• Journal of Ocean Engineering and Technology
• /
• v.17 no.1
• /
• pp.55-60
• /
• 2003

The effect of size and volume fraction of ceramic particles, with sliding velocity on the wear properties were investigated for the metal matrix composites fabricated by the pressureless infiltration process. The metal matrix composites exhibited about 5.5 - 6 times the wear resistance compared with AC8A alloy at high sliding velocity, and by increasing the particle size and decreasing the volume fraction, the wear resistance was improved. The wear resistance of metal matrix composites and AC8A alloy exhibited different aspects. Wear loss of AC8A alloy increased with sliding velocity, linearly : whereas, metal matrix composites indicated more wear loss than AC8A alloy at the slow velocity region. However, a transition point of wear loss was found at the middle velocity region, which shows the minimum wear loss. Further, wear loss at the high velocity region exhibited nearly the same value as the slow velocity region. In terms of wear mechanism, the metal matrix composites generally exhibited abrasive wear at slow to high sliding velocity； however, AC8A alloy showed abrasive wear at low sliding velocity and adhesive and melt wear at high sliding velocity.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2002.10a
• /
• pp.379-384
• /
• 2002

The effect of size and volume fraction of ceramic particles with sliding velocity on the wear properties were investigated for the metal matrix composites fabricated by pressureless infiltration process. The particulate metal matrix composites exhibited about 5.5 - 6 times of excellent wear resistance compared with AC8A alloy at high sliding velocity, and as increasing the particle size and decreasing the volume fraction the wear resistance was improved. The wear resistance of metal matrix composites and AC8A alloy exhibited different aspects. Wear loss of AC8A alloy increased with sliding velocity linearly. whereas metal matrix composites indicated more wear loss than AC8A alloy at slow velocity region, however a transition point of wear loss was found at middle velocity region which show the minimum wear loss, and wear loss at high velocity region exhibited nearly same value with slow velocity region. In terms of wear mechanism, the metal matrix composites exhibited the abrasive wear at slow to high sliding velocity generally, however AC8A alloy showed abrasive wear at low sliding velocity and adhesive and melt wear at high sliding velocity.

• Elastomers and Composites
• /
• v.56 no.1
• /
• pp.12-19
• /
• 2021

The abrasion behaviors of NR/BR blend vulcanizates were investigated using NR/BR = 100/0, 80/20, and 60/40 compounds. The abrasion test was performed using a laboratory abrasion tester (LAT) at slip angles of 1° and 7°. The size distributions of the wear particles and the abrasion rates were examined according to the rubber compositions and slip angles. The most abundant wear particles at the slip angle of 1° were sizes above 1,000 ㎛, irrespective of the rubber composition. The most abundant wear particles at 7° slip angle had sizes in the range of 212-500 ㎛, except for the NR = 100 sample. The wear particle size distribution shifted to a smaller size as the slip angle and BR content increased. The abrasion rate at 7° was much larger than that at 1° slip angle. Furthermore, the abrasion rate was notably increased by adding BR to NR.

• Elastomers and Composites
• /
• v.41 no.3
• /
• pp.194-204
• /
• 2006

The effects of the particle size and the structure of carbon blacks on the friction and the wear behavior of filled natural rubber were investigated in this study. The particle size and the structure of carbon black had a significant effect on the wear rates and the worn surface pattern, and the effect of them on abrasion resistance should be considered for the optimum design of desired wear properties. Ten carbon blacks with various sizes and structures are mixed with natural rubber in order to investigate the effects on the wear rate ($W_R$). The friction and the wear behavior were examined by self-made blade type friction-wear abrader, and the ,elation with characteristic parameter (${\psi}=\sqrt{{N_2^2}+{DBP^2}}$), obtained from the particle size and the structure, was studied. The wear rate ($W_R$) had a Power Law relation with the frictional work ($W_f$) and it was inversely proportional to the characteristic parameter of carbon black. It means that smaller particle size and better structure development of carbon black resulted in improved abrasion resistance.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.201-202
• /
• 2002

The abrasive wear behaviour of $Al_2O_3$ particle-reinforced aluminium composite was investigated. The wear rate of the composite and the matrix alloy has been expressed in terms of the applied load, sliding distance and particle size using linear factorial design approach.

• Proceedings of the KSR Conference
• /
• 2004.10a
• /
• pp.704-709
• /
• 2004

The wear behavior and the mechanical property of Cu-$TiB_2$ composites were examined. Cu-$TiB_2$ composites were fabricated by hot extrusion and cold drawing with $TiB_2$ contents(1$\∼$5vol.$\%$) and the size of $TiB_2$ particles(10$\mu$m and 20$\mu$m). The pin-an-disk wear test was carried out under dry sliding wear conditions which loads varied with from 20N to 100N. At the time, counterpart wear material used SM45C. The experimental results showed that the friction coefficient and wear rate decreased with increasing the $TiB_2$ contents and decreasing the size of $TiB_2$ particle. Also, the depth of plastically deformed zone decreased with increasing the $TiB_2$ contents and decreasing the size of $TiB_2$ particle.

