Re-distribution of Welding Residual Stress Due to Tensile Pre-load and Its Effects on Fatigue Strength in Padding Plate Weldment

Padding plate 용접구조의 인장 정하중 이력에 의한 용접잔류응력 변화 및 피로강도에의 영향

Static loadings on ship structure induced either by water pressure before service such as a tank test and ballasting or by cargo pressure during first laden voyage cause relatively much greater stress than dynamic loadings induced by wave. With these static pre-loadings, the initial residual stresses around welded joint, where fatigue strength is concerned(in most cases, where stress concentration occurs) are expected to be shaken-down in a great extent by the elasto-plastic deformation behavior of material. Therefore, it is more resonable to assess the fatigue strength of ship structure with S-N data which have taken into account the effect of shaken-down residual stresses(re-distributed stresses) on the fatigue strength. In this research work, the re-distribution of residual stresses by the tensile pre-loading is measured using an ordinary sectioning method for specimens of padding plate weldment. Fatigue tests are performed also to evaluate the fatigue strength of the both as-welded and pre-loaded specimens.

건조 후 수행하는 수압시험 또는 화물의 적재 등과 같은 정하중은 파랑변동하중에 비하여 선체구조물에 상당히 큰 응력을 유발한다. 이러한 정하중이력에 의하여, 선체구조물의 응력집중으로 인해 피로강도가 문제되는 용접이음부에서는, 재료의 탄소성 거동에 의하여 초기용접잔류응력이 상당히 이완될 것으로 예상된다. 따라서, 이러한 용접이음부의 피로강도를 평가할 때에는 이완된 잔류응력의 영향을 고려하는 것이 보다 합리적이다. 본 연구에서는 선체구조물의 여러 가지 용접형태 중 Padding plate가 용접된 형태에 대하여 정하중이력($0.5{\sigma}Y,\;0.85{\sigma}Y$)에 의한 초기 용접잔류응력의 변화를 측정하며, 잔류응력의 변화가 피로강도에 미치는 영향을 검토한다.