• 한국잠사곤충학회지
• /
• 제45권2호
• /
• pp.121-125
• /
• 2003

Dissolution of Antheraea pernyi silk fiber was carried out in a zinc nitrate 6 hydrate (Zn(NO$_3$)$_2$ㆍ6$H_2O$) solution with various dissolving conditions. The solubility was significantly dependent on the concentration of zinc nitrate, dissolving temperature and time. Regenerated A. pernyi silk fibroin powder was obtained through dialysis process to remove chaotropic salt. FTIR and X-ray diffractometer showed that the conformation of regenerated A. pernyi silk powder was sheet structure.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제41회 하계 정기 학술대회 초록집
• /
• pp.235-235
• /
• 2011

ZnO 나노구조체를 성장하는 여러 가지 방법 중에서 전기 화학 증착법은 컨트롤이 용이하며 저렴한 가격으로 낮은 온도에서 성장이 가능할 뿐만 아니라 대면적으로 성장할 수 있는 장점이 있다. 나노구조체의 직경과 길이는 indium-tin-oxide와 Ag/AgCl 전극 사이의 전류 밀도 증가에 따라 변화하는 것을 알 수 있었다. Zinc nitrate 몰 농도를 조절하여 다양한 형태의 ZnO 나노구조체를 만들 수 있었다. 70$^{\circ}C$에서 4시간 동안 성장한 ZnO 나노구조체를 대기에서 400$^{\circ}C$로 2분 동안 열처리를 하였다. 성장된 ZnO 나노구조체에 대한 X-선 회절 측정 결과로부터 (0002) 피크가 34.35$^{\circ}$에서 나타나는 것을 확인하였다. 주사전자현미경 측정 결과로부터 zinc nitrate의 몰 농도가 낮을 때 성장한 ZnO 나노구조체는 와이어 형태로 형성되었음을 확인하였다. 그러나 zinc nitrate의 몰 농도가 높아지게 되면 ZnO 나노구조체의 모양이 와이어에서 막대 또는 접시 형태로 변화 되는 것을 알 수 있었다. 300K에서의 광루미네센스 스펙트럼 결과로부터 zinc nitrate의 농도에 따라 다르게 형성된 ZnO 나노구조체는 엑시톤과 관련된 피크가 zinc nitrate의 몰 농도 변화에 따라 달라지는 것을 확인 하였다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제38회 동계학술대회 초록집
• /
• pp.187-187
• /
• 2010

ZnO의 나노 구조는 화학적으로 안정하고 큰 결합에너지를 가지는 성질 때문에 청색 영역에서 작동하는 광전소자의 제작에 대단히 유용하다. ZnO 나노 구조들은 화학 기상 성장법, 기상 에피텍시 성장법, 화학적 용액 성장법과 같은 여러 가지 방법으로 성장하고 있다. 여러 가지 성장방법 중에서도 전기 화학 증착법으로 성장된 ZnO의 나노 구조는 가격이 저렴하고 낮은 온도에서 성장이 가능하며 대면적화를 할 수 있는 장점이 있다. 전기 화학 증착법으로 ZnO을 성장할 때 3개의 전극을 사용하여 성장하였다. ITO 기판을 음극으로 백금 전극을 양극으로 사용하였고 기준 전극은 Ag/AgCl을 사용하였다. Zinc Nitrate의 몰 농도를 변화하면서 ZnO 나노구조를 성장 하였다. 성장한 ZnO 나노구조를 $400^{\circ}C$에서 2 분정도 열처리를 하였다. 성장된 ZnO을 X-선회절장치를 분석하게 되면 (0002) 피크가 $34.35^{\circ}$에서 주되게 나타났다. 주사 전자 현미경상은 Zinc Nitrate의 몰 농도가 낮을 때 성장한 ZnO 는 나노세선 형태로 형성되었음을 보여주었다. Zinc Nitrate의 농도가 높아지게 되면 ZnO 나노구조가 나노 막대 또는 나노 접시 모양으로 변화되었다. 300 K에서 광루미네선스 스펙트럼은 형성된 나노구조가 엑시톤과 관련된 주된 피크가 Zinc Nitrate 농도에 따라 변화하게 되는 것을 알 수 있었다. 이 실험결과는 ZnO 나노구조의 미세구조와 광학적 성질이 Zinc Nitrate의 농도에 영향을 많이 받는 것을 알 수 있었다.

