• Journal of the Korean Ceramic Society
• /
• v.29 no.6
• /
• pp.419-430
• /
• 1992

Fabrication possibility of low-shrinkage alumina without oxidation and wetting agent was presented on the basis of observation about oxidation behavior, microstructure and physical characteristics of such reaction agents free Al2O3-Al system. The composition less than Al 10w/o where Al can act as a sintering agent for Al2O3 was excluded. Under the condition of present experiments oxidation of Al2O3-Al system was dependent not on holding time but mainly on oxidation temperature. In thes case of Al powder not comminuted effectively during powder mixing of Al2O3-Al, columnar structure which would act as a hindrance to the densification during sintering developed more during oxidation with higher Al contents, and which made the fabrication of low-shrinkage Al2O3 ceramics impossible. If Al powder was comminuted effectively due to co-mixed Al2O3 characteristics, densification was improved because of no columnar structure and made the fabrication of sintered body with -2.7% dimensional change and 81% relative density possible. As a result, it is possible to fabricate dense low-shrinkage Al2O3 ceramics without oxidation and wetting agent under conditions such as smaller particle size of Al, Al contents below 50v/o, higher green density of Al2O3-Al compact and the use of Al2O3 powder used for high-density ceramics.

• The Journal of Korean Institute of Communications and Information Sciences
• /
• v.18 no.8
• /
• pp.1102-1107
• /
• 1993

Microwave dielectric properties of CaTiO3 and CaTiO3-TiO2 ceramics for the composition range between 40 and 50 mol% CaO in CaO-TiO2 binary system were investigated. CaTiO3 ceramics with50 mol% CaO showed the dielectric constant (e,) of 178, the temperature coefficient of resonant frequency(c,) of+1000 ppm/'c and the qualify factor Q of 2760 (f0=2.7 GHz ). Dielectric constant and temperature coefficient of resonant frequency of ceramics with dual phases of CaTiO3 and TiO2 decreased gradually from those of CaTiO3 as the CaO content decreased. Q value and density were found to have minimum at the composition of 47 mol% CaO. The degradation of Q value and density in dual phase ceramics seems to be caused by the large pores at grain boundaries and/or within grains remained after rapid growth of CaTiO3 grains as TiO2 Phase decreased.

• Journal of the Korean Ceramic Society
• /
• v.22 no.5
• /
• pp.76-84
• /
• 1985

Mechanical property enhancing mechanisms of $Al_2O_3-ZrO_2$ two phase ceramic composites were studied for several compositions of different $ZrO_2$/$Al_2O_3$ ratio. Microstructural analysis of $Al_2O_3-ZrO_3$(pure) composites indicated that pre-existing microcrack due to larger $ZrO_2$ particle at grain boundary extended along alumina grain boundaries within process zone. Microcracks also nucleated when very small $ZrO_2$ particles at the grain boundaries transformed to monoclinic phase at near of main crack tip. These types of microcracks could contribute to the toughening achieved by creating additional crack surface area during crack propagation. Microstructural analyses also showed that the average grain size and abnormal grain size of $Al_2O_3$ were decreased with increasing $ZrO_2$ vol% in $Al_2O_3$ matrix. As a result it could be concluded as follows In TEX>$Al_2O_3-ZrO_3$(pure) system 1. Microcrack nucleation (stress-induced microcracking) and extension was effective mechanism for absorpiton of fracture energy 2, More narrow distribution and smaller grain size of $Al_2O_3$ due to $ZrO_2$particles mainly contributed to main-tatin the strength and hardness.

• Journal of the Korean Ceramic Society
• /
• v.39 no.6
• /
• pp.528-534
• /
• 2002

CaO ceramics were prepared by conventional sintering process and their hydration behaviors were evaluated by measuring weight increment on saturated water vapor pressure at ambient temperature. CaCO$_3$ and limestone were used as CaO source materials and $Al_2$O$_3$, MgO and SiO$_2$ were added as sintering agents. $Al_2$O$_3$ was a liquid phase sintering agent to increase densification and grain growth rates, whereas MgO and SiO$_2$, densification and grain growth inhibitors. Regardless of composition, all of the prepared CaO ceramics showed the improved hydration resistance as bulk density increased. Especially, when bulk density was more than 3.0 g/㎤, there was no weight increment after 120 h of hydration. Therefore, to decrease contact area between CaO and water vapor by increasing bulk density with the $Al_2$O$_3$ sintering additive was effective for the improvement of CaO hydration resistance.

• Journal of the Korean Ceramic Society
• /
• v.11 no.3
• /
• pp.19-26
• /
• 1974

Mechanical properties of the system PbO-B2O3-V2O5 low melting glass during crystallization by heat-treatment were investigated. Wettability of the system PbO-B2O3-V2O5 was excellent and appropriate for commercial sealing as a low melting solder glass. Crystals, during heat-treated at 30$0^{\circ}C$ of the system PbO-B2O3-V2O5 were $\beta$-4PbO.B2O3, 5PbO.4B2O3, and Pb2V2O7 mainly. The percent of crystallinity was 82$\pm$5%. Mechanical properties of the system PbO-B2O3-V2O5 were influenced not only by the differences of density and coefficient of thermal expansion and the stress induced from the difference in the density and coefficient of thermal expansion between glass phase and crystals but also crystallization conditions.

