• 한국광물학회지
• /
• 제15권1호
• /
• pp.78-84
• /
• 2002

New pyrochlore-type phases($A_2$$B_2$$O_{7}$) were synthesized in the systems: CaO-C$eO_2$-T$iO_2$, CaO-$UO_2$(T$hO_2$)-Z$rO_2$, CaO-$UO_2$(T$hO_2$)-$Gd_2$$O_3$-T$iO_2$-Z$rO_2$, 및 CaO-T$hO_2$-S$nO_2$. The starting materials were pressed with the pressure of 200~400 MPa and sintered at 1500~ 155$0^{\circ}C$ for 4~8 hours in air and at 1300~ 135$0^{\circ}C$ for 5 ~50 hours under oxygen atmosphere. The products were characterized using XRD, SEM/EDS and TEM. In the bulk compositions of CaCe$Ti_2$$O_{7}$, CaTh$Zr_2$$O_{7}$,($Ca_{0.5}$ Gd$Th_{0.5}$)(ZrTi)$O_{7}$) ($Ca_{0.5}$Gd$Th_{0.5}$)(ZrTi)$O_{7}$, ($Ca_{0.5}$G$dU_{0.5}$)(ZrTi)$O_{7}$ and CaTh$Sn_2$$O_{7}$ , pyrochlore was the major phase, together with other oxide phase $of_2$$O_{7}$ fluorite structure. In the samples with target compositions CaU$Zr_2$$O_2$및 $Ca_{0.5}$ G$dU_{0.5}$)$Zr_2$T$iO_{7}$ pyrochlore was not identified, but a fluorite-structured phase was detected. The formation factor as the stable phase depended on crystal chemical characteristics of the actinide and lanthanide elements of the system concerned.

• 한국표면공학회지
• /
• 제34권5호
• /
• pp.499-502
• /
• 2001

Functionally gradient NiCrAlY/$ZrO_2$-$Y_2$$O_3$ and NiCrAlY/$ZrO_2$- $CeO_2$-$Y_2$$O_3$ coatings were prepared by APS. The as-sprayed microstructure consisted of metal-rich and ceramic-rich regions, between which $Al_2$$O_3$-rich layers existed owing to the oxidation during APS. During oxidation between 900 and $1100^{\circ}C$ in air, the pre-existing $Al_2$$O_3$-rich scales grew, due mainly to the preferential reaction of Al with inwardly transporting oxygen along the heterogeneous phase boundaries. As the amount of ceramics in the coating increased, the oxidation resistance increased.

• 대한화학회지
• /
• 제28권5호
• /
• pp.293-301
• /
• 1984

단일 희석법을 이용한 X-선형광분광법으로 주석, 슬랙중 $Ta_2O_5$와 $Nb_2O_5$, $ZrO_2$등을 정량분석하였다. 이 방법은 표준 검정 곡선을 직선으로 되게끔 수학적으로 보정하는 것이다. 시료의 조성과 비슷한 한개의 합성표준시료와 분석시료를 무수물의 $Li_2B_4O_7$으로 묽혀서 각각 시료가 1%, 2%, 3%되게 한다. 묽힌 시료들을 $1150^{\circ}C$에서 30분간 용융하여 유리화된 구슬을 만든 다음, 곱게 갈아서, 다시 유압기로 압축하여 분석시편을 만든다. 이 시편을 사용하여 X-선 세기를 측정하고, 원소의 특성 X-선 세기에 관한 J. Scherman의 식으로부터 유도한 식에 대입하여 분석 결과를 계산했다. 이들 분석결과들을 표준검정곡선법으로 얻은 기준값과 잘 일치하며, 결과에 대한 재현성도 좋음을 보여 주었다.

• 대한화학회지
• /
• 제28권5호
• /
• pp.302-308
• /
• 1984

이중희석법을 이용한 X-선 분광법으로 주석-슬랙 중 $Ta_2O_54, $Nb_2O_5$ 및 $ZrO_2$등을 정량하였다. 주석시료와 이것과 조성이 비슷한 한개의 합성표준시료를 무수 $Li_2B_4O_7$으로 희석하여 희석된 시료중 이들의 함량이 1.00%, 2.00%, 3.00% 되게 잘 혼합하였다. 혼합시료를 $1,150^{\circ}C$에서 30분간 용융하여 유리상태로 만들었다. 다시 잘 분쇄하고, 유압기를 이용하여 Pellet로 만들어 분석 시편으로 사용했다. 형광 X-선 세기를 측정하여 희석식에 대입하여 각 시료에서 분석성분의 함량을 계산하였다. 이중희석법으로 얻은 분석결과들은 대표적인 분석법인 표준검정 곡선법에 의한 값들과 혀용오차범위내에서 잘 일치하고 있다. 아울러 단일희석법에 의한 결과와도 잘 일치하고 있으며 각 분석결과에 대한 재현성도 좋음을 보여 주었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.259-259
• /
• 2007

The low temperature sintering of dolomite type borates, $CaZr(BO_3)_2$[CZB] ceramics and their microwave dielectric properties were investigated The sintering temperature of CZB ceramics could be reduced from $1150^{\circ}C$ to $925^{\circ}C$ by the addition of sintering additive. $CaZrO_3$, $ZrO_2$ and $CaB_2O_4$ second phases were found in the CZB ceramics. The syntheses, sintering properties, microstructures, and dielectricnproperties of dolomite-type borates were examined by XRD, thermal analysis, electron microscopy, network analyzer, and the results are discussed intensively. The compatibility with silver electrode was also explored.

