• 한국레이저가공학회지
• /
• 제9권2호
• /
• pp.1-9
• /
• 2006

In this paper, we investigated the characteristics of fatigue fracture on TB(Tailored Blank) weldment by comparing the fatigue crack propagation characteristics of base metal with those of TB welded sheet used for vehicle body panels. We also investigated the influence of center crack on the fatigue characteristic of laser weld sheet of same thickness. We conducted an experiment on fatigue crack propagation on the base metal specimen of 1.2mm thickness of cold-rolled metal sheet(SPCSD) and 2.0mm thickness of hot-rolled metal sheet(SAPH440) and 1.2+2.0mm TB specimen. We also made an experiment on fatigue crack propagation on 2.0+2.0mm and 1.2+1.2mm thickness TB specimen which had center crack. The characteristics of fatigue crack growth on the base metal were different from those on 1.2+2.0mm thickness TB specimen. The fatigue crack growth rate of the TB welded specimens is slower in low stress intensity factor range $({\Delta}K)$ region and faster in high${\Delta}K$ region than that of the base metal specimens. The slant crack angle slightly influenced the crack propagation of the TB specimen of 2.0+2.0mm thinkness.

• Journal of Welding and Joining
• /
• 제28권1호
• /
• pp.66-71
• /
• 2010

With large specific strength and outstanding corrosion resistance and erosion resistance in sea water, titanium and titanium alloy are widely used in heat exchanger production. In particular, pure titanium demonstrates outstanding molding performance and may be considered optimal for production of heat exchanger. Since titanium is very vulnerable to oxidation and embrittlement during welding, processes with less heat input are widely used, and laser welding is widely applied by considering production performance and shield etc in atmosphere. So far, 1st report and 2nd report compared and analyzed embrittlement degrees by bead colors of weldment through oxygen and nitrogen quantitative analysis and hardness measurement, and evaluated welding performance and mechanical properties of butt welding. This study evaluated field applicability of lap welding to heat exchange plate of LPG re-liquefaction device for ships through tensile stress test, hardness test and internal pressure test etc after deducing optimal weding condition and applying to actual heat exchange plate. In bead overlap area, the experiment produced sound welds with no porosity or defect by increasing and decreasing laser power, and tensile-shear test results indicated virtually the same tension and yield strength as base metal. As a result of measuring hardness at lateral cross section and bead overlap zone of actual heat exchanger welds, hardness difference within 20Hv was produced at base metal, HAZ and weldment, and as a result of pneumatic and hydraulic pressure test, no leakage occurred.

• Journal of Welding and Joining
• /
• 제28권4호
• /
• pp.18-25
• /
• 2010

Super-duplex stainless steels (SDSS) have a good balance of mechanical property and corrosion resistance when they consist of approximately equal amount of austenite and ferrite. The SDSS needs to avoid the detrimental phases such as sigma(${\sigma}$), chi(${\chi}$), secondary austenite(${\gamma}2$), chromium carbide & nitride and to maintain the ratio of ferrite & austenite phase as well known. However, the effects of the subsequent weld thermal cycle were seldom experimentally studied on the micro-structural variation of weldment & pitting corrosion property. Therefore, the present study investigated the effect of the subsequent thermal cycle on the change of weld microstructure and pitting corrosion property at $40^{\circ}C$. The thermal history of root side was measured experimentally and the change of microstructure of weld root & the weight loss by pitting corrosion test were observed as a function of the thermal cycle of each weld layer. The ferrite contents of root weld were reduced with the subsequent weld thermal cycles. The pitting corrosion was occurred in the weld root region in case of the all pitted specimen & in the middle weld layer in some cases. And the weight loss by pitting corrosion was increased in proportional to the time exposed at high temperature of the root weld and also by the decrease of ferrite content. The subsequent weld thermal cycles destroy the phase balance of ferrite & austenite at the root weld. Conclusively, It is thought that as the more subsequent welds were added, the more the phase balance of ferrite & austenite was deviated from equality, therefore the pitting corrosion property was deteriorated by galvanic effect of the two phases and the increase of 2nd phases & grain boundary energy.

