• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.718-723
• /
• 2002

$Ti_{1-x}$ $Al_{ x}$N thin films as barrier layer for memory devices application were deposited by reactive magnetron sputtering. The crystallinity, micro-structure, oxidation resistance and oxidation mechanism of films were investigated as a function of Al content. Lattice parameter and grain size of thin films were decreased with increasing the Al content Oxidation of the film with higher Al content is slow and then, total oxide thickness is thinner than that of lower Al content film. Oxide layer formed on the surface is AlTiNO layer. Oxidation of $Ti_{1-x}$ /$Al_{x}$ N barrier layer is diffusion limited process and thickness of oxide layer with oxidation time increased with a parabolic law. The activation energy of oxygen diffusion, Ea and diffusion coefficient, D of $Ti_{0.74}$ /X$0.74_{0.26}$N film is 2.1eV and $10^{-16}$ ~$10^{-15}$ $\textrm{cm}^2$/s, respectively. $_Ti{1-x}$ /$Al_{x}$ XN barrier layer showed good oxidation resistance.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.9
• /
• pp.681-685
• /
• 2012

We investigated the dry etching characteristics of TiN in $TiN/Al_2O_3$ gate stack using a inductively coupled plasma system. TiN thin film is etched by BCl3/He plasma. The etching parameters are the gas mixing ratio, the RF power, the DC-bias voltages and process pressures. The highest etch rate is in $BCl_3/He$ (25%:75%) plasma. The selectivity of TiN thin film to $Al_2O_3$ is pretty similar with $BCl_3/He$ plasma. The chemical reactions of the etched TiN thin films are investigated by X-ray photoelectron spectroscopy. The intensities of the Ti 2p and the N 1s peaks are modified by $BCl_3$ plasma. Intensity and binding energy of Ti and N could be changed due to a chemical reaction on the surface of TiN thin films. Also we investigated that the non-volatile byproducts such as $TiCl_x$ formed by chemical reaction with Cl radicals on the surface of TiN thin films.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.5
• /
• pp.281-287
• /
• 2005

Titanium aluminium nitride((TiAl)N) film is anticipated as an advanced coating film with wear resistance used for drills, bites etc. and with corrosion resistance at a high temperature. In this study, (TiAl)N thin films were deposited both at room temperature and at elevated substrate temperatures of 573 to 773 K by using a two-facing-targets type DC sputtering system in a mixture Ar and $N_2$ gases. Atomic compositions of the binary Ti-Al alloy target is Al-rich (25Ti-75Al (atm%)). Process parameters such as precursor volume %, substrate temperature and Ar/$N_2$ gas ratio were optimized. The crystallization processes and phase transformations of (TiAl)N thin films were investigated by X-ray diffraction, field-emission scanning electron microscopy. The microhardness of (TiAl)N thin films were measured by a dynamic hardness tester. The films obtained with Ar/$N_2$ gas ratio of 1:3 and at 673 K substrate temperature showed the highest microhardness of $H_v$ 810. The crystallized and phase transformations of (TiAl)N thin films were $Ti_2AlN+AlN{\rightarrow}TiN+AlN$ for Ar/$N_2$ gas ratio of 1:3, $Ti_2AlN+AlN{\rightarrow}TiN+AlN{\rightarrow}Ti_2AlN+TiN+AlN$ for Ar/$N_2$ gas ratio of 1:1 and $TiN+AlN{\rightarrow}Ti_2AlN+TiN+AlN{\rightarrow}Ti_2AlN+AlN{\rightarrow}Ti_2AlN+TiN+AlN$ for Ar/$N_2$ gas ratio of 3:1. The above results are discussed in terms of crystallized phases and microhardness.

