oe compared to that of Mg:BaFe12O19=1:4. This clearly suggests that the refinement of BaFe12O19 powders during MA process for Mg:BaFe12O19=4:1 and 3:2 tends to be suppressed due to ductile Mg powders.

• 대한전기학회논문지
• /
• 제44권8호
• /
• pp.1068-1074
• /
• 1995

Effect of (Zn$_{1}$3/Nb$_{2}$3/) $O_{2}$ addition on the phase changes and microwave dielectric properties of BaTi $O_{3}$-3Ti $O_{2}$ ceramics were investigated. Addition of (Zn$_{1}$3/Nb$_{2}$3/) $O_{2}$ to BaTi $O_{3}$-3Ti $O_{2}$ resulted in the formation of Ba $Ti_{4}$$O_{9}$, $Ba_{2}$ $Ti_{9}$ $O_{20}$, Ba(Zn$_{1}$3/Nb$_{2}$3/) $O_{3}$, and Ti $O_{2}$ phases. Ba $Ti_{4}$$O_{9}$ phase was gradually transformed to $Ba_{2}$ $Ti_{9}$ $O_{20}$. This was identified by XRD and microstructure. As the Ba $Ti_{4}$$O_{9}$ phase transformed to $Ba_{2}$ $Ti_{9}$ $O_{20}$ phase, the dielectric constant increased to 37.5. Q*f$_{o}$ value was 40000 at x=0.04, and the temperature coefficient of resonant frequency was +10ppm/.deg. C.C.. C.C.