• International Journal of Automotive Technology
• /
• 제5권1호
• /
• pp.55-59
• /
• 2004

Spot welding is a very important and useful technology in fabrication of thin sheet structures such as the parts in an automobile. However, because the fatigue strength of the spot welding point is considerably lower than that of the base metal due to stress concentration at the nugget edge, the nugget size must be estimated to evaluate a reasonable fatigue strength at a spot welded lap joint. So far, many investigators have experimentally studied the estimation of fatigue strengths of various spot weldments by using a destructive method. However, these destructive methods poses problems so testing of weldments by these methods are difficult. Furthermore, these methods cannot be applied to a real product, and are time and cost consuming, as well. Therefore, there has been a strong, continual demand for the development of a nondestructive method for estimating nugget size. In this study, the effective nugget size in spot weldments have been analyzed by using thermoelastic stress analysis adopting infrared thermography. Using the results of the temperature distribution obtained by analysis of the infared stress due to adiabatic heat expansion under sinusoidal wave stresses, the effective nugget size in spot welded specimens were estimated. To examine the evaluated effective nugget size in spot weldments, it was compared with the results of microstructure observation from a 5％ Nital etching test.

• Journal of Welding and Joining
• /
• 제32권1호
• /
• pp.6-14
• /
• 2014

This paper has an aim to evaluate microstructure and fracture toughness of TMCP steel weldment applied for off-shore wind tower with the focus on the effect of heat input on the weldment with various welding processes; FCAW(13kJ/cm and 30kJ/cm), SAW(62kJ/cm), and EGW(177kJ/cm). Based on experimental results developed from this study, it was found that the impact toughness of top side for TMCP steel weldments with heat input up to 62 kJ/cm satisfied the required minimum value except the EGW(177kJ/cm). The heat input and microstructure are the main factors of impact toughness. The heat input of 13kJ/cm on back side with low heat input increased the amount of grain boundary ferrite which has low impact toughness, and heat input of 177kJ/cm on top side is significant enough to produce the austenite grain growth. The compositions and sizes of inclusions which are the dominant factors for the formation of acicular ferrite were analyzed by OM and EDS. As the heat input increased, the inclusions also grew and a nucleation site decreased. The size of nonmetallic inclusions and the crack width was nearly similar, therefore the inclusions were related with the crack propagation.

• 대한조선학회논문집
• /
• 제38권4호
• /
• pp.75-82
• /
• 2001

건조 후 수행하는 수압시험 또는 화물의 적재 등과 같은 정하중은 파랑변동하중에 비하여 선체구조물에 상당히 큰 응력을 유발한다. 이러한 정하중이력에 의하여, 선체구조물의 응력집중으로 인해 피로강도가 문제되는 용접이음부에서는, 재료의 탄소성 거동에 의하여 초기용접잔류응력이 상당히 이완될 것으로 예상된다. 따라서, 이러한 용접이음부의 피로강도를 평가할 때에는 이완된 잔류응력의 영향을 고려하는 것이 보다 합리적이다. 본 연구에서는 선체구조물의 여러 가지 용접형태 중 Padding plate가 용접된 형태에 대하여 정하중이력($0.5{\sigma}Y,\;0.85{\sigma}Y$)에 의한 초기 용접잔류응력의 변화를 측정하며, 잔류응력의 변화가 피로강도에 미치는 영향을 검토한다.