• Journal of Sensor Science and Technology
• /
• v.23 no.6
• /
• pp.420-424
• /
• 2014

Aluminum-scandium nitride ($Al_{1-x}Sc_xN$) thin films with a TiN buffer layer have been fabricated on SUS430 substrate by RF reactive magnetron sputtering at room temperature under 50% $N_2$/Ar. The effect of Sc-doping on the structure and piezoelectric properties of AlN films has been investigated using SEM, XRD, surface profiler and pressure-voltage measurements. The as-deposited AlN films showed polycrystalline phase, and the Sc-doped AlN film, the peak of AlN (002) plane and the crystallinity became very strong. With Sc-doping, the crystal size of AlN film was grown from ~20 nm to ~100 nm. The output signal voltage of AlN sensor showed a linear behavior between 15~65 mV, and output signal voltage of Sc-doped AlN sensor was increased over 7 times. The pressure-sensing sensitivity of AlN film was calculated about 10.6mV/MPa, and $Al_{0.88}Sc_{0.12}N$ film was calculated about 76 mV/MPa.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.7
• /
• pp.17-25
• /
• 1999

Tungsten nitride($WN_x$) films were deposited by PECVD method on silicon nitride($WSi_3N_4$) substrate. The characteristics of $WN_x$ film were investigated with changing various processing parameters ; substrate temperature, gas flow rate, rf power, and different nitrogen sources. The nitrogen composition in $WN_x$ film varied from 0 to 45% according to the $NH_3$ and $N_2$ flow rate. The highest deposition rate of 160 nm/min was obtained for the $NH_3$ gas and relatively low deposition rate of $WN_x$ films were formed by $N_2$ gas. $WN_x$ films deposited on $WSi_3N_4$ substrate had higher deposition rate than that of TiN and Si substrates. The purity of $WN_x$ film were analyzed by AES and higher purity $WN_x$ films were deposited using $NH_3$ gas. The XRD analysis indicates a phase transition from polycrystalline tungsten(W) to amorphous tungsten nitride($WN_x$), showing improved etching profile of $WN_x$ films Thick $WN_x$ films were deposited on various substrates such as Tin, NiCr and Al and maximum thickness of $1.6 {\mu}m$ was obtained on the Al adhesion layer.

• Proceedings of the IEEK Conference
• /
• 2003.07b
• /
• pp.1061-1064
• /
• 2003

In this paper, we deposited A1$_2$O$_3$ thin film using atomic layer deposition(ALD) method on Ti and fabricated metal-insulator-metal(MIM) capacitor. In the result of this study, the typical deposition rate was about 1.12$\AA$/cycle. About 30 nm of Ti was consumed during deposition and TiO$_{x}$ was formed at the interface of A1$_2$O$_3$ and Ti. Its surface roughness was 1.54nm. The leakage current density was 1.5 nA/$\textrm{cm}^2$. The temperature coefficient of capacitance(TCC) of MIM capacitor was 41 ppm/$^{\circ}C$ at 1MHz and 100 ppm/$^{\circ}C$ at 100 kHz.z.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.2
• /
• pp.54-60
• /
• 2010

Polymer-assisted deposition is a chemical solution route to high quality thin films. In this process, the polymer controls the viscosity and binds metal ions, resulting in a homogeneous distribution of metal precursors in the solution and the formation of crack-free and uniform films after thermal treatment. We review our recent effort to epitaxially grow metal-nitride thin films, such as hexagonal GaN, cubic TiN, AlN, NbN, and VN, mixed-nitride $Ti_{1-x}Al_xN$, ternary nitrides tetragonal $SrTiN_2$, $BaZrN_2$, and $BaHfN_2$, hexagonal $FeMoN_2$, and nanocomposite TiN-$BaZrN_2$.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.7 no.5
• /
• pp.801-804
• /
• 2006

[ $GdAlO_3(GAO)$ ] buffer layer for $YBa_2Cu_3O_{7-{\delta}}(YBCO)$ coated superconductor wire was fabricated by sol-gel processing. Precursor solution was prepared by dissolving 1:1 stoichiometric quantaties of gadolinium nitrate hexahydrate and aluminum nitrate nonahydrate in methanol. The solution was spin-coated on $SrTiO_3(STO)$(100) single crystal substrates and heated at $1000^{\circ}C$ for 2h in wet $N_2-5%\; H_2$, atmosphere. A SEM(scanning electron microscopy) observation of the surface morphology of the GAO layer has shown that it has a faceted morphology indicating epitaxy. It was shown from x-ray diffraction(XRB) that GAO buffer layer was highly c-axis oriented epitaxial thin film with both good out-of-plane($FWHM=0.29^{\circ}$ for the (002) reflection) and in-plane ($FWHM=1.10^{\circ}$ for the {112} reflection) alignment.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.1 no.4
• /
• pp.202-208
• /
• 2001

