• 한국표면공학회지
• /
• 제47권2호
• /
• pp.93-98
• /
• 2014

The $Cr_2AlC$ carbides oxidized at 700, 850 and $1000^{\circ}C$ in air from 70 hours up to 360 days. They oxidized according to the reaction; $Cr_2AlC+O_2{\rightarrow}{\alpha}-Al_2O_3+CO(g)$. The scales consisted primarily of the thin, essentially pure $Al_2O_3$ layer and the underlying Al-dissolved $Cr_7C_3$ layer. They grew via the outward diffusion of Al and carbon, and the inward diffusion of oxygen. The oxidation resistance of $Cr_2AlC$ was excellent due to the formation of the protective $Al_2O_3$ layer. Even when $Cr_2AlC$ oxidized at $1000^{\circ}C$ for 360 days, the ${\alpha}-Al_2O_3$ layer was only about 4 ${\mu}m$-thick.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제48권2호
• /
• pp.92-97
• /
• 1999

The mechanical and electrical properties of the hot-pressed and annealed $\beta-Sic$+39vol.%$ZrB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of $Al_2O_3+Y_2O_3(6:4wt%)$. In this microstructures, no reactions and elongated $\alpha$-SiC grains with equiaxed $ZrB_2$, gains were observed between $\beta-SiC$ and $ZrB_2$, and the relative density was over 97.6% of the theoretical density. Phase analysis of the composites by XRD revealedmostly of $\alpha$-SiC(6H, 4H), $ZrB_2$, and weakly $\beta-SiC$(15R) phase. The fracture toughness decreased with increasing $Al_2O_3+Y_2O_3$ contents and showed the highest of $6.37MPa.m^{\fraction ane-half}$ for composite added with 4wt% $Al_2O_3+Y_2O_3$ additives at room temperature. The electrical resistivity increased with increasing $Al_2O_3+Y_2O_3$contents and showed the lowest of $1.51\times10^{-4}\Omega.cm$ for composite added with $Al_2O_3+Y_2O_3$ additives at $25^{\circ}C$. This reason is the increasing tendency of pore formation according to amount of liquid forming additives $Al_2O_3+Y_2O_3$. The electrical resistivity of the composites was all positive temperature coefficient resistance(PTCR) against temperature up to $700^{\circ}C$.

• 한국세라믹학회지
• /
• 제26권2호
• /
• pp.210-220
• /
• 1989

The properties of the powder of Al2O3-15v/o ZrO2(＋3m/o Y2O3) system prepared by co-precipitation method at the pH values of 7, 9, 10 and 11 were investigated. Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Zirconium hydroxide decreased the specific surface area of aluminum hydroxide of AlOOH type, while increased the specific surface area of aluminum hydroxide of Al(OH)3 type, and formed co-network structure of Al-O-Zr type with the aluminum hydroxides. The rate of transition to $\alpha$-Al2O3 from co-precipitated materials occurred in the order of 7≒10, 9 and 11 of pH values. Al2O3 and ZrO2 interacted to bring about coupled grain growth, and the growth of ZrO2 crystallite size rapidly occurred within $\theta$-Al2O3 matrix. Segregation did not occur in the system Al2O3-15v/o ZrO2(＋3m/o Y2O3) and Y2O3 acted as a stabilizer to ZrO2. The lattice strain of tetragonal ZrO2 was increased by the constraint effect of Al2O3 matrix.

• 한국세라믹학회지
• /
• 제43권4호
• /
• pp.242-246
• /
• 2006

[ ${\alpha}-Al_2O_3$ ] nanopowders were fabricated by the thermal decomposition and synthetic of Ammonium Aluminum Carbonate Hydroxide (AACH). Crystallite size of 5 to 8 nm were fabricated when reaction temperature of AACH was low, $8^{\circ}C$, and the highest $[NH_4{^+}][AlO(OH)_n{(SO_4){^-}}_{3-n/2}][HCO_3]$ ionic concentration to pH of the Ammonium Hydrogen Carbonate (AHC) aqueous solution was 10. The phase transformation fem $NH_4Al(SO_4)_2$, rhombohedral $(Al_2(SO_4)_3)$, amorphous-, ${\theta}-,\;{\alpha}-Al_2O_3$ was examined at each temperature according to the AACH. A Time-Temperature-Transformation (TTT) diagram for thermal decomposition in air was determined. Homogeneous, spherical nanopowders with a particle size of 70 nm were obtained by firing the 5 to 8 m crystallites, which had been synthesized from AACH at pH 10 and $8^{\circ}C,\;at\;1150^{\circ}C$ for 3 h in air.

• 한국세라믹학회지
• /
• 제28권9호
• /
• pp.705-711
• /
• 1991

Alumina precursor sol was obtained by the reaction of Al(OC4H9)3 and acetylacetone in the solvent followed by the partial hydrolysis. This sol was measured by viscosity and the effect of pH. The powders obtained from this sol were calcined at the various temperatures. The transition of crystals and crystal state were investigated at the various temperatures. The powders dried at 90$^{\circ}C$ showed amorphous and ${\gamma}$-Al2O3 at 900$^{\circ}C$, ${\alpha}$-Al2O3 mono-phase at 1050$^{\circ}C$ respectively. As a result of Al27-MASNMR analysis, amorphous and ${\alpha}$-Al2O3 powders showed 6-coordinated Al, ${\gamma}$-Al2O3 4-coordinated Al respectively.

