• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.3
• /
• pp.103-109
• /
• 2020

The effect of La₂O₃ addition on the crystalline phase, microstructure, and dielectric properties of BaTiO₃ has been studied as a function of the amounts of La₂O₃. 0.3 mol% TiO₂-excess BaTiO₃ powder was synthesized by solid-state reaction, and then the powder compacts with various amounts of La₂O₃ were sintered at 1250℃ for 2 hours. Room temperature XRD showed changes in the lattice parameters and a decrease of tetragonality (c/a) as the amounts of La₂O₃ increased. It can be explained that the phase transition from tetragonal to cubic phase occurred because La³⁺ replaced Ba²⁺ site, which increased the instability of the tetragonal phase. As La₂O₃ was added over 0.1 mol%, the critical driving force for growth (Δg_c) increased over maximum driving force (Δg_max). As the result, the grain size decreased with La₂O₃ addition. Dielectric constant decreased as the amounts of La₂O₃ increased, which was analyzed with crystal structure and microstructure.

• Journal of the Korean Ceramic Society
• /
• v.39 no.4
• /
• pp.359-366
• /
• 2002

The purpose of this study is to investigate the properties of LSGM electrolyte and LSM cathode. The unit cell based on the optimum conditions and processing for high performance was fabricated and measured. The single phase of $LaGaO_3$ was obtained on sintering at $1500^{\circ}$ for 6h with composition of $(La_{0.85}Sr_{0.15})(Ga_{0.8}Mg_{0.2})O_{3-\delta}와 (La_{0.8}Sr_{0.2})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$ and $(La_{0.85}Sr_{0.15})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$. The grain size of the sintered body was about $10∼30{\mu}m$ and electrical conductivity was 0.13 S/cm measured at $800^{\circ}$. The single phase of $LaMnO_3$ structure in $(La1-xSrx)MnO_3$ system was obtained at x=0∼0.2 and the particle size of the synthesized powder was about 40 nm. The unit cell was prepared by firing at $1200^{\circ}$ for 1h with $(La_{0.9}Sr_{0.1})MnO_3$ cathode and 0.9NiO-0.1YSZ anode screen-printed on surfaces of $(La_{0.8}Sr_{0.2})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$ electrolyte. The grain size of the electrode was close to $1{\mu}m$ and the electrode had porous structure. The maximum power density of unit cell showed $0.3W/cm^2$ at $800^{\circ}$.

• Journal of the Korean Ceramic Society
• /
• v.39 no.4
• /
• pp.352-358
• /
• 2002

The variations of the properties of Sr and Mg added $LaGaO_3$ system electrolyte with the amount of the additive and the sintering condition were studied. Main phase was (La$_{1-x}Sr_x)(Ga_{1-y}Mg_y)O_{3-\delta}$ phase for each compositions and the single phases $(La_{0.85}Sr_{0.15})(Ga_{0.85}Mg_{0.15})O_{3-\delta},(La_{0.85}Sr_{0.15})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$ and $(La_{0.8}Sr_{0.2})(Ga_{0.8}Mg_{0.2})O{3-\delta}$ were obtained with the decrease in the sintering temperature and Mg addition. Thermal expansion coefficient of the $(La_{0.8}Sr_{0.2})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$ decreased with the increase in the sintering temperature. Electric conductivity of electrolyte sintered at $1500^{circ}C$ for 1h was 0.14 S/cm at $800^{circ}C$ with 1 mA.