In Recent results suggested that doping $Ta_2O_5$ with a small amount of $TiO_2$ using standard ceramic processing techniques can increase the dielectric constant of $Ta_2O_5$ significantly. In this paper, this concept is studied using RTCVD (Rapid Thermal Chemical Vapor Deposition). Ti-doped $Ta_2O_5$ films are deposited using $TaC_{12}H_{30}O_5N$, $C_8H_{24}N_4Ti$, and $O_2$ on both Si and $NH_3$-nitrided Si substrates. An $NH_3$-based interface layer at the Si surface is used to prevent interfacial oxidation during the CVD process and post deposition annealing is performed in $H_2/O_2$ ambient to improve film quality and reduce leakage current. A sputtered TiN layer is used as a diffusion barrier between the Al gate electrode and the $TaTi_xO_y$ dielectric. XPS analyses confirm the formation of a ($Ta_2O_5)_{1-x}(TiO_2)_x$ composite oxide. A high quality $TaTi_xO_y$ gate stack with EOT (Equivalent Oxide Thickness) of $7{\AA}$ and leakage current $Jg=O.5A/textrm{cm}^2$ @ Vg=-1.0V has been achieved. We have also succeeded in forming a $TaTi_x/O_y$ composite oxide by rapid thermal oxidation of the as-deposited CVD TaTi films. The electrical properties and Jg-EOT characteristics of these composite oxides are remarkably similar to that of RTCVD $Ta_2O_5, suggesting that the dielectric constant of $Ta_2O_5$ is not affected by the addition of $TiO_2$.

• Journal of Periodontal and Implant Science
• /
• v.30 no.1
• /
• pp.187-203
• /
• 2000

The precipitation of calcium phosphate on implant surface has been known to accelerate osseointegration and to enhance osseous adaptation. The present study was performed to examine whether the precipitation of calcium phosphate on Ti-6Al-4V alloy could be affected by the immersion in NaOH solution and heat treatment. Ti-6Al-4V alloy plates of $15{\times}3.5{\times}1mm$ in dimension were polished sequentially from #240 to #2,000 emery paper and one surface of each specimen was additionally polished with $0.1{\mu}m$ alumina paste. Polished specimens were soaked in various concentrations of NaOH solution(0.1, 1.0, 3.0, 5.0, 7.0, 10.0 M) at $60^{\circ}C$ for 24 hours for alkali treatment, and 5.0 M NaOH treated specimens were heated for 1 hour at each temperature of 400, 500, 600, 700, $800^{\circ}C$. After the alkali and heat treatments, specimens were soaked in the Hank's solution with pH 7.4 at $36.5^{\circ}C$ for 30days.The surface ingredient change of Ti-6Al-4V alloy was evaluated by thin-film X-ray diffractometer(TF-XRD) and the surface microstructure was observed by scanning electron microscope(SEM), and the elements of surface were analyzed by X-ray photoelectron spectroscopy(XPS). The results were obtained as follows ; 1. The precipitation of calcium phosphate on Ti-6Al-4V alloy was accelerated by the immersion in NaOH solution and heat treatment. 2. In Alkali treatment for the precipitation of calcium phosphate on Ti-6Al-4V alloy, the optimal concentration of NaOH solution was 5.0 M. 3. In heat treatment after alkali treatment in 5.0 M NaOH solution, the crystal formation on alloy surface was enhanced by increasing temperature. In heat treated alloys at $600^{\circ}C$, latticed structure and prominences of calcium phosphate layer were most dense. On heat treated alloy surface at the higher temperature(${\geq}700^{\circ}C$), main crystal form was titanium oxide rather than apatite. The above results suggested that the precipitation of calcium phosphate on the surface of Ti-6Al-4V alloy could be induced by alkali treatment in 5.0 M-NaOH solution and by heat treatment at $600^{\circ}C$.