• 한국군사과학기술학회지
• /
• 제6권3호
• /
• pp.54-61
• /
• 2003

$SnO_2$ gas sensor for the detection DMMP, simulant of nerve gas was fabricated and its characteristics were examined. Sensing materials were $SnO_2$ added by TEX>$\alpha$-$Al_{2}O_{3}$ with 0∼20wt.% and $In_{2}O_{3}$ with 0∼3wt.% and were physically mixed each material. They were deposited by screen printing method on alumina substrate. The sensor was consisted of sensing electrode with interdigit(IDT) type in front and a heater in back side. Its dimension was 7$\times$10$\times$0.6$\textrm{mm}^2$. Crystallite size 8t phase identification, specific surface area and morphology of fabricated $SnO_2$ powders were analyzed by X-ray diffraction(XRD), surface area analyzer(BET) and by a scanning electron microscope(SEM), respectively. Sensor was measured as flow type and sensor resistance change was monitored as real time using LabVIEW program. The best sensitivities were 75% at adding 4wt.% TEX>$\alpha$-$Al_{2}O_{3}$, operating temperature $300^{\circ}C$ and 87% at adding 2wt.% $In_{2}O_{3}$, operating temperature $350^{\circ}C$ to DMMP 0.5ppm. Response and recovery times were about 1 and 3 min., respectively. Repetition measurement was very good with $\pm$3% in full scale. As a result, operating temperature was lower TEX>$\alpha$-$Al_{2}O_{3}$ than $In_{2}O_{3}$, but sensitivity was higher $In_{2}O_{3}$ than $\alpha$-$Al_{2}O_{3}$.

• 한국세라믹학회지
• /
• 제24권1호
• /
• pp.23-32
• /
• 1987

Synthesis of high purity ultrafine Si3N4 and ${\beta}$-Sialon powders was investigated via the simultaneous reduction and nitriding of amorphous SiO2, SiO2-Al2O3 system prepaerd by hydrolysis of alkoxides, using carbonablack as a reducing agent. In Si(OC2H5)4-C2H5 OH-H2 O-NH4OH system, hydrolysis rate increased with increasing reaction temperature and pH. Pure ${\alpha}$-Si3N4 was formed at 1350$^{\circ}C$ for 5 hrs in N2 atmosphere. In Si(OC2H5)4-Al(OC3H7)3-C6H6-H2 O-NH4OH system, weight loss increased as Si/Al ratio decreased. Single phase ${\beta}$-Sialon consisted of Si/Al=2 was formed at 1350$^{\circ}C$ in N2 and minor phases of ${\alpha}$-Si3N4, AIN, and X-phase were existed besides theSialon phase at other Si/Al ratios. The Si3N4 and Sialon powders synthesized from alkoxides consisted of uniform find particles of 0.05-0.2$\mu\textrm{m}$ in diameter, respectively.

• Korean Chemical Engineering Research
• /
• 제52권3호
• /
• pp.340-346
• /
• 2014

Continuous and dense ZIF-7 membranes were successfully synthesized on ${\alpha}-Al_2O_3$ porous substrate via two-step crystallization technique. ZIF-7 seeding layer was first deposited on porous ${\alpha}-Al_2O_3$ substrate by in-situ low temperature crystallization, and then ZIF-7 membrane layer can be grown through the secondary high-temperature crystallization. Two synthesis solutions with different concentration were used to prepare ZIF-7 seeding layer and membrane layer on porous ${\alpha}-Al_2O_3$ substrate, respectively. As a result, a continuous and defect-free ZIF-7 membrane layer can be prepared on porous ${\alpha}-Al_2O_3$ substrate, as confirmed by scanning electron microscope. XRD characterization shows that the resulting membrane layer is composed of pure ZIF-7 phase without any impurity. A single gas permeation test of $H_2$, $O_2$, $CH_4$ or $CO_2$ was conducted based on our prepared ZIF-7 membrane. The ZIF-7 membrane exhibited excellent H2 molecular sieving properties due to its suitable pore aperture and defect-free membrane layer.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2002년도 추계총회 및 연구발표회 초록집
• /
• pp.23.2-23
• /
• 2002

• 환경위생공학
• /
• 제15권1호
• /
• pp.62-68
• /
• 2000

This study was investigated to the recovery of alumina from the first calcined waste pottery using alkaline sintering. This study was based on calcination result of a commercial ${\alpha}-Al2_O_3$ with NaOH powder. $NaAlO_2$ was formed by calcination of ${\alpha}-Al_2O_3$ with NaOH and conversion of $NaAlO_2$ from ${\alpha}-Al_2O_3$ was 91.4% at calcination condition ; weight ritio of $NaOH/{\alpha}-Al2_O_3$ 1.5, $800^{\circ}C$, and 90min. The first calcined waste porrery from the manufacturing Procedure of H Ltd. was grinded to 170/270mesh by a ball mill and calcined over $500^{\circ}C$ with NaOH powder. The calcined sample was dissolved in $25^{\circ}C$ water and sodiumaluminosilicate solid was formed. After filtration, the contained aluminum was leached out by dissolving sodiumaluminosilicate solid in 1N HCl. We estimated the efficiency of Al extraction from waste pottery by ICP analysis and NaOH was added to the filtrate and then aluminum compound was precipitated with $Al(OH)_3$ and recovered. The investigation was carried out with the variables ; the calcination temperature($500-900^{\circ}C$), the calcination time(30~90min), and the weight ratio of NaOH/waste pottery(0.5~1.5). The treatment efficiency of the waste pottery and the recovery of Al as 97.9%, 91.9% were obtained under the optimum conditions as followed ; the weight ratio of NaOH/waste pottery was 1.5 and the calcination conditions were $900^{\circ}C$ and 60min.