• Korean Journal of Clinical Laboratory Science
• /
• v.50 no.4
• /
• pp.501-510
• /
• 2018

This study examined the neurotoxicity induced by lead acetate (LA) on cultured C6 glioma cells and the protective effects of Euphorbiae humifusae L. (EH) extract against LA-induced cytotoxicity. In this study, LA exhibited neurotoxicity in a dose-dependent manner compared to the control, and was determined to be highly-toxic according to the toxic criteria. The $XTT_{50}$ value of LA was calculated at a concentration of $38.6{\mu}M$ after C6 glioma cells were incubated for 72 hours in the media containing $30{\sim}50{\mu}M$ of LA, respectively. In addition, LA-induced neurotoxicity was suggested to correlate with the level of oxidative stress because vitamin E, an antioxidant, increased the cell viability damaged by LA-induced cytotoxicity. The EH extract effectively prevented cell injury from LA-induced cytotoxicity via its antioxidative effects, such as inhibitory ability of lipid peroxidation, superoxide dismutase-like activity and 1,1-diphenyl-2-picrylhydrazyl-radical scavenging activity. These antioxidative effects may result in components, such as polyphenol or flavonoids including gallic acid or quercetin. In conclusion, natural resources, such as EH extracts, may be a useful putative agent for the treatment of diseases associated with oxidative stress, such as lead neurotoxicity.

• Applied Chemistry for Engineering
• /
• v.22 no.4
• /
• pp.376-383
• /
• 2011

The CMCs of LA and LA3 nonionic surfactants obtained from the reaction between glycidol and lauryl alcohol were found to be $0.97{\times}10^{-3}mol/L$ and $1.02{\times}10^{-3}mol/L$ respectively and the surface tensions for 1 wt% surfactant were 26.99 and 27.48 mN/m respectively. Dynamic surface tension measurements using a maximum bubble pressure tensiometer showed that the adsorption rate of surfactant molecules at the interface between the air and the surfactant solution was found to be relatively fast in both surfactant systems, presumably due to the high mobility of surfactant molecules. The contact angles of LA and LA3 nonionic surfactants were 27.8 and $20.9^{\circ}$ respectively and the dynamic interfacial tension measurement by a spinning drop tensiometer showed that interfacial tensions at equilibrium condition in both systems were almost the same. Also both surfactant systems reached equilibrium in 2~3 min. Both surfactant solutions showed high stability when evaluated by conductometric method and the LA nonionic surfactant system provided the higher foam stability than the LA3 nonionic surfactant system. The phase behavior experiments showed a lower phase or oil in water (O/W) microemulsion in equilibrium with an excess oil phase at all temperatures studied. No three-phase region was observed including a middle-phase microemulsion or a lamellar liquid crystalline phase.

• Applied Chemistry for Engineering
• /
• v.31 no.6
• /
• pp.674-678
• /
• 2020

In this study, a Pd/TiO2 catalyst which oxidized H2 at room temperature without an additional energy source was prepared. And a specific surface area of TiO2 as a support was not proportional to H2 oxidation reaction performance of Pd/TiO2 catalyst. In addition La2O3 was added to Pd/TiO2 catalyst in order to evaluate the performance effect due to the change of catalysts physical properties. A Pd/La2O3-TiO2 was prepared by adding different amounts of La2O3 to TiO2 and CO chemisorption analysis was performed. Compared to the conversion rate (14% at 0.5% H2) of the Pd/TiO2(G) catalyst, the Pd/La2O3-TiO2 catalyst showed 74% which was improved by more than five times. It was found that the larger the metal dispersion of Pd as an active metal is, the more favorable to H2 oxidation reaction is. However, when the added La2O3 amount exceeded 10%, the catalyst performance decreased again. Finally, it was concluded that the physical properties of the Pd/La2O3-TiO2 catalyst have a dominant influence on the catalytic activity until 0.3~0.5% of injected H2 concentrations and the catalyst reaction rate was controlled by substance transfer from 1% or more concentrations of H2.