• 한국세라믹학회지
• /
• 제48권5호
• /
• pp.471-478
• /
• 2011

Investigations of crystal structure and phase transition of $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics doped with A-site substitution impurity (La, Nd) or B-site substitution impurity (Sb, Nb) at 2 mol% concentration were carried out. X-ray diffraction patterns of impurities doped $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics have been measured at pressures up to ~5 GPa with diamond anvil cell and synchrotron radiation. The patterns were obtained at room temperature using methanol-ethanol mixture as pressure-transmitting media. In order to refine the crystal structure, Rietveld analysis has been performed. The structures of impurities doped $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics are tetragonal in space group P4mm at ambient pressure and are transformed into a cubic phase in space group Pm$\bar{3}$m as the pressure increases. In this study, when A-site substitution donor $La^{3+}$ or $Nd^{3+}$ ion was added to $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics, the phase transition phenomena showed up at the pressure of 2.5~4.6 GPa, but when B-site substitution donor $Nb^{5+}$ or $Sb^{5+}$ ion was added to it, the phase transition appeared at relatively lower pressure of 1.7~2.6 GPa.

• Bulletin of the Korean Chemical Society
• /
• 제22권11호
• /
• pp.1231-1235
• /
• 2001

Pseudotetragonal ZrO0.75S whose space group is P212121 was synthesized and the cell dimensions were a=5.110(2) $\AA$, b=5.110(7) $\AA$, and c=5.198(8) $\AA.$ The space group P212121 seems to be resulted from lowering the symmetry of cubic ZrOS structure with P213 space group by lattice distortion due to the oxygen defects. In the distorted structure, bond shortening between metal-nonmetal by reduction of cell volume and alternation of Zr-Zr distance were observed. Dielectric constant and loss data of the bulk material in temperature range -170 to 20 $^{\circ}C$ and frequency range 50 Hz to 1 MHz showed that there was dielectric transition at around -70 $^{\circ}C$ originated from the relaxation of Zr-S segment. Comparing with ZrO2 exhibited the dielectirc constants, 9.0 at room temperature, ZrO0.75S showed high dielectric constant, k = 200.2 at 100 kHz. The activation energy of relaxation time due to dielectric relaxation of Zr-S was 0.47 eV (11.3 kcal/mole). According to the impedance spectra, ZrO0.75S showed more parallel circuit character between the resistance and capacitance components at the temperature (-70 $^{\circ}C)$ that the Zr-S dielectric relaxation was observed.

• 한국분말재료학회지
• /
• 제18권6호
• /
• pp.568-574
• /
• 2011

As operating temperatures of engines or turbines continually increase for higher efficiency, significant amounts of researches have been focused on finding new materials, which would be alternatives to conventional yttria-stabilized zirconia (YSZ) for thermal barrier coatings (TBCs). In this study, phase evolution and thermo-physical properties of $La_2(Zr_{1-x}Hf_x)_2O_7$ pyrochlore systems are investigated for TBC applications. $La_2(Zr_{1-x}Hf_x)_2O_7$ systems are comprised by selecting $La^{3+}$ as A-site ions and $Zr^{4+}/Hf^{4+}$ as B-site ions in $A_2B_2O_7$ pyrochlore structures. For the developed phases in $La_2(Zr_{1-x}Hf_x)_2O_7$ compositions, thermo-physical properties such as thermal conductivity, thermal expansion coefficient are examined. The potential of these $La_2(Zr_{1-x}Hf_x)_2O_7$ compositions for TBC application is also discussed.

• 마이크로전자및패키징학회지
• /
• 제7권2호
• /
• pp.29-36
• /
• 2000

후막 페이스트용 glass frit의 내산성에 영향을 미치는 프릿트 제조방법 및 첨가제의 영향을 연구하였다. 프릿트 제조 방법에 따른 내산성을 관찰하기 위하여 $PbO-SiO_2-B_2O_3$기본 조성을 습식 및 건식 등의 흔합 방법 및 용융 횟수를 변수로 연구하였고, 첨가제에 의한 내산성 연구를 위하여 첨가제로 $ZrO_2$, $Al_2O_3$, $TiO_2$등을 0-l0wt% 첨가하여 첨가제에 따른 내산성 변화를 관찰하였다.

• 암석학회지
• /
• 제27권1호
• /
• pp.37-47
• /
• 2018

백두산에서 역사시대에 분화한 화산재의 시료에 대하여 다양한 방법으로 주성분과 미량성분을 분석하였다. 화산재의 주성분 원소 함량은 $SiO_2$ 58.8~71.1 wt.%, $Al_2O_3$ 9.6~16.8 wt.%, ${Fe_2O_3}^T$ 4.5~6.9 wt.%, MgO 0.1~1.7 wt.%, CaO 0.3~1.6 wt.%, $Na_2O$ 5.2~6.3 wt.%, $K_2O$ 4.3~5.9 wt.% 그리고 $TiO_2$ 1.2 wt.%이하로 분석되었다. Ba, Cu, Cr. Co, Ni, Sr, V, Zn와 Zr을 포함하는 32개 미량원소가 분석되었는데, 이들 화산재는 일부 미량원소와 경희토류 원소의 부화정도에 따라 두 그룹(그룹 A, 그룹 B)으로 구분되며, 그룹 A에는 1천년 전의 밀레니엄 분화물, 1668년과 1903년 분화물이, 그룹 B에는 1702년 분화물이 해당된다. 중금속원소인 Cu, Co, Zn, Mn 등은 소량 함유되어 나타난다. 백두산 화산재는, 섭입대 기원의 일본 사쿠라지마 화산의 화산재와 비교하여, 미량성분원소 중 Y, Nb, Pb, U, Sc, V, Ni 그리고 Cu 함량은 낮게 나타나며, Zr, Ba, Hf, Cr, Co, Zn 그리고 희토류(Eu제외) 등은 높은 함량을 나타낸다.