• Journal of the Korean Ceramic Society
• /
• v.52 no.2
• /
• pp.114-118
• /
• 2015

$V_2O_5-P_2O_5-ZnO-Sb_2O_3$ glasses modified with BaO and $Al_2O_3$ are synthesized as a sealing material for large-scale dye-sensitized solar cells (DSSCs). A compositional study is performed in order to determine the glass that can be sintered below $500^{\circ}C$ with a high chemical stability against the electrolyte. The flow size of the glasses after the heat treatment and the glass stability are increased with the addition of $Al_2O_3$ and BaO, while the glass transition temperature is decreased. After the reaction with the electrolyte at $60^{\circ}C$ for 72 h, the addition of 5 mol% of BaO and 2 mol% of $Al_2O_3$ considerably enhances the chemical stability of the glass. X-ray diffraction (XRD) and scanning electron microscope (SEM) are used to examine the reaction between the electrolyte and glasses. The structural contribution of the additives is also investigated and discussed.

• Journal of Welding and Joining
• /
• v.31 no.6
• /
• pp.65-70
• /
• 2013

In joining Alumina to copper plate by Mo-Mn metallizing process, the effects of the composition of metallizing paste on the bonding strength were investigated. The bonding strength increased with increasing Mn amount in the paste up to 20% but followed by the decrease with addition of Mn. The maximum bonding strength reached 50MPa at 20%Mn when heated to $1550^{\circ}C$ for 60minute. The addition of Si to the metallizing powder increased the bonding strength of the joint by enhancing the mechanical bonding between the Alumina and the metallizing layer due to the decrease of layer viscosity with the addition of $SiO_2$. It is thought that MnO reacted with $Al_2O_3$ to yield $MnAl_2O_4$ spinel, forming a joint.

• Journal of the Korean Ceramic Society
• /
• v.37 no.6
• /
• pp.583-588
• /
• 2000

Antioxidation characteristics of carbon at high temperature with the co-addition of Al and Si powder in Al2O3-C system refractory were analyzed. The use of surface-modified phosphate carbon as a starting material was found to be very effective in improving the mixing effect of raw materials and antioxidation behavior of carbon. In particular, this effect was dominant at higher temperatures than 130$0^{\circ}C$.

• Advances in nano research
• /
• v.3 no.4
• /
• pp.243-255
• /
• 2015

In this investigation, ecotoxicity of nano and micro metal oxides, namely silica ($SiO_2$) and alumina ($Al_2O_3$), on the growth of green algae (Porphyridium aerugineum Geitler) is discussed. Effects of nano and micro particles on the growth, chlorophyll content and protein content of algae are analysed using standard protocols. Results indicate that $SiO_2$ nano and micro $SiO_2$ particles are non-toxic to P. aerugineum Geitler up to a concentration of 1000 mg/L. In addition, $Al_2O_3$ microparticles are less toxic to P. aerugineum Geitler, whereas $Al_2O_3$ nanoparticles are found to be highly toxic at 1000 mg/L. Moreover, $Al_2O_3$ nanoparticles decrease the growth, chlorophyll content, and protein content of tested algae. In addition, zeta potential and contact angle are also important in enhancing the toxicity of metal oxide nanoparticles in aquatic environment. This study highlights a new insight into toxicity evaluation of nanoparticles on beneficial aquatic organisms such as algae.

• Korean Chemical Engineering Research
• /
• v.61 no.3
• /
• pp.479-486
• /
• 2023

In this study, we investigated the effect of the Ce_xZr_1-xO₂ (CZ) addition onto Ni/Al₂O₃ catalysts on the catalytic performance in methane steam reforming. In the reaction results, the CZ-added Ni/Al₂O₃ catalyst showed higher CH₄ conversion and H₂ yield under the same reaction conditions than Ni/Al₂O₃. From the characterization data, the two catalysts had similar support porosity and Ni dispersion, confirming that the two properties could not determine the catalytic performance. However, the oxygen vacancy over the CZ-added Ni/Al₂O₃ catalyst induced an efficient steam activation at low reaction temperatures, resulting in an increase in the catalytic activity and H₂ yield.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.2
• /
• pp.80-86
• /
• 2002

$Al_{2}O_{3}/SiC$ nanocomposites were made by infiltrating partially sintered alumina bodies with polycarbosilane (PCS) solutions, which is a SiC polymer precursor, with pressureless sintering. The SiC content, densification, phases, strength, and microstructure were investigated with the processing parameters such as PCS solution concentration and heat treatment condition for PCS pyrolysis and sintering. The results were compared with those for pure alumina and nanocomposite samples made by the existing polymer precursor route (i.e. the PCS addition process). The SiC contents of up to 1.5 vol% were obtained by the PCS infiltration. PCS pyrolysis, followed by air heat treatment, was needed before sintering to avoid a cracking problem and to attain a densification as high as 98 % of theoretical. The nanocomposites exhibited significantly higher strength than pure alumina and those prepared by the PCS addition process despite larger grain size. Besides $\alpha-Al_{2}O_{3}/SiC$ and $\beta-SiC$ phases, mullite was present a little in the nanocomposites, which resulted from the reaction of $SiO_{2}$ in the pyrolysis product of PCS with the $Al_{2}O_{3}$ matrix during sintering. The nanocomposites had intagranular particles believed to be SiC, which is a typical feature of $Al_{2}O_{3}/SiC$ nanocomposites.