• Journal of Microbiology
• /
• v.39 no.1
• /
• pp.79-82
• /
• 2001

The influence of levulinic acid (LA) on the production of copolyester consisting of 3-hydroxybutyrate (3HB) and 3-hydroxyvalerate (3HV) by Ralstonia eutropha was investigated. Addition of LA into the culture medium greatly increased the molar fraction of 3HV in the copolyester, indicating that LA can be utilized as a precursor of 3HV. In shake flask culture, the 3HV content in the copolyester increased from 7 to 75 mol% by adding 0.5 to 4.0 g/L LA to the medium containing fructose syrup as a main carbon source. A maximal copolyester concentration of 3.6 g/L (69% of dry cell weight) was achieved with a 3HV content of 40 mo1% in a jar fermentor culture containing 4.0 g/L of LA. When LA (total concentration, 4 g/L) was added repeatedly into a fermentor culture to maintain its concentration at a low level, the copolyester content and the 3HV yield from LA reached up to 85% of dry cell weight and 5.0 g/g, respectively, which were significantly higher than those when the same concentration of the LA was supplied al1 at once. The present results indicated that LA is more effective than propionate or valerate as a cosubstrate fur the production of copolyesters with varying molar fractions of 3HV by R. eutropha.

• Journal of the Korean Ceramic Society
• /
• v.36 no.3
• /
• pp.301-306
• /
• 1999

CO2 감지용 La2O3-SnO2 계 후막형 소자를 제조하여 CO2가스에 대한 기초 감지 특성을 조사하였고, 감지 분말의 입자크기와 제조방법에 따른 감도 변화를 고찰하였다. 후막 소자는 40$0^{\circ}C$의 작동온도와 4wt.%의 La2O3가 첨가되 srjt에서 가장 좋은 감도를 나타내었고, 낮은 습도영역에서 우수한 감지 특성을 보였다. 분말 혼합법에 의해 제조된 소자에 있어서 La2O3와SnO2 분말의 입자가 미세할수록 우수한 감도를 나타내었고, La2O3의 입도가 SnO2의 입도 보다 감도에 더 큰 영향을 주었다. SnO2 후막 표면에 La 용액을 코팅하여 제조된 센서는 가장 우수한 CO2 감도특성을 보였다.

• Journal of the Korean Ceramic Society
• /
• v.29 no.11
• /
• pp.900-904
• /
• 1992

High temperature electrical conductivity was measured for perovskite La0.98Sr0.02MnO3 at 200~130$0^{\circ}C$ as a function of Po2 and 1/T. Perovskite La1-xSrxMnO3 system is the typical oxygen electrode in solid oxide fuel cell (SOFC). Acetate precursors were used for the preparation of mixed water solution and the calcined powders were reacted with Na2CO3 flux in order to obtain highly reactive powders of perovskite La0.98Sr0.02MnO3. The relative density was greatly increased above 90% because of the homogeneous sintering. From the conductivity ($\sigma$)-temperature and conductivity-Po2 at constant temperature, the defect structure of La0.98Sr0.02MnO3 was discussed. From the slope of 1n($\sigma$) vs 1/T, the activation energy of 0.069 and 0.108eV were evaluated for above 40$0^{\circ}C$, respectively. From the relationship between $\sigma$ and Po2, it was found that the decomposition of La0.98Sr0.02MnO3 was occurred at 10-15.5 atm(97$0^{\circ}C$) and 10-11 atm(125$0^{\circ}C$). It is supposed that the improvement of p-type conductivity may be leaded by the increase of Mn4+ concentration through the substitution of divalent/monovalent cations for La site in LaMnO3.

• Journal of the Korean Applied Science and Technology
• /
• v.27 no.1
• /
• pp.29-36
• /
• 2010

The effects of La addition to Ni/$CeO_2$ methane partial oxidation catalysts were investigated. Catalysts were prepared by the impregnation and urea methods. In the preparation of catalysts, La content was changed from 1 wt% to 3wt%. Catalysts that contain 2wt% La showed the highest methane conversion of about 80% and CO selectivity of 84% and $H_2$ selectivity of 70%. This result may be stemmed from that, when La content is 2wt%, a fluorite oxide-type structure is well formed and carbon deposition is also decreased. Among the catalysts, 2.5wt% Ni/Ce(La)Ox showed the highest catalytic activity. From the experiment of changing reaction temperature with 2.5wt% Ni/Ce(La)Ox catalyst, it was found that the optimum reaction temperature is $750^{\circ}C$ and at this temperature methane conversion was about 90%, CO and $H_2$ selectivities were 94 and 80%, respectively.