• Corrosion Science and Technology
• /
• 제16권2호
• /
• pp.49-58
• /
• 2017

Many research efforts on the effect of nitrogen on the corrosion resistance of stainless steels have been reported, but little research has been conducted on the effect of nitrogen for the weldment of stainless steels by the seal-weld method. Therefore, this work focused on the determining the corrosion resistance of tube/tube sheet mock-up specimen for sea water condensers, and elucidating the effect of shielding nitrogen gas on its resistance. The pitting corrosion of autogenously welded specimen propagated preferentially along the dendritic structure. Regardless of the percent of shielding nitrogen gas, the analyzed nitrogen contents were very much lower than that of the bulk specimen. This can be arisen because the nitrogen in shielding gas may partly dissolve into the weldment, but simultaneously during the welding process, nitrogen in the alloy may escape into the atmosphere. However, the pitting resistance equivalent number (PREN) of the interdendrite area was higher than that of the dendrite arm, regardless of the shielding gas percent; and the PREN of the interdendrite area was higher than that of the base metal; the PREN of the dendrite arm was lower than that of the base metal because of the formation of (Cr, Mo) rich phases by welding.

• 한국가스학회지
• /
• 제11권2호통권35호
• /
• pp.31-36
• /
• 2007

가스 냉온수기용 STS 304 배관 용접부의 부식특성을 연구하기 위하여, 0.5M $H_2SO_4+0.01M$ KSCN 수용액 중에서 전기화학적 분극시험, 금속조직시험 과 경도시험을 실시하여 STS 304배관 용접부의 양극분극거동, 인가전위에 따른 부식거동, 용접부의 금속조직 및 경도거동를 고찰하였다. 다음과 같은 결론을 얻었다. 1) 임계양극전류밀도는 모재보다 용접열영향부에서 많이 배류되고, 기본부동태전위는 모재보다 용접열영향부에서 더 높게 된다. 2) 부동태전류밀도는 모재보다 용접열영향부에서 더 많이 배류되고, 부동태영역은 용접열영향부보다 모재가 더 크게 된다. 3)인가전압에 의한 용접열영향부의 전류밀도는 모재의 전류밀도보다 더 많이 배류된다.

• 대한기계학회논문집
• /
• 제11권2호
• /
• pp.314-321
• /
• 1987

본 논문에서는 용접열영향부(heat affected zone: HAZ)의 인성에 영향을 미치 는 인자중에서 잔유응력의 영향은 중대한 문제로 주목되고 있으며, 이로 인한 용접재 의 기계적 성질의 저하를 경함하기 위한 방법으로 용접후열처리(post weld heat trea- tment: PWHT)에 의한 제거방법을 이용하고 있다.그러나 이 열처리는 보톤 600.deg. C 이 상의 고온에서 실현되기 때문에 열처리과정에서 템퍼링(tempering)효과로 인한 HAZ의 열화가 때때로 발생하고 있어서 용접 시공상 문제로 되고 있다. 또한 PWHT시에는 가 열중이나 냉각중에도 열처리효과가 진행되고 있다고 볼 수 있으므로, PWHT가열속도는 기계적 성질의 개선이라는 이유외에 경제적 측면에서도 중요시 된다. 특히 용접조직 의 포화는 파괴의 양식에 직접반영되어, 파면형태의 차로 나타나므로, 본 조직의 포화 와 관련시켜 검토하기 위하여 열처리된 HAZ를 대상으로 작용된 응력의 크기와 가열속 도가 HAZ의 파괴인성에 어떠한 영향을 미치는지를 COD파괴인성시험과 미소경도측정, 그리고 주사전자현미경관찰을 통하여 고찰하였다.

• Journal of Welding and Joining
• /
• 제32권4호
• /
• pp.1-9
• /
• 2014

A quantitative understanding on the effect of the welding conditions on weld joint dimensions and weld thermal cycle is difficult through experimental studies alone. The experimental realization of temperature distribution in the weld pool is proved to be extremely difficult due to the small size of welds, high peak temperature and steep temperature gradients in weld pool. This review deals with the heat transfer and fluid flow analysis to understand the parametric influence of a single wire submerged arc welding (SAW) and multi-wire SAW processes on the weld bead dimensions, temperature and fluid flow distribution in the weldment.