• The Korean Journal of Ceramics
• /
• v.5 no.4
• /
• pp.371-374
• /
• 1999

Y2O3 and Nb2O5 co-doped tetragonal zirconia polycrystals((Y, Nb)-TZP) containing 10 to 30 vol% $Al_2O_3$ were prepared and hydrothermal stability of the composites was evaluated after aging for 5 h at the temperature range of $150^{\circ}C$ $250^{\circ}C$ under 4 MPa $H_2O$ vapor pressure in an autoclave. The (Y, Nb)-TZP/Al2O3 composites showed excellent phase stability under the hydrothermal conditions, as compared with the 3Y-TZP/$Al_2O_3$ composites, due to the combined effects of the Y-Nb ordering in the $t-ZrO_2$ lattice, the reduction of oxygen vacancy concentration, and the $Al_2O_3$ addition. The strength and fracture toughness of the (Y, Nb)-TZP/$Al_2O_3$ composite, containing 20 vol% of 2.8 $Al_2O_3$ particles, were 700 MPa and 8.1 MP.$am^{1/2}$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.26 no.5
• /
• pp.705-711
• /
• 1989

The glass-ceramics was prepared with the scoria(CaO-MgO-Al2O3-SiO2 system) of the locally occurring volcanic ejecta containing 10-13w/o of (FeO＋Fe2O3) by melting at 140$0^{\circ}C$ for 4 hours and thermally treated for nucleation and crystallization. The sucrose was added to the scoria to adjust the Fe2+/Fe3+ ratio during the melting process. The addition of 1-2w/o of sucrose showed the glass-ceramics body with the finest particle developed and dispersed over the entire range. It is concluded that the impurity content of iron oxide and titanium oxide play the most-influencial effect on the crystallization. When 1-2w/o of sucrose was added to the scoria, the value of Fe2+/Fe3+ ratio was 0.93-1.32 and showed the best result of crystallization. The nucleation temperature and time were calculated by the measurements of exothermic peak temperatures of DTA for quenched and thermally treated glasses. The nucleation temperature of scoria glass without the addition of sucrose was estimated as 75$0^{\circ}C$, but the addition of sucrose by 2w/o showed the nucleation temperature 6$25^{\circ}C$. The nucleation time was calculated with the same DTA curves. The nucleation times estimated were about 150min. for both of glasses without and with sucrose added. Finally, the activation energies for crystallization were calculated with the DTA data. The calculated activation energies were 143 Kcal/mole for the glass without addition of sucrose and 90Kcal/mole, 87Kcal/mole, 85Kcal/mole and 71Kcal/mole for the glasses of 1w/o, 2w/o, 3w/o and 4w/o addition respectively.

• Korean Journal of Materials Research
• /
• v.17 no.10
• /
• pp.560-566
• /
• 2007

AlN plates were fabricated by hot pressing at $1700-1900^{\circ}C$ using yttria and alumina (3 and $10\;{\mu}m$ particle size) powders as additives and characterized: density, thermal conductivity, transverse rupture strength, and grain size measurement by SEM and EDS. Density values of $3.31-3.34\;g/cm^3$ are largely attributed to hot pressing of powder mixtures in carbon mold under $N_2$ atmosphere which caused effective degree of oxygen removal from yttrium-aluminate phase expected to form at $1100^{\circ}C$. The grain size of hot pressed AlN was almost homogeneous, with size approximately from 3.2 to $4.0\;{\mu}m$ after hot pressing. $Al_2O_3$ powder of $3\;{\mu}m$ particle size resulted in better transverse rupture strength and finer grain size compared to $10\;{\mu}m$ $Al_2O_3$ powder. The thermal conductivity of AlN ranged between $83-92.7\;W/m{\cdot}K$ and decreased with $Al_2O_3$ addition. Fine grain size is preferred for better mechanical properties and thermal conductivity.

• Journal of the Korean Ceramic Society
• /
• v.35 no.2
• /
• pp.129-136
• /
• 1998

The effects of MgO on the resistance to corrosion and oxidation of Al2O3-SiC-C refractory have been in-vestigated. The resistance to oxidation was improved as the amount of MgO increased. The resistance to corrosion was enhanced until 2 wt% MgO content but degraded over that content. From the dependence of temperatuer on the oxidation resistance oxidation was suppressed by the microstructural densification caused by spinel formation over 1200~130$0^{\circ}C$and the formation MgO-Al2O3-SiO2 liguid-phase over 130$0^{\circ}C$ The weight loss of specimens containing MgO with various purity at range of 95 to 99% and par-ticle size of -0.045 mm to -0.074 mm was examined. The oxidation resistance was not changed signficantly with the particle size and purity of MgO powders.