• Journal of Powder Materials
• /
• v.13 no.6 s.59
• /
• pp.421-426
• /
• 2006

The microstructural and mechanical properties of Al-Si alloyed powder, prepared by gas atomization fallowed by hot extrusion, were studied by optical and scanning electron microscopies, hardness and wear testing. The gas atomized Al-Si alloy powder exhibited uniformly dispersed Si particles with particle size ranging from 5 to $8{\mu}m$. The hot extruded Al-Si alloy shows the average Si particle size of less than $1{\mu}m$. After heat-treatment, the average particle size was increased from 2 to $5{\mu}m$. Also, mechanical properties of extruded Al-Si alloy powder were analyzed before and after heat-treatment. As expected from the microstructural analysis, the heat-treated samples resulted in a decrease in the hardness and wear resistance due to Si particle growth. The friction coefficient of heat-treated Al-Si alloyed powder showed higher value tough all sliding speed. This behavior would be due to abrasive wear mechanism. As sliding speed increases, friction coefficient and depth and width of wear track increase. No significant changes occurred in the wear track shape with increased sliding speed.

• Korean Journal of Materials Research
• /
• v.12 no.5
• /
• pp.407-413
• /
• 2002

Eutectic high chromium cast irons containing 17%Cr and 26%Cr were produced for this research by making each of them solidify unidirectionally. Abrasion wear test against SiC or $Al_2$O$_3$bonded paper was carried out using test pieces cut cross-sectionally at several distances from the chill face of castings. The wear resistance was evaluated in connection with the parameters such as eutectic colony size($E_w$), area fraction of boundary region of the colony($S_B$) where comparatively large massive chromium carbides are crystallized and, average diameter of chromium carbides in the boundary region($D_c$). The wear rate($R_w$), which is a gradient of straight line of wear loss versus testing time, was influenced by the type and the particle size of the abrasives. The $R_w$ value against SiC was found to be larger than that against A1$_2$O$_3$under the similar abrasive particle size. In the case of SiC, the $R_w$ value increased with an increase in the particle size. The $R_w$ value also increased as the eutectic colony size decreased, and that of the 17%Cr iron was larger than that of the 26%Cr iron at the same $E_w$ value. Both of the $S_B$ and $D_c$ values were closely related to the $R_w$ value regardless of chromium content of the specimens. The $R_w$ values of the annealed specimens were greater than those of the as-cast specimens because of softened matrix structures. As for the relationship between wear rate and macro-hardness of the specimens, the hardness resulting in the minimum wear rate was found to be at 550 HV30.

• Journal of the Korean Ceramic Society
• /
• v.34 no.8
• /
• pp.854-860
• /
• 1997

The tribological property of ceramics is very important for use in seal rings, pump parts, thread guides and mechanical seal, etc. In the present study, which RBSC/graphite composites were manufactured by adding graphite powders with different particle sizes to mixtures of SiC powder, metallic silicon, carbon black and alumina, effects on the tribological property of each RBSC/graphite composite was investigated in accordance with the particle size of the added graphite powder. The water absorption, the bending strength and the resistance for the friction and wear were measured, and the crystalline phase and the microstructure were respectively examined by using XRD and SEM. In case that the particle size of the graphite powder was fine(2${\mu}{\textrm}{m}$), the formation of $\beta$-SiC was accelerated, thereby making the increase of the bending strength and the decrease of the water absorption, but no improvement for the tribological properties. Furthermore, in case that the particle size of the graphite powder was some large(88~149${\mu}{\textrm}{m}$), the formation of $\beta$-SiC was not accelerated, to thereby make the decrease of the bending strength and the increase of the water absorption, but the improvement for the tribological property of only the composite having the graphite powder of 20 vol%. In addition, in case that the particle size distribution of the graphite powder was large (under 53 ${\mu}{\textrm}{m}$), there was no improvement for every properties. However, the composites, which the graphite powder with the particle size of 53~88 ${\mu}{\textrm}{m}$ was added in 10~15 vol%, had the most increased resistance for the friction and wear which show the worn out amount of 0.4~0.6$\times$10-3 $\textrm{cm}^2$, and the value of the bending strength is 380~520 kg/$\textrm{cm}^2$.

• Elastomers and Composites
• /
• v.58 no.4
• /
• pp.179-190
• /
• 2023

The effect of the particle size and silica structure on the wear behavior of Silica/Styrene-Butadiene Rubber (SBR) compounds was investigated using a blade-type abrader and the findings were compared with those obtained with an Akron abrader. The compensated characteristic parameter (Ψ_c), which was the contributory factor of the combined effect of the particle size and filler structure, was introduced. This parameter was found to exhibit a linear relationship with the Young's modulus. The Young's modulus correlated more with Ψ_c than the uncompensated characteristic parameter (Ψ) modeled for carbon black. The wear rate and volume loss measured using a blade-type abrader and Akron abrader were respectively observed to be inversely proportional to Ψ_c, that is, the wear resistance of Silica/SBR compound improved as the particle size became smaller and the silica structure became intricate. The coefficient of determination (R²) obtained from the linear relationship between Ψ_c and wear rate was higher than those between Ψ_c and volume loss for the Silica/SBR compound. Thus, the blade-type abrader exhibited high potential to be used for accurately evaluating the effect of particle size and structural properties of silica on the wear behavior of SBR compounds.