• Journal of the Korean Chemical Society
• /
• v.50 no.1
• /
• pp.60-64
• /
• 2006

has been synthesized using the layered organic-inorganic hybrids, Cu2(OH)3(CH3COO)·H2O as a precursor. Cubic Cu2O is synthesized by reducing Cu2(OH)3(CH3COO)·H2O with glucose in water at 75oC. The effects of precursor and glucose are investigated. The structure of Cu2(OH)3(CH3COO)·H2O plays an important role in preparing the uniform size of Cu2O.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.5
• /
• pp.406-412
• /
• 2003

FT-IR and thermography were used to investigate the infrared radiation characteristic of SiO$_2$ film and SiO$_2$/Fe$_2$O$_3$film coated on aluminum. Through FT-TR spectrum, SiO$_2$film showed high infrared absorption in accordance with the stretching vibration of Si-O-Si, and as$ Fe_2$$O_3$was mixed additional absorption band appeared resulting from the stretching vibration of Fe-O at $590cm^{-1}$ and the bond of Si-O-Fe at $900 cm^{-1}$ The two kinds of film measured by the integration method and the reflective method coincided with each other in the wavelength area of infrared absorption and radiation, and corresponded well with Kirchhoff's law as the infrared emissivity is high in wavelength where infrared absorption rate is high. The emissivity of $SiO_2$ film was 0.65 and that of $SiO_2$/Fe$_2$$O_3$film was 0.77, so the addition of$ Fe_2$$O_3$ raised the infrared emissivity by approximately 13%.$ SiO_2$$Fe_2$$O_3$ film is efficient as an infrared radiator at below $100^{\circ}C$. The temperature of heat radiation after 7 minutes was 117$^{\circ}C$ in aluminum plate and $155^{\circ}C$ in $SiO_2$$Fe_2$$O_3$ film, $38^{\circ}C$ higher than the former.

• Journal of the Korean Ceramic Society
• /
• v.32 no.3
• /
• pp.295-304
• /
• 1995

Stabilization of the perovskite phase and sequence of reactions occuring during calcination were studied with solid solutions formed between Pb(Zn1/3Nb2/3)O3 and Pb(Fe1/2Nb1/2)O3. In the PZN-PFN composition of equal molar ratio, rhombohedral type pyrochlore phase (Pb2Nb2O7) and PbO-rich distorted cubic type pyrochlore phase (Pb3Nb2O8) were coexisted as intermediate phases at temperatures below 85$0^{\circ}C$, and these phases transformed to a stable cubic type pyrochlore phase, Pb3Nb4O13 solid solution and a perovskite solid solution at temperatures above 85$0^{\circ}C$. The major stable phase as increasing sintering temperatures was a perovskite phase in this binary system and prominent suppression of the pyrochlore phase was achieved by substituting Zn2+ with Fe3+ or by increasing sintering temperature. The composition containing 20mol% PZN possessed the best dielectric properties, and the dissipation factor was lower than 5% in all compositions.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.11
• /
• pp.969-974
• /
• 1998

The effects of $La_2O_3$on the microstructure and electrical characteristics of Pr-based ZnO varistors were investigated. The average grain size increased in the range of 21.9~56.3$\mu$ m with increasing $La_2O_3$additive content(0.0~2.0 mol%). La was, of course grain boundary, largely segregated at the nodal point. As $La_2O_3$additive content increases, threshold voltage and nonlinear coefficient decreased and leakage current increased. In particular, 2.0 mol% $La_2O_3$-added varistor exhibited low threshold voltage 17.0V/mm and nonlinear coefficient of about 6. Based on these results, this varistor can be said to be used as low-voltage varistor, if nonlinear coefficient is somewhat improved forward.

• Journal of the Korean Ceramic Society
• /
• v.38 no.12
• /
• pp.1137-1143
• /
• 2001

In this study, glass-ceramics containing cordierite(2MgO$.$2Al$_2$O$_3$5SiO$_2$) as a major crystalline phase was prepared from MAS (MgO-Al$_2$O$_3$-SiO$_2$) glass system for the application to reflector. Glasses prepared with addition of TiO$_2$as a nucleating agent were crystallized by two-step heat treatment of nucleation and crystal growth. Then nucleation and crystal growth behavior were investigated and the influence of heat treatment schedule on the nature of crystal phases and the diffuse reflectance spectrum was investigated. As a result, cordierite and rutile were precipitated as a major crystalline phases for the glass-ceramics with the nucleation at 750$^{\circ}C$ for 3 hours and then crystallization at 1100$^{\circ}C$ for 5 hours, and this glass-ceramics showed the reflectance over 90% in 570∼2500nm specturm region.