• Bulletin of the Korean Chemical Society
• /
• 제33권6호
• /
• pp.1949-1954
• /
• 2012

We have developed a novel and eco-friendly synthetic route for the preparation of a two-dimensional layered zinc hydroxide with intercalated nitrate anions. The layered zinc hydroxide nitrate, called 'zinc basic salt', was, in general, successfully synthesized, using an electron beam irradiation technique. The 2-propanol solutions containing hydrated zinc nitrate were directly irradiated with an electron-beam at room temperature, under atmospheric conditions, without stabilizers or base molecules. Under electron beam irradiation, the reactive OH radicals were generated by radiolysis of water molecules in precursor metal salts. After further radiolytic processes, the hydroxyl anions might be formed by the reaction of solvated electrons and the OH radical. Finally, the $Zn_5(OH)_8(NO_3)_2{\cdot}2H_2O$ was precipitated by the reaction of zinc cation and hydroxyl anions. Structure and morphology of obtained compounds were characterized by powder X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and high resolution transmission electron microscopy (HR-TEM). The chemical components of the products were determined by Fourier transform infrared spectroscopy (FT-IR) and elemental analysis (EA). The thermal behavior of products was studied by thermogravimetric (TG) and differential thermal analysis (DTA).

• 대한화학회지
• /
• 제38권5호
• /
• pp.397-403
• /
• 1994

질산니켈과 아연을 에탄올 용매하에서 환류반응시켜 얻은 활성화시킨 촉매는 히드라진 존재하에서 방향족 니트로화합물을 주로 아족시 화합물로 환원시켜 주었다. 그러나 질산니켈 대신 염화니켈을 사용하여 얻은 촉매는 같은 조건하에서 단지 방향족 아민만을 얻을 수 있었다. 활성화시키지 않고, 방향족 니트로화합물, 염화니켈이나 질산니켈, 아연 그리고 히드라진 혼합물을 환류반응 시킬 때는 낮은 수율의 아조, 아족시와 아민 화합물을 얻을 수 있었다.

• Transactions on Electrical and Electronic Materials
• /
• 제18권3호
• /
• pp.155-158
• /
• 2017

In this paper, ZnO Thin Film Transistors (TFTs) were fabricated by a sol-gel method using a low-temperature process, and their physical and electrical characteristics were analyzed. To lower the process temperature to $200^{\circ}C$, we used a zinc nitrate hydrate ($Zn(NO_3)_2{\cdot}xH_2O$) precursor. Thermo Gravimetric Analyzer (TGA) analysis showed that the zinc nitrate hydrate precursor solution had 1.5% residual organics, much less than the 6.5% of zinc acetate dihydrate at $200^{\circ}C$. In the sol-gel method, organic materials in the precursor disrupt formation of a high-quality film, and high-temperature annealing is needed to remove the organic residuals, which implies that, by using zinc nitrate hydrate, ZnO devices can be fabricated at a much lower temperature. Using an X-Ray Diffractometer (XRD) and an X-ray Photoelectron Spectrometer (XPS), $200^{\circ}C$ annealed ZnO film with zinc nitrate hydrate (ZnO (N)) was found to have an amorphous phase and much more oxygen vacancy ($V_o$) than Zn-O bonds. Despite no crystallinity, the ZnO (N) had conductance comparable to that of ZnO with zinc acetate dihydrate (ZnO (A)) annealed at $500^{\circ}C$ as in TFTs. These results show that sol-gel could be made a potent process for low-cost and flexible device applications by optimizing the precursors.

• 전기학회논문지
• /
• 제61권5호
• /
• pp.705-710
• /
• 2012

An anti-reflection layer (AR) is used in the solar cell to improve the amount of the irradiated light, resulting in the improvement of the performance of the solar cell. In this study, the zinc oxide (ZnO) AR is applied to the dye-sensitized solar cell (DSC) by using zinc nitrate solution. The conditions such as solution concentration and sintering temperature for fabricating the ZnO AR are changed to optimize the performance of the AR. As a result, the best performance is shown when the zinc nitrate solution with 100mM concentration is used and the sintering temperature is $600^{\circ}C$. And then, the ZnO AR formed with these optimal conditions is applied to the DSC. Consequently, a DSC with a ZnO AR had an increased current density up to 13.86$mA/cm^2$ and an enhanced efficiency of 6.32%.

• 전기학회논문지
• /
• 제65권11호
• /
• pp.1835-1839
• /
• 2016

In this study, ZnO nanorods were grown by a hydrothermal method. $SiO_2/Si$ wafers and glass were used as substrates. ~20 nm-thick ZnO thin films were rf magnetron sputtered for seed layers. The precursor was prepared by mixing zinc nitrate hexahydrate and hexamethylenetetramine (hexamine) in DI water. The concentration of zinc nitrate hexahydrate was fixed at 0.05 mol, and that of hexamine was varied between 0 mol to 0.1 mol. The reactor containing substrates and precursor was put in an oven maintained at $90^{\circ}C$ for 1 h. X-ray diffraction was carried out to analyze the crystallinity of ZnO nanorods, and a field emission scanning electron microscope was employed to observe the morphology of nanorods. Transmittance and absorbance were measured by a UV-Vis spectrophotometer. Photoluminescence measurements were conducted using 266 nm light.

• 한국미생물생명공학회:학술대회논문집
• /
• 한국미생물생명공학회 1979년도 춘계학술대회
• /
• pp.115.3-115
• /
• 1979

중금속을 함유한 13종의 질산염을 명 농도별로 첨가하여 주정효모 Saccharomyces cerevisine의 주정생산과 발효작용에 미치는 영향을 조사하였다. 1. 일반적으로 중금속을 함유한 질산염은 그 첨가량이 0.0001mo1. 보다 고농도일수록 Saccharo-myces cerevisiae의 발효작용을 점차 억제하였다. 2. Nickel nitrate, chromium nitrate들의 0.0001 moi.의 첨가는 Saccharomyces cerevisiae의 alcohol 발효작용을 약간촉진시켰다. 3. Cadmium nitrate 0.001mo1. 이상, cupric nit-rate, nickel nitrate, cobalt nitrate 0.01mo1. 이상, 그리고 silver nitrate, mercurous nitrate, manganese nitrate, zinc nitrate, lead nitrate, chromiun nitrate, ferric nitrate, bismuth nitrate 0.1mol. 의 농도에서 Saccharomyces cerevisiae 의 발효작용은 완전히 조지되었다.

• 한국응용과학기술학회지
• /
• 제34권3호
• /
• pp.487-494
• /
• 2017

질산성 질소는 수용액에서 상당히 안정하게 존재하기 때문에 제거하는 데에 있어 상당한 기술이 요구된다. 또한 저 농도의 질산성 질소는 쉽게 제거되는 반면 고농도 질산성 질소는 제거하기가 힘들다. 따라서 본 연구에서는 직경 3mm 정도의 아연 ball을 이용하여 고농도의 질산성 질소를 기체 질소의 형태로 제거하는 것을 목적으로 하였고, 다양한 반응조건에서 질산성 질소의 제거 특성을 실험하였다. 본 연구의 결과로 아연 ball을 사용하여 연속식 처리를 통한 질산성 질소의 처리효율은 약 80%정도 되었다. 하지만 폐수를 수소이온농도 2 정도의 산성 분위기로 유지시켜야하고 처리된 폐수를 중화 처리하여 방류시켜야하는 등의 문제점은 상존하고 있다.